Fourteen members of the Board and officers nf6re present; and seven guests. Prof. E. K. Judd was appointed Managing Editor of the Institute's publications.

Jan 11, 1917

By Lawrence A. Soltis

Senior engineering or executive management positions are filled by engineers who are evaluated on their performance, knowledge, skill, and maturity. Not only is technical expertise required but a knowledge of sales and marketing, finance, law, industrial relations, and public affairs is necessary. The University of Wisconsin-Extension offers an innovative post-baccalaureate degree program blending technical and professional subjects the Professional Development Degree in engineering (PDD)-designed to bring various opportunities for learn-

Jan 4, 1978

Jan 9, 1951

By Ian W. Wark, Keith L. Sutherland

IT has been shown' that in the absence of heavy metal salts, the nature of the alkali used to promote differential flotation-whether caustic soda, lime or sodium carbonate-is unimportant. The hydroxyl ion is the active depressant upon which differentiation depends, and the pH value determines whether a film of collector forms on any given mineral surface. Even when sodium cyanide is used in conjunction with alkalies, it is the pH value and not the nature of the alkali or its concentration that is important, for upon the pH value alone depends the fraction of the added sodium cyanide that is present as cyanide ion, which is the true depressant. When heavy metal salts become dissolved from partly oxidized ores, or are added intentionally as activators, conditions are different, and metallurgists have found that lime and sodium carbonate do not give identical results, even when added in amounts sufficient to produce the same pH value. In the few instances in which we had attempted to confirm this view, we had failed to do so, for, with nothing to guide us, we had inadvertently chosen solutions that gave contact curves of a "standard type," which correspond to conditions of ready floatability. Now, however, we find that, in the presence of copper salts, and within a restricted range of reagent concentrations, the nature of the anions present is important, and that sodium carbonate does influence the results, apart from the usual effect due to its influence on pH value. With the recognition of this anion effect, and with the control of temperature already introduced,2 it appears that the factors of major importance in connection with this set of reagents have been taken into consideration, and that the results obtained and the conclusions drawn from contact tests will be of more immediate value to the operator. It is not difficult to suggest an explanation for the influence of the carbonate ion in the presence of copper sulphate. The works of Picker-

Jan 1, 1939

By J. Stuart Warner

The reaction COSO4(c)?CoO(c) + So3(g)was investigated from 950° to 1170OK by two different methods. The sulfate was decomposed in a previously evacuated space and Pso3 calculated from the measured total pressure on the assumption that Pso2 = 2P02. The sulfate was also decomposed under conditions of controlled oxygen pressure. The difference in the results obtained by these experimental techniques is attributed to the effects of thermal diffusion. The standard free energy change for the reaction is given by ?F° = 66,292 + 17.273T log T — 102.57 T (±300 cal/mole). It was found by DTA and X-ray diffraction studies that CoS04 undergoes a transformation at 617°± 4°C. THE metal sulfates may decompose directly to the oxide or pass through one or more intermediate basic sulfates. Provided the oxidation state of the cation does not change in the course of the reaction, the decompositions may be described in general as follows: One of the major objectives of this work was to determine the validity of Eq. [3] as much of the existing sulfate data has been calculated from decomposition pressures by Eq. [5]. The type of apparatus generally used for these measurements consists of a reaction vessel at high temperature which communicates with a manometer at room temperature. A temperature gradient is thus imposed on the gas phase causing thermal diffusion which brings about a partial separation of the different gaseous species present in an initially uniform mixture. The basic theory and experimental facts associated with this phenomenon are summarized elsewhere1 and it will suffice to state here that the heavier gaseous species diffuses down the temperature gradient. Since thermal diffusion destroys the homogeneity of the gas phase, it is not necessarily true that Pso2 = 2Po2 in any particular volume element of the gas phase even though there are twice as many molecules of SO, as of 0, in the gas phase considered as a whole. Under these conditions, the decomposing sulfate gives off SO, which dissociates to SO, and 0, and all three species are distributed throughout the system by thermal diffusion. However, the sulfate will continue to dissociate until the equilibrium value of PSo3 is established on the hot zone. Thermal diffusion may distribute SO2 and O2 throughout the gas phase in any way so long as Eq. [2b] is satisfied in the hot zone; i.e. Pso2(Po2)1/2=K3pso3. When a steady state is reached, we can characterize Pso2 in that

Jan 1, 1962

Prof. H. O. Hofman, Massachusetts Institute of Technology, Boston, Mass. (communication to the Secretary): When Mr. Stetefeldt quotes me as saying that " silver-assays are uniformly made by scorification," he has evidently not understood that I was referring solely to the practice of silver-lead smelting-works. Everybody knows that silver-mills do not employ the scorification-assay for regular work ; and it is equally certain that in very few, if any, silver-lead smelting-works will the crucible-assay be found in use for determining silver. The second part of the quotation, "as it is adapted to all kinds of ores and gives excellent results unless organic matter is present," although, of course, also intended in a restricted sense, might very well be extended to a general one. Mr. Furman, in his Manual of Practical Assaying,* says, on page 123: "We believe that the Colorado practice is preferable, as most ores will yield higher silver-results by scorification." The fact that the scorification-assay is the accepted one in Colorado is strong presumptive evidence for its accuracy, as exactness would nowhere else be more jealously demanded. Mr. Stetefeldt cites Albert Arents- as a supporter of his preference for the crucible-assay, although I had already done so in favor of scorification. Looking up again the reference, I find that I was justified in quoting him, as, while Mr. Arents advocates the crucibleassay for low-grade gold ores, not on account of the greater accuracy of its results, but because it is quicker and less expensive, he condemns it§ for the assay of silver-ores, and prefers the scorifier for rich goldores, and for coppery ores, and in general for ores containing both silver and gold. As I, like Mr. Stetefeldt, have kept no detailed

Jan 1, 1895

By Z. Moser, W. Ptak

The experiments were carried out by the method of measuring the electromotive force of concentration cells having zinc as a reference electrode, the second electrode being the liquid alloy Zn-Sn-Cd-Pb. The electrolyte consisted of liquid chlorides and had zinc ions. The measurements were made for seventy -five alloys of different mole fractions within the temperature range of 714° to 877°K. The experimental results enabled the calculation of the activity of zinc in tested solutions. The activities of zinc were calculated by means of Krupkowski's formulas.3 In addition, the formulas for coefficients of activity of zinc, tin, cadmium. and lead as the function of composition and temperature were given. Activity of zinc was compared with the values obtained from experimental results, and good agreement has been observed. On this basis it can be stated that the theoretical formulas are suitable for determining the thermodynamic properties of liquid quaternary metal solutions. IN the metallurgical processes being carried out at present multicomponent liquid metal solutions take part. For the thermodynamic analysis of these processes it is necessary to know the thermodynamic properties of these solutions. Therefore, many experimental and theoretical papers deal with this problem. The theoretical papers are generally based on the assumption that the structure of liquid metals is similar to their structure in the solid state. In this manner the model of liquid solution, consequently described by means of statistical thermodynamics, has been accepted. This method is being lately developed, especially for solid solutions. Statistical thermodynamics was applied among others by Guggenheim 1 for describing the thermodynamic properties. Unfortunately, the formulas of statistical thermodynamics are often not suitable for the interpretation of experimental results. Attention should be drawn to the relations obtained by means of formulas of phenomenological thermodynamics which always have constants derived with the aid of experimental methods. In the case of the multi-component solutions which contain some additions of impurities besides the basic metal, wagner2 introduced interaction parameters. Equations for the relationship between the activity coefficients and composition were also given by Krupkowski." he application of these formulas requires a good knowledge of the thermodynamic properties of the corresponding binary systems. In these formulas, as in Wagner's, there appear constants which should be determined from ex- perimental data. Nowadays, different experimental methods are applied for evaluating the thermodynamic functions of solutions, for instance: vapor pressure measurements, calorimetric methods, and the measurements of electromotive force of concentration cells. In the present paper this last method for evaluating the thermodynamic properties of four-component systems, Zn-Sn-Cd-Pb, was applied. For instance in the case of Zn-Sn solutions Alabyshev and Landratov, 4 Fiorani and Valenti, 5 and ptak6 performed the investigations. The Zn-Pb system was worked out by Kleppa 7 and Cd-Pb and Cd-Sn by Elliot and chipman.' This method was also applied for determining the activity of zinc in ternary solutions. 1) EXPERIMENTAL METHOD The experimental arrangement with detailed description is given in Fig. 1. It consists of resistance furnaces, one serving for melting samples and the other containing the flat-bottomed, measuring quartz tube with the liquid electrolyte. Liquid metals and alloys are in glass supremax tubes, which have an opening in their lower part above the metal level. This opening allows the filling of the tubes by the electrolyte. In these tubes tungsten wires are placed which by means of suitable conductors are connected with a potentiometer. It is assumed that tungsten dissolves Fig. 1—Schematic diagram of the experimental arrangement for the investigation of the thermodynamic properties of liquid metal solutions: 1, resistance furnaces; 2, autotransfor-mers; 3, galvanometers; 4, regulator of temperature; 5, gas purifier with concentrated H2SOP; 6, U-tube with P2O5; 7, thermostats; 8, steel block for thermostating; 9, supremax tubes for alloys; 10, tungsten electrodes; 11, inlet and outlet of argon; 12, measuring quartz tube; 13, tube for melting samples; 14, tube for thermocouple; 15, cover of quartz tube; 16, rubber seal; 17, bottom cover; 18, outlet of electrodes to potentiometer; 19, outlet of thermocouples to potentiometer; 20, upper view of the quartz tube cover; 21, orifices for cover screws; 22, orifice for argon inlet; 23, orifice for thermocouple; 24, orifices for tubes containing liquid metals; 25, inlet for water-cooling system.

Jan 1, 1969

By R. M. Brick, M. A. Williamson

Certain features of the response of copper and brass to deformation and recrystallization remain obscure. The textures obtained on rolled sheet are listed by Schmid and Boas1 as: No adequate explanation has been advanced for the presence of the secondary deformation texture of copper and its absence in brass or for the origin of the cubic recrystallization texture of copper.2 A recent publication3 attempted to rationalize the above empirically described annealing texture of brass on the basis of retention of the (110) [112] rolling orientation plus twinning about the central octahedral poles of the usual secondary (110) [115] orientation. The difierence in the textures of annealed copper as compared to 70-30 brass is also shown by the difference in the position of ears for drawn copper, at o° and go", as compared with drawn brasses, at 45o, for all compositions between oo-10 and 70-30.4 Data on indi- vidual crystals are as yet too few to permit of an analysis of these textures comparable to that of mild steel as made by Barrett and Levenson.5 Experimental Methods The materials studied included copper specimens cut from the central, equiaxed crystal portion of a tough-pitch wirebar; brass made from this copper and high-purity (99.99 per cent) zinc including alloys of 7 per cent, 15 per cent, 24 per cent, 29 per cent and 36 per cent Zn and large single crystals of 70-30 bras. Sections 1/4 in. thick of the cast polycrystalline copper and brasses were reduced 40 per cent by rolling, recrystallized to a common grain size of 0.045 mm. and then rolled directly to foil 0.002 in. thick. Hardness readings employing both the Vickers and Rockwell machines were taken at intervals during the reduction. For comparison, similar specimens were cross-rolled—i.e., turned through 90° for each pass—and comparable hardness data were secured. Finally sections from the single crystals of brass were cut to obtain the following initial orientations; these sections were rolled, hardness data secured and a complete micrographic record of structural changes obtained.

Jan 1, 1941

By R. M. Brick, M. A. Williamson

Certain features of the response of copper and brass to deformation and recrystallization remain obscure. The textures obtained on rolled sheet are listed by Schmid and Boas1 as: No adequate explanation has been advanced for the presence of the secondary deformation texture of copper and its absence in brass or for the origin of the cubic recrystallization texture of copper.2 A recent publication3 attempted to rationalize the above empirically described annealing texture of brass on the basis of retention of the (110) [112] rolling orientation plus twinning about the central octahedral poles of the usual secondary (110) [115] orientation. The difierence in the textures of annealed copper as compared to 70-30 brass is also shown by the difference in the position of ears for drawn copper, at o° and go", as compared with drawn brasses, at 45o, for all compositions between oo-10 and 70-30.4 Data on indi- vidual crystals are as yet too few to permit of an analysis of these textures comparable to that of mild steel as made by Barrett and Levenson.5 Experimental Methods The materials studied included copper specimens cut from the central, equiaxed crystal portion of a tough-pitch wirebar; brass made from this copper and high-purity (99.99 per cent) zinc including alloys of 7 per cent, 15 per cent, 24 per cent, 29 per cent and 36 per cent Zn and large single crystals of 70-30 bras. Sections 1/4 in. thick of the cast polycrystalline copper and brasses were reduced 40 per cent by rolling, recrystallized to a common grain size of 0.045 mm. and then rolled directly to foil 0.002 in. thick. Hardness readings employing both the Vickers and Rockwell machines were taken at intervals during the reduction. For comparison, similar specimens were cross-rolled—i.e., turned through 90° for each pass—and comparable hardness data were secured. Finally sections from the single crystals of brass were cut to obtain the following initial orientations; these sections were rolled, hardness data secured and a complete micrographic record of structural changes obtained.

Jan 1, 1941

By James W. Burns

Thin, heavily doped n-type layers of GaSb have been grown on p-type GaSb substrates. Techniques have been developed for the growth of the n-type layers from a tellurium-doped gallium-rich solution. The solution used consists of 95 at. pct Ga and 5 at. pct Sb. The process consists of immersing the p-type wafer in the solution at a temperature slightly above the liquidus temperature, holding briefly to permit dissolution of the substrate surface, then decreasing the temperature to a value slightly below the liquidus to obtain 1 HE resistivity of n-type GaSb varies linearly with applied hydrostatic pressure, while the resistivity of p-type GaSb is insensitive to such pressure.1,2 The growth. Growth from a solution of GaSb in tin will also be described. In either case the substrate is clamped to a shelf at one end of a graphite boat, and immersion of the wafer and subsequent decanting of the solution is accomplished simply by tilting the furnace. The process is useful for the formation of p-n junctions in III-V compounds and has the advantage that the problems normally associated with diffusion of Group VI elements are not present. Layers up to 4.0 mils in thickness have been grown by the process. material therefore should be useful in a hydrostatic pressure-sensing device. A practical hydrostatic pressure sensor, however, requires the fabrication of GaSb sensing elements of several hundred ohms resistance. Attempts were made to prepare such elements by diffusion, taking advantage of the high sheet resistance of the thin diffused layers and depending upon the p-n junction to provide isolation from the base layer. Additionally, thin layers of conductivity type opposite from that of the base layer were pre-

Jan 1, 1969

By Harlowe Hardinge

[Crushing Tests by Pressure and Impact (T.P. 1895, by F. C. BOND,, Min. Tech. Jan. 1946). Discussion by H. HARDINGE and the author 1 Pumping Sands, Slurries and Slimes and Installation and Performance of Sand Pumps (T.P. 2013, by W. B. STEPHENSON, Min. Tech., May 1946 and T.P. 1978, by C. G. SOUTHMAYD, Min. Tech., March 1946). Discussion by OSCAR LEE, G. J. HOLT, L. D. ANDERSON, and the author 2 Rapid Polarographic Method for Determination of Copper, Zinc and Lead in Flotation Tailings (T.P. 2010, by G. A. CROWE and W. T. BISHOP, Min. Tech., March 1946). Discussion by E. H. ROSE and the authors 4 Ball Wear and Functioning of the Ball Load in a Fine-grinding Ball Mill (T.P. 1984, by W. I. GARMS and J. L. STEVENS, Min. Tech., March 1946). Discussion by J. F. MYERS, E. W. DAVIS, F. M. JARDINE, H. HARDINGE, F. C. BOND and the authors 5 Correlation between Mineral Behavior in Cataphoresis and Flotation (T.P. 2005, by A. M. GAUDIN and S. C. SuN, Min. Tech., May 1946). Discussion by 0. C. RALSTON, G. L. SIMARD and D. J. SALLEY 7 Accident Experience in Milling (T.P. 1981, by J. F. MYERS and S. E. SHARP, Min. Tech., May 1946). Discussion by C. E. MCKNIGHT, C. H. BENEDICT, T. S. WILSON and S. POWER WARREN9 Mill Design for Labor Economy (T.P. 1997, by NORMAN WEISS, Min. Tech., May 1946). Discussion by R. S. HANDY and the author13] Crushing Tests by Pressure and Impact (0.C. Ralston presiding) HARLOWE HARDINGE.*-Has the impact method described in the paper been used to compare the resistance to reduction in size of various materials with actual operation results of mills in the field? Is this impact method a better index of the true resistance to grinding under actual field conditions than other methods the author has reported in the TRANSACTIONS? F. C. BOND (author's reply).-The impact crushing device was designed to measure relative resistance to crushing, or what may be called the crushability, and is not used for comparing the resistance to grinding, or grindability. The correlation between crushability and grindability of different materials is not at all close, since fractures, zones of weakness, and structural features of rock have a much greater effect upon the crushability than upon the grindability. We still depend upon our standard grindability tests for measuring resistance to grinding, and use the impact crushing tests only in relation to crusher installations. The impact crushing device has several advantages over the measurement of crushing strength in pounds per square inch as an index of crushing resistance.

Jan 1, 1946

By J. E. Pavlick, W. W. Mullins, H. W. Paxton

The growth of nitrogen-austenite during nitriding of large-gvained ferrite between 650" and 800°C has been studied as a functimz oJ time and nitrogen potential of the atmosphere for a variety of alloying elements dissolved in the ferrite. Whereas no preferential grain boundary penetration by aistenite takes place in zone-refined iron, the addition of aboit I zot pct oj' V, Ti, Cr. Si, or A1 produces significant protrusion of austenite down former 0-0 boundaries. This group of elernents also produces ragged y-0 interfaces in the a grains which advance more slozuly than those in zone-refined iron. 1 zut pct of Ni, Co, Mn, or Mo dissolved in ferrite leads to essentially smooth 7-a interfaces, which advance at rates very sinzilar to those in zone-refined iron. The reasons for this effect are not clear. Two possible limiting hypotheses, not necessarily exclusive, are discussed. One involves p.referentia1 grain bozindary diffusion of nitrogen. the other the production of a zone of ferrite, stpersatcirated with respect to nitrogen, from which austenite precipitates helerogeneozisly on the a-a gyain boundaries. In many phase transformations which occur by nu-cleation and diffusion-controlled growth, information on the parameters which control the rates of nuclea-tion and of growth is frequently not quantititative. The present work describes a continuation of efforts to obtain quantitative data on growth rates in systems where thermodynamic and kinetic factors are known independently, and thus where comparison with models of the growth process is possible. The work has been conducted on iron-base systems for two reasons. Firstly, there are several interesting transformations in this system, many of which are of practical importance. Secondly, the information on phase diagrams, activities, and diffusion coefficients is more complete in this system than in any other. These data are still inadequate to check all the effects of alloying elements, but at worst it is possible to make estimates and thus examine order-of-magni-tude agreement with proposed models. It will be necessary to do this in the present work. The problem studied was the growth of nitrogen-austenite in from the surface of large-grained columnar crystals of alloyed ferrite exposed to an NHs/Hz atmosphere. Earlier work by Grozier et al.' had suggested that growth of austenite may occur preferentially along grain boundaries of alloyed ferrite, whereas zone-refined (ZR) iron shows no such effect, Fig. 1. Growth of nitrogen-austenite into single crystals of zone-refined ferrite is planar provided sufficient nu-cleation sites for austenite are present, and is controlled by volume diffusion of nitrogen through the

Jan 1, 1967

By H. W. Paxton, C. C. Busby

IT has been shown previously' that strain aging can markedly improve the tensile properties of low carbon martensites, especially the yield-tensile ratio, without seriously affecting the ductility. In view of interest in high strength steels, an investigation has been made of the effect of strain aging following tension or rolling on the tensile properties of A1S1 4340 in an attempt to obtain a tensile

Jan 1, 1957

By D. Weinstein

Yieldilzg in annealed arc-cast molybdenunz in torsion was studied as a function of strain rate and tem-perature. The temperature dependence of the yield point for different strain rates was used to calculate a heat of activation for the yield point. The heat of activation was not a constant but was approximately a linear function of the stress at yield. It is proposed that the rate effect in yielding is determined in part by a site place-change of C (or other interstitial atom) in the metal. THE low-temperature embrittlement phenomenon in metals and alloys has been known to exist for a long time. Although a transition from ductile to brit-tle behavior has been observed in some close-packed hexagonal metals1 and a face-centered cubic alloy, the most common class of metals exhibiting this be-havior has a body-centered cubic lattice structure. For example, a ductile to brittle transition has been observed in iron,3 molybdenum,4 chromium,5 colum-bium,6 and tungsten.7 In the present investigation, molybdenum specimens were tested in torsion over a wide range of temperatures at three widely separated strain rates, and the temperature for onset of embrittlement was determined. Characteristic of body-centered cubic metals and closely associated with plastic deformation is the appearance of a sharp upper and lower yield point. Theoretical explanation of the yield point in iron and low-carbon steel is due to Cottrell,8 who attributes the phenomenon to the pinning of dislocations by the formation of impurity atmospheres around the dislocations. These atmospheres tend to lock the dislocations and make them more difficult to move. The stress required to move a dislocation and thereby cause plastic deformation is greatly increased, and thus an upper yield point is observed. In addition, theoretical analysis,9 as well as experimental observations, show that the upper yield point is strongly a function of temperature. The upper yield point is observed to decrease with an increase in testing temperature, and above a certain temperature (-700° K in iron) it no longer appears. This is consistent with the concept that thermal vibrations will help free a dislocation from its atmosphere, so that the external stress required to free a dislocation from its pinning atmosphere decreases with increasing temperature. Furthermore, with increasing temperature the equilibrium concentration of impurity atoms around a dislocation decreases exponentially with the result that the dislocation is less firmly pinned. In Cottrell's theory of yield point a static model is visualized in which the pinning atmospheres, particularly interstitial atoms, are immobile, and the dislocations are anchored to stationary positions in the lattice. However, experiments1,7 show the upper yield point to be time-dependent or a function of the rate of straining, a high strain rate causing a high upper yield point. Present theory does not adequately account for the rate dependence of the yield point, and the exact function of the interstitial atom is not under stood. Nevertheless, observation of the temperature dependence and rate dependence strongly suggests that the upper yield point phenomenon is due to the interaction between dislocations and pinning atoms, and that a diffusion mechanism is important in determining the yield point.

Jan 1, 1962

By Sherwin F. Kelly, Bela Low

THE WORK OF THE DRILLER and of the oil geologist is seriously handicapped by the impossibility of actually seeing what is going on inside a borehole as it is being drilled. Visual information of the position and condition of the casing, and of the characters and attitudes of strata passed through would be of inestimable benefit. The best substitute for putting a periscope down a hole is the taking of photographs of its interior at points where information is desired. An apparatus for this purpose has been constructed by Dr. Thomas Reinhold, of Heemstede, Holland, and one instrument of his design has been put into practical use by the Geological Survey of The Netherlands in searching for water. To the best of our knowledge, this instrument has not been applied to oilfield problems, although the possibility has been mentioned in the one or two brief notices of the camera which have appeared in the literature.' The purpose of presenting this description of the instrument, with some examples of its work, is to suggest that it might be adapted to serve a variety of useful purposes in American oilfields, and with the hope that discussion will bring out any modifications necessary to make the apparatus more valuable to drillers and geologists.

Jan 1, 1932

By L. F. Coffin

Monotonic tension and controlled cyclic-strain tests have been conducted on an annealed steel at various strain rates and temperatures in the weep range. Evidence of a strain-induced precipitate reaction abozle 500°C was determined from pronounced cyclic-hardening effects, increase inflow stress, inter granular fracture, drastic decrease in low-cycle fatigue resistance, and loss in tensile fracture ductility, as well as through electron-microscopy examination. It was found that strain rate as well as temperature had a pronounced effect on these observations. A parameter of the form P = T(7.95 - log ip) was determined, which was directly related to the ductility, defined either as the true strain at fracture in the case of simple tension, or as 2N 1/2 ? E p in the case of cyclic plastic strain. A highly satisfactory comparison of the cyclic life as measured and as computed from the ductility predicted by this parameter was obtained for a range of temperatures from 400° to 650°C and for crosshead speeds of 0.002 to 0.2 in. per min. MANY metals subjected to sustained loading at elevated temperatures derive resistance to creep from solid-state reactions of various alloying constituents. These reactions can be many and varied, and occur as a consequence of time and temperature according to reaction-rate principles. Strong evidence exists that many of these reactions are influenced by plastic strain, the argument being put forth that dislocations act as sites for nucleation and growth for the new phase.' Many examples can be cited where plastic strain during transformation influences the structure, and as a consequence affects the properties.2 The low-alloy steels serve as particularly good examples for investigating the effect which aging reactions have on resulting properties. Alloying elements such as carbon and nitrogen, and carbide formers such as manganese, chromium, molybdenum, and so forth, can, by the particular aging reaction which occurs, produce strengthening effects at various temperatures, and so endow strength to the alloy over a broad range of temperatures. These effects have been systematically studied by Glen both during creep3 and for constant strain-rate tension testing.4,5 The work of Glen is of considerable interest in connection with the present study, particularly in regard to the effect of various alloying additions on the true stress-strain curve and on fracture ductility at various elevated temperatures. He has shown that strain-age hardening occurred during plastic straining, which was quite specific both to the temperature of the test and to the alloying element involved. When strain-age hardening was noted at a particular temperature, a .minimum in reduction of area was also obtained. Provided the temperature for the minimum reduction of area exceeded 300°C, all minimum ductility fractures were found to be inter-crystalline in nature. For carbon steels containing molybdenum, two minima in reduction of area were noted, one occurring at 200° to 250°C, the precise temperature depending on the percentage of molyb-

Jan 1, 1964

By G. R. Leverant, M. Gell

The high- and low-cycle fatigue poperties of MAR-M200 directionally -solidified into columnar-grained and single crystal forms were determined at 1400" and 1700°F. These results were compared with the corresponding properties of conventionally -cast MAR-M200. The low-cycle fatigue lives of the columnar-grained and single crystal materials were similar at both temperatures and were one to two orders of magnitude greater than those of conventionally-cast material. The variations in the fatigue lives among the three forms of MAR-M200 were related to the more rapid rate of intergranular muck propagation compared to that of transgranular propagation. In conventionally-cast MAR-M200, cracks were initiated in grain boundaries and crack popagation occurred rapidly along an almost continuous grain boundary path. In the columnar-grained material, crack initiation occurred on short transverse segments of grain boundaries, but crack propagation was transgranular. The fatigue lives of columnar-grained and single crystal materials were approximately the same because most of the life in both materials was spent in trans-granular propagation. For the directionally -solidified materials, the number of cycles to failure, Nf, can be related to the total strain range, , by: heT = K where n and K are 0.16 and 0.044 at 1400'F and 0.29and 0.098 at 1700, respectively. In addition to intergranular crack initiation in the columnar-grained material, initiation also occurred at we-cracked MC carbides and micropores in both directionally-solidified materials. At 1400°F, fatigue life was reduced with increasing MC carbide size, but at 1700 there was no effect of carbide size. THE creep and stress-rupture properties of conventionally-cast nickel-base superalloys can be greatly improved by directional solidification into either single crystal or columnar-grained forms. The improvement in properties results from a reduction in intergranular cavitation and crack growth in the columnar-grained materials and the complete absence of this fracture mode in the single crystals. This paper describes the effect of grain boundaries on the elevated temperature fatigue properties of the nickel-base superalloy MAR-M200. The effect of cycling frequency on cracking arid fatigue life and the role of MC carbides and micropores on crack initiation are also emphasized. The fatigue properties of columnar-grained and single crystal MAR-M200 at room tem- perature,4,5 and the change in the mode of fatigue crack propagation with temperature6 have recently been described. I) EXPERIMENTAL PROCEDURE The material used in this study was the nickel-base superalloy MAR-M200, directionally-solidified into columnar-grained and single crystal forms. The columnar grains were approximately 0.5 mm in diam. The nominal composition of these materials in wt pct was 0.15C, 9Cr, 12.5W, loco, 5A1. 2Ti, lCb, 0.05Zr. 0.015B, bal Ni. They were solutionized for 1 to 4 hr at 2250°F followed by aging at 1600°F for 32 hr. which resulted in 0.2 pct offset yield stresses of 150,000? 144,000, and 95,000 psi at room temperature? 1400°, and 1700°F, respectively. The corresponding elastic moduli parallel to the testing direction were 19.2. 15.0, and 12.5 x 106 psi, respectively. Specimen design, testing procedures and alloy mi-crostructure have been described previously and will only be summarized here. Following the 1600°F aging treatment. MAR-M200 contains an ordered, cuboidal, y' precipitate 0.3 1 on edge, which is coherent with the 1 matrix. The y' precipitate is quite stable; even after testing at 1700°F. the precipitate is only slightly enlarged and its corners somewhat rounded. The alloy also contains a small volume fraction of micropores, and MC carbides. some of which contain preexisting cracks5 formed during casting. These cracks are always parallel to the long dimension of the carbide. Measurement of MC carbide size has been described previously.5 Axial fatigue tests were conducted in air over a wide range of strain amplitudes in both the high - and low-cycle fatigue regions, with specimen lives varying from about 10' to 10' cycles. Low-cycle fatigue (LCF) tests were strain-controlled with strain varied between zero and a maximum tensile value at a frequency of about 2 cpm. High-cycle fatigue (HCF) tests were stress-controlled with the stress varied between 5000 psi and a maximum tensile value less than the yield stress at a frequency of either 10 cps or 0.033 cps (2 cpm). The temperature in the gage section was controlled to 52°F. Specimen axes were within 5 deg of the [001] growth axis of the single crystals and the common [001 ] growth axis of the columnar-grained material. Specimen gage sections were electro polished prior to testing. After the standard heat treatment, three specimens were coated with a typical aluminide coating applied as a slurry. An additional specimen was given the coating heat treatment without actually being coated. In all cases: specimens were reaged at 1600°F for 32 hr after receiving the coating heat treatment at 1975'F for 4 hr.

Jan 1, 1970

By F. M. Jardine

I1944 the cry was for higher production more tons, more metal. New plants were built, capacity of old plants was increased and millmen all over the country were treating tonnages far above normal, sacrificing recoveries to vet that extra metal from extra tons. The list of "critical minerals," at first long, has been scratched until there remains, not a list, but only an item or two. Stocks of all metals and minerals, with possibly one or two exceptions, are now entirely adequate and numerous plants have curtailed or suspended operation.

Jan 1, 1945

By C. Pin, J. Bruce Wagner

In order to demonstrate the role of defect chemistry in the solid state to a process-metallurgy reaction, laboratory experiments were carried aut to remove copper from liquid lead using lead sulfide which had been doped to provide definite concentrations of cation vacancies. The removal of copper decreases in the order: bismuth- or antimony-doped PbS, undoped PbS or tin-doped PbS, and silver-doped PbS. The data are explained using the simple mass -action law and in terms of the exceedingly rapid interstitial diffusion of coppw in PbS to vacant cation sites. Results are in agree-ment with thermodynamic predictions and certain industrial practices that copper may be removed from lead below the limit of its coexistence with pure Cu,S and pure PbS. The role of defects in solids has been exploited in semiconductors and many device applications, in explaining tarnish formation, dissolution rates, and mechanical properties. The application of these principles to many process-metallurgical problems has not received as much attention. It was the purpose of this study to illustrate the role of defect structures of solids in a process-metallurgical application. When lead is refined, the ore, galena (PbS), is reduced by a series of operations to liquid lead (lead bullion) containing impurities such as copper, bismuth, antimony, arsenic, and silver depending on the original composition, the fluxes added, and the particular type of operation, see Fig. 1. In order to produce a pure lead, a series of refining operations are carried out. A typical lead-bullion analysis before drossing is shown in Table I. Copper is removed first as its presence increases the zinc consumption during the desilverizing process. For preliminary copper removal the lead bullion is brought to a temperature of 440°C in a kettle of 60 metric tons capacity. Some tar (or sawdust or resins) is usually added and the kettle is cooled slowly to 400°C while the liquid is stirred. A solid phase, called a dross, floats on top of the liquid and the particles of the solid phase adhere to the tar. This "hot dross" is collected. It contains mostly lead and copper which are partly oxidized and/or sulfurized if the lead bullion contains some sulfur.*

Jan 1, 1963

By G. B. Misra

Though resistance to flow offered by mine airways supported with timber sets has been an object of study over the last half century, no accurate relation has yet been established from which prediction of the resistance coefficient of a projected timbered airway can be made. Zenofontowa et al. developed an empirical relation, but this relation has not been found to satisfactorily correlate experimental data obtained by Sales and Hinsley. This led the author to develop a set of simple theoretical relations between the resistance coefficient of timbered airways and the various parameters affecting it, such as the type and spacing of sets as well as the shape and size of members forming the set. Experiments were designed with the help of a laboratory model airway to verify the validity of the relations developed. With the experiments conducted so far with 4, 3 and 1-piece sets of 3.4 x 3.4, 2..5 x 2.5, and 4.5 X 4.5-cm square-section timbers in a 45.8 x 38-cm model airway, the theoretical relations have been shown to hold.

Jan 1, 1972