Search Documents

By E. A. Steigerwald, G. L. Hanna

The influence of work-hardening exponent on the variation of fracture toughness with material thickness was studied for high-strength steel, aluminum, and titanium alloys. The results indicate that, when materials are compared at similar fracture toughness to yield strength ratios, the material with the lower work-hardening exponent undergoes the transition from flat to slant fracture at a larger thickness than material with a high work-hardening exponent. In the thickness range where complete slant fracture is obtained the reverse is true and a lower work-hardening exponent results in a lower fracture toughness. The influence of work-hardening exponent on fracture toughness is, therefore, dependent on the particular fracture mode. In the transition region a low work-hardening exponent is beneficial for fracture toughness while in the 100 pct slant region it is detrimental. THROUGH the use of fracture mechanics analyses, the influence of geometric variables on the crack propagation resistance of structures can be interpreted with reasonable consistency. However, in order to gain a more complete understanding of the fracture process, the influence of material parameters on crack propagation must be defined and coupled to the macroscopic fracture mechanics approach. The work-hardening exponent, which characterizes specific material behavior, may serve as an effective parameter to allow some degree of coupling to be accomplished. In the extension of a crack in a specimen of suitable dimensions the propagation process occurs in a stable manner when the crack extension force is balanced by the resistance to crack extension, which exists in the material at the crack tip. As the applied stress, and therefore the crack extension force, on the specimen increases, the resistance also increases primarily because the effective plastic zone at the crack tip, which is the main energy absorption process, becomes larger. Since the work-hardening rate of a material influences the stress-strain relationship, it will also influence the energy absorption process in the plastic enclave at the crack tip and hence should have an effect on crack propagation. A number of studies have been made correlating the strain-hardening exponent or the strain to tensile instability with the ability of a material to resist fracture. Gensamer1 concluded that a low-strain-hardening exponent would result in a steep strain gradient at the base of a notch. He reasoned that a large work-hardening coefficient would result in high-energy ab- sorption due to the increased area under the stress-strain curve. Larson and Nunes2 experimentally observed in Charpy tests on steels heat-treated to below 200,000 psi yield strength that the energy to failure in the fibrous mode, i.e., above the brittle-to-ductile transition temperature, was logarithmically related to the strain-hardening exponent. In order to avoid the complicating effects present in studying materials which undergo a brittle-to-ductile transition, Ripling evaluated the notch sensitivity of a variety of fcc metals with varying work-hardening exponents.3 The results indicated that the relative notch sensitivity, as determined from tests on specimens with a sharp notch, decreased with increasing values of strain hardening. Although the energy required for ductile or fibrous fracture increases with increasing work hardening, high-strength steels often exhibit improved crack propagation resistance when heat-treated to obtain low values of strain hardening.4,5 An analysis of whether low strain hardening is beneficial or detrimental to crack propagation resistance must depend on the particular fracture criterion involved. At temperatures where the material is relatively ductile and the development of a critical strain is required for fracture, high strain hardening increases the energy required to produce failure. In the transition region and below, however, a critical stress law appears to be valid6 and a low rate of work hardening may produce superior resistance to semibrittle crack propagation. The experimental program is aimed at studying these possibilities and determining the specific influence of strain hardening on the crack propagation resistance of several high-strength materials. MATERIALS AND PROCEDURE The alloys, chosen as representative of various classes of high-strength materials, are summarized in Table I. The heat treatments evaluated along with the smooth tensile properties are presented in Table 11. Pin-loaded sheet tensile specimens were employed to determine the smooth tensile properties. A strain gage extensometer (measuring range 0.200 in.) was used at a strain rate of 0.02 in. per in. per min. The work-hardening exponents were determined from the stress-strain curves generated in the smooth tensile tests and the assumption that the portion of the stress-strain curve beyond the yield point can be described by the power relationship: where a is the true stress, P is the true plastic strain,

Jan 1, 1969

By K. E. J. Rapperport, C. S. Hartley

The only slip system observed in zirconium crystals deformed at 77", 575", and 1075OK was (1010) [1210] with a critical resolved shear stress in tension of 1.0 kg per sq mm at 77°K; 0.2 kg per sq mm at 575 °K; and 0.02 kg per sq mm at 1075 OK. The active twin planes were {1012}, (1121}, (11221, and (11233) with varying temperature dependence. A detailed analysis for the slip direction using Laue spot asterism is appended. NeARLY all metals of the hexagonal close-packed structure exhibit basal slip, i. e.,(0002)<1120>- type slip. This is true of magnesium,&apos; zinc,&apos; cadmium,3 beryllium,4 titanium,= yttrium,6 and rhenium.Many of these such as titanium 5&apos;8-&apos;0beryllium,4&apos;" magnesium, and zinc13&apos;14 display other slip modes even at room temperature, and nearly all have been reported to slip on other systems under particular loading or temperature conditions of testing. As is shown in this paper, basal slip was not found at any of four test temperatures from 77" to 1075°K in hexagonal close-packed zirconium under the simple loading conditions of tension and compression, even though in one case the resolved shear stress on the inactive (0002) <llgO> system was twenty-five times higher than the critical resolved shear stress on the active (1010) [1210] system. This result is consistent with prior studies on the active deformation processes in zirconium deformed at room temperature. &apos;&apos;-I7 SPECIMEN PREPARATION A) Material—The zirconium used in this work was of two types: 1) as-deposited reactor grade crystal-bar, and 2) arc-melted and forged reactor grade crystal-bar. Typical chemical and spectrographic analyses of these materials as received, and after hydrogen removal and crystal growth are given in Ref. 17. Crystals of type 1) above have the letter prefix (A) and those of type 2) have the prefix (B) throughout this paper. B) Crystal Growth— he zirconium was machined into rectangular parallelepipeds about 0.2-in. scl in cross section and 2 in. iong. These were hand polished through 4/0 abrasive paper, electropolished, given a hydrogen removal anneal, and subjected to long-time anneals at 840 °C in vacuo to produce usable crystals.&apos;7 A second technique used to obtain large crystals was to cycle the samples two or three times between 1200" and 840°C, allowing them to remain at the higher temperature for about 4 hr and at the lower temperature for 5 days.17 These techniques yielded some grains which occupied the entire cross section of the bar and were as long as 3/4 in. C) Orientation Determination—After the growth of large crystals by thermal cycling, the samples were repolished with extreme care through 4/0 abrasive paper and electropolished. Metallographic examination after polishing showed the surfaces to be free of visible deformation traces. Standard Laue back-reflection X-ray techniques were used to find the crystallographic orientations of selected large grains with respect to a specimen face and edge. Fig. 1 shows the stereographic projections of the stress axes for the crystals used. The sharpness of the spots on the Laue photographs indicated that the crystals were of good quality. EXPERIMENTAL METHODS Nine crystals were deformed in tension at 77"K, nine in tension and five in compression at 300°K in previous tests,17 fifteen in tension at 575"K, and eleven in tension at 1075°K. All specimens were stressed by load increments. After a predetermined load was applied, the specimen was removed from the loading appratus and metallographically examined for deformation traces. An attempt was made to initially stress each bar so that some crystals slipped a small amount and others not at all. This was done to bracket the critical resolved shear stress. One bar of special orientation (B-11) was repolished and annealed at 1075°K for 1 hr after lower temperature deformation, before final deformation at 1075°K. In the other bars the loading by increments, followed by metallographic examination, was continued until the surface distortion would interfere with analysis, or until fracture. One example of a crystal pulled to fracture is shown in Fig. 2. This photograph shows a crystal (B-14C) which was pulled at 1075°K and failed by slip on two (10i0) planes. The approximate orientation of this crystal is illustrated in the figure. Specimens were deformed at 77°K in liquid nitrogen on a tensile machine using an insulated bucket with an internal hook to accept a clamped specimen.

Jan 1, 1961

By G. A. Moore

A brief review is given of methods designed to produce metallic iron of high purity, and typical results are listed. A recent method, utilized at the National Bureau of Standards, consists of the extraction of ferric chloride by ether, reduction of this ferric chloride to ferrous chloride, further purification of this chloride, and the subsequent electrolytic deposition of metallic iron. iron produced by this procedure apparently is softer than, and otherwise different in properties from, any iron previously prepared and contains appreciably smaller amounts of impurities. THE history of attempts to produce "pure" iron reaches to antiquity and it may be presumed that each ancient armorer who succeeded in making a better steel concluded, correctly, that he had done a better job of removing the "base metals," and incorrectly, that he now at last had a "pure" metal. Early metallurgical papers mentioned use of "pure iron" in making alloys—this "pure" iron in most cases being inferior to some commercial stocks of the present time. Improvement has been continuous, and usually at a sufficient rate to convince each succeeding group of workers that they, at last, were using the really pure metal (until the analysts also improved their techniques to again discover the impurities). These adventures were reviewed in some detail by Cleaves and Thompson.&apos; Although the ores of a metal may be abundant, difficulties in extracting it may make the pure metal very rare. When impurities are restricted to a total of a few parts per million, nearly all pure metals become rarities. Lead, copper, gold, mercury, silver, zinc, aluminum, bismuth, and the six platinum metals are claimed to be available with total impurities ranging from 2 to 50 ppm. The present small and scattered world supply of so-called "pure" iron holds an unimpressive place in another group of 16 metals having approximately 100 ppm of foreign material. Of about 20 less rare metals, only the platinum metals are more costly to prepare. While the production of such rare varieties of iron may appear insignificant in the presence of thousand-ton operations with 95 to 99 pct metal, it must be emphasized that all researches on commercially interesting irons and steels are in fact studies of the modifications of the properties of iron by additional materials. Until the properties of high purity iron are directly measured, all ferrous research must operate without known base values. Traces of impurities may affect the properties of a metal in many ways. Infinitesimal traces of solutes, by disturbing the electronic configuration, greatly change the electrical properties of transistors and semiconductors2-3 and slightly larger traces might alter these quantities in iron. Soluble impurities which disturb the perfection of lattice arrangement not only may alter the magnetic constants and electric properties, but by their close association with dislocation phenomena probably control the very existence of the "yield point"; determine the value of yield stress; and perhaps control the selection of slip and cleavage planes. It has been speculated that impurities might even cause the allotropic transformation in iron, but in any case their rearrangement must contribute to the unreliability of heat capacity and other thermodynamic measurements. Impurities which do not remain in solution may cause even greater effects on the properties. Microscopically visible amounts of phases other than ferrite can be found in all high purity irons which have come to my attention. It can be calculated that from 50 to as little as 2 ppm of an insoluble material might be sufficient to completely film all grain boundaries in irons having grain sizes from ASTM Nos. 10 to 1. Should this occur, such films, even though invisible, may be very important in fracture problems, especially at extremes of temperature:&apos; Studies of grain growth and diffusion normally imply consideration of a single-phase system, hence, in the presence of insoluble impurities they can be expected to give ambiguous data." High purity iron is also in demand for use as chemical and spectro-chemical standards; for work in classifying the lines of the iron spectrum; for biological work in nutrition; and for work in nuclear physics. where the presence of some sensitive

Jan 1, 1954

By George W. Orton

i\- number of investigations have established that tungsten monocarbide (WC) forms throughout a wide range of temperatures (800° to 2200°C), but the di-tungsten carbide (W2C) forms only at the high end of this temperature range.1"7 In addition the decomposition of WC into WzC and C at elevated temperatures has been observed.8"10

Jan 1, 1964

By Phyllis A. Lyday

Jan 1, 1985

By F. S. McNicholas

Various methods of block caving and draw practice are classified and the advantages, disadvantages, rock, treatment, size of orebody, costs, and profit comparisons, and other factors which determine the selection of the proper method are outlined.

Jan 1, 1951

By R. J. Blackwell

By E. C. Wade, R. D. Valentine

This paper describes a computer applications engineering system and it&apos;s use to apply a thermal dryer fan motor in a coal preparation plant. The computer hardware and software systems are described to indicate the general approach taken and a specific case study is reviewed to show how computer power is brought to projects in the coal industry.

Jan 1, 1983

By C. G. Fink, G. L. Putnam

The dissolution of gold by cyanide solutions was studied by determining the time required for the solvents to dissolve gold leaf. Minute traces, even 0.5 ppm, of sulphide ion retard the dissolution of gold, and this behavior cannot be accounted for by the presently accepted hypotheses involving oxygen-depletion or thiocyanate formation. On the other hand, traces of the salts of lead, bismuth, mercury, and thallium considerably accelerate the dissolution. The beneficial effect of lead is dependent upon the pH and cyanide ion concentration of the solution.

Jan 9, 1950

By H. W. Schadler

The superplastic behavior of low carbon and manganese bearing steels has been evaluated. The results of elevated-temperature stress-strain rate and elongation tests are reported which indicate that high strain rate sensitivity (>0.5) and adequate elongations are achievable in ultrafine-grained steels 1 to 2 p, but at strain rates which are not commercially attractive. It has been demonstrated that the fine grain size is retained after long times and high strains if the temperature is kept within the range of the two-phase (a + ?) field. INTEREST in superplasticity has been stimulated by the desire to: 1) understand the origin of, and mechanisms responsible for, the large uniform elongations observed, and 2) exploit this property for commercial advantage in metal forming operations. Although the Zn-22 wt pct Al alloy presently being studied as a model material1-5 may find application in sheet forming and extrusion, the potential of super-plasticity should best be realized in large tonnage materials, such as steel and aluminum alloys. The degree of superplasticity in low-carbon and manganese-bearing steels has been evaluated. The results of elevated-temperature stress-strain rate and elongation tests on ultrafine grain size material are reported. Avery and Backofen6 and Hart7 have shown that geometrically stable flow leading to extensive uniform elongation in the tension test is associated with high values of the strain rate sensitivity, m, defined: Lozinsky had reported that titanium and zirconium experience permanent deformation if subjected to a constant load and cyclic heating through the temperature range of the phase transformation. Although strain rate sensitivities in excess of about 0.2 had not been reported previously for steel, permanent deformation had been observed11-13 in a wide variety of steels subjected to a constant load and cyclic heating through the temperature range of the a-? phase transformation. Thus by analogy, steel could be expected to exhibit high strain rate sensitivity but only in the a + ? condition. High strain rate sensitivity has been observed at 650°C (a + Fe3C), but not reported as such, by Bailey, Dickenson, and pearson14 in 1931 at a strain rate of about 10-9 per min. It then remained to determine whether high tensile elongations would be observed in a rate-controlled test at constant temperature and at what strain rate strain rate sensitivity values greater than 0.5 would be observed. Since previous experience8 had indicated the importance of fine grain size to realizing high m at reasonable strain rates, it was first necessary to produce an ultrafine grain size and then keep the grains from growing during the test. The results of this investigation show that fine grain size can be readily produced16 and maintained by restricting the temperature of testing to below the ? transus. Further, superplasticity (high m and large uniform elongation) is observed. However, the strain rate range is only marginally useful for commercial forming operations with the finest grain size produced. MATERIAL The material investigated initially was a 1.9 wt pct Mn, 0.42 wt pct C, hot-rolled bar previously used by Low and Turka1015 and available in the laboratory. The 0.500-in. round was cold-rolled to a 0.090-in. flat, annealed for 4 hr at 850°C in argon, air-cooled, and cold-finished to 0.050 in. Subsequently, four additional steels of the compositions given in Table I were investigated to explore the effects of manganese, carbon, and test temperature on the observed stress-strain rate behavior. These steels were melted under argon, cast to 0.75 by 2 by 5 in. slabs, hot-rolled at 850°C, surface-finished to 0.13 in., and cold-finished to 0.050 in. Sheet tensile specimens 0.200 in. x thickness with 1- or 2-in. gage length were cut parallel to the rolling direction. Table I also includes the nominal transformation temperatures for the AISI 1340 and the four experimental steels. EXPERIMENTAL PROCEDURE Production of Fine Grain Size. Ultrafine grain size (1 to 5 p) was considered essential for this studv. Grange16 has described two techniques for producing

Jan 1, 1969

By Frank Doxey

AT Dominion Steel & Coal Corp. it has long been recognized that continued mechanization of mine operations is necessary in the Pictou, Cumberland, and Sidney coal fields of Nova Scotia. The varied physical conditions in these fields call for special consideration of individual cases before planning is finalized. Because standard equipment cannot be procured which would operate successfully, many experiments have been necessary over the years to keep pace with the progress made in other countries. There are two mines, producing 2000 tpd, located in the Pictou coal field. The field is badly distorted and crossed by many faults. Seams are highly inclined and irregular and vary in thickness from 5 to 40 ft. Entries are difficult to maintain because of squeezing of the coal. ribs and movement of the roof and pavement. Output from the three operating mines in the Cumberland field is 3000 tpd. The field is highly inclined, inclination varying from 12° to 32°. Overlying beds consist of shales and massive sandstone lenses of extreme toughness and are responsible for bumps when the stresses are relieved by extraction. At greatest depth these are among the deepest coal workings in the world. Depth of cover ranges from 2300 to 4000 ft. This prohibits room-and-pillar working and necessitates longwall operation. Working of contiguous seams concurrently to maintain output increases the already difficult conditions. The Sydney field, with a frontage of about 30 miles, is the most important of the Nova Scotia coal fields. With the exception of one small area it is now wholly submarine. Output is approximately 21,000 tpd. Seams are 21/2 to 8 ft thick, and cover in the areas varies from 600 to 2300 ft, with an average of 1500 ft from sea bottom to the top of the seam. The seams dip in a seaward direction, pitches ranging from 6" to 4.0". The shoreline is the last place of entry to the seams and distance from the bank to the working faces is generally over 3½ miles, in some cases as much as 6½ miles. Ventilation is a problem and requires the construction of large permanent airways. Getting and Loading Coal: In 1925, in view of heavy pressures exerted by thickness of cover overlying the seams, roadways and pillars of the room-and-pillar system being worked began to break up and coal was lost. It was decided that a change in the method of extraction in areas with heavy cover was necessary, and experiments were made with many short walls and longwalls varying between 90 and 250 ft. Trial and error proved that the best operating length was between 400 and 500 ft, delivering all coal to the dip, with roadways to the face following a level course. The change-over was gradual, and the technique of roof control developed with the system, so that falls to the face are now very infrequent. An advantage of longwall mining is that it yields 95 pct extraction, especially important in coal seams of high quality or in seams where faults or disturbances restrict the workable areas. This percentage of extraction is based on the fact that the longwall advancing system takes development faces where pitch permits instead of driving headings and leaving roadway pillars. This system yields high tonnage during development and limits loss in extraction to duff left during operations. Accompanying disadvantages, on the other hand, are the heavy construction cost of main roadways and the necessity of driving all new flank face roadways through the gob. If the main roadways are driven through the solid, and large enough pillars are left on each side for protection against flank face weights, then the width of solid coal is approximately 1700 ft. This represents 10.6 pct of the coal available, or 89.4 pct extraction of the whole. These pillars, however, are of such size that they provide a useful pillar drawing area as a final operation of the mine. It may be that although the seam cannot be generally mined by the room-and-pillar method, it can be adapted to

Jan 1, 1955

By R. R. Boucher, O. J. C. Runnalls

A pronounced thermal effect has been observed on heating or cooling a1wninum-rich Al-U and Al-Pu alloys. From microscopic and X-ray diffractionstudies, the effectl has been attributed to trnsfor)nations in the inlemetallic phases UAl, and PuAl , involuing rearrangement or cluslering of vacancies The transformation obsrved in Al-20 wi oct U alloys occurred near the a Al-UAl4 eutectic tem-perature of 646°C making it difjicult to detect from heating curves. When cooling, howeoer, thermal mad X-ray analyses indicnted that the high-temperati~re phase labeled p UAL, precipitated initially during euitectic solidification. As solidification continued and after an induction period o-f 5 lo 20 tnin the nu-cleatiorz and growth of the low- twmperature phase, a UAl4 produced an euolution of energy which raised the observed alloy temperature by 1° to 2°C. in Al-Pu alloys the transformation occurred at 645°C, 5 deg below the eutectic solidification temperccture. The eslimated latent heat of transformation was 25 +5 cnl per g PuAl,. The high-tetnpevcl-ture forms of UAl, and PuAl, were easily 9-etccined by chill casting Al-U and Al-Pu alloys and on reheating the alloys the trcltzsforrnation to the a phase was sluggish even above 600°C. Separated single cryslals o-f UAl4, joy example, showed no evidence Of transformalion after heating for 16 hr at 620°C. The transformation rates increased yapidly enough with increasing temperature, however, that a a spontaneous liberation of energy lens observed on occasion when bealing cast Al-20 wt pet U to neal- the RECENT phase studies on A1-Pu alloys have indicated that earlier reported equilibrium diagrams should be modified to take account of several poly- morphic transformations in the intermetallic compound PuAl,.&apos; During the course of the latter work an unexpected heat evolution was observed while cooling a solid alloy consisting of a mixture of a aluminum and PuA1,. The evolution occurred at 645°C, y below the a A1-Pu A1, eutectic solidification temperature. Subsequent thermal-analysis experiments with A1-U alloys showed that heat was evolved there also at a temperature nearly coincident with the a A1-UA1, eutectic solidification temperature of 646°. A search of the literature revealed that similar thermal effects had been observed before for both A1-U and A1-Pu but had never been fully explained.2,3 The purpose of the present paper is to describe thermal-analysis and X-ray diffraction experiments which have led to the conclusion that the thermal effects are due to transformations which involve the rearrangement of vacancies in the intermetallic compounds UA1, and PuA1,. EXPERIMENTAL PROCEDURE The A1-U alloys were prepared by heating super-pure aluminum (99.99 pct +) obtained from the Aluminum Co. of Canada in a graphite crucible surrounded by an induction coil. At 1000°C high-purity uranium metal produced by the Eldorado Mining and Refining Co., Ltd. was dropped into the liquid aluminum and was dissolved completely within 15 min. The impurities in the uranium were A1—4 ppm, Ca-4, C-70, Cr-3, Cu-6, Fe-30, Mg-2, Mn-10, Ni-25, Si-25, and Zn-2. The A1-Pu alloys were prepared by reacting plutonium dioxide with liquid aluminum under cryolite (3 NaF . AlF,) for 10 min at 1100°C in graphite crucibles exposed to the air. The plutonium was 99.8 pct pure, containing trace impurities of Ca, Cu, Fe, Pb, Si, and Zn. The liquid alloys were usually poured into water-cooled molds to provide castings of uniform composition from which samples could be cut for heat treatment and thermal-analysis experiments.

Jan 1, 1965

By Michael J. Abrams

The large amount of data available from Landsat has made digital processing necessary to extract and display that subset of data relevant to the problem being considered. Computer image processing techniques developed and used at the Jet Propulsion Laboratory can be divided into four categories: rectification, cosmetics, display, and analysis. These techniques have been applied to various geologic problems, including mineral exploration, lithologic mapping, hydrology, and tectonics.

Jan 1, 1977

By Harry A. Perry

The Highlad underground uranium mine is located in the southern Powder River Basin, Converse County, Wyoming. Development by Exxon Minerals Company began in 1973 and average production from the complex roll- front deposit ranges from 500 to 600 stpd. A staff of six eight grade control technicians work within the Geology Department to guide and monitor production, to minimize waste and to account production to reserve estimates. A thorough knowledge of the complex roll- front deposit aids in accounting production to reserve estimates. Grade control technicians assist the mine geologist in making geologic cross sections, in estimating reserves, and in predicting monthly and quarterly production grades.

Jan 1, 1980

By Jack A. Caldwell

Jan 1, 1985

Jan 1, 1892

By Dan Chun

Abstract-To facilitate the efficient handling of large volumes of information generated by logging exploration drill cores, a computer data bank system (GEOBANK) has been developed to store and retrieve the normally difficult to handle geologic information as well as the physical testing data. The data bank systematized the logging of drill core by first developing a standard list of adjectives or descriptors (with the corresponding assigned numerical codes) for the various stratigraphic categories that are also assigned numerical codes. The system uses the "floating-slot" concept and handles the data bank with one single input form.

Jan 9, 1978

Eckley B. Coxe, Drifton, Pa.: Anthracite coal differs from other fuels in its greater solidity. It does not burn like coke or wood, or like bituminous and coking coals, which become more or less spongy when heated, so that combustion can take place to some

Jan 1, 1892

By S. G. Valentine

Blast-furnace blowing engines are broadly of two main types: either steam - or gas-driven reciprocating engines, or turbine-driven rotary engines.

Jan 1, 1915

By Ta M. Li

This article draws freely on the experiences of the engineering and operating staff of P.T. Inco and its parent firm Inco Ltd. In addition, information was derived from papers presented during the recent International Laterite Symposium, held in conjunction with the 1979 AIME Annual Meeting, New Orleans, La., February 19-21. The author wishes to acknowledge all contributors and, in particular, Roy Aitken, president and managing director, P. T. Inco.

Jan 7, 1979