Search Documents

By C. H. Lee, R. Maddin

The diffusion rates of Ag110 in cylindrical single crystals of 99.99 pct pure silver, which were twisted to a total surface strain of 0.91 during the diffusion anneal at temperatures of 700°, 750°, and 800°C, were measured by sectioning and counting as a function of the strain rates. The ratio of the diffusivities while strain ing occurred (Ds) to those of the unstrained specimens varies linearly with the rate of twisting and attains values of near 100 for some of the rates used. The enhancement of diffusion by straining is inversely proportional to the temperature at which diffusion occurs. The activation energy for diffusion determined from the data plotted as a function of the rate of twisting decreases from 44,090 cal per mole for zero strain, to an asymptotic value of 21,000 cal per mole for the strain rates of 22 x it)"5 see-l. Qualitative explanation for the observations based on the generation of nonequilibrium number of defects by plastic deformation will be discussed. The initial research of Buffington and cohen1 on self-diffusion in a iron under compressive stresses contributed the first quantitative information concerning the effect of applied stresses on diffusion. These results were obtained from radioactive Fe55 plated on one of the horizontal surfaces and compressing the large-grained specimens while the diffusion-anneal was occurring. Enhancement of diffusion of a maximum of seventeen times was observed provided the strain was in the tertiary stage of creep and the rates of straining were at least as fast as rates used in the normal creep test. On the other hand, Darby, Tomizuka, and Balluffi,2 extending silver single crystals up to 30 pct elongation at rates of straining about equal to those used by Buffington and Cohen observed no effect. For the past two and a half years at the University of Pennsylvania, we have been investigating the effect or torsional strains on self-diffusion in silver single crystals. If enhancement is observed as has been reported1 a possible explanation may be based upon the generation of fairly large numbers of point defects and their role in the diffusion process. Hence, since torsion should produce an abundance3 of point defects, an increase in the diffusivity while the crystal is being twisted should easily be measured. EXPERIMENTAL PROCEDURE Our research uses single crystals of silver prepared from 99.99 Ag by the Bridgman method in a dynamic vacuum of less than 25 µ. As grown, they are about 25 cm long by 1.3 cm in diam. The crystals are cut into 7.5 cm lengths with a jeweler's saw and machined to the shape shown in Fig. 1. The test length of the crystal is machined to a 0.6 cm diam after which the ends are masked and the test section etched heavily in HNO3, and KCN:(NH4),S2Os , solution to remove the effects of machining. The specimen is then annealed in vacuum for 8 to 12 hr at 800°C to remove any residual stresses and also to recrystallize the end sections. The recrystallized ends are necessary since experiments showed that single-crystalline end sections are too soft to transmit the desired torque. Occasionally, recrystalliza-

Jan 1, 1960

By G. S. Rice

IT is evident from Professor Louis' remarks that he holds a different opinion on certain phenomena connected with a specific type of surface subsidence from mining than is held by many engineers in the United States. The question which appears to be at issue is whether or not the line or plane of "draw" produced in ground movement resulting from extraction of pillars may, under certain conditions, be vertical or even inclined toward the workings rather than inclined for- ward over the unworked mineral, as it is universally agreed occurs in mining by the longwall advancing method. In discussing this case it is well to take the simplest condition, such as specified by Professor Louis, of a flat bed, whether it be coal, iron or other mineral, where the overburden is stratified rock and where there is no overlying quicksand. Professor Louis says in effect that his experience is that the ultimate angle of draw is always positive and inclined 5" to 15" from the perpendicular over the unwrought mineral. My experience under Illinois coal-mining conditions is that .'where longwall advancing is used the draw is always positive as Professor Louis describes it, but that in extracting of panels by withdrawal of pillars, the ground movement is manifested, after the first roof' beam break, by the forming of an unstable dome over the goave. Then subsequently, by the falling of individual slabs from the under side, the dome gets larger and higher until it breaks through to the surface of the rock., Up to this time, arch stresses buttress the rocks above the solid coal or mineral. When, however, after. the dome breaks through and the central hole - #enlarges so the arch is no longer sufficiently supported -the stratified rocks cantilever out .from over the solid unworked mineral and tend to break off in masses triangular in vertical cross-section, until the broken loose material, sliding down against the solid rock, .has such a thrust that it balances the tendency ,for the solid stratified rock to break away and slide toward the excavation.

Jan 1, 1929

By Eugene S. Meieran

The effects of methods of crystal growing, wafer sawing, polishing, routine handling, diffusion, and epitaxial growth on the defects in GaAs are reviewed and studied using reflection and transmission X-ray topographic techniques. In general, it was found that boat-grown crystals exhibited fewer defects than Czochralski crystals, although all crystals showed large numbers of precipitates visible when examined in the electron microscope. Mechanical surface treatments such as sawing and mechanical polishing introduce damage to a depth of about 5 µ, most of which can be removed by suitable chemical or chem-mechanical polishing. In addition, defects can be introduced through routine handling of wafers, for example with metallic tweezers. These defects can be quite severe, and have been observed 20 µ below the wafer surface. Defects can also be introduced through diffusion and epitaxial growth. These defects, which include precipitates, growth pyramids, stacking faults, dislocations, and so forth, can be detrimental to device fabrication. It is shown that wafers or films which appear defect-free optically can contain defects visible in the X-ray topographs. WHILE the use of GaAs in the semiconductor industry has increased very rapidly in the last few years, due mainly to the recent development of many important GaAs devices,1,2 the major limit to the production of commercial quantities of many GaAs devices remains a severe lack of suitable materials technology. This lack is apparent in two critical areas. First, production quantities of high-quality GaAs crystals, reproducibly doped and precipitate-free, simply are not available commercially, although some reasonable quality material is available on a limited first-come, first-serve basis. Second, in comparison to silicon technology, little is known about the effects of processing variables on the defects either present in as-grown GaAs or introduced through processing and handling of wafers. These areas are now receiving some attention from semiconductor device manufacturers, who are studying defects in GaAs in order to better understand how either to prevent their occurrence or to cope with their existence. Most investigations of the defects in GaAs have been made by optical microscopy3-5 or transmission electron microscopy techniques.'-' Recently, however, the imaging techniques of X-ray topography, electron mi-croprobe analysis, and scanning electron microscopy are being applied to the study of GaAs.9-14 In the case of X-ray topography, a one-to-one image is obtained that must be photographically enlarged. In compensa- tion, the defects within entire wafers may be imaged by simple scanning (Lang technique15) if the wafer is reasonably perfect, or by using the scan oscillation technique developed by Schwuttke16 if the wafer is warped or distorted. The purpose of this paper is to both review and extend the general application of X-ray topographic techniques to GaAs. Emphasis will be placed on the effects of growth and process variables on the quality and perfection of both bulk and epitaxial GaAs. Reference to optical or electron microscopy results will be made when useful. Since the effects on defects of a wide variety of processing variables such as crystal growing, sawing, polishing, diffusion, and epitaxial growth will be somewhat superficially reviewed, a fairly extensive bibliography of the most important recent results in these areas is included. However, for completeness, important defects will be illustrated here, although such defects have been previously shown by others. While this paper is concerned with defects rather than with the physics of X-ray scattering, the mechanisms of contrast formation in the topographs will of necessity be briefly mentioned. EXPERIMENTAL GaAs crystals, both boat-grown18 and Czochralski-grown,'8 containing a variety of dopants of various concentrations, were purchased from outside vendors. Wafers were sliced from the crystals using a Hamco ID saw and were mechanically polished using 1 µ diamond paste. Chem-mechanical polishing was done in bromine-methanol as described by Sullivan and Kolb.18 Chemical polishing was done using a modified sulfuric-peroxide solution, 11 parts H2SO4, 1 part 30 pct H2O2, 1 part DI water.5 Zinc diffusion was carried out in a closed tube, using a 10 pct Zn-In source at 825°C for 1 hr. Oxide masking techniques were used to select the area to be diffused. Epitaxial wafers were either purchased or prepared here. All epitaxial runs prepared here were carried out using a Ga-GaAs-AsC13 source in a closed tube at a substrate temperature of 750°C. Wafers were chem-mechanically polished and gas-etched prior to deposition. The X-ray topographs were taken on a Krystallos Lang camera, operating in the transmission scanning geometry (Lang technique15) or in the reflection scanning geometry (modified Berg-Barrett technique20,21). MoKa, radiation was used for all transmission topographs using a Jarrell-Ash 100-µ spot focus. CuKal radiation was used for all reflection topographs using a General Electric CA-7 1-mm spot focus X- ray tube. Topographs were printed from an intermediate contrast inversion film, so the contrast shown in all figures here is the same as that of the original 50-µ-thick emulsion L4 Iiford nuclear plate used to record the topograph.

Jan 1, 1969

By C. S. Sivil

To modern civilization the platinum metals are of inestimable value. Their distinctive properties, both physical and chemical, render them indispensable in an age in which the processes of the laboratory are becoming an essential part of the daily life of the world. Generally, their function, though vital to particular processes, is not spectacular, and so remains unknown to all except the operators. EARLY METHODS OF MANUFACTURE The properties of platinum were recognized as of prime importance for scientific work at. a very early date, probably between 1750 and 1760. The difficulty of making articles from it seemed almost insurmountable, because no means of attaining the temperature necessary to melt it were known at that time. It is true that solid platinum could be obtained by fusing the metal with a more volatile metal such as arsenic, which was subsequently driven off by baking, but such a method, at its best, would give only a very brittle product, which was totally unsuitable for the purposes for which it was intended. Little, if any, progress could be made until it was discovered that platinum sponge, heated to white heat and hammered in an iron or clay mold, would metallize and retain the shape of the mold. This was a process that could not be wholly satisfactory but from it developed the method of pressing the sponge in a mold and forging it at white heat into wire or sheet. At present a somewhat similar process must be used for fabricating articles of tungsten, molybdenum and other metals of high fusing point, as with these metals we face today the same problems that the scientists of the eighteenth century encountered with platinum, but possibly the next significant advance in the metallurgy of these metals will be the devising of means to melt and cast them.

Jan 1, 1931

By W. F. Hower, W. Brown

Large-scale sand consolidation tests were conducted in an effort to determine the reasons for the successes and failures of this method of sand control. Several different consolidating materials were used in treating both clean and bentonitic sands that were packed in a chamber having a capacity of 3.3 cu ft. The results were essentially the same for all of the different consolidating materials, The data show that low-viscosity consolidating materials pumped at a relatively slow rate gave the best results. Where the formation has produced sand, the treating fluids can compress the formation, thus permitting the channeling of fluids to another horizon. Pressure-packing these zones before attempting to consolidate is recommended. Sands containing more than 4 per cent of water-swelling clays are not good candidates for consolidation. It is indicated that loose sand, particularly when it is bentonitic, can be fractured during the placement of the treating fluids. INTRODUCTION Sand production in oil and gas wells has plagued the industry for many years, and numerous cures for this problem have been suggested. Most methods have been successful to a certain degree, but the great variety of well conditions that exist in the different areas has magni- fied the problem and limited the successful use of the various systems. Four review papers1-4 present a wealth of information concerning the degrees of success that have been obtained by the different sand-control methods. The bridging of sand grains by the use of gravel packs and screens has been quite successful. However, these methods do not leave the casing clear for all types of multiple completions, and the cure does not last for the production life of the well in some instance:;. The control of loose sands by sand consolidation with resins has never been as successful as desired. It has always been hoped that such a treatment would eliminate all sand problems for the life of the well, but. initial applications, starting in the middle 1940's, were only moderately successful. Lott, et a1,3 reported a success ratio of approximately 50 per cent and made the following conclusions. The highest percentage of successes were obtained where: a. Consolidation of a zone was made at the time of initial completion or prior to the production of sand. b. The interval treated was less than 12 ft in length. c. Between 30 and 50 gill plastic/ft of producing interval was displaced through the perforations. REASONS FOR SAND CONSOLIDATION FAILURES Our own experiences in the field of sand consolidation point toward the following conditions as the major reasons for the failure of sand consolidation attempts. 1. Mud-plugged perforations and mud invasion of the formation. 2. Sand in the casing covering all or part of the perforations. This sand could be either formation sand or one of the coarser sands used as propping agents in hydraulic fracturing. 3. Holes in the casing. 4. Channels behind the casing. 5. Attempting to treat too long a perforated section. 6. Too high a percentage of water-swelling clays in the formation. 7. Formations that have produced sand. Recent attempts were made to treat perforated sections ranging from 10 to 30 ft, in wells that have produced sand, by using a straddle packer that was raised and lowered through the perforations as the consolidating material was being pumped. In most instances, the pressure required to pump fluid into the formation varied considerably as the tool was raised and lowered. This suggested the possibility that significant differences in permeability were present or that only part of the formation had produced sand. There were times when a sudden break in pressure indicated that a fracture was being formed. Research conducted several years ago concerning the problem of the control of water in air and gas drilling indicated that shale sections could be fractured quite easily. In addition, it was determined that it was easier to pump fluids into shale bodies by fracturing the shale itself, or the interface between the shale and sand, than to pump into a fluid-saturated formation. Formations that produce sand are usually adjacent to shale bodies and frequently have shale streaks of various thicknesses inter-bedded in the sand. Therefore, where shale is exposed to fluid pressure it

By Charles C. Fatino, Joel S. Hirschhorn

Loose compacts of strained and annealed stainless-steel powders were sintered at various temperatures and times to determine the effect of residual strains on the sintering behavior. The atomized powders were prepared by annealing, ball milling, and rean-nealing. The residual strains and domain size were determined by a Fourier analysis of X-ray diffvaction dala. The specimens were prepared by siwzultaneously sintering cylinders of both strained and unstrained powder. The evaluation of the sintered compacts included density measurements, metallographic examinations, and analyses of X- ray diffraction data. The results of these studies reveal a definite increase in sintered density and sintering rate for the strained powders. THE pressure compacting of metal powders causes deformation of the particles, mechanical interlocking, and increased contact area. After the deformation, severe residual strains remain in these particles. The subsequent contributions of these strains to the sintering process have been considered to be negligible, since the recovery and recrystallization temperatures usually occur prior to the temperature required for the sintering process. Sintering is con-sidered to be the process by which the powders are transformed into solid compacts at temperatures below their melting points. The sintering operation for stainless steel usually takes place in the range of 2050" to 2400°F (0.84 to 0.95 T,, where T, is the absolute melting point or liquidus temperature) while the temperature required for recovery is approximately 1800°F (0.75 T,). However, it has been shown for several metal powders that densification becomes significant in the range of 0.35 to 0.45 T,.' It is the purpose of this study to determine what effect residual strains have upon the sintering behavior of stainless-steel compacts. Loose compacts were selected for study in order to isolate the strain contributions and eliminate the variables inherent in sintering of pressure-formed compacts. Additional variables were minimized by using only one mesh size, one composition, one particle shape, and also by simultaneously sintering both types of powder. Very little work has been carried out previous to the present study to delineate the effect of strains on sintering behavior. Lenel et 01.2 observed that residual stresses in copper compacts caused shrinkage at comparatively low temperatures. Delisle3 loose-sintered ball-milled electrolytic iron and observed that bonding among particles began at a lower temperature as compared to the behavior of annealed powder. Increased densification of ball-milled oxide powders has also been noted.4'5 EXPERIMENTAL PROCEDURES Powder Preparation. The powder used for this study was a commercial-type 316L stainless steel made by the atomization process. A typical chemical analysis is: C- 0.025 pct Mo- 2.2 pct Cr-18.6 pct Ni-12.5 pct Fe—Balance The atomizing process is essentially the rapid freezing of liquid droplets. This nonequilibrium cooling causes coring to occur and two distinct phases are present within the solid particle, the austenitic phase and the ferritic phase. Due to the presence of this ferritic phase, the particles tended to fracture as well as become cold-worked during the subsequent ball-milling operation. (It was also found that this type of cooling produced a broadened and shifted

Jan 1, 1968

By L. F. Mondolfo, B. E. Sundquist

The crystallographic orientation relationships resulting when lead is nucleated from the liquid by Ni, Cu, Ag, and Ge were determined. For each nucleating agent several definite orientatioz relationships were found. These relationships seemed to be controlled by good symmetry relations and low crystallographic disregistry between mating planes. For any given nucleating agent the under colling for nucleation was found fairly constant and independent of the orientation relationship and consequent disregistry. It was also found that, upon re melting and refreezing the Pb, the orientation relationship was changed. These findings prove that crystallographic disregistry is not the controlling factor in heterogeneous nucleation from the liquid. The results of this investigation tend to confirm the theory presented in a preceding paper that heterogeneous nucleation starts with the formation of an adsorbed layer of nucleated metal on the nucleat-ing impurity. Evidence is given that cavities in the nucleating agent act as centers of nucleation. IT has long been known' that solid extraneous particles are active in catalyzing phase transformations that occur in a system, particularly condensation and crystallization. It is well established that these heterogeneities act as catalysts by providing surfaces upon which nuclei of the precipitating phase can form with activation energies smaller than those required for homogeneous nucleation. Numerous investigations have shown that in this process of heterogeneous nucleation: a) the nucleus forms with one, or several, definite crystallographic orientation relationships with the nucleating phase2-4 and b) that there is a small range of undercoolings or super saturations characteristic of the nucleation of a given solid on a given Substrate.5-10 Turnbull and vonnegut11 have developed a theory based on theories developed by Volmer12 and Turn-bull and Fisher1= for heterogeneous nucleation from gases and liquids, that relates the super saturation or undercooling required for nucleation to the dis-registry between the lattices of the nucleus and the nucleating agent. This theory predicts that nucleation should occur with the orientation relationship between the nucleus and nucleating agent that minimizes the disregistry. Further, it predicts that the undercooling or super saturation necessary for nucleation should be a function of the disregistry. Numerous investigations have dealt with the orientation relationships resulting from the condensation of vapors onto crystalline solid substrates2,3 and a few with the nucleation of one phase by a second phase in solidification4,14. Others have dealt with the supersaturation8-10 and undercooling5-7 associated with nucleation in condensation and solidification respectively. However, there is virtually no report that gives both of these factors for the same system. In this investigation a study was made of the undercoolings and orientation relationships resulting when Pb is nucleated from the liquid by Ni, Cu, Ag, and Ge. It was the purpose of this investigation to check the Turnbull-Vonnegut theory, i.e., the importance of crystallographic disregistry between nucleating catalyst and nucleated metal. The results indicate that disregistry is not an important factor in nucleation and that the nucleation process is probably somewhat more complex than current theories suggest. EXPERMENTAL PROCEDURE Small single crystals of nickel, copper, silver, and germanium were prepared from materials of four to five nines purity, and the Pb used was also 99.999+ pet pure. Cu and Ag single crystals were prepared by sealing small chips of Cu or Ag in an evacuated quartz capsule and heating the capsule at 2000°F for 1 hr before cooling. Nickel crystals of 200 diam were also prepared in evacuated quartz capsules, but melting was done by heating the capsules in an oxy-acetylene flame for a few minutes. These spheres were invariably polycrystalline so

Jan 1, 1962

By David W. Mitchell

WHILE pure magnesium does not corrode rapidly the presence of even very small quantities of certain other metals accelerates corrosion remarkably. Because magnesium is such an electropositive metal (E° = +2.34 volts)' the presence of substances that permit galvanic activity is extremely undesirable. It is stated that as little as 0.017 pct of iron in magnesium causes a marked increase in the corrosion rate.2 Magnesium and its alloys are commonly melted in iron or steel pots; consequently the commercial metal has the opportunity to pick up iron if it has that tendency. Quantitative data on the solubility of iron in magnesium are of practical as well as of academic interest. Some magnesium alloy castings tend to have large grain size unless suitable treatment is given to the liquid metal just prior to casting. One method of grain refinement consists of "superheating" the metal just prior to casting. "Superheating" is heating to a temperature 100 to 200°C above the casting temperature and holding for a short period of time. Superheated metal has a much finer grain than unsuperheated metal. A satisfactory explanation of this phenomenon has not been forthcoming. One hypothesis attributes the grain refinement in the superheated metal to precipitation of some phase that is miscible at the temperature of superheat but not miscible just below the casting temperature and which is thought to provide nucleating centers for crystallization. This phase, if the foregoing hypothesis is correct, would probably be a metal or an intermetallic compound. Of the metals likely to be found in magnesium alloys, iron is one of the most likely candidates for the role of grain refiner for iron occurs in small quantities in all commercial magnesium and magnesium alloys. A. Beck' states that magnesium, in either the liquid or the solid state, cannot dissolve iron and that iron exists as a finely divided suspension which does not settle out because of its extreme fineness. Beck also presents a micrograph showing a large iron dendrite in magnesium but does not comment on the crystallization of iron from a solution supposed to contain none. It is doubtful that dendrite formation from suspended iron would be possible. This suspension theory is the basis of patents4 covering the removal of iron from magnesium by allowing the iron particles to act as nuclei for the formation of primary magnesium crystals which can be separated by segregation. Also covered by patents is the removal of iron by the addition of another metal to form an intermetallic compound with the iron which, because of its increased particle size, is able to settle out of the molten metal. Here, too, quantitative information on the extent of iron solubility in liquid magnesium is of more than theoretical interest. M. Hansen,5 in his critical collection of the data on binary alloys, states that iron is not soluble in liquid magnesium. W. R. D. Jones6 who studied the physical properties of low iron magnesium alloys observed a

Jan 1, 1948

By W. A. Tiller, W. C. Johnston

The solute distribution ahead of an advancing solid-liquid interface is controlled by varying the momentum boundary layer thickness in the liquid adjacent to the interface. Single pass zone-melting experiments on Pb-Sn alloys are described in which the liquid is caused to rotate in the plane of the solid-liquid interface due to the influence of a magnetic .field rotating in this plane. The variation of the diffusion boundary layer thickness with field strength is determined. DURING the freezing of an alloy a partitioning of solute occurs at the solid-liquid interface, the magnitude depending upon the difference in the solid and liquid solubilities at the interface temperature. Because the diffusion coefficient is so small in the liquid relative to normal freezing rates, either a pileup or a depletion of solute occurs at the interface when the partition coefficient, kO, is either less than or greater than unity, respectively. This solute distribution is completely characterized by i) the solute concentration in the liquid far from the interface, C) the ratio of freezing velocityf, to diffusion coefficient, D, iii) the partition coefficient, ko, and iv) the thickness of the diffusion boundary layer, 6,, at the interface (this assumes that an electric field is not applied across the interface). For a particular system, C ko and D are fixed so that the character of the solute distribution can be changed only by a variation of either f or 6c. As is well known, the freezing velocity can be changed by varying the thermal environment of the alloy. Whereas, the thickness of the solute rich layer can be changed by varying the fluid flow conditions in the liquid. It is the purpose of this paper to describe a technique for controlling the fluid flow conditions in the liquid. During most solidification experiments the driving force for fluid flow arises from either mechanical mixing, thermal convection or electromagnetic mixing. The momentum boundary layer thickness, 6m at the solid-liquid interface, within which negligible movement of the liquid occurs, has been calculated for the special case of mechanical mixing where crystals are solidified by the Czochralski technique.l,2 The calculation of 6m for the case of thermal convection has also been made.3 In some calculations it has been assumed that the momentum boundary layer thickness, 6,, may be equated to the thickness of the diffusion boundary layer 6c, at the interface. However, as may be seen from Appendix I this is only true in very special cases and in general where a is a constant of magnitude determined by the particular liquid alloy. Neither calculations nor experimental data exist for the dependence of upon electromagnetic mixing. In this paper experiments are described in which the liquid is caused to rotate in the plane of the interface due to the torque developed on it by a magnetic field, H, rotating in this plane. The variation of is controlled by the variation of H. A magnetic field rotating in a plane perpendicular to the interface has been used for the purification of aluminum. Experimentally, we determined the variation of 5C with H by using the zone-melting technique of pfann5and a theoretical relationship of Burton et a1.2 pfann5 has shown that, after the passage of one molten zone through a long cylindrical charge of uniform concentration, CO, the solute distribution, C,, in the solid is as shown in Fig. 1. The equation describing this distribution is

Jan 1, 1962

By H. E. Cline, J. L. Walter

Grain boundary sliding and migration were studied in pure aluminum bicrystal and polycrystal samples with two-dimensional grain structure. Scratches, 50 P apart, were used for measurement of sliding and migration distanceso. Samples were deformed at constant rate at 315C and events recorded continuously on wrotion picture film. Electron micrograPhs of boundary-scratch intersections were obtained. Yield and flow stress values were measured. The sequence of sliding and migration events for a three-grain junction is described in detail. Sliding depended only on the resolved shear stress imparted to the boundary. Sliding was accowmodated by formation of shear zones in grains opposite triple points and adjacent to curved boundaries. These shear zones provided the driving force for grain boundary migration. Migration caused rumpling of the boundaries, decreasing the sliding rate. Sliding and migration generally began at the same time, occurred simultaneously and ended at the same time. In the bicrystal, sliding and migration rates were proportional. Initial sliding rules of 5 X joe cm per sec. were measured for the polycrystal and bicrystal samples. These sliding rates agree wilh the internal friction experirnents of K;. The observations seem consistent with a viscous boundary sliding nzechanism. GRAIN boundary sliding is the translation of one grain relative to its neighbor by a shear motion along their common boundary. Sliding is thought to be an important mode of deformation at elevated temperatures and at low strain rates such as prevail in creep,' and perhaps in the area of superplastic behavior.2"4 Although much work has been done to investigate grain boundary sliding, the effort has not led to the identification of a mehanism. KG showed that grain boundaries in aluminum exhibit a viscous nature under very small displacements of internal friction measrements. Various dislocation mechanisms have been proposed but are without conclusive experimental support. Attempts to relate sliding to 6's viscous boundaries have been unsuccessful in that measured rates of sliding are always several orders of magnitude lower than KG'S results would predict.= In bi crystals7and polycrystalsR of aluminum tested under constant load, the grain boundary sliding was found to be proportional to the total creep elongation which indicated that sliding might be controlled by deformation of the grains. Shear zones were observed to extend beyond grain boundaries at triple points to accommodate the sliding.8 Surface observations brought forth the opinion that sliding and migration occurred alternately, in sequence.' Measurements of sliding at the surface have been criticized because they might not be representative of the interior of the sample. Generally speaking, it seemed that much of the previous work and knowledge was based on observations made at relatively low magnification and examination of samples after deformation had been accomplished. Thus, it was the purpose of the present study to continuously record, at high magnification, the events occurring during the deformation of pure aluminum. Samples with two-dimensional grain structures were used to simplify interpretation of the results. The sliding and migration of small areas of many samples were continuously recorded by time-lapse motion pictures. Replicas of the surface were used to provide high-resolution electron micrographs. These observations, coupled with tmsile strength data, provide sufficient information to arrive at an understanding of the phenomenon. EXPERIMENTAL PROCEDURE An ingot of 99.999 pct A1 was rolled to sheet, 0.127-cm thick. Tensile specimens, with a gage length of 0.85 cm, were machined from the sheet. Bicrystal tensile specimens, of the same dimensions, were spark cut from a large bicrystal ingot. The grain boundary was oriented at 45 deg to the tensile axis. The surfaces of the tensile samples were ground flat on fine metallographic paper and were then electropolished in a solution of 75 parts absolute alcohol and 25 parts of perchloric acid. The solution was cooled in an ice-water bath. Using a weighted sewing needle suspended from a small pivot on a precision milling machine, a grid of fine scratches, 50 p apart, was scribed on one surface of the sample. The polycrystalline samples were then annealed in hydrogen for 15 min at 350" to 400°C to produce a two-dimensional grain structure of about 0.2-cm average grain diameter which would not undergo further growth at the test temperature, 315OC. Examination of both surfaces of the samples showed that the grain boundaries were perpendicular to the surface of the polycrystal and bicrystal samples. A hot-stage tensile machine was constructed for use with an optical microscope as shown in Fig. 1. The specimen is shown mounted in the grips. The grips ride in V-ways so that the sample can be mounted without damage. The rear grip is free to slide so that when the sample expands during heating it is not put under a compressive stress. When the grips and samples are at temperature, the rear grip is locked in place by two set-screws. The other grip is connected to a synchronous drive motor which, through a worm gear and a fine-threaded rod, deforms the

Jan 1, 1969

By Robert I. Jaffee, Bruce W. Gonser

RECENT work by the authors1 established the constitutional diagram of the gold-germanium system. Of particular interest in the simple euctectiferous system was the eutectic alloy at 12 per cent Ge, which melted at the very low temperature of 356°C. and had an unusually fine eutectic structure. It was of interest to investigate the effect of third components on the melting point, microstructure, and strength of this alloy, and in this work the effect of copper is discussed rather completely, with less complete data on the effects of silver, platinum, nickel, and zinc. No reference in the literature has been found on ternary systems with gold-germanium. MATERIALS AND ALLOYING As in the work on the binary system, gold-germanium, the germanium used in this investigation was the cyanide-reduced, 99.9 per cent product, produced by the Eagle-Picher Co. Fine gold sheet from Handy and Harmon, pure platinum sheet from the American Platinum Works, copper magnet wire from Anaconda, nickel wire assaying 99.6 per cent Ni, and electrolytic zinc were used for alloying. To make the alloys, charges of the pure metals were put in a graphite crucible and melted in an atmosphere of pure hydrogen. The temperature was brought up to about 1050°C., and the metal allowed to freeze in the crucible. Except with alloys containing zinc, melting losses were consistently less than a few milligrams. When zinc was a component, weight losses up to half the weight of the zinc present were incurred, and the alloy compositions were calculated by assuming the entire weight loss to be that of zinc. In all other cases the composition of the alloys could safely be taken as that of the charge. The ingots, as solidified, were segregated, the heavier primary phases being at the bottom and sides of the ingots and the lighter primary phases at the top, but by sectioning the entire ingot vertically for microscopic examination, this factor could be evaluated. Ingots for microscopic examination weighed one gram, and those for thermal analysis weighed three grams. THERMAL ANALYSIS In this work, the eutectic line composition and thermal arrests were desired, and, after microscopic exploration had established the position of the eutectic line at a given percentage of the third component, a thermal analysis was run at that composition. The method of thermal analysis used in the work on the binary Au-Ge system,1 a method particularly well suited for a small quantity of material, was used in this work. Clearly defined arrests were obtained, although with some alloys containing platinum

Jan 1, 1946

By C. M. Wayman, M. Miyagi

COMPARED to many of the binary alloys of iron, Fe-Ir alloys have received very little tud.'' Virtually nothing is known about the Fe-Ir equilibrium diagram' except for a few details concerning the liquidus-solidus positions for dilute iron-based alloys. It is reported1 that the y to a transformation temperature in Fe-Ir alloys (up to 40 wt pct Ir) is composition-dependent, varying from -900°C for pure iron to 0" to 100°C for Fe-40 pct Ir in an almost linear manner. The y to a transformation appears to be reversible,' the transformation hysteresis width increasing with increasing iridium content. In a qualitative way, the composition dependence of the y to a (and vice versa) transformations appears similar to those in the widely studied Fe-Ni system. In that the y phase (in Fe-40 pct Ir) can transform at -1000C, it

Jan 1, 1967

By E. F. Johnson, F. H. Brinkman, H. J. Welge, S. P. Ewing

This paper presents a method for predicting the manrler in which oil will be displaced from a porous body by enriched gas. The calculations apply to a gas rich enough to give a partially, but not a completely, misci-ble displacement. The method — a three-component, two-phase analysis — takes into account condensation of some of the intermediate hydrocarbons from the injected gas into the oil, as well as enhanced volatility of heavier hydrocarbons at elevated pressures and temperatures. The condensation swells the oil and decreases its viscosity, thus aiding in its recovery. The calculations have been extended to apply to actual crude oil-natural gas systems by arranging the components into three groups according to their volatility. As an approximation, each group is then treated as a single component in the analysis. The influence of an angle of dip for an inclined displacement is also taken into account. The recovery predictions are corroborated by experiments which used both consolidated sand cores and un-consolidated glass beads. In some of these tests, actual live crude oil was displaced by a multicomponent gas typical of enriched gases used in oil fields. INTRODUCTION This paper presents a method for predicting the amount of oil that can be displaced from a homogeneous, linear, porous body at various stages during the injection of enriched, or "wet", gas. The porous body can be in either a horizontal or an inclined position. 'This type of displacement is sometimes known as condensing gas drive The method is developed especially for the case in which the injected gas is enriched enough to be partially, but not completely, miscible with the reservoir oil. The need for a calcula-tive procedure for this type of operation is emphasized by the number of field projects where completely miscible drives are not practical, but where near-miscible conditions are feasible. The factors taken into account in the predictive calculations include: (1) the condensation of gas components into the oil, with a resulting increase in oil volume; (2) the lowering of oil viscosity by the addition of lighter ends from the gas; (3) the increase in oil volatility at high temperatures and pressures; and (4) the physical displacement of the oil by the gas. The techniques developed in the paper can be extended to other nonequilibrium displacement processes. Other such processes that we have analyzed include a displacement by lean gas which stripped intermediates from the oil, and a water flood in which the water con. tained in solution a substance somewhat soluble in the oil. ANALYSIS OF ENRICHED-GAS DRIVE GENERAL PRINCIPLES Our method for predicting the amount of oil that can be displaced by an enriched gas uses an analogy between a three-component and a multicomponent system.' The predictive method is based on these assumptions: (1) constant, or nearly constant, pressure; (2) complete equilibrium by diffusion perpendicular to the main direction of flow, but no significant mixing along the direction of flow; (3) constant injection velocity; and (4) flow in a linear porous body. The composition of a liquid or a vapor with respect to three components can be plotted on a three-component, or ternary, diagram like that in Fig. 1. Let Point A represent the composition of the oil originally in place. In this case, Oil A is undersaturated with gas. If Point A lay on the equilibrium Curve BF, the oil would be saturated. In the extreme case where the original oil contained no intermediates or dissolved gas, Point A would lie at the lower left-hand corner of the ternary diagram. In a displacement of Oil A by Gas D, there will be a progressive change in the composition of the oil phase as more and more gas is brought into equilibrium with the oil. The end result of this progressive change is an oil having the composition represented by Point F. This oil is richer in intermediate hydrocarbon and methane than the original oil and, therefore, has a greater forma-

By H. Conrad, V. V. Damiano, G. J. London

A method is described for producing single crystals of high-purity beryllium, Be-4.37pct Cu, and Be-5.24 pct Ni. These crystals were prepared for testing in compression parallel to the [0001] by orienting and lapping to within ±3' of arc of the (0001). Microstrain testing apparatus is described along with c axis compression results for ingot purity beryllium, twelve-zone-pass material, and the above-mentioned alloys. Results show no measurable plasticity for the ingot purity material from -196" to 400°C, although some surface traces of (1122) slip was observed at 200°C and above. The twelve-zone-pass material shows substantial microstrain plasticity at 220°C with slip on (1122). Both alloys show significant plasticity at room temperature and above with slip also on (1122) planes. THE two slip systems which normally operate during the plastic deformation of beryllium in the vicinity of room temperature are:' basal slip (0001)(1120) and prism slip . Pyramidal slip with a vector inclined to the basal plane has been reported for elevated temperatures,'-a but occurs near room temperature only at very high stresses.~ A summary of the available data on the effect of temperature on the critical resolved shear stress for slip on these systems has been compiled by Conrad and Perlmutter.~ It has been postulated6'7 that one of the principal factors contributing to the brittleness of poly crystalline beryllium at temperatures below about 200°C is the difficulty of operating pyramidal slip with a vector inclined to the basal plane. Hence, detailed information on the operation of such a slip system is important to understanding the brittleness of beryllium. The operation of pyramidal slip with a vector inclined to the basal plane is best accomplished in beryllium by compressing single crystals in a direction parallel to the c axis. In such a test the resolved macroscopic shear strzss on the basal and prism planes is zero and (1012) twinning which is favored by tension along the c axis does not occur. Hence, in c axis compression of beryllium the normal deformation modes are inhibited and the operation of pyramidal slip with a vector inclined to the basal plane is favored. In the present investigation, c axis compression tests were performed on beryllium single crystal as a function of temperature (77" to 700°K), purity (commercial and twelve zone pass), and alloy content (4.37 wt pct Cu and 5.24 wt pct Ni). Presented here is a description of the test techniques employed and the gross mechanical behavior observed. A detailed analysis of the slip traces developed on the surfaces of the deformed specimens during these tests and the results of electron transmission studies of the deformed crystals are given in a separate paper.B PROCEDURE 1) Materials and Preparation. Single crystals about 1 in. diam were prepared of the following materials: commercial-purity beryllium, high-purity beryllium, and two beryllium alloys, one with 4.37 wt pct Cu and the other with 5.24 wt pct Ni. The commercial-purity single crystals were obtained by cutting specimens from large-grained ingot of Pechiney SR material, which is approximately 99.98 pct pure. The high-purity crystals were prepared by floating-zone refining (twelve passes) a rod (7 in. by 1 in, diam) of Pechiney SR grade cast and extruded beryllium. Although an absolute chemical analysis of the zone-refined material was not established, mass spectro-graphic analysis, emission spectrographic analysis, and y activation analysis indicated that it contained in atomic fractions about 5 to 10 ppm each of carbon and oxygen, 1 to 5 ppm each of nickel and iron, and about 1 to 2 ppm of copper, with the remaining residual impurities being less than 1 ppm. Further indication of the purity of this material is provided by the critical resolved shear stress for basal slip, which was approximately 300 psi. The starting material for the alloy single crystals was 1-in.-diam floating-zone-refined (six passes) rod of Pechiney SR grade beryllium. Two such rods were wrapped respectively with sufficient weight of wire of high-purity copper (99.999 pct) or nickel (99.999 pct) to yield a 5 wt pct alloy. A seventh floating-zone pass was then applied to each of the rods to accomplish the initial alloying and an eighth pass for homogenization. Analytical samples were taken from regions of the rod immediately adjacent to where the mechanical test specimens were cut; these indicated 4.37 wt pct Cu and 5.24 wt pct Ni. 2) Crystal Orientation. To avoid the occurrence of basal slip during c axis compression testing, it is necessary to load the crystals as nearly parallel to the c axis as possible. Preliminary c axis compression tests indicated that plastic flow and/or fracture occurred at stresses of the order of 300,000 psi; hence on the basis of a critical resolved shear stress for basal slip of 300 to 400 psi, the maximum crystal misorientation permitted is about 4 to 5' of arc. Since this accuracy cannot be obtained using the usual back-

Jan 1, 1969

By E. W. McAllister

The decision of the California Oil Umpire's' office to accept well potentials established from subsurface-pressure data has brought to the attention of many operators for the first time the application of such data to production problems. This paper reviews the development and application of subsurface-pressure data in kettleman Hills, where these data have been used in production work since 1932. The Kettleman Hills field was discovered in October 1928. The first subsurface-pressure surveys were made early in 1932 and by the middle of 1933 the two major operators in the field were making routine pressure runs in thcir respective wells. Shortly therefter, these companies agreed to exchange pressure data, and later a third company entered into the agreement. This made it possible to analyze the effects upon the reservoir pressure of past production practices, which are discussed in the latter part of the report. It is interesting that many of the applications of subsurface-pressure data discussed herein were anticipated by C. L. Clark and C. B. Kimberlint in a report2 dated March 1933. PRODUCTIVITY Index In the majority of individual well problems involving the use of subsurface- pressure data, it is necessary to use a factor known as the "productivity index," which indicates the ability of a well to produce and represents the number of barrels of oil or oil and water per day that will enter the well bore for each pound per square inch pressure drop made opposite the producing interval of the well. The productivity index may be determined from pressure and production data for one or more rates of flow and a static or shut-in pressure survey or from production and pressure data for two or more rates of flow. Productivity indices may be based upon either net oil or total fluid production. All indices referred to in this report are based upon net oil. The value of the productivity index for Kettlcman Hills wells decreases generally with time and it is not uncommon for the index to vary in value at any specific time fur various rates of flow. The decline of the productivity index may be attributed partly to the loss of reservoir pressure. As the reservoir pressure decreases, gas originally in solution is released from the oil, congesting the flow of fluids through the formation and increasing the viscosity and surface tension of the oil; thus the flow resistance of the fluids through the formation is increased, resulting in a decrease of the productivity index. For convenient reference, the productivity indices for each well are plotted against time and a curve is drawn through the points showing the trend of the average index value. Plotted on Fig. I are index values for five

Jan 1, 1941

By E. W. McAllister

The decision of the California Oil Umpire's' office to accept well potentials established from subsurface-pressure data has brought to the attention of many operators for the first time the application of such data to production problems. This paper reviews the development and application of subsurface-pressure data in kettleman Hills, where these data have been used in production work since 1932. The Kettleman Hills field was discovered in October 1928. The first subsurface-pressure surveys were made early in 1932 and by the middle of 1933 the two major operators in the field were making routine pressure runs in thcir respective wells. Shortly therefter, these companies agreed to exchange pressure data, and later a third company entered into the agreement. This made it possible to analyze the effects upon the reservoir pressure of past production practices, which are discussed in the latter part of the report. It is interesting that many of the applications of subsurface-pressure data discussed herein were anticipated by C. L. Clark and C. B. Kimberlint in a report2 dated March 1933. PRODUCTIVITY Index In the majority of individual well problems involving the use of subsurface- pressure data, it is necessary to use a factor known as the "productivity index," which indicates the ability of a well to produce and represents the number of barrels of oil or oil and water per day that will enter the well bore for each pound per square inch pressure drop made opposite the producing interval of the well. The productivity index may be determined from pressure and production data for one or more rates of flow and a static or shut-in pressure survey or from production and pressure data for two or more rates of flow. Productivity indices may be based upon either net oil or total fluid production. All indices referred to in this report are based upon net oil. The value of the productivity index for Kettlcman Hills wells decreases generally with time and it is not uncommon for the index to vary in value at any specific time fur various rates of flow. The decline of the productivity index may be attributed partly to the loss of reservoir pressure. As the reservoir pressure decreases, gas originally in solution is released from the oil, congesting the flow of fluids through the formation and increasing the viscosity and surface tension of the oil; thus the flow resistance of the fluids through the formation is increased, resulting in a decrease of the productivity index. For convenient reference, the productivity indices for each well are plotted against time and a curve is drawn through the points showing the trend of the average index value. Plotted on Fig. I are index values for five

Jan 1, 1941

OF THE many categories into which scientific knowledge has been arbitrarily divided, the one which has proved most applicable in our attempts to gain an insight into the details of steelmaking processes is physical chemistry. To the young metallurgist who has only recently survived a college course in this subject, the application of its principles to reactions in liquid steel should not be difficult. To one who has had no such course or whose auld acquaintance with the subject has all but been forgot, such application is all too often thwarted by the abstruse presentations of the subject found in many of the available textbooks. AS a tool for the control of a complex process involving many chemical reactions, physical chemistry can become very valuable. The specialist who is using this tool for many purposes and perhaps contributing to its development will want to know a great deal more about it than can be included in this book. He will be interested in its history, its accomplishments and limitations, and its applications to many and varied problems. To the steelmaker or metallurgist, however, it is only one of a number of tools that he must use. He is willing to forego the detailed study of its inner workings in order to concentrate upon the development of skill in its application. It is the purpose of this chapter to present a simplified view of physical chemistry as a tool of great potential usefulness. This purpose and the desire for brevity have required the elimination of many of the gadgets with which the tool is usually adorned. It is hoped that this simplification will be conducive to clear understanding. The beginner is urged not to overlook the more extended treatments of the standard textbooks.* He is assured at the same time that the basic tool is sound and serviceable and is guaranteed to give satisfaction if regularly lubricated with common sense. Certain parts of physical chemistry require rather formidable mathematics for their complete development, but in the main those applications in which we are here interested can be expressed in fairly

Jan 1, 1944

By H. H. Uhlig

Soon after general use of stainless steels began, it was observed in practice that certain combinations of factors tended to induce corrosion by pitting. For most applications this was a serious drawback, not so much because the structural properties of the metal were impaired but because of the rapidity with which heavy sections of the alloys were penetrated by small elongated pits. These pits seemed to initiate readily in oxidizing metal salt solutions like ferric chloride and in chloride solu-tions like sea water. It was observed that in sea water pitting was more frequent in stagnant or polluted waters than in highly aerated, moving waters. The steels in these chloride solutions were observed to be sensi-tive to long contact with material such as sand grains or attached bar-nacles. At points of attachment or contact it was not uncommon to discover initiation of corrosion. Pits once begun at contact faces were observed to grow rapidly, usually elongating phenomenally in the direc-tion of gravity until the metal was perforated. Hydrochloric acid and other nonoxidizing acids, on the other hand, were observed to corrode stainless steels generally; the weight losses often were higher, but the penetration less than for the pitting type of corrosion. The causes of pitting, a type of corrosion recognized as character-istic not only of stainless steels but of many additional metals and alloys, are important in corrosion studies. A possible explanation bears prac-tical significance, for once it is known why pits begin where they do and continue to grow after initiation, intelligent direction can be given to diminishing corrosion. This can be done either by some alteration in the composition and treatment of the alloy or by some alteration in the environment. It appears foremost in importance to discover the nature of pit foci, for if initiation of pits can be discouraged their growth will be no longer a factor to be considered. In a multi-component alloy containing many impurities normal to production of such an alloy, each of which may play a part in pitting, and whose corrosion resistance is sensitive to heat-

Jan 1, 1940

By R. G. Agarwal, Ramey Jr. H. J., Al-Hussainy R.

Although it has long been realized that gas recovery from a water-drive gas reservoir may be poor because of high residual saturations under water drive, it appears that only limited infomlation on the subject has been available until recently. This study was performed to show the qiiantitative potential importance of water influx. Results indicate that gas recovery may be very low in some cases: perhaps as low as 45 per cent of the initial gas in place. Gas recovery under water drive appear to depend in an important was on: (I) the prodirction rate and manner of production; (2) the residual gas saturation; (3) aquifer propertie.); and (4) the volumetric displacement effciency of water invading the gas reservoir. The manner of estimating water-drive gas reservoir recovery can vary considerably. Examples are: the steady-state tnethorl. the Hurst modified steady-state method, and various unsteady-state methods such ac. those of van Ever-dingen-Hurst, Hurst, and Carter-Tracy. The Carter-Tracy water influx expression was used in this study. In certain cases, it appears that gas recovery can be increased significantly by controlling the production rate and manner of production. For this reason, the potential importance of water influx in particular gas reservoirs should he investigated early to permit adequtrtr planning lo optirtize the pay reserves. INTRODUCTION In recent years, the economic importance of natural gas production has become increasingly apparent. This has been evidenced by more intensive exploration efforts aimed at gas production, and exploitation of both deep, as well as low-permeability gas reservoirs. Technical developments such as deep-penetration fracturing have made development of such formations economically feasible. Unfortunately, water influx has forced abandonment of a number of gas reservoirs at extraordinarily high pressures. Although reservoir engineering methods for estimating water influx have long been available, it appears that application of these methods to the water-drive gas reservoir has been sporadic.'a Available methods for estimating water influx which can be applied to the water-drive gas reservoir problem include the steady-state method,1 the Hurst modified steady-state method and various unsteady-state methods such as those of van Everdingen-Hurst. Hurst, and Carter-Tracy. Interesting applications of these solu- tions to gas reservoir and the aquifer gas-storage problems have appeared recently.3,12,14 The experimental study of residual gas saturations under water drive by Geffen et al. in 1952 indicated that residual gas saturations could be extremely high. A value of 35 per cent of pore volume is often used in field practice when specific information is not available. The study of Geffen et al. showed that residual gas saturation might be much higher in some cases. Naar and Henderson concluded that the residual non-wetting phase saturation under imbibition should be about half of the initial non-wetting phase saturation. The Naar and Henderson result that residual gas saturation under water influx should be about half the original gas saturation is recommended as an estimate if laboratory measurements are not available. Thus, it is clear that a considerable portion of the initial gas in place might be trapped in a water-drive gas reservoir as residual gas at high pressure. A full water-drive would result in loss of residual gas trapped at initial reser.voir pressure. Consideration of transient aquifer behavior leads to the conclusion that high-rate production of water-drive gas reservoirs could result in improved gas recovery by reduction of the abandonment pressure. However, there appears to be little quantitative information on this possibility. One of the few advantages of water-drive gas production appears to be improved deliverability through water-drive support of the reservoir pressure. There may also be an advantage in higher condensate recovery caused by pressure maintenance for gas-condensate water-drive reservoirs. In view of the preceding, this study was made to assess the potential importance of water-drive in gas reservoir engineering. The Carter-Tracy approximate water-influx expression was used because this equation offers some advantages in hand-calculation which do not appear to have been generally recognized.' However, calculations were performed in the main with a high-speed digital computer to permit evaluation of the effect of water-drive under a large variety of conditions. CALCULATION METHOD Water-drive gas reservoir performance can be estimated in a manner completely analogous to oil reservoir calculations: a materials balance is written for the reservoir, and a water influx equation is written for the aquifer. Siniltaneous solution provides the cun~ulative water influx and the reservoir pressure. When reservoir performance data (gas produced and reservoir pressures) are available, it is usually possible to match performance data to determine the initial gas in place and the water influx parameters —

Jan 1, 1966

By J. L. Huitt, S. R. Darin

The use of a partial monolayer of propping agent to obtain a high flow capacity for a hydraulically induced fracture is discussed. From the results of laboratory work it was shown that a modified form of the Kozeny-Carman relation could be used to describe the flow in the partial monolayer propped fracture. With equations presented in the paper, the density pattern of the propping agent (number of particles per unit of fracture surface) that results in the maximum flow capacity for the fracture can be determined. The maxitnum flow capacity obtained with a partial monolayer is often an order of magnitude greater than the flow capacity obtained in greater width fractures containing multilayers of the propping agent. INTRODUCTION One of the predominant factors controlling the success of a hydraulic fracturing operation is the propping of the fracture. The trend in hydraulic fracturing recently has been an increase in the ratio of propping agent-to-fluid. The primary purpose of this increased ratio is to sustain a propped fracture of greater width. It was shown in a recent study' that for some formations low concentrations of propping agent would result in "closing" or "healing" of the fracture. In some cases, in an effort to insure sufficient propping agent concentration, the fracturing operation is designed to obtain a pack of the propping agent in the fracture. The placing of a pack of propping agent in the fracture provides a fracture of maximum width; however, the width alone does not control the flow capacity of the fracture. The flow capacity is dependent on the permeability of the fracture, as well as the fracture width. Thus, increasing the permeability to obtain larger flow capacities is as important as obtaining a greater width fracture. By increasing the concentration and particle diameter of the propping agent, fractures of sufficient flow capacities are obtainable for effective well stimulation in a number of formations. However, in some of the recovery techniques, the fracture capacity obtained by commonly used practices in fracturing is inadequate. One such recovery technique is gravity drainage via a horizontal fracture placed near the base of the productive zone. For this recovery technique, the fracture capacity desired is usually one to two orders of magnitude greater than the fracture capacity normally obtained in fractures propped with the size of sand commonly used (20-40 mesh). By the use of particles of larger diameter, the permeability of a pack2 is increased; however, even a multilayer pack results in a fracture flow capacity lower than that desired for some formations. For example, a fracture of 1/4-in. width, packed with 8-12 mesh sand of about 2,000 darcies permeability, would result in a fracture flow capacity (permeability X fracture width) of only 40,000 md-ft. If the fracture flow capacity needed is an order of magnitude greater than that cited in the example, an approach different from the formation of a pack in the fracture is needed. One approach is a partial monolayer of large-diameter propping agent. In working with this type of fracture system, it was found that the flow problems were unique to the system; therefore, the study discussed in this paper was made. THEORY AND RELATED STUDIES Previous studies, although related to that described in this paper, have not pertained directly to the flow in a fracture propped with a partial monolayer of propping agent. However, studies such as flow between parallel plates,' flow in packed columns,' fracture flow capacity' and flow in simulated fractures reduce the scope of this flow problem considerably. A fracture propped with a partial monolayer of dropping agent may be considered to be between two extremes — between an open fracture and a bed of particles packed In a conduit of fracture geometry. Thus, it seems appropriate to review the extreme cases.