By D. M. Dunbar, H. C. SCHLILTZ

HE Chile Exploration Co.'s mine and reduction plant are at Chuquicamata, Chile, on the eastern edge of the Atacama Desert, 163 miles northeast of Antofagasta, 80 miles from the Pacific Ocean, and 70 miles from the Bolivian border and at an altitude of 10,000 ft. Guggenheim Brothers started prospecting in -4pri1, 1912, and purchased the main property, in October of that year; the property is now controlled by the Anaconda Copper Mining Co., which acquired it in January, 1923. The orebody strikes north 10" east, and has a dip of about 64" west. The length, as far as developed, is approximately 1% miles; the width averages sightless than mile.

Jan 1, 1925

By A. F. Witt, A. M. Gaudin, A. K. Biswas

Finite contact angles in the rutile-water-organic liquid system are traceable to contamination or are due to addition of a surface-active agent. Finite contact angles are invariably accompanied by hysteresis.1-7 Besides surfactant concentration and pH, the nature of the organic liquid is found to be a factor influencing the magnitude of contact angle hysteresis. In a recent paper the authors have reviewed principles and applications of measurement methods for contact angles and their hysteresis.22 In this paper, these methods are applied to a system consisting of rutile, an organic liquid (benzene, decane, or dode-cane) and water. Surfactant (dodecylamine hydro-chloride) was used at various concentrations and various pH values. MATERIALS A synthetic rutile crystal supplied by the Linde Co. was used. It is a cylinder 1/2 in. diam, with faces cut perpendicular to the c-axis. The crystal is stated to be alumina-free and to be 99.9% pure. Rutile is a high surface energy solid, its calculated average field strength being 2.7 x 105 e.s.u.,9 its dielectric constant10 is 114. The zero point of charge of rutile was measured11 and found to be at pH 6.0. The atomic distances and bond angles of the tetragonal crystal of rutile have been precisely determined.l2 The organic liquids were specially purified. Reagent grade benzene was repeatedly shaken with concentrated sulfuric acid to remove thiophene, then neutralized with sodium hydroxide solution, rinsed with distilled water, dried overnight over anhydrous calcium chloride and filtered. The refractive index of this chemically purified benzene was 1.4977 (at 25°C) - very close to that of pure benzene (n25 1.4979).13 Both n-decane and n-dodecane were washed with aqueous sodium hydroxide, concentrated sulfuric acid (repeatedly, until the acid layer was colorless) and again with alkali, to free the organic hydrocarbon from fatty acids and unsaturated hydrocarbons. The organic phases were subsequently washed with distilled water and dried over anhydrous sodium sulfate. The filtered hydrocarbons were then distilled under vacuum (9-10 mm pressure). Decane, thus purified, showed traces of unsaturated and of carboxylic compounds. On gas chromatographic analysis the purified n-dodecane showed the presence of two impurities. However, the relative retention times of these components did not change substantially when measured on a polar or a nonpolar column. This indicates that the compounds were probably in the same polarity class, i.e. the components were nonpolar like dodecane. Conductivity water has always been one of the liquids. Conductivity of the water used was 10-6 ohm-' cm". Dodecyl ammonium chloride was prepared from pure amine (supplied by Armour and Co., Chicago), by Li in the MIT Mineral Engineering Laboratory.14 The critical micelle concentration at 25°C is known, 0.0138 mol per liter15 or 3.06 gpl. All our experiments have been done at concentrations lower than the critical micelle concentration. The glass vessels, glass drop holder and the rutile crystal were all cleaned with hot chromic acid followed by distilled water, concentrated hydrochloric acid, and again distilled water, and conductivity water. During the experiments, a nitrogen atmosphere was maintained. For this purpose, commercially purified nitrogen was further purified by passing it over hot copper wire at 450°C, then through columns of acidic chromous chloride solution, concentrated alkali solution and distilled water. APPARATUS AND METHODS Hysteresis was produced by the "captive drop" or constant volume drop method as well as by the "expanding-contracting drop" or variable volume drop method. The image of the drop while it is expanding, contracting or moving is projected on a screen and photographed. The developed film is projected through an enlarger and the contact angles measured with a protractor.

Jan 1, 1964

By John E. Conley

THE production of lime by the burning or calcination of limestone, including all varieties from true dolomites and magnesian limestones to high-calcium types, continues as one of the essential basic industries. In 1937, a total of 4,124,165 tons of lime valued at approximately $30,091,000 was produced in the United States.1 The importance of any contribution to our knowledge on the mechanism of the lime-burning process is, therefore, obvious. The burning of limestone has been practiced since the earliest days of our civilization, and the literature on the various phases of the industry is voluminous. Calcination of the various types of limestone has been studied by many previous investigators, but some points require additional research. Each occurrence of limestone provides an opportunity for specific investigation, because the characteristics of stones in different localities vary Knibbs13 has given an excellent discussion of available data on the theory of lime and magnesia burning. The thermal dissociation of calcium carbonate has been studied more recently by Johnston,2 Smyth and Adams,3 Ralston et al.,4 Furnas,5 Potapenko,6 and Southard and Royster.7 As a result of these investigations the dissociation temperature at atmospheric pressure has been established as 894º to 898º C. The dissociation of dolomite and magnesite, although studied by several investigator,4, 6, 8 still requires clarification by additional data. The calcination of limestone was studied for a twofold purpose: (1) to extend our information on the mechanism of the lime-burning process and (2) to standardize the conditions for calcination of high-calcium and dolomitic limestones for subsequent hydration tests on the lime.

Jan 1, 1939

By John Conley

THE production of lime by the burning or calcination of limestone, including all varieties from true dolomites and magnesian limestones to high-calcium types, continues as one of the essential basic industries. In 1937, a total of 4,124,165 tons of lime valued at approximately $30,091,000 was produced in the United States.1 The importance of any contribution to our knowledge on the mechanism of the lime-burning process is, therefore, obvious. The burning of limestone has been practiced since the earliest days of our civilization, and the literature on the various phases of the industry is voluminous. Calcination of the various types of limestone has been studied by many previous investigators, but some points require addi-tional research. Each occurrence of limestone provides an opportunity for specific investigation, because the characteristics of stones in different localities vary. Knibbs13 has given an excellent discussion of available data on the theory of lime and magnesia burning. The thermal dissociation of calcium carbonate has been studied more recently by Johnston,2 Smyth and Adams,3 Ralston et al.,4 Furnas,5 Potapenko,6 and Southard and Royster.7 As a result of these investigations the dissociation temperature at atmospheric pressure has been established as 894° to 898° C. The dissociation of dolomite and magnesite, although studied by several investigators, 4,6,8 still requires clarification by additional data. The calcination of limestone was studied for a twofold purpose: (1) to extend our information on the mechanism of the lime-burning process and (2) to standardize the conditions for calcination of high-calcium and dolomitic limestones for subsequent hydration tests on the lime.

Jan 1, 1939

By John E. Conley

The production of lime by the burning or calcination of limestone, including all varieties from true dolomites and magnesian limestones to high-calcium types, continues as one of the essential basic industries. In 1937, a total of 4,124,165 tons of lime valued at approximately $30,091,000 was produced in the United States.' The importance of any contribution to our knowledge on the mechanism of the lime-burning process is, therefore, obvious. The burning of limestone has been practiced since the earliest days of our civilization, and the literature on the various phases of the industry is voluminous. Calcination of the various types of limestone has been studied by many previous investigators, but some points require additional research. Each occurrence of limestone provides an opportunity for specific investigation, because the characteristics of stones in different localities vary. Knibbs13 has given an excellent discussion of available data on the theory of lime and magnesia burning. The thermal dissociation of calcium carbonate has been studied more recently by Johnstonr2 Smyth and Adams,3 Ralston et al.,4 Furnas,6 Potapenko,6 and Southard and Royster.7 As a result of these investigations the dissociation temperature at atmospheric pressure has been established as 894" to 898' C. The dissociation of dolomite and magnesite, although studied by several investigators,4,6,8 still requires clarification by additional data. The calcination of limestone was studied for a twofold purpose: (I) to extend our information on the mechanism of the lime-burning process and (2) to standardize the conditions for calcination of high-calcium and dolomitic limestones for subsequent hydration tests on the lime.

Jan 1, 1942

By John E. Conley

The production of lime by the burning or calcination of limestone, including all varieties from true dolomites and magnesian limestones to high-calcium types, continues as one of the essential basic industries. In 1937, a total of 4,124,165 tons of lime valued at approximately $30,091,000 was produced in the United States.' The importance of any contribution to our knowledge on the mechanism of the lime-burning process is, therefore, obvious. The burning of limestone has been practiced since the earliest days of our civilization, and the literature on the various phases of the industry is voluminous. Calcination of the various types of limestone has been studied by many previous investigators, but some points require additional research. Each occurrence of limestone provides an opportunity for specific investigation, because the characteristics of stones in different localities vary. Knibbs13 has given an excellent discussion of available data on the theory of lime and magnesia burning. The thermal dissociation of calcium carbonate has been studied more recently by Johnstonr2 Smyth and Adams,3 Ralston et al.,4 Furnas,6 Potapenko,6 and Southard and Royster.7 As a result of these investigations the dissociation temperature at atmospheric pressure has been established as 894" to 898' C. The dissociation of dolomite and magnesite, although studied by several investigators,4,6,8 still requires clarification by additional data. The calcination of limestone was studied for a twofold purpose: (I) to extend our information on the mechanism of the lime-burning process and (2) to standardize the conditions for calcination of high-calcium and dolomitic limestones for subsequent hydration tests on the lime.

Jan 1, 1942

By William R. Webster

At the Florida meeting of the Institute, in March, 1895, I presented a Note on a Proposed Scheme for the Study of the Physics of Cast-Iron,1 giving an outline which, for convenience of reference, I here repeat. Suggested Lines for DiScuSsion and IvestiGation. I.—Correspondence between chemical composition and melting-point, fluidity, shrinkage, fracture, chill, micro-structure, and other physical properties. II.—Influence of: 1. Cupola-mixture, use of steel and other scrap, oxidized or clean material, 2. Manner of melting, flux, etc., 3. Casting-temperature, A. Fracture. 4. Manner of handling melted metal and B. Micro-structure. method of casting, C. Physical properties. 5. Size and form of casting, D. Shrinkage. 6 Kind of mold, green sand (under dif- on E. Chill. ferent conditions of ramming, amount F. Residual strew of moisture, and skin-dried), dry sand, G. Condition and quan- loam, and chills, tity of carbon and 7. Rate and mode of cooling castings, other elements. 8. Manner and temperature of heating for annealing, 9. Additions of nickel or aluminum, III. —-Segregation as affected by : 1. Composition ; 2. Casting-temperature; 3. Rate of cooling ; 4. Size and shape of casting. IV. —Blow-holes, their volume and position as affected by: 1. Composition; 2. Casting-temperature; 3. Casting-pressure ; 4. Rate of cooling; 5. Size and ehape of casting ; 6. Special additions. It was hoped that a discussion might thus be elicited, similar in interest and value to the discussion of the physics of steel, which had been so widely and gratefully welcomed by students and practitioners in that department. That this hope was not

Jan 1, 1905

By R. L. Orr, J. D. G. Masse, Ralph Hultgren

The relative partial molar enthalpies of gold and tin in liquid Au-Sn alloys have been measured from Xsn = 0.474 to 0.510 at 696°K, slightly above the melting point of solid AuSn. Within an average precision of 6 cal per g-atom, the data are represented by two smooth curves, which satisfy the Gibbs-Duhem relationship and which do not show any anomalous behavior in the range of composition studied. The results give no support to the hypothesis that atomic associations in the equiatomic liquid alloy resemble those in solid AuSu. LITTLE has been firmly established as to the nature of atomic distribution in liquid metallic phases. A favored hypothesis assumes the existence of atomic groupings in the liquid phase which are similar to those in solid phases occurring at lower temperatures. Beginning with this hypothesis, it is often possible to adjust the values of certain parameters (such as degree of association) so that approximate agreement is achieved with certain features of the X-ray diffraction pattern of the liquid, even though many other possible structures might satisfy the data equally well. Thus, in this manner, the structure of liquid tin has been described as a dispersion of fragments of gray tin in a matrix of metallic tin.1 Four X-ray diffraction studies2"5 have been made of the liquid alloy of composition AuSn at temperatures slightly above the melting point of the solid. Each investigator concluded, on somewhat different grounds, that the liquid consisted to a large extent of arrays of atoms similar to the solid, with admixture of more disordered arrays. Solid AuSn has the nickel arsenide crystal structure: each tin atom has six nearest neighbors, all gold atoms; and each gold atom has six tin and two gold atoms as nearest neighbors. It remains highly ordered to the melting point. The liquid alloy has a large exothermic (?H700° K = -2700 cal per g-atom6) enthalpy of formation, favoring ordering and making the hypothetical molecular association not unreasonable. The possible existence of such solidlike arrays, or of a high degree of order that occurs preferentially at a specific composition in a liquid alloy, might also be revealed by thermodynamic behavior somewhat analogous to that in highly ordered solid alloy phases. The latter often exist over wide composition ranges, within which the highest degree of order occurs at the ideal composition for which the atomic fractions are equal to the fractions of sites which are "right" for each kind of atom. On departing from the ideal composition, the excess atoms occupy "wrong" positions, raising the internal energy and making it progressively easier for additional atoms to occupy "wrong" positions. Thus, on either side of the ideal composition, there should be a pronounced rise in the entropy and enthalpy, which would be shown particularly by the change in the relative partial molar enthalpies, ?Hi, since they depend strongly on d?H/dx. In the one case where accurate measurements have been made, the solid AuCu ordered phase, the structure becomes much less ordered as the composition deviates from the ideal, and relative partial molar enthalpies change sharply as shown by the data6 given in Table I. This suggests the possibility of finding similar pronounced changes in the relative partial molar enthalpies of gold and tin in liquid alloys near the composition AuSn if the postulated solidlike ar-

Jan 1, 1967

By Wm. E. Milligan

DESPITE the zero weather of Monday, the morning meeting on nonferrous ore-reduction metallurgy got under way promptly under the efficient control of Arthur A. Center. The first and third portions of the paper on the Tri-State region were presented by B. M. O'Harra, with R. H. Lowe substituting for co-author Illidge on the second part. Attention was drawn to the compact design attainable when "Sink and Float" was employed as a means of primary concentration. The teaching profession should welcome this concise correlation of data from such a renowned center of lead and zinc production. H. R. Hanley and C. R. Hay¬ward were much interested in the mechanics of charging, manufacture, and life of the retorts.

Jan 1, 1943

By J. B. Bassett, E. S. Rowland

INTRODUCTION THE experimental work reported herein was inspired by the publication of a paper by Grange and Stewart,1 in which it was suggested that at low chromium contents the effect of this element on the [M,] point was greater than at higher chromium contents. It was argued that, if a small increase of chromium in solution in austenite caused a sharp lowering of the [M,] point, it might lead to an explanation of occasional unsolved stress cracking of SAE 52100 during heat treatment. Commercial hardening is carried out at temperatures of incomplete solution, leaving carbides available to enrich the austenite during any inadvertent increase in temperature. Such enrichment of the austenite in chromium content would lower the [ M,] point nearer room temperature where cracking is more likely to occur. Accordingly, it was decided to investigate the effect of chromium, in quantities between o and 2 pct, on the[ M,] point of commercial steels. Fig I summarizes the data available on chromium steels. For purposes of comparison, the [M, ] temperature values were corrected by means of the Grange and Stewart formula§ to (I) Hypoeutectoid compositions: 0.50 pct carbon and 0.80 pct manganese (2) Hypereutectoid compositions: 1.00 pct carbon and 0.35 pct manganese. Only the steels having compositions reasonably close to these corrected values were included, because large adjustments inevitably introduce increased errors such as are experienced in using the formula. The straight lines of Fig I were drawn by the authors. These data obviously do not settle the question of the effect of chromium on the [M,] point, particularly at low chromium contents. While it is fairly well established that chromium causes the [M,] to be lowered when present in quantities of I pct or more, Grange and Stewart1 have suggested that in small amounts (less than I. pct) it is more effective in lowering the[ M,] point, while Klier and Troiano2 have suggested that in small amounts it is less effective in lowering the []M,] point. Payson and Savage3 concur with Klier and Troiano and further suggest that the effect is not linear at these concentrations. Rose and Fischer4 report that small amounts of chromium actually raise the-[M,] point of a 0.20 carbon steel. MATERIAL Two series of 35 lb induction heats were melted for this work, the analyses of which are given in Table I. One series was aimed at 0.50 pct carbon and 0.80 pct manganese with chromium additions in 0.25 pct increments from o to 1.5 pct with a single heat at 2.0 pct Cr. This series was considered necessary because the commercial heat treatment of SAE 52100 does not generally introduce more than about 0.60 pct carbon in solution in the austenite. The high

Jan 1, 1948

By A. Cochardt, D. H. Feisel

HE success of the sintered aluminum powder material (SAP)' in raising the maximum useful temperature of aluminum alloys has stimulated effort in investigating similar systems in which the metallic matrixes have higher melting points. Examples of such systems which have been studied are nickel-alumina,2, 3copper-silica,4 copper-alumina,4 titanium-cerium oxide,5 and 80/20 nickel-chromium,8 cobalt,= and molybdenum7 matrixes with various hardeners. Conventional precipitation-hardened high-temperature alloys are often thermally unstable in service. The original fine particles that are responsible for good strength properties grow in size at elevated operating temperatures, a process termed "over-aging." This growth of precipitated particles causes a gradual loss in strength properties. A previous paperb describes the factors that govern the process of overaging, and estimates the time required for overaging of a nickel-alloy matrix dispersion-hardened by various precipitates such as are found in current high-temperature alloys, and by alumina. These calculations indicate that nickel-base alloys hardened with Ni3Al, Tic, or TiN are quite unstable at 1340" F (727°F). Such alloys should overage within a few hours at that temperature. A nickel-base alloy hardened with alumina, on the other hand, should behave differently. It should not overage appreciably within a thousand years. It was further shown8 that the thermal stability of the oxide-hardened alloy is mainly due to the low solubility of oxygen in equilibrium with alumina in the nickel-base matrix. Since the oxygen solubility is small, little oxygen can diffuse, and structural changes require very long times. This paper illustrates the effects of time and temperature on the structural stability of nickel alloy matrixes hardened by dispersions of Ni3A1, Ni3Ti, Tic, and alumina, and of nickel-chromium matrixes hardened by alumina. Hardness measurements and metallography have been used as a measure of structural stability. EXPERIMENTAL PROCEDURE Using the best information from published phase diagrams,'-l4 compositions of the Ni-Al, Ni-Ti, and Ni-Ti-C alloys were determined so as to have 5 vol pct of precipitate at 1350° F(732°C), the temperature selected to illustrate the effect of time on structural stability. Table I lists the chemical compositions of these alloys. Standard laboratory melting and alloying techniques were used in preparing ingots of the F-Series of alloys. The cast ingots, 1 3/4 in. in diam, were forged to 3/8-in. diam rods.

Jan 1, 1960

JOHN H. NELSON, Worcester, Mass.-At our plant we have done considerable work on notch-bar testing and are farther at sea now than when we started. So far, we have been unable to get the notch-bar test to be consistent with any other known test. Lately, I have been investi-gating the effect of the position of the notch-bar specimen in a, bar. To do this I took a 3, ½ in. square bar and quartered it, then heat treated the four quarters. Each of these pieces was again quartered and a specimen machined and notched. "In this way we would have notch-bar tests from the exterior to the interior of the bar. These were made of such lengths that it was possible to make four impact tests on each speci-men. Extreme care was taken in marking the position of these test speci-mens in the original bar. The notches were then cut with relation to position of the specimen in the original bar. The second notch was cut 90° from the first, and so on around the specimen. In this way, we have found that, with a 3 ½ in. bar of 0.4 or 0.5. per cent. carbon steel when properly heat treated, we could get impact values ranging from 15 to 100 ft.-lb. Just why this is the case we are unable to state; but it does appear to be a fact that along the outside of the original bar the notch-bar test seems to be low and increases toward the center, but it is not always consistent. For instance, we may have, on a single specimen; one notch-bar test giving us 15 ft.-lb. and another 100 ft.-lb. We have not found such inconsistencies in alloy steels. Alloy steel is consistently good or consistently bad. If it. is good, you cannot readily destroy the impact value, no matter what you do; if it is bad-that is, if it is a poor notch-bar steel-and you have sufficient latitude in your draw, you may correct it. In other words, if the hardness you are working to will allow you to draw to about 1050° F.(561° C.) or over and then quench this steel from the draw heat, you. can raise the im-pact value of the steel from about 4 or 10 ft.-lb. up to-40-or 50 ft.-lb: Just what occurs I do not know. There is evidently a critical-point in steels that have poor impact value, in the neighborhood of 1000 F. to 1050° F. (536° to 561° C.).

Jan 12, 1919

By ROBERT E. HARDWICKE

THE QUESTION of whether the production of oil should be limited to market demand has been constantly discussed during the last two years. Oil men, legislatures and courts have reached highly conflicting conclusions. Opponents of limitation to market demand assert that it is a scheme of the big purchasing companies to fix prices and to create a monopoly. Proponents, on the other hand, declare that such a limitation is necessary to prevent physical waste and that the effect on prices is merely incidental. A brief review of market demand legislation will disclose the confusion existing. The laws of Oklahoma,' prohibiting waste of oil and gas, specifically' authorize limitation to market demand as a method of preventink such waste. These laws and the proration orders based thereon have been upheld by the Supreme Court of Oklahoma, by several three-judge Federal District Courts, and by the Supreme Court of the United States.' Kansas has a similar law3 but no case has been found which discusses its validity. About a year ago the California Legislature passed a comprehensive conservation act, generally known as the Sharkey Bill giving authority to restrict production to an amount representing current requirements for use, taking into consideration oil and products in storage. This may be considered as equivalent to limitation to market demand. The Act was defeated upon referendum vote after a hard fought campaign in which it was charged that the Act would result in destruction of the independent operators.

Jan 1, 1932

By A. E. Wells, H. O. Hofman, R. P. Reynolds

A Discussion of the Paper of H. O. Hofman, R. P. Reynolds and A. E. Wells, read by title at the London Meeting, July, 1906 ; presented at the New York Meeting, April, 1907, and printed in Bi-Monthly Bulletin, No. 13, January, 1907, pp. 37 to 52. GEORGE A. PACKARD, Boston, Mass. (communication to the Secretary*) :-The very interesting results obtained by Prof. Hofman and his assistants came to my attention when I had temporarily assumed charge of the metallurgical department of the Missouri School of Mines, and had found it, pending the completion of a new building, lacking a furnace in which to roast ore preparatory to the customary lead blast-furnace run. An attempt at lime-roasting had been already determined upon, but the use of a charge which would make a slag of definite composition was a new idea. The results following were obtained by Messrs. Aubrey Fellows, J. C. Long, E. R. Wash, and Dr. T. C. Tseung, under my supervision. It is regretted that the data are not more complete; but the work was done simply incidentally to securing the desired ore for the blast-furnace, with no idea of obtaining any results of especial interest. It is submitted because of the metallic lead obtained, no notice of which has been seen elsewhere. The ore was an aggregate of several lots of concentrates, apparently from Missouri ores. The analysis follows, with that of the limestone and sandstone used, as far as made:. Ore, SiO2, 3.04; Fe, 0.77; CaO, 2.53; Pb, 68.74; Zn, 5.77; S, 13.9 per cent.; limestone, SiO2, 1.0 ; CaO, 54.35 per cent.; sandstone, SiO2, 99.8 per cent. The converter was made in the shops from a sheet of No. 14 iron riveted in the shape of a truncated cone, 20 in. in diameter at the top, 15 in. at the bottom and 22 in. high. A grate of No. 8 iron, 17 in. in diameter, with 130 s-in. holes placed at about 1.25-in. centers, was held in place by the shape of the

Jul 1, 1907

By Bruce W. Gonser, Robert I. Jaffee

Recent work by the authors1 established the constitutional diagram of the gold-germanium system. Of particular interest in the simple euctectiferous system was the eutectic alloy at 12 per cent Ge, which melted at the very low temperature of 356°C and had an unusually fine eutectic structure. It was of interest to investigate the effect of third components on the melting point, microstructure, and strength of this alloy, and in this work the effect of copper is discussed rather completely, with less complete data on the effects of silver, platinum, nickel, and zinc. No reference in the literature has been found on ternary systems with gold-germanium. Materials and Alloying -4s in the work on the binary system, gold-germanium, the germanium used in this investigation was the cyanide-reduced, 99.9 per cent product, produced by the Eagle-Picher Co. Fine gold sheet from Handy and Harmon, pure platinum sheet from the American Platinum Works, copper magnet wire from Anaconda, nickel wire assaying 99.6 per cent Ni. and electrolytic zinc were used for alloying. To make the alloys, charges of the pure metals were put in a graphite crucible and melted in an atmosphere of pure hydrogen. The temperature was brought up to about I050 C, and the metal allowed to freeze in the crucible. Except with alloys containing zinc, melting losses were consistently less than a few milligrams. When zinc was a component, weight losses up to half the weight of the zinc present were incurred, and the alloy compositions were calculated by assuming the entire weight loss to be that of zinc. In all other cases the composition of the alloys could safely be taken as that of the charge. The ingots, as solidified, were segregated, the heavier primary phases being at the bottom and sides of the ingots and the lighter primary phases at the top, but by sectioning the entire ingot vertically for microscopic examination, this factor could be evaluated. Ingots for microscopic examination weighed one gram, and those for thermal analysis weighed three grams. Thermal Analysis In this work, the eutectic line composition and thermal arrests were desired, and, after microscopic exploration had established the position of the eutectic line at a given percentage of the third component, a thermal analysis was run at that composition. The method of thermal analysis used in the work on the binary Au-Ge system,' a method particularly well suited for a small quantity of material, was used in this work. Clearly defined arrests were obtained, although with some alloys containing platinum

Jan 1, 1946

By Robert I. Jaffee, Bruce W. Gonser

Recent work by the authors1 established the constitutional diagram of the gold-germanium system. Of particular interest in the simple euctectiferous system was the eutectic alloy at 12 per cent Ge, which melted at the very low temperature of 356°C and had an unusually fine eutectic structure. It was of interest to investigate the effect of third components on the melting point, microstructure, and strength of this alloy, and in this work the effect of copper is discussed rather completely, with less complete data on the effects of silver, platinum, nickel, and zinc. No reference in the literature has been found on ternary systems with gold-germanium. Materials and Alloying -4s in the work on the binary system, gold-germanium, the germanium used in this investigation was the cyanide-reduced, 99.9 per cent product, produced by the Eagle-Picher Co. Fine gold sheet from Handy and Harmon, pure platinum sheet from the American Platinum Works, copper magnet wire from Anaconda, nickel wire assaying 99.6 per cent Ni. and electrolytic zinc were used for alloying. To make the alloys, charges of the pure metals were put in a graphite crucible and melted in an atmosphere of pure hydrogen. The temperature was brought up to about I050 C, and the metal allowed to freeze in the crucible. Except with alloys containing zinc, melting losses were consistently less than a few milligrams. When zinc was a component, weight losses up to half the weight of the zinc present were incurred, and the alloy compositions were calculated by assuming the entire weight loss to be that of zinc. In all other cases the composition of the alloys could safely be taken as that of the charge. The ingots, as solidified, were segregated, the heavier primary phases being at the bottom and sides of the ingots and the lighter primary phases at the top, but by sectioning the entire ingot vertically for microscopic examination, this factor could be evaluated. Ingots for microscopic examination weighed one gram, and those for thermal analysis weighed three grams. Thermal Analysis In this work, the eutectic line composition and thermal arrests were desired, and, after microscopic exploration had established the position of the eutectic line at a given percentage of the third component, a thermal analysis was run at that composition. The method of thermal analysis used in the work on the binary Au-Ge system,' a method particularly well suited for a small quantity of material, was used in this work. Clearly defined arrests were obtained, although with some alloys containing platinum

Jan 1, 1946

By Robert I. Jaffee, Bruce W. Gonser

RECENT work by the authors1 established the constitutional diagram of the gold-germanium system. Of particular interest in the simple euctectiferous system was the eutectic alloy at 12 per cent Ge, which melted at the very low temperature of 356°C. and had an unusually fine eutectic structure. It was of interest to investigate the effect of third components on the melting point, microstructure, and strength of this alloy, and in this work the effect of copper is discussed rather completely, with less complete data on the effects of silver, platinum, nickel, and zinc. No reference in the literature has been found on ternary systems with gold-germanium. MATERIALS AND ALLOYING As in the work on the binary system, gold-germanium, the germanium used in this investigation was the cyanide-reduced, 99.9 per cent product, produced by the Eagle-Picher Co. Fine gold sheet from Handy and Harmon, pure platinum sheet from the American Platinum Works, copper magnet wire from Anaconda, nickel wire assaying 99.6 per cent Ni, and electrolytic zinc were used for alloying. To make the alloys, charges of the pure metals were put in a graphite crucible and melted in an atmosphere of pure hydrogen. The temperature was brought up to about 1050°C., and the metal allowed to freeze in the crucible. Except with alloys containing zinc, melting losses were consistently less than a few milligrams. When zinc was a component, weight losses up to half the weight of the zinc present were incurred, and the alloy compositions were calculated by assuming the entire weight loss to be that of zinc. In all other cases the composition of the alloys could safely be taken as that of the charge. The ingots, as solidified, were segregated, the heavier primary phases being at the bottom and sides of the ingots and the lighter primary phases at the top, but by sectioning the entire ingot vertically for microscopic examination, this factor could be evaluated. Ingots for microscopic examination weighed one gram, and those for thermal analysis weighed three grams. THERMAL ANALYSIS In this work, the eutectic line composition and thermal arrests were desired, and, after microscopic exploration had established the position of the eutectic line at a given percentage of the third component, a thermal analysis was run at that composition. The method of thermal analysis used in the work on the binary Au-Ge system,1 a method particularly well suited for a small quantity of material, was used in this work. Clearly defined arrests were obtained, although with some alloys containing platinum

Jan 1, 1946

By Thunaes, Arvid

Pilot plant test work in 1942 and 1943 showed that by a combination of desliming, fine-size classification, and Sullivan deck concentration it is possible to recover heavy minerals such as cassiterite at least as fine as 10 microns in size. This appreciable improvement in gravity concentration practice has been substantiated by several full-sized plants.

Jan 1, 1950

By Charles Hart

A STUDY of the various ores that have been discussed impresses one with the need of beneficiation, in many cases. This applies to the ores that have lain dormant, due to necessity for further preparation, or to ores that now find a market due to a changed condition. Processes of beneficiation will come into their own as our richer ores become exhausted. Many efforts at improvement have been commercial failures, due to prematurity. Thomas A. Edison, with characteristic foresight, attempted concentration of the low- grade New Jersey magnetites some thirty years ago. Due to high costs and the discovery of the Mesabi range, his efforts were futile. However, a successful crusher, designed by Mr. Edison, resulted from this attempt. Agglomeration of concentrates had not, at that time, been brought to its present efficiency, when sinters and briquettes of excellent physical condition are obtainable. Recent efforts in the beneficiation of the lean magnetites of the East Mesabi resulted in an excellent sinter, but that operation is also ahead of its time.

Jan 1, 1929

By Zay Jeffries

IN this paper, it is proposed to outline a method for the determination of melting points of those metals and alloys having high fusion temperatures. The application of the method as used to determine the melting points of alloys of tungsten and molybdenum will be given. It will be seen from these results that tungsten and molybdenum form a completely FIG. 1.-PARTIAL SECTION OF APPARATUS USED TO DETERMINE MELTING POINTS OF TUNGSTEN AND MOLYBDENUM ALLOYS. isomorphous series. This is also verified by the accompanying photomicrographs. Tungsten and molybdenum have been found to crystallize in the salve system, namely, isometric, and the crystal units are cubes. These determinations were made by examining etching pits in the pure metals.

Jan 7, 1916