By Eleanor Haslem, Carl A. Zapffe

THE present investigation has three principal purposes: I. To develop a method for measuring hydrogen embrittlement that avoids certain errors complicating previously used methods. 2. To explore in a preliminary way some of the fundamental factors controlling embrittlement. 3. To apply the measurements specifically to stainless grades of steel, whose sensitivity or insensitivity to hydrogen embrittlement has never been clearly defined. SELECTING A TEST METHOD Hydrogen embrittlement is a condition of low ductility resulting from excessive absorption of hydrogen by the steel at some period in its history, and may be revealed by almost any test involving cold deformation. Tensile tests, impact tests, and bend tests are commonly used for detecting hydrogen embrittlement; although numerous other tests, such as cold-upsetting or extrusion, could be used. The simplicity of using a wire specimen for cathodic and acid pickling tests, and the especial adaptability of the bend test to wire specimens, led to selection of the bend test for the present research. Bend tests usually have been of three general types: (I) fatigue, (2) reversed bend, and (3) single bend. The first two types, though widely used, are inaccurate because their measurements are counteracted by an aging effect; and the third type has not been developed to its fullest utility. The effect of cold-working in removing hydrogen is well known. During a bend test hydrogen can be observed escaping from the convex side simply by coating the specimen with oil; and any technique employing flexing or reverse bending may therefore have its measurements masked because the mechanical action reduces the embrittlement during the test. This factor is so important that even elastic flexing of a hydrogen-charged wire specimen should be avoided before testing if accurate measurements are desired. DEVELOPING A MACHINE FOR MEASURING HYDROGEN EMBRITTLEMENT As for the single-bend test, its theory is good, and recovery caused by mechanical work is kept to a minimum. With a given degree of hydrogen embrittlement, a specimen will break at a given angle if the bending is applied unidirectionally and uniformly. The radius of the bend must be kept constant; and the rate of bending should be a constant, slow enough to allow reading of the breaking angle, and yet rapid enough to prevent significant recovery from the escape of hydrogen during bending. A simple apparatus (Fig. I) was constructed using a type H Foxboro drive unit A, which is a synchronous motor with a gear-reduction ratio of 600 to I. A cord, fixed at one end to a wooden pulley B on the drive shaft of the motor, follows the pe-

Jan 1, 1946

By John E. Conley

THE slate industry of the United States has shown a marked decline in value of products made annually since the peak year 1925, although there has been moderate improvement over the lean years 1932 to 1934. In 1940, the value of all slate products sold was approximately 5 ¾ million dollars for a total output of 473,450 short tons. The quantity sold was a little less and the value a great deal lower than the annual averages for the past two decades. Enormous quantities of waste materials result from the quarrying, splitting and milling of slate. Obviously, utilization of such waste material is desirable, not only from the viewpoint of economical operation but also for the purpose of conserving natural resources. One possible use is to produce expanded or puffed lightweight aggregate for use in concretes. Such concretes are strong enough for specific uses, and the advantage of lightness could be obtained in such structures as the walls and roofs of buildings, suspension-bridge roadways and various other applications where weight is a factor. Conceivably, these uses could consume an appreciable annual tonnage. USE OF WASTE SLATES FOR MAKING AGGREGATES The lightweight-aggregate industry has been discussed elsewhere4.5 and need not be covered in detail in this paper. The materials commonly utilized are naturally occurring aggregates such as volcanic cinder, tuff and pumice; by-product materials, such as ordinary cinders and air-cooled slags; and the specially manufactured products, including Haydite, Pottsco, Gravelite, Cel-seal, Superock and Waylite. Slates, however, have not been given the consideration they merit, especially in the United States. In the British Isles, some work has been done3 on certain Welsh slates by the Building Research Station to stimulate the use of these wastes. REQUIREMENTS FOR RAW MATERIALS As pointed out by Hughes,4 the light-weight-aggregate industry is segregated in regions adjacent to large cities in order to localize the market and avoid the necessity of long freight haulage. Waste slate from the deposits of eastern Pennsylvania, northern Maryland, and Virginia would meet the basic requirement of any low-priced structural raw material. One apparent advantage is attained when slate waste, normally discarded, is utilized in the manufacture of a by-product. Mining or quarrying costs usually have been assessed against the main product. Some additional grinding might be desirable, but this operation would be relatively cheap, as most slates grind easily. It is believed that virtually all slates, when properly heated, will expand to some degree. However, types that will expand from 3 to 7 times their original volume are preferred. Fig. I illustrates the expansion of a Pennsylvania slate. The cube originally

Jan 1, 1942

By L. D. Wooddy, Robert Moscrip

The simultaneous solution of the volumerric balance and the unsteady-state equation has been used for several years to make performance calculations for combination drive reservoirs. This method makes possible the calculation of volumetric changes of fluids in the gas cap, oil zone, and aquifer which occur as a result of withdrawals and reservoir pressure changes. It does not provide a means for the determination of reservoir fluid distribution changes corresponding to these vollrmetric changes. A knowledge of the fluid saturation distribution in the reservoir at various stages of depletion is important for the determination of the efficiency of gas and water as oil-displacement media and, therefore, for the reliable predicrion of ultimate oil recovery. To provide this knowledge, the displacement equations are solved simultaneously with the volumetric balance and unsteady-state equations. The described calculation procedure has been used satisfactorily to analyze the past performance and to predict the future behavior of combination drive reservoirs under both primary and pressure-maintenance operations. INTRODUCTION The three basic mechanisms by which oil is displaced from a reservoir are: (1) dissolved gas drive—the displacement of oil by the expansion of liberated solution gas, (2) water drive—the displacement of oil by water which enters the oil zone from the aquifer, and (3) gas cap drive—the displacement of oil by gas which ex- pands into the oil zone from the gas cap. The action of gravitational forces may be effective in increasing the efficiency of the basic drive mechanisms. Gravitational forces favor the segregation both of gas and oil and of oil and water, thus tending to shorten the transition zone between oil and displacing fluids. Most reservoirs produce under the influence of a combination of these drives and are designated "combination drive reservoirs". Fig. 1 is a cross section of a typical combination drive reservoir. A calculation procedure for analyzing the performance of combination drive reservoirs has been developed by combining the displacement equations' with the volumetric balance equation' and the unsteady-state equations. The pressure-production performance and the positions of the gas-oil and oil-water contacts are calculated for several stages of reservoir depletion by solving these equations simultaneously, thus affording a basis for: 1. Determining instantaneous and ultimate oil, gas, and water production under various operating conditions. 2. 'Establishing a maximum efficient rate of production, 3. Determining the advantages of pressure maintenance and unitization, and 4. Designing surface installations necessary for primarv and pressure-maintenance operations. DEFINITIONS The calculation procedure for combination drive res-

Jan 1, 1957

By R. J. Charles

SEARCH for a consistent theory to explain the relationship between energy input and size reduction in a comminution process has accumulated, over the years, an enormous amount of plant and laboratory data. Although some correlation of these data has been possible for purposes of engineering design and for the advancement of research in fracture, there is still great need of a means of predicting behaviour of a solid when it is reduced in size by mechanical forces. The best known hypotheses proposed to describe the energy-size reduction relationships in crushing and grinding stem from a common origin. The present article analyzes problems of comminution in the light of the precepts of this origin. Its object is to reconcile points of difference between these well known hypotheses and to present relationships more widely applicable to comminution studies.

Jan 1, 1957

By T. E. Leontis, R. S. Busk

WORK was initiated several years ago at The Dow Chemical Company to determine the applicability of powder metallurgy processes to magnesium and its alloys. Although it was found possible to apply the normal techniques of compacting and sintering, it was discovered early that the technique of extrusion offered special promise. This technique and the alloys produced were therefore studied extensively, and the present paper is a partial report of those studies. It is expected that a second paper will discuss more extensively some of the alloy systems simply mentioned here. Although the literature on powder metallurgy is very extensive, there are only two articles dealing with magnesium13,14 and there is no reference to the direct extrusion of the powder of any metal without the preliminary step of compacting. Furthermore, no mention has been made of the possibility of designing alloys by the technique of powder extrusion, particularly alloys that cannot be made in any other way. Sauerwaldl3 discusses the extrusion of magnesium and aluminum powder to produce alloys containing nonequilibrium phases, but again he emphasizes the importance of pre-compacting before extrusion. There seems to be general agreement that some form of hot-pressing is essential to obtain in a compact the full theoretical density of the metal used.'-" The nearest approach to the technique of direct powder extrusion is that of extrusion of pre-sintered compacts,'-" for which the best review through 1944 is that by Kieffer and Hotop.11 Ensign* discussed a specialized technique of "extruding" already compacted and sintered gears for the purpose of sizing. Sauerwa1d13 discussed the compacting and extrusion of magnesium and magnesium-aluminum alloy band-saw chips. The properties of the extruded compacts were found to be comparable with those of extrusions prepared from solid billets. He also extruded a compacted mixture of magnesium and aluminum powder and found the properties to be somewhat different from those obtained on an extrusion made from a cast billet of the same composition. The second reference dealing specifically with the powder metallurgy of magnesium is Stern's patent," in which is described the extrusion of scrap chips and turnings following a hot-pressing and sintering step. Considerable emphasis in most of these articles is placed on the necessity of atmospheric protection to minimize the danger of oxidation. Experimental Procedure The first experiments were made with the small extrusion press shown in fig. 1. With this press, billets of about 1/2 in. diam are used to produce wire

Jan 1, 1951

By C. H. Mathewson, H. M. Day

The constitution of the system silver-mercury has attracted the attention of many investigators during the last two decades, but since their results are for the most part in poor agreement, there is little need for a review of their individual contributions. It remained for the very careful thermal and microscopic investigation of Murphy1 in 1931 to give the constitutional diagram in its present and unquestioned form, which is shown in Fig. 1. He devised methods for taking cooling curves on alloys under high pressures and for the microscopic observation of alloys which contained liquid mercury as a structural constituent at ordinary temperatures. The compositions of the intermediate phases were confirmed and supplemented through X-ray analyses by Preston2 and Stenbeck.3 According to Murphy, at 2760 C. silver is able to dissolve 44 to 45 weight per cent of mercury, which may increase at lower temperatures to about 50 per cent. Preston concluded that the saturation boundary occurred at 46 ± 2 per cent at 100° C. From the values reported in the literature, these are the only ones that may be accepted as lying even in the right region. Preparation of Alloys The silver used in the present investigation was supplied by the United States Metals Refining Co. through the courtesy of the Committee on Industrial Uses of Silver and, since a complete spectrographic and chemical analysis was furnished, no attempt was made to purify it or to further establish the impurities present. The analyses reported by the company are shown in Table 1. Milligan4 has found that the magnesium content is probably less than 0.0005 per cent.

Jan 1, 1938

By H. M. Day, C. H. Mathewson

The constitution of the system silver-mercury has attracted the attention of many investigators during the last two decades, but since their results are for the most part in poor agreement, there is little need for a review of their individual contributions. It remained for the very careful thermal and microscopic investigation of Murphy1 in 1931 to give the constitutional diagram in its present and unquestioned form, which is shown in Fig. 1. He devised methods for taking cooling curves on alloys under high pressures and for the microscopic observation of alloys which contained liquid mercury as a structural constituent at ordinary temperatures. The compositions of the intermediate phases were confirmed and supplemented through X-ray analyses by Preston2 and Stenbeck.3 According to Murphy, at 2760 C. silver is able to dissolve 44 to 45 weight per cent of mercury, which may increase at lower temperatures to about 50 per cent. Preston concluded that the saturation boundary occurred at 46 ± 2 per cent at 100° C. From the values reported in the literature, these are the only ones that may be accepted as lying even in the right region. Preparation of Alloys The silver used in the present investigation was supplied by the United States Metals Refining Co. through the courtesy of the Committee on Industrial Uses of Silver and, since a complete spectrographic and chemical analysis was furnished, no attempt was made to purify it or to further establish the impurities present. The analyses reported by the company are shown in Table 1. Milligan4 has found that the magnesium content is probably less than 0.0005 per cent.

Jan 1, 1938

By H. R. Aldrich

This paper presents some of the results obtained during the field season of 1919 while mapping, in detail, the stratigraphy of the Gogebic Range in Wisconsin. The detailed stratigraphic section for the range was first published, in 1919, by W. 0. Hotchkiss,1 State Gcologist of Wisconsin. The idea of the continuity of the definite succession thus established was the result of underground work in the productive part of the range in Michigan and Wisconsin, where most of the required data also were obtained. The bulk of the range in Wisconsin is heavily covered by drift; in fact, there is but one satisfactorily exposed section across the entire formation, few partial sections, and only scanty outcrops of any size. Evidently mapping of the detailed members of the formation could only be established at a few points; and if from these small areas the .unexposed portions were to be mapped by projection, the only apparent method for projection was straight-line interpolation modified or supported by data from the scanty outcrops and from test workings. It was found that by tracing a magnetic line, the position of which in the formation may be determined from test pits and outcrops, the projection of that member through the drift-covered areas can be accomplished. The magnetic line serves as a datum horizon within the formation to which reference may be made in correlating outcrops and ledge matter thrown from test workings. The foot wall is easily located also, and from the two datum horizons thus available and the known proportional thickness of the several members in the type sections, outcrops and artificially exposed ledges can be correlated by lithological characteristics. As a result, the tracing of magnetic lines became the basis of our work on the stratigraphy and we were able to carry the mapping of detailed members throughout the length of the range. It was found that the magnetic horizon at the base of the Tyler slate was most easily followed by the dip needle; that discontinuity caused by cross-faulting could be established; that folding along the strike could be detected in a repetition

Jan 1, 1922

By C. V. Millikan

When a flowing oil well is being drilled in with cable tools, it is difficult to determine when an additional streak of pay sand is drilled. By placing a gas meter on the gas-release line from the oil and gas separator, any increase in volume of gas that comes with oil production is recorded. In addition to the better knowledge of sand conditions, these data are a valuable aid in determining the size and depth of shots, plugging off water, and estimating ultimate production. The meter also gives a record of operation while the well is drilling in; and if allowed to remain on the well after completion will give information that may lead to a more efficient recovery of the oil from the sand. A VERTICAL cross section of any oil sand will show great variation in porosity and oil content. In some sands, the entire thickness contains oil, the variation being only the degree of porosity or oil content, but more often the pay streaks are distinctly separated by shells or barren streaks. These pay strata vary in number and may be thin or thick. The total thickness of the sand may be several tens of feet while the part containing oil may be only 1 or 2 ft. thick. The amount of production is not proportional to the thickness of the sand but rather the thickness of the pay streaks. If the total thickness of the sand or the amount that can be drilled is small, or if the initial production is small, the depth at which each stratum of pay is encountered can be determined sufficiently accurately for all present economic purposes. However, when drilling through sand of considerable thickness, giving large initial production, especially where conditions necessitate that the production go through the same gas trap with that from one or more wells already producing, it is difficult to determine the depth at which the pay strata are encountered even accurately enough to guide the placing of shots, and small pay streaks are apt not to be recognized at all.

Jan 9, 1925

By Hillary W. St. Clair

An equation is derived for the rote of reaction of a sphere of metal oxide in a restricted enclosure through which a reducing gas is flowing. The equation takes into consideration the reaction rate coefficient, transport through the gas and through the porous shell of reduced oxide, the rate of gas flow, THIS paper describes a mathematical study of the chemical and physical processes that determine the rate of reduction of solid metal oxide with a reducing gas. The study was a part of a theoretical study leading to the development of a mathematical model for the simulation of the thermochemical behavior of the iron blast furnace. An essential feature of such and the volume of- space surrounding the sphere available for gas flow. The equation is applied to experimental data on vote of reduction of iron oxide in hydrogen. The equation serves as a model for predicting the course of reduction of a particle of. metal oxide in a shaft furnace. a model is an adequate mathematical relationship defining the rate of reaction in terms of all the important chemical and physical phenomena that affect the rate of reaction. This includes not only the reaction rate coefficients, equilibrium ratios, gas composition, and temperature, but also the relevant physical properties of the oxide, rate of gas flow, and relative volumes occupied by gas and solid. In many previous experimental studies of the rate of reduction of oxides by hydrogen or carbon monoxide, the rate of reduction was assumed to be controlled primarily by the chemical reaction at the

Jan 1, 1965

By John Jermain Porter

THe value of any particular ore, coke, or limestone, for iron-making, depends upon its effect, first, upon the quality or value of the resultant product; and second, upon the cost of smelting. The factors under the first head are the percentages of phosphorus, manganese, and other elements, which remain in the pig-iron ; while those under the second head are the percentages of iron, carbon, or lime, the slag-forming constituents, which must be fluxed, and any other ingredients which give rise to variations in cost of fuel and flux. The first of these criteria of value is perhaps not capable of being reduced to a general formula embracing all cases, since it must vary to a great extent with market-fluctuations. For example, Bessemer pig is worth sometimes more and sometimes less than foundry-pig; and the premium paid for high manganese varies within wide limits. The second, or smelt-ing-value, however, can be expressed numerically with a fair degree of accuracy; and it is with this phase of valuation that the present paper is concerned. The utility of a means of comparing numerically the relative smeltiug-values of difierent ores, cokes, and limestones, is self-evident, although it may not have importance in Northern practice, where materials are largely standardized. On the other hand, there are, especially in the South, many furnace-managers who must use a great variety of materials of widely varying grade; and it is with special reference to this district, and in connection with the efficiency-methods which I have elsewhere proposed,' that the methods herein described were devised.

Jan 1, 1913

By L. Segle, R. Resnick

NUMEROUS experiments in the past few years have proven that void formation occurs quite generally in the diffusion zone of bimetal specimens1-4 The phenomenon has been explained in terms of the accumulation of lattice vacancies resulting from unequal diffusion of the constituents and their eventual precipitation as holes.= Attention has recently been directed to the fact that voids also form within homogeneous metals during high-temperature creep.' The idea has been put forward that these voids form by the condensation of excess lattice vacancies generated by intersecting dislocations.".' If the precipitation of lattice vacancies from solution is treated as a nucleation and growth process, the predicted vacancy concentration for homogeneous nucleation of voids at an observable rate is 100 to 1000 times the normal thermal equilibrium concentration. It appears that voids actually form during diffusion at vacancy supersaturations which are much lower than this8 According to the calculations of Machlin,' the same must be true for voids formed in homogeneous metals during creep, if these are considered to arise from the precipitation of lattice vacancies. Therefore, if the vacancy mechanism is valid, it seems that the holes which form in diffusion and creep specimens are heterogeneously nucleated by imperfections or impurities in the metal. Irregularities in the frequency and distribution of voids in diffusion couples bear out this explanation.' , It is not known at the present time what the nuclei are on which vacancies condense. Various investigators have speculated that they could be certain dislocation configurations, already existing voids produced during solidification or working, gas pockets, or inclusions in the metal. Relatedly, the precise value of the degree of vacancy supersatura-tion for void nucleation is still uncertain. An initial attempt to estimate this value from diffusion data, made by Balluffi, indicated that voids form in diffusion couples at vacancy concentrations which may

Jan 1, 1958

By Galen Clevenger

THE losses of gold and silver occurring during the conversion of the precipitate, resulting from the cyanide process, into bullion may occur in two ways: first, there may be mechanical losses during the handling of the precipitate up to the time that it is charged into the melting furnace; and second, there may be losses after the precipitate reaches the melting furnace. Much of the loss during the handling of the pre-cipitate can be eliminated, and in fact, in modern plants this loss is known to be very small; particularly since preliminary acid treatment of the precipitate with the attendant extra operations has been abandoned in all but certain plants where gold predominates and this extra step is still deemed necessary. The losses in the melting furnace are from dusting and volatilization; losses in the furnace bottom and linings; floor sweepings; and slag and matte. The gold and silver in the: products which do not: go out of the flue are readily recoverable by standard methods, and while there may be considerable gold and silver tied up at times, the ultimate loss with careful "work should be small. The losses resulting from volatilization and dusting in connection with the melting of the silver slime from copper refineries have been determined by standard methods, and the possible recovery: definitely estab-lished through the installation and operation of electro-static precipitation units. This subject has not been thoroughly investigated in connection with the melting of`. cyanide precipitate; at least, there are no published accounts of such tests. Experiments have been made in the past to determine melting losses by weighing and assaying the precipitate, but this method gives results which are uncertain on account of the difficulty of accurately sampling and assaying cyanide precipitate. Attempts to ascertain these losses by bubbling a measured sample of the gas through cyanide solution or, other absorbent have likewise failed to give depend-able results.

Jan 1, 1922

By E. W. Davis

THE mysterious Lake Erie price for iron ore, established each spring, determines the maximum price that will be paid during the following season for ore of Mesabi Non-Bessemer base grade. This price is impor-tant to the ore producers, but since most of the ore in the Lake Superior district is owned or controlled by consuming inter-ests, the really important question to them is not the price of ore but how much it will cost them to mine and transport their season's requirements to their furnace plants. However, a few million tons are actually sold each year, and considerable quantities are traded for mixing purposes, and the negotiations for these sales and trades usually begin with some reference to the Lake Erie price. There is no difficulty with the Lake Erie price itself or with the manner in which it is established, but the system prescribed for determining the values of ores that are not exactly base grade is incomplete. The Lake Erie price takes into consideration only the iron and phosphorus contained in the ore, but when the ore producer is negotiating a sale or trade, he is confronted by the fact that his ore must be studied and the price adjusted, not only on the basis of the iron and phosphorus analyses, as specified by the Lake Erie price, but also on the basis of silica, alumina, man-ganese, structure, etc. The vague and unsatisfactory methods used in making these adjustments bear some relation to the manner in which the ore is supposed to act in the blast furnace. The ore producer may not understand all of the idiosyncrasies of the blast furnace, but if the smelting-plant operators have a system more accu-rate than the Lake Erie price method for determining the relative values of different ores, why not pass this information on to the ore producers, so that they can make use of it and perhaps modify their practice in such a manner as to benefit both them-selves and their customers? There is a lack of understanding and appreciation between these two groups that may, to some extent, be unavoidable, but in the interests of efficiency and conservation rules that are more accurate and complete than the Lake Erie price method in use at the present time should be established for the guidance of the ore producers.

Jan 1, 1940

By H. J. Booss

THERE is a considerable lack of data on thermody-namic properties of hard-metal alloys. Only two papers 1,2 give mean values of specific heat in an unknown temperature range; more recently the author3 gave more detailed information on the mean specific heat in the temperature range from 20" to -190° C.. EXPERIMENTAL 1) Method—Experimental procedure followed a method suggested by Oelsen and coworkers.4 It requires samples of some 100 g of weight. The time of measurement is prolonged (30 min) but one run allows the measurement of a lot of positions on the heat-content curve. Results4 were found to be in good agreement with "best values" given by kelley,5 Kubaschewsky and Evans,6 etal.

Jan 1, 1960

By Howard N. Eavenson

WHEN the A.I.M.E. was formed 75 years ago the bituminous coal industry was in its swaddling clothes, although it had been operating for more than a century and coal was being mined in every state now producing it, and its output had long passed that of anthracite. In 18/1, the value of bituminous coal was about seventy per cent of the value of all metals produced and more than one fifth of the value of all products of mines, both metallic and nonmetallic.[1a] While many of the operating mines then shipped by rail, most of the development was along waterways, although the canal era of transportation was nearly at its end. Coal mining is a heavy industry and one of the best measures of its progress is its output throughout the period. Fig. 1 shows this graphically from 1800 to 1945. From 1870 to 1910, the production-which is very nearly the consumption-almost doubled every decade, a most amazing growth. In 1918, in World War I, a peak was reached and a decline began, which ended in 1932. A gradual recovery then started, interrupted in 1938 but culminating in the record output of 1944, when, owing to World War II, a tonnage of 619,576,000 was produced. It is evident that the forces leading to the continuous increase ending in 1918 have spent themselves and that only unusual conditions will require so large a production again. The postwar conditions of World War II will probably

Jan 1, 1947

By George A. Roberts, Robert F. Mehl

When austenite first forms from aggregates of cementite and ferrite, it is not homogeneous.' This inhomogeneity, consisting of both undissolved carbide and carbon concentration gradients, has a profound effect upon the characteristics of the austenite-pearlite reaction. The rate of formation of pearlite is increased by the presence of inhomogeneities2,3 and because of this (when the inhomogeneity is sufficiently pronounced) the hardenability of the steel is reduced.4,5 In addition to this kinetic effect, inhomogeneities will cause the direct formation of spheroidite from austenite at temperatures just below the Ael.6-11 The present report attempts quantitatively to evaluate the effect of inhomogeneity upon the rate of the austenite-pearlite reaction, presents a method of determining the austenitizing cycle necessary to obtain "practical homogenization," and considers the effect of inhomogeneity on hardenability. Effect of Inhomogeneities on Reactions Near Ae1 Few quantitative data are available representing the effect of undissolved carbide or of carbon concentration gradients upon the rate of the austenite-pearlite reaction. In procuring such data it is necessary to separate the effect of undissolved carbide from that of grain size, and this is not an easy task. The solution of carbide is always accompanied by an increase in the grain size, both effects contributing to the retardation of the reaction rate. It has been possible to make this separation and to obtain data that are independent of the grain size by the use of steels that differ only with respect to their tendency toward grain-coarsening. Steels C and D in Table I are such steels. These steels have been studied previously ;l,2,12 they differ only with respect to deoxidation practice; C was deoxidized with silicon while D, teemed from a portion of the same heat, was deoxidized with additional auantities of aluminum in the mold. C therefore is what is normally termed a "coarse-grained steel" and D is a, "fine-grained steel." These steels can be compared at the same grain size by heating c to a low temperature and heating D to an elevated temperature, producing a structure of austenite plus residual carbide in the former while forming homogeneous austenite in the latter; in such

Jan 1, 1943

By George A. Roberts, Robert F. Mehl

When austenite first forms from aggregates of cementite and ferrite, it is not homogeneous.' This inhomogeneity, consisting of both undissolved carbide and carbon concentration gradients, has a profound effect upon the characteristics of the austenite-pearlite reaction. The rate of formation of pearlite is increased by the presence of inhomogeneities2,3 and because of this (when the inhomogeneity is sufficiently pronounced) the hardenability of the steel is reduced.4,5 In addition to this kinetic effect, inhomogeneities will cause the direct formation of spheroidite from austenite at temperatures just below the Ael.6-11 The present report attempts quantitatively to evaluate the effect of inhomogeneity upon the rate of the austenite-pearlite reaction, presents a method of determining the austenitizing cycle necessary to obtain "practical homogenization," and considers the effect of inhomogeneity on hardenability. Effect of Inhomogeneities on Reactions Near Ae1 Few quantitative data are available representing the effect of undissolved carbide or of carbon concentration gradients upon the rate of the austenite-pearlite reaction. In procuring such data it is necessary to separate the effect of undissolved carbide from that of grain size, and this is not an easy task. The solution of carbide is always accompanied by an increase in the grain size, both effects contributing to the retardation of the reaction rate. It has been possible to make this separation and to obtain data that are independent of the grain size by the use of steels that differ only with respect to their tendency toward grain-coarsening. Steels C and D in Table I are such steels. These steels have been studied previously ;l,2,12 they differ only with respect to deoxidation practice; C was deoxidized with silicon while D, teemed from a portion of the same heat, was deoxidized with additional auantities of aluminum in the mold. C therefore is what is normally termed a "coarse-grained steel" and D is a, "fine-grained steel." These steels can be compared at the same grain size by heating c to a low temperature and heating D to an elevated temperature, producing a structure of austenite plus residual carbide in the former while forming homogeneous austenite in the latter; in such

Jan 1, 1943

By J. A. Thompson, M. A. Mayers

IN recent years, the problem of damage to coke-oven walls by expanding coal charges undergoing carbonization has engaged great attention on the part of research workers in this field, and has led to the development of many devices for estimating these pressures.1-14 Only in Russell's method11 and in the Koppers ovens7 are conditions quite similar to those in commercial ovens. Tests even in these ovens are empirical because no information has been published to permit an evaluation of "scale effects." Owing to the relatively large wall area in these test ovens, the average wall pressure determined may be lower than that existing in localized areas. This factor may be compensated for in part by the testing of coal charged into the test oven at a bulk density that is as high as the highest that is believed to exist in commercial ovens. Both of these lacks might be filled by the development of an adequate gauge for the direct measurement of wall pressure exerted by the charge in commercial coke ovens in normal operation. Previous attempts to elaborate such instruments7,15 have resulted in units which, because they had to be water-cooled, probably produced changes in the conditions of carbonization, and which had to be removed from the oven before carbonization was complete, to avoid their destruction. Late in 1941 the Coal Research Laboratory undertook to develop such a gauge, in which gas pressure was balanced against the charge pressure and which thus would not require water cooling, on a suggestion made in 1937 by one of the present authors and William B. Warren, a former member of the Laboratory staff. The gauge heads themselves were to be simple and cheap enough so that they might be discarded after each run if seriously damaged. This would permit them to be left in place throughout the carbonizing period, when they could be pushed out with the coke. The basis of the design, of which the latest exemplification is shown in Fig. I, was that as the internal gas pressure within a flexible metal envelope was increased, the flexible wall would move away from a stop when the gas pressure just overbalanced the charge pressure. If the stop were an insulated electrical contact, the point of balance could be indicated by the breaking of an electric circuit. It was anticipated that, while the instrument must operate at high temperature, the presence of a strongly reducing atmosphere throughout the carbonizing period would so reduce-the danger of scaling that mild steel could be used for the gauge. This expectation has been justified. Danger of attack on silica oven walls by the steel gauge body can be eliminated by cementing asbestos paper or an alundum or silica plate to the back of the gauge body. The gauge head itself has a relatively heavy mild-steel body, A, into which standard ¼ in. pipe B is screwed to conduct gas and electrical leads. The body is closed by a single bellows C. consisting of two annuli of 0.011-in. (0.28-mm.) cold-rolled shim-steel spot-welded together at their outside edges. The lower one is

Jan 1, 1944

In March 1962, over three months ahead of schedule, production began from the Ventersdorp Contact Reef of the Western Deep Levels Ltd. mine on the West Witwatersrand. Few mines have captured the interest of mining men and the public as has Western Deep Levels. It has presented the gold mining industry with a challenge which involved the opening of an ultradeep mine with the attendant problems of exceptionally heavy capital commitments ($77 million to start of production), high rock temperatures and pressures at great depths, cementation and pumping in an area notorious for the volume of subsurface water, and the necessity for entirely new thinking and the application of new ideas. HISTORY Not all the problems facing Western Deep Levels were, however, new. Situated 43 miles from Johannesburg, just off the main road to Potchefstroom, Western Deep Levels was the sixth company to undertake mining operations on what is known as the West Wits line and it could draw on the wealth of experience gained by other pioneer mines in the area.

Jan 12, 1962