By Mohamed Ahmed, A. Kawy

"Smelting of scrap copper and residual anodes and cathodes carried out in a reverberatory type furnace. In this, deoxidation process is carried out by wood, which acts as a resource of reduction gases such carbon monoxide, hydrogen and methane. Use of wood causes the formation of soot pollutants and efficiency of oxygen removal from copper is low leading to added costs in removing contaminants. This expensive problem was solved by using of reformed natural gas as a source of reduction gases (CO+ H2).IntroductionThree reverberatory furnaces were used for smelting of scrap copper and residual anodes and cathodes. Each furnace had a 7tpd capacity and was operated at 1183 °C.In this furnace, Step1-compressed air supplied by tubes from the side of the furnace to remove sulfur from copper matte by oxidation .The copper is also oxidized to copper oxide .[1]Step 2- copper from matte is deoxidized by a reductant. Typically deoxidation process is carried out using wood as a resource of carbon monoxide, hydrogen and methane which are the reduction gases. Use of wood causes the following:1- Forms soot pollutants2- Oxygen removal efficiency from copper is low; more contamination in copper matte increased energy in deoxidation3-the process is highly expensive.In the recent trends, this problem has been solved by using reformed natural gas as a source of reduction gases (CO+ H) .This results in 1-Reduced pollution during smelting.2- High efficiency in the removal of oxygen from copper to produce oxygen free copper. The surface of copper produced from this method is smooth which helps in forming and machining.3- Low cost and natural gas is more readily available in Egypt than wood."

Jan 1, 2010

By Hao Rang

The article Is specially to Introduce the recovery process of Nb, Mn, P from slags and reutilization techniques of the remaining slags. Nb-Mn-Fe alloys which contain 14-16% Nb, 40-60% Mn can be obtained after using fire refining process of " Blast Furnace-Revolving Furnace-Electric Furnace -Electric Furnace, "meanwhile, phosphorous slags which the content of phosphorus pentoxide Is 29.21%. Further going through wet metallurgical processing and electrowinning technics to recover grading 99°o metallic manganese. Finally, phosphorous slags are grinded finely to be as phosporous fertilizers to be directly used for farmlands. Small particle size (0-8mm) rich slags are mixed with slight solid additions for balling directly, and taken Into blast furnace with blocky slags all together. The remaining tall slags are fully used as constructional materials, slags cement as well as a serial of wall materials, road materials, ground ornamental materials without burning operation and steam curing. The compressive strength range of those materials is up to 15-30 MPa. There is no more solid waste slags effluent In the full technical process.

Jan 1, 1994

By C. M. Davidson

Contamination of by-product: sulfuric acid, by dissolved oxides of nitrogen ('nitrates') occurs under some operating conditions encountered in sulfide roasting and smelting,, notably when oxygen-enriched air is used. This 'nitrate' lowers the value of the acid and increases the effective cost of smelter gas desulfurization. The present paper describes measures taken at one smelter acid plant to remove this 'nitrate'; it discusses the mechanism by which 'nitrates' in some cases concentrate in one part of the plant and can be purged for more efficient treatment; and it describes a process developed by C-I-L Inc. for removal of 'nitrates' from such a purge stream. Advantages of the process include very low reagent cost, recovery of all sulfuric acid values and safe handling of nitrous fumes.

Jan 1, 1983

By I. Hilerio

Chromium Nitride (CrN) thin films were deposited on AISI steel 316 substrates by means of the reactive magnetron sputtering method. CrN films were produced under two different conditions. In the first one, the substrate was heated by a DC source. For the second coating a negative substrate bias voltage was applied. X ray diffraction, quantitative energy dispersion and scanning electron microscope were employed to characterize the two different phases, their chemical composition as well as their microstructure. In addition, a microhardness test was carried out. The results show that a better phase formation of CrN thin films was achieved when a heating source was present (first case). Both coatings presented homogeneous surface. Their compositions show differences even when the gases flowing are the same in composition. Regarding to the hardness test results, there can be found a higher value when using a heating source.

Jan 1, 2009

By M. Oliazadeh

The present study was performed to develop a process for solvent extraction of molybdenum and cobalt from an acidic solution generated by an electrodeposition process of nanocrystalline cobalt alloys. Solvent extraction is a common practice in hydrometallurgical and refining processes to produce metals; however its application for separation of molybdenum and cobalt from this specific solution is new, because molybdenum and cobalt are not commonly associated together in nature. Five commercial organic extractants were examined for extraction of cobalt and molybdenum from synthetic acidic solutions with pH ranging from 1 to 5. Preliminary results showed that at pH 2, any of the Cyanex 923, Alamine 336, Aliquat 336 and Hostarex A327 could be used to extract 99% of molybdenum from solutions, while from pH 3 to 5, Aliquat 336 was able to extract about 100% of molybdenum. Cobalt extraction, on the other hand, varied from 15% to 23% at pH 3 and 30% to 53% at pH 2 using different extractants. Based on results obtained, Aliquat 336 was applied on mixed solutions of cobalt and molybdenum at various pHs. The results showed that molybdenum could be extracted as much as 99% from a mixture of molybdenum and cobalt at acidic pHs, while less than 1% of cobalt was separated at pH 2 to 4 simultaneously.

Jan 1, 2003

By G. C. Gullo, H. Wabusseg, P. J. Uggowitzer, H. Kaufmann

"The basic concept of New Rheocasting (NRC) is described and the application of wrought alloys with this process is discussed. Practical experiments with the aluminium alloy AIMgSi I are explained. For this alloy the proper NRC - casting temperature was determined by using Thermo Cale - computer software and DT A and the essential processing conditions are shown. In the experiments the melt was taken from an aluminium holding furnace and cast into NRC steel cups. After controlled cooling the resulting slurries were cast into a 4-step die on an UBE HVSC 350 Squeeze Casting machine. The characteristic microstructural values such as grain size and shape factor were measured and compared with classical casting alloys. The influence of the wall thickness of the step part (6 mm, 10 mm and 14 mm) on the microstructure is described. Tensile properties in different heat treatment states are compared with characteristic prope1ties of the same alloys in forged condition. The ew Rheocasting - process CNRC)The NRC process is a recently developed new semi-solid processing method which allows the production of pore-free, pressure tight components.In the NRC process a fu lly liquid, but only slightly superheated melt is taken from a holding furnace and poured into specially designed steel crucibles, which are placed on a carousel next to the Vertical Squeeze Casting machine. In this ,NULL,slurry maker'· globul ar a-Al grains grow, following forced homogeneous nucleation at the cup wall [ 1, 2]. In the few minutes during which the melt is cooled to sem i-so lid processing temperature, a stable ske leton of a-Al phase forms. The resulting slug keeps a cylindrical shape during its slide into the sleeve of the Vertical Squeeze Casting machine, where it is cast into shape."

Jan 1, 2000

By C. M. F. Vieira

The main characteristics and physical and mechanical properties of clays from the county of Campos dos Goytacazes, located at the northern part of the State of Rio de Janeiro, Brazil, are presented. The characterization included mineralogical composition, chemical composition and particle size distribution. The properties related to water absorption, linear shrinkage and flexural rupture strength were obtained in samples that were prepared by 20 MPa uniaxial pressing and fired at 950 and 1100oC. The results showed that the clays are predominantly kaolinitic with high percentage of clay minerals. The kaolinitic structure associated with a small amount of fluxes confers a refractory behavior which makes difficult the sinterization and impairs the ceramic consolidation.

Jan 1, 2009

By Bo Zhou

During secondary aluminum recovery, complex aluminum scraps are melted and refined often in a rotary melting furnace and the aluminum metal has to pass through a molten salt layer and melt down in a bottom aluminum bath. Previous experimental study and industrial observations have indicated that salt shell formation and re-melting on the metal solids in the early stage plays a critical role in the overall melting process of the scrap. In the present paper, mathematical models are developed to simulate the process of salt shell formation and its re-melting, as well as aluminum melting in the molten melt. Influence of the salt layer properties, the residence time of the metal particles in the salt layer, the particle size, the temperature of bulk melt were investigated. Reasonable agreement with the measurement data was reached. The developed melting model will be used to construct a population balance model of the scrap melting behavior for a rotary melting furnace, taking into account the distributed characteristics of the scrap. Finally, an overall process model based on Computational Fluid Dynamics (CFD) for the rotary furnace will be constructed, coupling with the population balance model for the scrap melting.

Jan 1, 2003

By Takeshita. Takuo

"In this work, the progress of the HDDR process is discussed mainly on the Nd-Fe-B magnet system. There are three technologies being used for the Nd-Fe-B permanent magnet production; the sintering technique, the rapid quenching annealing and the HDDR process. The HDDR process utilizes· the HDDR phenomenon, in which hydrogen absorbing intermetallic compounds go through as they are heated in hydrogen atmosphere, Hydrogenation - Decomposition Desorption - Recombination. In the HDDR process, these four steps in the HDDR phenomenon are processed by choosing suitable reaction conditions regarding to hydrogen gas pressure, temperature, rate ·of desorption and etc., and we can produce permanent magnet powders of good magnetic properties with microstructures consisting with sub-micron size crystalline grains. In the anisotropic magnet powders, the sub-micron size crystals are being mostly aligned in the crystallographic c-axis direction. Possible applications of the HDDR process to other systems are also discussed.Microstructures of the Nd-Fe-B Permanent MagnetsIt is well known that magnet properties of magnetic materials are very sensitive to their microstructures [l]. This is seen in almost all magnet materials from soft magnetic materials and hard magnetic materials to magnetic memory materials. In this regard, the production technology is very important for the control of microstructures of permanent magnets The Nd-Fe-B magnet is the most powerful permanent magnet as a practical permanent magnet, and its coercivity force is much dependant on the microstructure as is the case for other permanent magnets."

Jan 1, 2000

By Tadafumi Adschiri

"Supercritical water can provide an unique reaction atmosphere for synthesizing metal oxide nanoparticles. Due to the drastic change of properties of water around the critical point, including density, dielectric constant and ionic product, the reaction phase with O 2 or H2 gas and the reaction rate and equilibrium can be varied to synthesize new materials or define particle morphologies. In this work, hydrothermal crystallization experiments are performed with several types of flow apparatus that allow convenient manipulation of variables such as temperature, pressure, and residence time. Key features in the flow modes and material preparation are discussed. The proposed supercritical hydrothermal synthesis method has the following desirable features: i) nanoparticles can be produced, ii) morphology of the produced particles can be controlled with small changes in pressure or temperature, and iii) a reducing or oxidizing atmosphere can be applied by introducing oxygen or hydrogen or other gases. An overview of this method is given for functional material synthesis of significant industrial interest including barium hexaferrite magnetic particles, YAO/Tb phosphor fine particles and lithium cobalt fine crystals.IntroductionHydrothermal crystallization, a method of metal oxide formation from metal salt solutions, is typically used at temperatures ranging from 373 K to 473 K. We are developing a new process for hydrothermal crystallizations that uses temperatures in the range of 673 K to 723 K, which is just above the critical temperature of water1 • 8 • In this work, we refer to this process as supercritical hydrothermal synthesis. The supercritical state of water allows one to vary reaction rate and reaction equilibrium by shifting the dielectric constant and solvent density with pressure and temperature. From of our research on material production in supercritical water, we have identified the following specific features of the supercritical hydrothermal synthesis method: (i) ultrafine particles can be produced, (ii) morphology of the produced particles can be controlled to some extent with pressure and/or temperature, and (iii) a homogeneous reducing or oxidizing atmospheres can be provided by introducing gases, such as O 2, H2, H2O 2• and so on.1"

Jan 1, 2000

By Ricardo Melamed

Metallic mercury has been extensively used for gold recovery. Although the solubility and mobility of metallic mercury is low, this metal can undergo many transformations, leading to mercury contamination in humans. The complexity of Hg chemistry in the environment reflects its different possible oxidation states and species, with different physical-chemical properties. The interaction of Hg in the terrestrial system, as well as in the aquatic environment, is important to understand the mercury cycle. This paper reports data on the adsorption of Hg onto an Oxisol soil. Results show that the interaction of Hg(II) at the soil-solution interface depends strongly on ligand concentration in solution, which can affect Hg mobility. The presence of the chloride anion in solution increases the mobility of Hg(II) through the soil, due to a relative lower affmity of mercury chloride at the oxide surface. In the absence of chloride, Hg(II) form strong complexes with the surface, and its adsorption behaviour is similar to the adsorption of other hydrolizable cations.

Jan 1, 1996

By S. S. B Wang

Zirconia-based ceramic materials have potential applications in high temperature furnace insulation, hot extrusion and casting dies, pressure nozzles, cutting tools, engine parts and electronic materials. High purity and superfine powders of zirconium oxide (baddelyte) were synthesized from a solution containing zirconium oxychloride and urea under hydrothermal conditions. crystallization of the metastable tetragonal zirconia using magnesium oxide or yttrium oxide as stabilizing agents was successfully achieved. The mechanism of hydrothermal reaction to produce these powders are discussed.

Jan 1, 1989

By P. Sergi

A method of characterizing gold ores with respect to processing is proposed. The method includes microscopical examinations to obtain qualitative and quantitative data that relate to processing. The main thrust, however, involves laboratory heavy liquid separation tests, laboratory amalgamation tests, and laboratory cyanidation tests to determine the proportions of gold that can be recovered in a conventional processing operation. Two different Brazilian gold ores: a quartz vein gold ore, and gold in metasediments were tested.

Jan 1, 1989

A simulation of a capper concentrate smelter was built with a capacity of 450,000 tons per year. The system's components to simulate were three : a Reverbetory furnace, a Wiente ' s modified converter ( TMC ) and two cranes. The system was classified as dynamic, stochastic and discrete. In the simulation language choice it was concluded that the most advantageous one was GPSS/H. The model verification was done through the interactive Debugger that the language has and the statistical validation was done through the result variables of sane activities, that as a whole characterize the system (charged matte and charged concentrate to the TMC, skimming white metal and skimning slag). The validation was done comparing the simulation results of these variables with the ones obtained for those variables in a specific month in the smelter. The comparison consisted in a difference of means test and in all cases the equality was accepted with a 95% of confidence. The animation tool was PROOF, a general purpose animator, that is used after processing the simulation.

Jan 1, 1994

By Xiaobing Yang, Abhishek Lahiri, Animesh Jha

"In the FFC-Cambridge process, the cathodic dissociation of oxide and CO/CO2 production on carbon anode is the basis for metal production in a CaCl2 bath. By using an inert intermetallic anode, the CO2 evolution can be eliminated altogether with acceleration in the electro-reduction kinetics. At present the process suffers from slow reduction kinetics of TiO2 to Ti metal, which can be enhanced significantly by the incorporation of alkali species in the TiO2 pellet at the cathode and in the CaCl2 bath in the presence of an intermetallic inert anode. Nearly full metallization with greater than 99% of Ti metal containing 1500 ppm of oxygen is possible to achieve in less than 16 hours of electro-reduction. Analyses of phase composition and the microstructures morphology in fully metallized pellets revealed the presence of localized solidified Ti layer, indicating that fast reduction process also involved formation of liquid phase as middle stage reaction. In addition, in situ creation of porosity and maintain higher current level during electrolysis process were two key factors to fully reduction of TiO2.IntroductionDuring cathodic dissociation of TiO2 in a CaCl2 bath and anodic evolution of CO2 on a carbon anode, which is the basis for the FFC Cambridge process [1], the rate of metallization slows down due to the formation of CaTiO3 at the reaction interface. Calcium and alkaline earth perovskites are known for their poor electrical conductivity which adversely affects the overall electro-reduction. One of the ways to increase the porosity is via the addition of polyethylene precursors in the pellet or by directly starting from perovskite [2, 3]. The experimental evidences shown in the literature confirm although the speed of reaction increases, but a complete or near complete metallization is not possible by enhancing the in-situ porosity alone, as the insulating perovskite is very slow to decompose under the equilibrium that prevails in the cell. Plethoric evidences on carbon anode show with the current decrease gradually, and finally stabilize at a very low value between 0.2 and 0.4 A, which is a testimony of the presence of perovskite insulating barrier in the current path. Our aim in this paper is to demonstrate the mechanism of enhanced electro-reduction when alkali ions are present in the oxide pellet at cathode and in the bath. We also show for the first time the use of an intermetallic anode for Ti-metal production using the FFC Cambridge process."

Jan 1, 2009

By Chang Wei, Fan Zhang, Zhigan Deng, Minting Li, Cunxiong Li, Gang Fan, Xingbin Li

Marmatite is an important resource of zinc, which exist in forms of high iron and high indium. In order to recycle the valuable metal from these ores, the testwork of simultaneous leaching on neutral residue mixed with zinc concentrate of high iron and high indium has been conducted. The primary objectives are to leach the zinc and indium remaining in the neutral leach residue as ferrite using acid, and to reduce the ferric iron in solution to the ferrous by zinc concentrate, thereby extracting the zinc and indium in the zinc concentrate. The results indicated that in the following conditions, mass ratio of neutral residue to zinc concentrate of 1:0.25, particle size of 74-58 μm, initial sulfuric acid concentration of 150 g/L, liquid to solid ratio of 8 L/kg, temperature of 90°C, reaction time of 4h, the leaching efficiency of zinc and indium were over 95%, nearly 90% Fe was Ferrous in the leaching solution. This process effectively extracted zinc and indium and converted Fe3+ into Fe2+ in solution, and simplified the traditional process of reduction after leaching.

Jan 1, 2016

By Norihiro Murayarna

Hydrothermal synthesis of K type zeolite was carried out by using coal fly ash as a raw material and KOH as an alkali source. The change in various physical properties of the obtained zeolite, such as the kind of zeolite crystal, cation exchange capacity, surface structure of zeolite and particle size distribution were investigated through the overall reaction of zeolitization. The reaction mechanism of K type zeolite from coal fly ash was investigated from these results in this study

Jan 1, 2002

By George Owusu

A study has been carried out on the use of solvent extraction, instead of the traditional zinc dust cementation process, to remove copper from concentrated zinc sulphate leach solutions. In a series of experiments using plant solution containing 1.9 g/L Cu, 2 g/L Fe, 173 g/L Zn, 7.9 g/L H,SO,, 0.25 g/L Cd, 15 mg/L Co etc. and LIX 622 in SX-1, up to about 97-98 % of copper present in the zinc sulphate leach solution was extracted with negligible co-extractions of zinc, iron, cadmium, cobalt, etc. pH modification was not required for this reagent. The copper loaded organic was almost completely stripped using 150 g/L sulphuric acid. Investigations into the effect of any possible organiclextractant contamination on zinc electrowinning showed (if any) little effect on current efficiency if the organic contamination is less than 45 ppm; current efficiencies of 95-97 % were obtained. At organic contaminations higher than 45 ppm, the current efficiency dropped to about 92- 94 %. Visually, the organic-contaminated cathode sheets had rough surface morphology, becoming more intense with increasing organic concentration, compared to the non-contaminated cathode sheets.

Jan 1, 1998

By Akira Yazawa

The continuous converting has attractive advantages, but further experimental studies on the slag are required, when the process is considered thermodynamically. The summarized experimental results, obtained with iron silicate slag and with ferrite slag and results relating to actual operation are described and discussed in this paper. At first, equilibrium relations at controlled oxygen potentials among three melts of silica-saturated iron silicate slag, white metal and copper are investigated. The results obtained for slag agreed with the thermo-dynamical predictions. Namely, to suppress a magnetite separation, the system should be at high temperature; in the case of the S02 gas of 10 kPa, for example, magnetite did not separate from the slag at 1300°C, but at 1250 and 1200°C the slag was saturated with magnetite even at lower SO2 pressure. Copper losses caused by dissolution of its oxide increased with increasing 5O2 pressure, and were slightly lower than those reported in previous papers without the matte phase. When the continuous converting slag does not contain any appreciable amount of silica - in contrast to the conventional smelting slag ferrite slag would form, but there was no published fundamental work on-ferrite slags. Hence, the melting behavior and activities of the system CaO-Cu2O-Fe2O3 have been investigated. The liquidus diagram in nitrogen atmosphere was, constructed using both thermal analysis and quenching method. The low liquidus temperature region without magnetite separation was found in the part of low content of Cu2O in the section Cu2O-CaO-Fe2O3 and Cu2O?Fe2O3¬CaO?Fe2O3. The activity of Cu2O in the system was also measured. Slags, composed-of CaO, Cu2O and Fe2O3, in platinum crucibles were equilibrated at 1250°C and controlled oxygen pressures. After quenching, the-composition of slag and platinum crucible were determined qualitatively. On the thermo-dynamic analysis of the results, iso-activity lines were drawn, and it was shown that the slag in the converting furnace of the Mitsubishi process exists in an adequate region of the composition triangle.

Jan 1, 1976

By Kunio Nakahara, Kashiwagim Junichi, Takao Hayashi

"There are many problems for electronic devices and parts which were caused electrostatic damage by static electricity. It is necessary for prevention of electrostatic charge to decrease surface resistivity of material using electroconductive coating. Mitsui Mining & Smelting Co., Ltd. developed metal oxide type electroconductive pigment PASSTRAN (trade mark) Type-IV which is barium sulfate coated with SnOz(Sb) thin electroconductive layer. This paper shows about pigment characteristics and film condition of antistatic transparency paint which contained PASS TRAN.L.IntroductionRecently rapid development of electronics technology diffused electronic devices and products to Office, Factory, Laboratory and our life. But the other side, there are many problems for electronics parts which were caused electrostatic damage under static electricity. Demand of antistatic materials were become lager by this situation.There is close relationship between surface resistivity of material and static electricity. If the surface resistivity of object is enough low (under 109 Q /Sq), static electricity is dissipated quickly. So it is necessary for prevention of electrostatic charge to decrease surface resistivity of material using electroconductive coating.1) There are many type of electroconductive materials, for example, carbon black, metal powder, electroconductive polymer and so on. Especially, carbon black is used for general purpose by reason of its low cost, but it has big problem of black color. It can not get any color without black, and it caused contamination of carbon.In recent years, metal oxide electroconductive pigment (ECP) was developed and used for special purpose which demands transparent coating or easy dispersion to make ECP paint or endurance under hard environment and so on. Mitsui Mining & Smelting Co., Ltd. developed electroconductive pigment PASSTRAN Type-IV which is BaS04 coated with electro-conductive Tin oxide layer."

Jan 1, 1998