By Sutham Niyomwas

Synthesis of alumina-mullite-silicon carbide composite (Al2O3-Al6Si2O13-SiCw) was obtained in situ by carbothermal reduction of a mixture of kaolin and two different silica sources. The carbothermal reduction was carried out in a horizontal tube furnace under flow of argon gas. The standard Gibbs energy minimization method was used to calculate the equilibrium composition of the reacting species. The synthesized products were mixtures of alumina, mullite and silicon carbide in the form of whiskers. The effects of adding two different silica sources of rice husk ash and silica powder to the mixture of kaolin and activated carbon were investigated. XRD and SEM analyses indicate complete reaction of precursors to yield Al2O3- Al6Si2O13-SiC as product powders, with the SiC having whisker morphology.

Jan 1, 2006

By Lucas Lopes da Costa

In this work, a natural foam extracted from the Amazon buriti palm tree is investigated as possible substitute for synthetic foams. The basic physical and mechanical properties of this biofoam were evaluated. Its sponge-like structure was characterized by the amount of pores and morphological aspects. It was found that the buriti biofoam displays a very low density of the order of 0.1 g/cm3 with a relatively good compressive strength. This would be suitable for several engineering applications and as a new material with the potential for replacing currently applied synthetic polymeric foams.

Jan 1, 2010

By Yunyan Wang

Diagrams of pc-pH for the complex ions concentration and pH value and -g- for activity coefficient and ionic strength ln±MnSOI4had been drew based on the thermodynamic principle of coordination chemistry and combined with Pitzer theory at 298.15K. The diagram of -g- indicated that -gincreased sharply from 0.0000 up to 1.2147 when I changed from 0.00 ln±MnSOIln4±MnSO4to 0.09; The increase of -gbecame slowly when I was more than 1.00 and less than 1.69; kept still when I ln±MnSOln4-g±MnSO4was more than 2.25 and less than 4.00. Diagrams of pc-pH illustrated that the minimum solubility of Mn(OH)2(s) increased with the increase of I, the pc increased from 6.5 to 5.5 when I increased from 0.00 to 4.00; The pH of the minimum solubility of Mn(OH)2(s) increased with the increase of I, the pH increased from 11.80 to 12.76 when I increased from 0.00 to 2.89, the pH kept still when I (I was less than 4.0) increased. There is single function relationship between the minimum solubility of Mn(OH)2(s) and relevant pH in different I.

Jan 1, 2010

By A. R. Kiani-Rashid

In this paper, the effect of aluminum content on the formation mechanism, volume fraction, morphology and particle size distribution of graphite has been investigated. Addition of aluminum on ductile iron causes some fundamental changes in iron-carbon phase-diagram and as a result, improves the graphite formation during eutectic transformation. The results reveals that aluminum compounds have been formed in the core of graphite nodules, thus aluminum plays an important role in the formation of graphite nodules. Furthermore, it is indicated that an increase in the aluminum content also leads to an increase in the number of graphite nodules and a decrease in the nodules size. By using EPMA, the segregation of aluminum and silicon between graphite nodules has been studied

Jan 1, 2010

By Sutham Niyomwas

The Fe-TiC composite powder was synthesized in situ by carbothermal reduction of ilmenite. The standard Gibbs energy minimization method was used to calculate the equilibrium composition of the reacting species. The effects of the reaction temperature (1300 °C - 1500°C) and milling time of precursors on the Fe-TiC conversion and powder morphologies were investigated using XRD and SEM method. The synthesized products showed that composite with iron matrix and titanium carbide as a reinforced phase was formed.

Jan 1, 2006

By Valerio Viti

In High Pressure Die Casting a molten metal is injected through a thin gate into the cast cavity. High injection pressures and high gate velocities create atomization phenomena which can negatively affect the final quality of the cast. In order to control atomization process it is essential to understand the atomization patterns and the two-phase flowfield that exist at the gate exit. In the present work, 2D numerical simulations of the flow of molten Magnesium through a high aspect-ratio rectangular gate are performed using a water analogue for an open and closed cavity. The numerical simulations made use of VOF-type (Eulerian) physical models and Lagrangian models. Further, a sub-grid scale model was implemented that, in conjunction with VOF-type equations can efficiently predict the general atomization pattern without the need for high-resolution grids. The numerical results were compared to experimental data for validation.

Jan 1, 2006

By Meghan McGrath

Third generation advance high strength steels with microstructures of acicular ferrite and retained austenite were investigated and meet mechanical property goals. A good combination of strength and ductility were achieved with duplex ferrite and austenite microstructures where cementite formation was suppressed. Transformation induced plasticity (TRIP) behavior produced rapid work hardening. The mechanical properties of two hot-rolled steels with duplex microstructures were compared and had the following compositions: (1) Fe-0.14C-13.87Mn-1.42Si-3.51Al; and (2) Fe-0.06C-14.2Mn-1.85Si-2.38Al. These steels were cast, homogenized, and hot rolled at 900ºC to obtain a refined microstructure with ultimate tensile strengths and elongations to failure of 865 MPa and 39% and 1,217 MPa and 28%, respectively. The amount of metastable austenite in both compositions decreased after tensile testing from 58% and 28% to 6% and 0%, respectively. Microstructures were characterized using optical microscopy, scanning electron microscopy (SEM), and x-ray diffraction.

Jan 1, 2010

By J. W. Bridge

Triaxial compression tests at various confining pressures and temperatures, as well as tangent modulus tests using ultrasonic waves, were conducted for wax-coated granular composite materials. The material used is a surface for Thoroughbred horse racing. The purpose of these tests is to examine how track shear strength and tangent modulus at a range of loads respond to changing temperatures. Previous work has shown that a wide range of operational temperatures are experienced which have been reproduced in the lab. Using differential scanning calorimetry, it is confirmed that these operational temperatures correspond to distinct thermal transition regions for the wax that is used to coat the sand in these surfaces. Preliminary results show that both shear strength and tangent modulus are sensitive to temperature changes with maximum strength and modulus correlating with major DSC wax transition regions.

Jan 1, 2010

By Hugo Cabrera-Real

This work investigated the chemical and mineralogical properties of CaO-SiO2-CrOx-CaF2- MgO slags. Synthetic slags were prepared and the effect of the slag basicity (CaO/SiO2) and MgO contents on the stability of the mineralogical species formed was analyzed. The morphology and composition of the slags were analyzed by XRD and SEM-EDS, whilst their chemical stability was evaluated by leaching with an aqueous acetic acid solution. It was found that in slags with CaO/SiO2 = 1, the main Cr-compound was MgCr2O4 spinel, which forms octahedron crystals. Small amounts of CaCr2O4 and CaCrO4 were also observed. It was found that increasing the slag basicity from 1 to 2 the compounds MgCr2O4 and CaCr2O4 were formed together with the Cr(V)-containing compound complex Ca5(CrO4)3F which forms hexagonal crystals. The results showed that the highest chromium concentration levels in the leaching liquors corresponded to slags with CaO/SiO2 = 2, probably owing to the formation of Ca5(CrO4)3F.

Jan 1, 2010

By Helga Larravide

A new on-line database of literature about copper has been created through a joint undertaking by the Copper Development Association Inc. and PROCOBRE-Chile, with funding provided in part through the International Copper Association, Ltd. The new database will permit Spanish-speaking technologists to access publications maintained by PROCOBRE-Chile by means of standard keyword searches. In addition, a new Spanish- English thesaurus has been written to enable Spanish-speaking individuals to search d access the Technology and Environmental databases of the Copper Data Center, which together comprise more than 80,000 publications dealing with the production, properties, uses and environmental effects of copper. Planned expansion of the new Spanish literature database is described.

Jan 1, 1999

By P. A. Mahanwar

Flyash were melt mixed with nylon 6 at a 30wt% concentration. TYZOR® TPT, a coupling agent, was used to facilitate the link between filler and matrix. The morphological characterization, using SEM, revealed sufficient matrix residue on the filler surfaces thus confirming the strong interfacial bonding between the filler and the matrix on treating. Tensile, impact and the flexural properties of the composites were also improved with the incorporation of coupling agent. As flyash particles tend to impart a grayish color to the plastic, TiO2 pigment was employed to make the formulations aesthetic. The pigment was added to the filled system in 0.1, 0.5, 1.0, 1.5, 2.0 wt/wt ratios. Scattering of incident light and spectral reflectance was higher for smaller particle size flyash. Moreover an increase in the scattering with increase in pigment concentration indicates better dispersion of the pigment, which again is due to the presence of coupling agent.

Jan 1, 2006

A series of electron beam, cold hearth, single melt Ti-6Al-4V plates (nominally 2.5 cm thick) impacted by 2cm diameter, 4340 steel projectiles (with 54g nominal mass) at velocities ranging from 0.633 to 1.027 km/s were sectioned along the impact axis and examined by optical metallography to characterize the formation, growth, and microstructure of adiabatic shear bands. Near ballistic limit velocities, the shear bands propagate towards the rear of the target where they coalesce and grow to provide a cylindrical solid state flow regime for the plug volume.

Jan 1, 2006

By P. N. Anyalebechi

The effects of solidification rate on the cast microstructures of aluminum alloys 6009 and 6016 have been investigated with directionally cooled laboratory-size ingots, at 0.2-10.1 K/s and 0.4- 23.1 K/s, respectively. These ranges of solidification rate are within those observed in commercial-size ingots. In both alloys, the average dendrite cell size and second phase particle size decreased with increase in average solidification rate and with a decrease in average local solidification time. However, at comparable solidification rates, the dendrite cells and second phase particles are finer in the shorter freezing range alloy 6009 than in the longer freezing range alloy 6016. This is provisionally attributed to the earlier formation of second phase intermetallics at higher temperatures during solidification and to the formation of greater amount of the relatively coarse plate-like ß -phase (Al9Fe2Si4) phases in alloy 6016. In general, in both alloys, the types and relative amounts of the second phase particles in both alloys are independent of solidification rate.

Jan 1, 2006

By F. A. Guo

Ultrafine-grained surface layers were obtained by surface mechanical attrition treatment (SMAT) in copper and titanium samples. The thermal properties of the deformed layers were characterized using a scanning thermal microscopy (SThM) that allows thermal conductivity to be mapped down to the submicrometer scale. A theoretical approach, based on this investigation, was used to calculate the heat flow from the probe tip to the sample and then estimate the thermal conductivities at different scanning positions. Experimental results and theoretical calculation demonstrate that SThM can be used as a powerful tool for the thermal property and microstructural analysis of ultrafine-grained microstructures.

Jan 1, 2006

By Clara María Lamus Molina

The following minerals found in the residual black sands from gold mining in El Bagre Antioquia (Colombia) were identified as having major economic interest: Ilmenite (FeTiO3), with an average of 49% of TiO2, frequently altered presenting crowns; lamellaes of rutile and alteration textures; titanomagnetite with up to 25% of TiO2; magnetite (Fe3O4) in individual grains or associated with others minerals as hematite and ferromagnesian silicates rutile (TiO2) with considerable quantities of Nb2O5(0.1-3.7%Wt); zircon (ZrSiO4) with 66%Wt of ZrO2 and monazite with an average of 63.43%Wt of REE, this frequently associated to xenotime and thorite forming textures as little drops. Analysis in EPMA and SEM/EDS showed percentages of minor elements and traces, thereby clearly establishing the applications of these minerals in diverse industries. Furthermore, a detailed granumetric study of the different minerals and textural relationships among them also allowed for establishing the basis for possible processing and exploitation.

Jan 1, 2006

By Kwong. Kyei-Sing

Gasification is a process that converts a carbon feedstock into synthesis gas (CO+H2). Slagging gasifiers operate at high temperature and pressure and in a corrosive-wear environment from the slag. Cr2O3-based refractory linings are used to protect the steel vessel that comprises the gasifier from the aggressive gasification environment. Increasing service life of the gasifier is one of the keys for wide spread development of this technology. In support of the goals, research on the gasifier atmosphere, the slag chemistry, the interaction of Cr2O3 refractory with different feedstock mixtures (e.g., coal and petcoke) were characterized by post mortem analysis of bricks from service in gasifiers and thermodynamics simulation of the environment. Examples demonstrating how thermodynamic calculations can explain the post mortem results and make predictions of material interactions will be given. Attention is placed on the possibility of Cr+6 in different feedstock mixtures and operating conditions.

Jan 1, 2010

By Taegong Ryu

Nanosized tungsten powder was synthesized by the hydrogen reduction of ammonium paratungstate (APT) in thermal plasma. The effects of operating conditions on the product composition and particle size were investigated. The particle size of synthesized W powder was less than 30 nm in all cases tested. The sintering behavior of the synthesized powder (25 nm average size) was then investigated and compared with those of commercial W powder of 500 nm average size and W powder of 23 nm average size produced by milling the commercial powder. The sintering was done at 1400oC with various holding times. The hardness of the resulting compact from the synthesized W powder (315 VHN) was similar to that from the milled W powder (309 VHN), but the plasma-synthesized powder had a much lower tendency to form cracks. The compacts of both nanopowders were significantly harder than that of the commercial powder (192 VHN).

Jan 1, 2009

By Jacques J. Eksteen

Any effort to improve the metallurgical control of industrial furnaces employed in the primary extraction of high carbon ferroalloys are bound to fail unless the variability of the melt is not fully accounted for. A number of sampling campaigns were performed on both 3phase AC submerged arc and single phase DC open arc furnaces at different smelter sites in South Africa where High Carbon Ferrochrome is produced. It was found that the heterogeneity between multiple samples during a single taps were much higher that for heterogeneity found within a sample. Moreover, this heterogeneity (as quantified by the relative standard deviation per tap) varied with the operating conditions of the furnace, the element monitored and the type of furnace. A relationship was found between the relative standard deviation of certain elements and the degree of subcooling of the melt.

Jan 1, 2006

By Tianjiao Luo

The electroless copper plating process for continuous carbon fiber using CuSO4?5H2O as the main salt and formaldehyde as reducing agent was experimentally studied, including the effects of pH values and concentration of chelating agents, stabilizing agents and reducing agent on the electroless plating process. The surface morphology and the composition of coating were investigated by means of Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray Spectroscopy (EDS), and deposited the coating thickness was measured by way of dissolution. The results indicated that the pretreatment of carbon fiber before plating was so important. This pretreatment could prevent the formation of the black cores, furthermore, it could form many active absorption cores with Ag as the center on the carbon fiber surface. Used the optimized parameters in this process, which led to a stable solution for plating, a homogeneous copper coating was conducted with the carbon fiber plated with favorable mechanical performance and high adhesion strength.

Jan 1, 2006

By Napisporn Memongkol

Syntheses of Al-TiC-Al2O3 and Al-SiC-Al2O3 composites were obtained in situ by carbothermal reduction of mixtures of Al powder, TiO2 powder and activated carbon powders and Al powder, SiO2 powder and activated carbon powders. The reductions were carried out in a horizontal tube furnace under flow of inert gas. The standard Gibbs energy minimization method was used to calculate the equilibrium composition of the reacting species. The synthesized products were mixtures of aluminum reinforce with titanium carbide and alumina and aluminum reinforce with silicon carbide and alumina. The effect of the reaction temperature (1000 o C ? 1200 o C) and condition of precursors on the Al powder, TiO2 powder and activated carbon powders and Al powder, SiO2 powder and activated carbon powders were investigated using XRD and SEM method. The synthesized products showed those composites with aluminum matrix and titanium carbide and alumina as reinforced phases and aluminum matrix and silicon carbide and alumina as a reinforced phase was formed.

Jan 1, 2006