Jan 1, 1957

Several of the current concepts of brittle fracture involve consideration of, the existence of defects or flaws. Griffith 1 observed that the tensile strength of brittle materials was several orders of magnitude less than might be expected from the calculated strength of the molecular bonds. He was able to show that the stress concentration at the tip of an elliptical crack is sufficient to raise the local stress level many fold. He therefore proposed that real materials do contain such stress risers in the form of minute cracks and that this accounts for the rather large difference between theoretical and actual strengths of brittle materials. The degree of stress magnification depends to a great extent upon the orientation of the crack with respect to the general stress system, and to the general geometry of the crack. It is but a small step to extend the theory to include flaws and defects of other sorts which, though they may be less tractable mathematically than cracks, may still function as stress risers in a real sense in real materials. Brace 2 proposed that the application of the Griffith theory to rock material could be tested in two ways: "(a) by finding the orientation of cracks from which macroscopic fractures have developed and (b) comparing failure strengths from tests at different conditions of loading." In 1963 the author and coworkers at the Bureau of Mines, Twin Cities Mining Research Center, working on a problem involving relationships between strength, sonic velocity, and microstructure "eveloped an experimental technique to examine several somewhat similar questions; namely. does the frequency of occurrence of actual or potential stress risers dictate the relative strength of the material as proposed by Weibull;4 can actual flaws or defects in the rock structure be identified and related to strength and perhaps other properties in accordance with Griffith's theory; and is the anisotropic strength and elastic behavior of certain rocks related to the preferred orientation of these actual or potential stress risers? The experimental approach developed to answer these questions appears equally applicable to the testing of Griffith's theory as proposed by Brace. Basically the approach consists of a series of point-load tensile tests followed by petrofabric examination of thin sections prepared from the specimens in order to identify and apply a quantitative measure to microstructural defects which may have contributed to the failure process. In the point-load test, tensile stresses are induced by a compressive load applied to the center of a disc-shaped specimen by means of two opposing hemispherical indentors. Failure generally occurs as a single fracture parallel to the axis of loading and bisecting the disc. Because of the geometrical symmetrical the induced tensile stresses are symmetrical about the loading axis

Jan 1, 1967

By Jack Parker, Bert Caverson

More than 6000 resin-anchored bolts have been installed at the White Pine mine, and their performance has proven excellent in both pull tests and "beam" building. With its improved reliability, resin anchorage will permit a more scientific approach to the design of roof bolting systems, and this should ultimately result in both better support and reduced costs. The White Pine mine lies five miles south of Lake Superior in Ontonagon County. Mich. The orebody occurs in gently dipping upper Keweenawan sediments midway between the Porcupine Mountains and the Bergland Hills, both of which are ranges of steeply dipping Keweenawan extrusives and intrusives.

Jan 1, 1971

By Joseph L. Gillson

In this volume, which is divided into chapters on a commodity basis, many subjects inevitably have a common interest with others, or are interrelated in one way or another. No group of commodities is so outstanding in this regard as is that group of which the basic raw material is a carbonate rock. There are chapters in this book on dimension stone, on crushed stone, on chalk and whiting, on cement, on lime, on magnesite, on sodium carbonate; all of which are entirely, or partly, products of the "carbonate rocks." Rhodochrosite, witherite and strontianite are other carbonates described respectively in chapters on manganese minerals, barium minerals and strontium minerals; and travertine and cave onyx are carbonate materials used as ornamental stones. High grade marble is used for monuments and statues and as a decorative building stone. The aggregate tonnage of the basic raw material, the carbonate rock, is so enormous that it exceeds the tonnage of any metallic ore mined and quarried in the United States, and in turn is exceeded only by coal, sand and gravel, and by water in the gross tonnage produced by the mineral industry in this country. The specialties, including magnesite, sodium carbonate, and rhodochrosite, witherite and strontianite are produced from uncommon rock types of limited occurrence. They are described adequately in the chapters devoted to these subjects. This chapter is concerned with the limestones and dolomites. No other solid rocks are as important as these in the industrial life of the world, nor are any so widely known. Massive units of some carbonate formations form many of the spectacular features of some of the most rugged mountains in the world, such as the Dolomite Alps, the Canadian Rockies, some rugged peaks of the eastern flanks of the American Rockies in Colorado, Wyoming and New Mexico and in many ranges in Utah, Nevada and Arizona. These continue down the Sierra Oriental in Mexico and on around the world to the flanks of the Himalayas, in the South China Highlands, and separating Asia and Europe in the flanks of the Ural Mountains where they form many reexhumed hills called Shikhany.50a Less rugged and more nearly flat-lying carbonate rocks underlie most of the area of our great Middle Western plain, the southern part of England and the northern part of Africa. These are the common rock formations known from boyhood to a large part of the world's population. The use of lime, produced by the burning of limestone, goes back to antiquity, and mortar was used widely in Biblical times. The cement made by mixing volcanic ash with lime was a basic material of construction when Pompeii was built. Our Eastern states are dotted with abandoned limestone quarries, and the ruins of old lime kilns which were operated in Colonial days. Many limestones and dolomites are found in flat-lying strata of a thickness convenient for quarrying as a building stone, so that houses and other structures have been built with them for centuries. In order to replace the muddy and rutted dirt roads with surfaces that could stand the hard usage of his wagons and carts, man learned to crush stone and put a layer of it on his old trails. Such roads built by the Romans have been in use over much of

Jan 1, 1960

By O. D. Gonzalez, R. A. Oriani

The migration of hydrogen and of deuterium dissolved in a iron and in nickel induced by an applied electrical potential has been measured over a range of temperature. In all cases the intevstitial solute migrates to the cathode. The deduced charges of transport are positive, independent of or slightly dependent on temperature, and markedly larger for the beavier mass. These results are interpreted as showing predominating momenlum transfer between electron holes and the acticated complex of the elementary diffusion act. THE migration of components of a metallic system under the action of an applied electrical potential is called electromigration or electratransport. This phenomenon has been known since 1861 and is becoming of increasing interest to metal scientists because of the opportunity it offers to explore the connections between mass transport and electron transport. Until recently, reliable data have been very scarce because of the difficulties inherent in the measurements. In addition, theoretical understanding has been either nonexistent or rudimentary and at present this situation is only moderately improved. Whereas the prevalent notion had been (and is still widely held) that electromigration directly reflects the state of ionization of a component in its equilibrium state in the metal, it is now becoming clear that the major, if not the sole, factor is the momentum transfer between the charge carriers, themselves in motion because of the applied field, and the metallic components in their activated state. It becomes important therefore to obtain reliable data over a range of temperature on electrornigration in systems where only one component moves, that is, either in pure metals (vacancy motion) or in interstitial solid solutions. Our choice of systems was dictated by our measurements' of the Soret effect in solid solutions of hydrogen and deuterium in iron and nickel. Indeed, the main reason for making measurements on electromigration at all is that we suspected a mechanistic connection between thermal diffusion and electromigration. In our former paper' we proposed that what is common to both phenomena is the momentum transfer between the charge carriers in the metal and the atom as it jumps from one equilibrium position to another. In Soret diffusion, however, there is in addition the dissipation of the energy of the jumping atom via pho-nons. We have since found that similar ideas for this interconnection have been developed by Fiks.2 In the present paper we will discuss in more detail our understanding of the mechanism of electromigration itself, but we turn first to a presentation of the experiments and results. EXPERIMENTS AND RESULTS Let us consider a metallic system in which only one component, m , can diffuse at the temperature in question, and to which are applied simultaneously an electrical potential gradient, grad cp, and a chemical potential gradient, grad p,. One may write3 for the material flux Jm and the electronic charge flux Je by applying the condition, grad = 0, to Eq. [I] and evaluating grad(um/T) for the isothermal case and for activity coefficient independent of composition over the relevant composition range. ere, c is the concentration and D the diffusivity of the mobile component. The experimental technique that we have used to measure Z* for the isotopes of hydrogen individually dissolved in each of two transition metals has been developed from a method used by Wagner and Heller.4 (A somewhat similar method was also used by Herold.5) A wire or thin rod of the metal under study connects two volumes of gaseous hydrogen at identical pressures; hence grad um = 0. A direct current is made to pass through the specimen, serving to maintain the specimen at the desired temperature and also to produce the electromigration of the hydrogen dissolved in the metal in equilibrium with the gaseous hydrogen. Under these conditions, the flux of hydrogen from one volume to the other is given, from Eq. [I] for grad( um/T) =0by

Jan 1, 1968

By A. T. Tye

REGARDING the results of preferential flotation at Cananea, Weinig has stated that "The concentrating mill of the Cananea Consolidated Copper Company at Cananea, Mexico, furnishes an excellent example of modern flotation practice. The complete figures are given because they present so forcibly the advantages of modern selective flotation."' L. O. Howard notes that "Perhaps the outstanding example so far published of improvements in results through the use of selective flotation is that at Cananea, Mexico." The following notes indicate the conditions under which the results were obtained at Cananea; also the effect of preferential flotation at the concentrator and at the smelter. In the majority of cases the full benefit of selective flotation is not fully realized, as the concentrates are shipped from the mill to smelters owned by other companies. The saving made at a certain concentrator by this method of flotation may be well understood but the saving resulting at the smelter from the results of preferential flotation at the mill is not so apparent, as the data are contained in the smelting records of some other company. Even at the smelter the great gains following preferential flotation may not be noted, as a variety of ores and concentrates from various sources are received and the difference from the changed concentrator operations of a certain mill may be obscured. As noted by Professor Weinig and Professor Howard, the results obtained at Cananea brought about a veritable metallurgical revolution at the smelter. There are probably plants at which a better preferential separation is being made than at Cananea. Many ores contain barren iron pyrite which, when depressed, does not carry copper into the tailing. Some concentrators use clean uncontaminated water for milling and in others the ore is ground much finer than at Cananea. All of these items are concerned in perfect separation. The details of preferential flotation at Cananea, therefore, are not presented on account of the perfection of the

Jan 1, 1928

By Robert L. Kidd

ONE time or another placer mining attracts the attention of a large number of people, because of the possible low initial investment, low operating cost, and quick returns. Much has been said about sampling and operating placer deposits but many are still inclined to jump at a property without giving much, if any, consideration to proper sampling. This statement does not apply to experienced mining engineers but I am hoping that readers will tear out this article and pass it along where it will do the most good and thus help to preserve the reputation of legitimate mining. It would appear that some people have an ability to sink test pits in high-grade gravel that is positively uncanny. One pit showing high-grade values proves to some property owners and promoters that the entire property will do the same. This is

Jan 1, 1937

ANY suitable characterization of the Utah Copper enterprise (now the Utah Copper Division of Kennecott Copper Corporation) involves the use of superlatives. If comparative records were compiled, after the fashion of baseball, the big opencut mine at Bingham Canyon, Utah, undoubtedly would hold dozens of championships in the mining world. For example, a few can be set down as follows: (1) The mine is the biggest man-made hole (excavation) in the crust of the earth! At the end of 1955 the total quantity of material moved (ore and overburden) was 1,673,000,000 tons or approximately 800,000,000 cubic yards. This is about3% times the yardage of earth moved in the original digging of the Panama Canal. It exceeds by fifty per cent the quantity dug in the justly famous Hull-Rust Mahoning open-pit iron mine on the Mesabi Range in Minnesota. (2) It holds first place among the mines of the world as to aggregate tonnage of ore mined and milled (734,000,000 tons at the end of 1955). (3) It holds first place among the mines of the world as to the aggregate quantity of metal produced (13,047,000,000 Ib- 6,523,500 tons-of refined copper). This is more than the actual production of all the mines in the United States during the eight-year period 1948 to 1955 inclusive. (4) In 1943, Utah established these world records: Tons of ore milled in a 24-hr day.. ................. 108,000 Tons of ore and waste moved in a 24-hr day.. ....... 235,000 Tons of ore milled in one month. ................... 3,074,000 Tons of ore milled in a year. ....................... 35,375,000 Pounds of copper produced in a year……….. 639,0000,000

Jan 1, 1957

By Clarence E. Sims

DURING the past several years the steel casting industry has made studies of heavy castings in which the test bar has been taken from heavy sections rather than from attached or separately cast coupons. It has been noted that the ductility properties of these heavy sections are often lower than those normally expected. Such lowered ductility is usually accompanied by a spotty test bar fracture and the ductility values often can be greatly improved if a low-temperature aging treatment is given to the casting. A loss of ductility of this type is considered "abnormal," since it is not accompanied by an increase of tensile strength or hardness, and "temporary" when the ductility can be restored by aging. The cure of such an abnormal condition represents a real improvement in the quality of the steel. Some hundreds of previous investigations, largely qualitative in nature, have established beyond reasonable doubt that hydrogen is normally present in newly manufactured steel and that this gas, in small amounts, can cause a temporary abnormal loss of ductility. The commonly observed association of high gas content and low ductility has given strong evidence for the presumption that hydrogen, possibly assisted by other gases, is the primary cause of the low ductility observed. Accordingly, the Steel Founders' Society of America has, since Nov. 1, 1944, sponsored investigations at Battelle Memorial Institute whose primary objective is to obtain quantitative information on the relation of the amount of hydrogen and nitrogen in steel, together with associated methods of steelmaking and treatment, to low-ductility effects and porosity.

Jan 1, 1947

By James Aston

THE origin of wrought iron may be taken as coincident with the earliest record of ferrous products. The limitations of primitive methods of manufacture undoubtedly resulted in a material conforming to the general characteristics of what we now classify as wrought iron. Iron has been known from prehistoric times. It is frequently mentioned in Egyptian literature, and some samples in the British Museum are believed to date from 3733 B. C. Iron instruments, tools and weapons were used in Greece in 1400 B. C., and in Assyria and. Italy in 1100 B. C. History records their use in Central and Western Europe in 1000 B. C. And in Styria and Carinthia before the Christian era. The noted Pillar of Delhi is generally assumed to date from 400 A. D. The use of iron was general in Europe in the Roman Empire, and heat treatment of weapons and tools was then practiced. All of this early iron was the result of direct reduction from the ore. It serves to illustrate the ease with which the extraction may be effected, and to point out the well known principle that a malleable product of relatively high purity may be produced from high-grade iron ore at temperatures well below the fusion point of-the metal. The fact is also emphasized that there is no novelty in the seemingly ideal and constantly recurring attempts to effect direct reduction. Economic and engineering considerations have been dominant factors in dictating today's two-step practice in the manufacture of wrought iron and steel. Bear' in mind that all of this history antedated the blast furnace, and a knowledge and use of cast iron. It was only in attempts to get greater output by use of shaft-type furnaces, that cast iron was produced in Germany in the period 1300 to 1400 A. D. This was the result of longer contact with the carbon of the fuel, and higher temperatures in the furnace. This period marked the beginning of the existing two-stage operation, involving as the second step the refining of the. cast iron to a malleable product. For a time this was effected in small hearths not unlike a blacksmith's forge.

Jan 10, 1926

By C. G. Dunn, W. W. Martin

Various X ray diffraction techniques have been developed for determining orientations of crystals. Transmission and back-reflection Laue methods1,2,3 in particular have been found to be very useful. In many applications, however, a need still exists for a simplification of the details of analysis so that orientations can be determined more rapidly, and operators with little or no training in crystallography can be easily instructed in the necessary procedures. Filling this need in part is a system of analysis that has been in use for several years in the Metals Section of the Laboratory, General Electric Co., Pittsfield, Mass. This method is an extension of the one of Majima and Togino,4 which uses fifty-five indexed standard transmission Lauemams to cover the entire range of crystal orientations. Greater rapidity in determining the orientation of a crystal is achieved by using a slightly larger set of standard Lauegrams and by systematizing the steps followed. This system of analysis in its present form constitutes the subject matter of the present paper. Although the method uses transmission X ray Laue patterns, many of the operations are applicable to the analysis of back-reflection Lauegrams. Very briefly the method is based on the fact that Bragg and azimuthal angles for two or more identified Laue diffraction spots completely determine the orientation of a crystal, and standard Laue photographs of the Majima and Togino type provide a ready means for identifying Laue spots. After a preliminary analysis, which consists of identifying the pattern in terms of one of the standard patterns, a correctly marked Lauegram is selected to carry out the final analysis. From measured Bragg and azimuthal angles, the normals (poles) of the reflecting planes for the selected Laue spots are located on a stereographic projection and the orient.at.ion of the crystal determined (in terms of the positions of cube poles for example) by a few additional operations on a \I1ulff net. The actual procedure followed will be illustrated in detail after a brief treatment or X ray problems connected with orientation determinations and a discussion of useful principles and techniques. X Ray and Plotting Problems RELATIVE ADVANTAGES OF BACK-REFLECTION AND TRANSMISSION LAUE DIFFRACTION METHODS In the back-reflection Laue method it is easy to make a direct measurement of the tilt of a zone of Laue spots. Specimen thickness also is generally no problem. In the case of thin specimens, however, the time of exposure is less for the transmission Laue method. For example, with silicon ferrite this advantage holds up to a thickness of 0.6 mm if tungsten radiation at 40 kv peak voltage is used. Furthermore, the transmission photograph represents the entire thickness of the crystal whereas the back-reflection picture represents only a surface layer (a thickness of less than 0.05 mm for silicon ferrite), the deeper layers supplying a negligible amount to the diffraction pattern. If a crystal is distorted, the transmission Laue pattern gives more information particularly with regard to the orientation of the crystal and the overall amount of spread in orientation. Finally a 3 1/4 X 4 in. film suffices for transmission photograms; a 4 X 5 in. or 5 X 7 in. film with a central hole is needed for back-reflection patterns Not only is the manipulation of film easier because of the size of film, but

Jan 1, 1950

By Pol Duwez, Ellis P. Frink, Paul Pietrokowsky

Ti-Au alloys in the composition interval 0 to 66 213 atomic pct Au have been studied over a temperature range from 400° to 1500°C. A partial phase diagram has been established from micrographic and macroscopic observations. All intermediate phases, Ti3Au, TiAu, and TiAu., exhibit open melting maxima. It has been observed that small additions of gold lower the allotropic transformation temperature of titanium. The P solid solution decomposes eutectoidally to a solid solution plus Ti3Au. The solubility of gold in a solid solution decreases with temperature. THERE have been several papers in the literature pertaining to the alloy system Ti-Au. However, a comprehensive study of this interesting constitu- tion diagram has not been conducted. Previous investigations have been concerned with the crystal structure of intermediate phases or partial phase diagrams. This paper represents a partial constitution diagram, Ti-TiAu,, the first portion of an investigation of the entire binary system. Laves and Wallbaum' reported the intermediate phase Ti,Au to be isomorphous with CuAu, L12 type. In a more recent paper, Duwez and Jordan' have concluded that TiAu has an atomic arrangement which is related to Cr,Si. The intermediate phase

Jan 1, 1957

By J. R. Jargon, H. K. van Poollen

Non-Newtonian fluids may be injected into a reservoir during secondary recovery operations. The non-Newtonian fluid used in this work is a power-law type of fluid that is, the viscosity of the fluid decreases as the flow rate or rate of shear increases. This paper presents equations for steady-state linear and radial flow of such fluids, transient behavior results from a finite difference model of a radial system, and transient behavior results from a field test. The equations that describe the flow of a non-Newtonian fluid are non-linear and are solved numerically. Finite difference solutions are presented as curves of dimensionless pressure drop at the wellbore us dimensionless time for a constant injection rate. Solutions were obtained for 5-percent, 10-percent and 100-percent PV of a non-Newtonian fluid for injection rates of 1, 10, 100 and 1000 cc/sec and for a 5 percent PV of non-Newtonian fluid located at T = Tw' 3, 10, 20, 50 and 100 ft for a flow rate of 1 cc/sec. The buildup curves do not exhibit a stmight-line portion as is the case for Newtonian flow through porous media. Correlations also are shown for the productivity index vs rate for the computer model study and the field tests. INTRODUCTION During various secondary recovery operations non-Newtonian fluids are injected. Such fluids, in general, include thickened water and gelled fluids. The term "non-Newtonian" implies that the viscosity is not only dependent upon temperature and pressure, but also on the rate of shear that is applied to the fluid. For example, water, which is a Newtonian fluid, will have essentially the same viscosity no matter what rate of shear is applied. A pseudo-plastic fluid exhibits a decreasing viscosity when higher rates of shear are applied; a dilated fluid has an increasing viscosity with increasing rates of shear. The objective of studies performed and described in this report is to obtain relationships and mathematical and empirical descriptions of the flow of non-Newtonian fluids through porous media. Simple mathematical relationships, computer studies that include the unsteady-state behavior of such fluids, and field tests are used. PREVIOUS LABORATORY STUDIES Laboratory studies have been performed by several investigators. The fluids used in one investigationl were surfactant-stabilized dispersions of water in hydrocarbons. Its Fig. 6 is reproduced as our Fig. 1. This effective-viscosity vs frontal-velocity diagram shows that this fluid is of the power-law type over a fairly large range of frontal velocities. Gogartyl developed an equation for the effective viscosity as a function of shear rate that reduces to Eq. 2 for frontal velocities greater than about 2 ft/D. The fluid characteristics used in the present study are similar to those reported by Gogarty. Christopher and Middleman2 performed experiments with power-law fluids flowing through pipes packed with glass beads. They used a modified Blake-Koteny

Jan 1, 1970

By J. J. Casey, R. S. Busk, D. L. Leman

The mechanical properties and the phase-temperature relationships of magnesium-lithium-aluminum, magnesium-lithium-zinc, and magnesium-lithium-aluminum-zinc alloys are presented. It is shown that the strengths of some of these alloys can be tripled by heat treating and aging but that the high strength is accompanied by brittleness and lack of stability. MAGNESIUM-LITHIUM alloys are interesting because the hexagonal structure of magnesium can be changed into the more ductile and workable body-centered cubic structure by the addition of only 10 pct lithium.1 After Loonam2 determined that the ductility of the magnesium-lithium alloys is destroyed by even trace quantities of sodium, it was possible to prepare ductile alioys and study their mechanical properties. Jackson3 and coworkers have ably described their results with both the binary and polynary magnesium-lithium alloys. The present paper is a report of the mechanical properties of wrought magnesium-lithium-aluminurn, magnesium-lithium-zinc, and magnesium-lithium-aluminum-zinc alloys. Experimental Procedure The alloys were made by melting 7 lb of magnesium in a steel crucible under a molten flux of 75 pct LiCl + 25 pct LiF3 previously dried at 1600°F. The metal was heated to 1300°F for alloying aluminum and zinc and then cooled to 1250°F for adding lithium (sodium content: 0.01 to 0.04 pct). After the lithium had been alloyed, dry LiF powder was sprinkled on the melt to thicken the excess flux. After a 15 min holding period, the flux was skimmed off. Paraffin vapors were used to protect the metal as it was poured into 3 in. diam by 11 in. long magnesium molds. Billets were extruded into 3/8-in. diam rod and 1/16 x 3/4-in. strip; sheet was prepared from 1/8x 7/8-in. extruded strip, first by hot rolling and then by cold rolling 2 pct per pass. Hot rollability, or the temperature range through which the alloys could be rolled, was determined by rolling the strip two passes at 30 pct reduction per pass. Cold rollability, or the percentage of cold reduction to cause detrimental cracking, was determined on 0.064-in. hot-rolled sheet. Standard ASTM procedures were followed to obtain the mechanical properties, using 0.2 pct offset for the yield strengths. The level of properties produced with commercial magnesium alloys using the procedure described is given in a previous publication." Results Magnesium - Lithium - Aluminum System: The good workability of magnesium-lithium alloys is illustrated by the data in table I, which shows approximately how the extrusion pressure decreases as the amount of cubic phase increases. Binary magnesium-lithium alloys are soft and weak, but aluminum raises their strengths con-

Jan 1, 1951

Discussion of the paper of H! M. CHANCE, presented at the Pittsburgh meeting, October, 1914, and printed in Bulletin No. 91, July, 1914, pp. 1461 to 1466. R. V. Norris, Wilkes-Barre, Pa.-In his resume of coal-taxation methods Mr. Chance has apparently confined his investigation to bituminous coal, so a summary of the anthracite situation as to coal assessment should be of interest. The anthracite region of Pennsylvania in its 484 square miles of measures lies in the counties of Wayne, Lackawanna, Luzerne, Carbon, Schuylkill, Northumberland, and Dauphin, and in each of these different methods of assessment have been adopted. The assessments for taxation in Pennsylvania are made under Acts of the Legislatures of 1841 and 1842, under which the assessors are re¬quired to "assess rate and value every subject of taxation according to the actual value thereof, and at such rates and prices as the same would bring at a bona fide sale after due notice." Under this general law coal land has been assessed as such, but up to about 25 years ago the coal was assessed at rates so low as to be unimportant, though the rates in each township and municipality, even in the same county, showed no agreement or ascertainable basis. In the late '80s, the need for greater revenue drew attention to the possibilities of collecting much larger taxes from the coal lands and, spurred by public demand, the assessing authorities in some counties undertook a reassessment of coal. The method pursued was to demand from each owner a statement of the area and average remaining thickness of coal on his lands. On this return, made in some cases under oath, an assessment based on foot-acreage was levied, with a resulting great increase in valuation, but the valuation per foot-acre was low and no serious objection was made. This assessment with occasional increases of rate remained in force until 1907, when, in the triennial assessment of that year, a complete revision of the valuation was again attempted, engineers were employed by the counties to check the accuracy of the returns from the owners, and, based on the foot-acreage thus obtained, an enormous increase, to $65 per foot-acre, was made in the valuation. This assessment was resisted in the courts by appeals resulting in very extensive litigation, and a final determination of the validity of the 1907 and all subsequent assessments has not yet been obtained. In the first appeals tried the rate calculated on a foot-acre valuation was reduced by the Luzerne County court to about $45, while the. Lackawanna County courts reduced a larger rate to $67. The county authorities were, how-

Jan 4, 1915

By George W. Maynard

In the death of Sir William Siemens, the Institute loses its most distinguished honorary member, one who, without exaggeration, may be ranked among the greatest Men of the century. In justification of this claim, I quote in part the words of two other men eminent in the walks of science. Professor Huxley, addressing the Royal Society, spoke of Siemens as "a marked example of vast energy, large scientific acquirements, and intellectual power of a high order," and as one " who had no superior in fertility and ingenuity of invention, while hardly any living man so thoroughly combined an extensive knowledge of scientific principles with the power of applying then] in a commercially successful manner. The value of his numerous inventions must be measured, not merely by the extent to which they have increased the wealth and convenience of mankind, but by the favorable reaction on the progress of pure science which they, like all such inventions, have exerted, and will continually exert." Dr. Wedding, in his address before the Verein zur Befarderung des Gewerbefleisses in Preussm, speaks of Siemens as being "so fortunate as to combine German erudition with British activity in such a manner that both nations, Gertnan as well as English, were equally proud of him; and, now that his rich life is ended, regret is expressed on both shores of the North Sea, first by the Germans that his entire life had not been spent in Germany, and his powers dedicated to Germany, and by the English that he was not born a Briton." Germany may well be proud of being the birth-place, not only of such a man, but of such a family; for where in history shall we find in a single family such a wide range of knowledge so successfully applied to the arts? The least distinguished name in the following list has added to the world's knowledge enough to satisfy the desire for fame of any ordinary man. This constellation is made up of:

Jan 1, 1884

By H. C. Boynton, Albert Sauveur

In the course of some experiments conducted in the Metallographical Laboratory of Harvard University, some interesting facts were brought to light which appear to be worth recording in advance of a more elaborate and exhaustive paper which the authors hope to present to the Institute in the near future. Fig. 1 shows, under a magnification of 100 diameters, the microstructure of the cross-section of a steel bar 1/2-inch square, containing 0.52 per cent. carbon, heated to 1100 degrees C. and cooled slowly with the furnace. Fig. 2 illustrates the structure of the same steel, heated to the same temperature but cooled more rapidly in the air. Both samples were cut from the same bar and heated side by side in the furnace. When a temperature of 1100 degrees C. had been reached, one sample was taken out of the furnace and allowed to cool in the air, while the other was cooled with the furnace. The only difference, therefore, in the treatment of both samples will be found in their respective rate of cooling. This variation in the rate of cooling resulted, as shown

Jan 1, 1904

By E. S. Tankins, G. R. Belton

A simple solution model, based upon the formation of molecular species, is developed for strongly electronegative dilute solutes in liquid binary-metallic solvents. Two approximations are considered for the relative concentrations of the species: the random and the quasi-chemical. Equations are presented for the partial molar free energy, enthalpy, and entropy of mixing of the solute. An experimental study has been made of equilibrium in the reaction H2 6) +0 (dissolved) = H2O(g))for the liquid Cu-Co alloys. The standard free energy of solution of oxygen is presented as a function of composition for the alloys at 1550°C and as a function of temperature for five of the alloys. The experimental results for these alloys and also for Cu-Ni alloys are shown to be in reasonable agreernent with the theory in the random approximation. A knowledge of the thermodynamic behavior of dilute solutes in liquid metals and alloys is of importance in understanding and designing refining and alloy-making processes. Accordingly, several attempts have been made to derive suitable solution models to forecast the effect of a third component on the activity coefficient of such a solute in a metal. Alcock and Richardson' reviewed the literature prior to 1958 and also showed that a regular solution model gave a reasonable description in the case of metallic solutes but failed to account for the behavior of the more electronegative solutes sulfur and oxygen. These same authors2 later modified their model by using the quasi-chemical approximation3 to calculate the average composition of the first coordination shell surrounding each solute atom. This modified model was shown to lead to a better qualitative description of the behavior of the electronegative solutes; however, quantitative agreement with experimental data for oxygen in alloys could only be achieved by assuming a very small coordination number. The authors concluded that the major source of error in the model was the assumption that pairwise interaction energies were independent of composition. Substitutional and interstitial random solution models by Wada and saito4 are essentially similar to the first model except that the required interchange energies were derived from the modified solubility parameter equation of Mott, instead of from experimental binary data. Most recently Hoch5 has presented a statistical model for interstitial solutions and has applied the model to the Fe-C-O system. However, as the various interaction energies needed in the model had to be derived from the ternary data, the model does not promise well as a means of forecasting ternary behavior. Each of the above models carries the assumption that the strongly electronegative solutes have the same configurational environment as metallic solutes; i.e., the solute can be treated as a substitutional or interstitial atom in a quasi-crystalline lattice and is surrounded by a normal coordination shell of solvent atoms. There are, however, a number of facts which suggest that this is unlikely. First, the heats of solution are large, being more typical of molecule formation rather than alloying. For example, the heats of solution of monatomic oxygen and sulfur in liquid iron are -90 kea16,8 and -74 kea1,7, 8 respectively. These are to be compared with maximum heats of solution of metallic solutes in liquid iron of about -13 keal (silicon is an exception with -28.5 kea17). The large depression of the surface tension of liquid iron by trace amounts of the electronegative solutes oxygen, sulfur, and selenium9 suggests, by analogy with aqueous systems, the possible existence of polar molecules in the liquid. The effect of these solutes is at least three orders of magnitude greater than normal metal solutes.10 As has been pointed out by Richardson,11 the electron affinities and ionization potentials of oxygen and sulfur are such that it is likely that they exist in metallic solution as negatively charged ions. If this is so, and it is assumed that electrostatic forces play an important role in determining the configuration, it is unlikely that the stable configuration will be that of an isolated ion surrounded by a symmetrical coordination shell of solvent ions. It is more likely that the energy of the system would be lowered by the formation of solute-solvent screened dipoles. The above arguments suggest the formation of "molecular species" between solute and solvent atoms. The idea of the existence of molecular species in such solutions is not new, however', for Marshall and chipman12 have explained in a semi-quantitative manner the C-O equilibrium in liquid iron by postulating the species CO. Chen and Chip-man13 interpreted their measurements on the Cr-O equilibrium in iron in terms of the species CrO. Zapffe and sims14 have also postulated the existence of such species in liquid-iron alloys.

Jan 1, 1965

Adams . Bernard . Student. South Dakota School of Mines .Rapid City . S . D . Ahlskog . Harold A. Student. Washington State College Pullman. Wash . Aldridge. John. Student. New Mexico School of Mines Socorro. N . M . Almstrom . Adne A .. Student. Met . Engrs.. Washington State College ..... .Pullman. Wash . Ancell . Virgil F.. Student. Missouri School of Mines Rolla. Mo . AnkudinoE. N., Mill Draftsman. Arthur G . McKee & Ch., 2422 Euclid Ave., Cleveland. Ohio . Avablaea . Salvador C.. Student. Univ. of California Los Angeles. Cal. Armstrong. Robert E .. Student. Lafayette College .Easton. P a Armstrong . Thomas E.. Student. Univ . of California Los Angela. Cal Aud. Robert A .. Student. Lafayette College Easton. Pa .

Jan 1, 1929

By T. R. Ingraham

The thermal decomposition of Nickel (II) sulfate was examined by determining the total pressure of SO3, SO2, and O2 developed over a sample when it was heated in an evacuated system fitted with a Pyrex-bellows mercury manometer. The equilibrium pressures were combined with previously published data on the oxide and sulfide systems to establish a predominance volume diagranz for the Ni-S-O system over the normal range of roasting temperature and gas composition used in the treatment of nickel minerals. The protective coating of NiSO4 which forms on the oxide during roasting, and which causes the sulfation reaction to almost cease, may be disengaged readily by temperature cycling. When nickel sulfide is roasted in air, either nickel sulfate or nickel oxide may be formed by altering the experimental conditions. Because of the differing stabilities of various metal sulfates and oxides, possibilities exist for separating some of the constituents of mineral mixtures by the technique of selective sulfation and oxidation roasting. The experimental information required to make reasonable predictions of the possibilities of this technique is incomplete and, in some cases, in conflict. As part of a general program of providing some of the required information, a study EXPERIMENTAL Materials, Apparatus, and Procedure. Fisher certified reagent-grade nickel sulfate hexahydrate was used in the source material for both nickel sulfate and nickel oxide. The manufacturer's analysis indicated: 0.001 pct Fe, 0.005 pct Cu, 0.003 pct Co, 0.001 pct C1, other 0.15 pct. The material was dehydrated, before use, by heating at 420°C for 5 hr. The oxide was prepared by roasting the sulfate in an open tray in a muffle furnace for 10 hr at950°C. Preliminary experiments which were made by thermogravimetric analysis and X-ray diffraction analysis established that only one crystal form of nickel oxide and one of nickel sulfate were involved in the equilibrium shown in Eq. [I]. The apparatus used in the experiments was described previously.1,3 The main feature is a corrosion-resistant, flexible Pyrex bellows which is used to protect the mercury in a u-tube manometer. Before a run was begun, the apparatus was washed thoroughly with hot hydrochloric acid and water and dried by heating under vacuum. The mixed sulfate -oxide sample was contained in a platinum bat rest-

Jan 1, 1967