By W. Klement

By quenching liquid alloys, single-phase solid solutions are obtained in the ranges 0 to 42.0 at. pct Co-Au and 0 to 15 and 75 to about 100 at. pet Co-Cu. Metastable solid solutions are also found in multiphase 42.0 to 49.0 and 69. 0 to about 100 at. pet Co-Au alloys. fie inability to achieve complete solid solubiliiies in Au-co and cu-co alloys is rationalized by a conszderation of the rate processes during cooling and solidification. Trends in lattice distortion and shifts in the compositions of the melting-point minima and critical points are discussed for the binary alloys of copper, silver, and gold with some of the transition metals of the first long period. By rapidly cooling alloys from the melt, a continuous series of metastable solid solutions can often be obtained for components of similar crystal structure which normally form eutectic systems.' The eutectic system Au-Co, Fig. 1, and the peritectic system Cu-Co, Fig. 2, were investigated in order to determine the extent of the metastable solid solutions attainable with the present technique.* EXPERIMENTAL PROCEDURES Most of the alloys were prepared by melting weighed quantities of the elements (purity greater than 99.9 pct) under hydrogen in alumina crucibles by means of induction heating. After reweighing, the alloys were cast under argon into 1 mm diam wires. However, it was not possible to prepare some of the Cu-Co alloys with the requisite homogeneity (over about 1 mm3) in this way. For these alloys, reduced powders (purity greater than 99.9 pct) were mixed for 12 to 48 hr, pressed into compacts that were sintered at 1000º to 1050°C for 6 to 48 hr under hydrogen, and then furnace-cooled. Alloy charges of a few mm3, cut from the cast wires or chipped from the sintered compacts, were heated to 1550º to 1600°C in 30 sec in an alumina insert held within a graphite support and then ejected by a pulse of helium onto a lightly polished copper strip on the inner periphery of a rotating wheel. The

Jan 1, 1963

Jan 1, 1943

Jan 1, 1943

Jan 1, 1961

By R. L. Moment

The anisotropic elastic behavior of rolled beryllium sheet has been measured, using a pulse echo technique, and compared with X-ray diffraction data. Calculated elastic stiffness constants compared favorably with published values for beryllium single crystals which were attributed to the strong (0002) rolling plane texture. Variations of Young's modulus in the yolling plane could be associated with the velative distribution of (0002) planes out of their ideal position in the rollitzg pkule. WHEN a metal is subjected to cold working such as drawing, forming, or rolling, a crystallographic texture develops which can significantly alter its physical properties. One method for detecting this texture is X-ray diffraction, but Alers and Liu' have recently pointed out how the prediction of anisotropic physical properties from pole figures alone is not always accurate due to differences in interpretation. Variations in Young's modulus with orientation or, more completely, the values of the effective elastic constants of the worked metal, also serve to indicate the presence of a texture. In fact, as Alers and Liu' pointed out, calculated variations in Young's modulus for assumed orientations, when compared with experimental data, can be used to eliminate some of the uncertainty in interpretation of X-ray pole figures. Thus, elasticity measurements can serve not only to clarify any unusual elastic behavior of worked metal, but also to detect and in part determine the nature of its texture. X-ray determination of the texture of rolled beryllium has been reported by Smigelskas and Barrett,2 who found a strong texture of (0002) in the rolling plane with (1070) planes normal to the rolling direction. In the case of metal rolled at room temperature, they reported that [1010] directions also appeared at positions 60 and 120 deg from the rolling direction in the rolling plane, while in more recent work Keeler3 found these directions were also tilted towards the rolling plane. The texture for beryllium rolled at 80O0C, however, only showed (1010) planes normal to the rolling direction and the spread of (0002) planes out of the rolling plane was less. In looking for elastic anisotropy one might consider unidirectional rolling of a metal as introducing an or-thorhombic symmetry through reorientation of the grains, since the three deformations, compression, extension in the rolling direction, and extension in the cross direction, are orthogonal to each other and unequal in magnitude. Thus the rolled sheet could be treated like an orthorhombic single crystal and the nine stiffness constants of the elasticity tensor used to calculate the anisotropy of Young's modulus, the shear modulus and Poisson's ratio. In this case we could write: which is symmetric about its diagonal. Borik and Alers4 have recently used this approach on rolled die steel with very good results. They found, however, that instead of displaying orthorhombic elastic symmetry their specimens could be considered tetragonal in which case Cr1 = c22, c13 = Ca, and c44 =cjj. This conclusion was made solely on the basis of the measured tensor elements, and serves to point out the advantage of this method for studying the anisotropy of rolled metals. Their calculated values for Young's modulus as a function of angle in the rolling plane also checked very well with direct measurements made on different specimens using the resonance technique. In the present study, cross-rolled beryllium was used which had been unidirectionally rolled about 11 pct for the final reduction. This imparted a slight anisotropy in the rolling plane which was detected both by X-ray techniques and elasticity measurements. For purposes of discussion in this paper, the rolling direction is that direction in which the most reduction passes were made and cross direction is the normal to the rolling direction in the rolling plane. It was also decided to consider the rolled sheet as displaying orthorhombic symmetry for the purpose of obtaining elasticity samples with the direction defined as in Table I. Any change in the final symmetry attributed to the sheet would then be made on the basis of the measured elastic stiffnesses. The final data would then be compared with that expected from the X-ray study and that reported for beryllium single crystals. EXPERIMENTAL PROCEDURE Rolling Schedule. The samples used in this study were taken from a large sheet which, because of its size, had to be unidirectionally rolled for the final reduction. The resulting texture was that of cross-rolled metal with a slight unidirectional texture superimposed. A cast beryllium ingot, 9.500 in. sq by 3.325 in. thick, was cross-rolled to 81 pct reduction followed by unidirectional rolling for an additional 11 pct to give a total reduction of 92 pct. The thickness of the final sheet ranged from 0.265 to 0.280 in. Reduction up to 67 pct was done at 980°C and the final 25 pct at 870°C. Analysis for metallic impurities showed aluminum 0.06 pct, iron 0.19 pct, and silicon 0.11 pct, giving a beryllium purity of 99.64 pct.

Jan 1, 1968

By F. C. Newton

RefineRs of lead by the Parkes process have always been solicitous of recovering the zinc used in the desilverization, and justly so, as the loss in zinc constitutes one of the heavy costs in this method of refining. Part of this loss is due to the absorption of zinc by lead, and in the present state of knowledge is not recoverable as metallic zinc. The remainder of the zinc, which finds its way into the precious-metal-bearing crust, is recoverable and naturally engages the operators' most exacting attention. Careful elimination of the impurities in base bullion has enabled the refiner to produce a zinc crust better adapted to retorting, which reflects favorably in the zinc recovery;- and to produce a richer crust, thereby lowering the zineking cost, as the increased efficiency of the zinc results in less of it being in circulation. It is obvious that if the ratio of concentration be increased, a lessening of the amount of crust formed will ensue, throwing less work on the retorts and diminishing the amount of retort metal sent to the cupels, thus making an actual money saving in all these operations. In the effort to obtain a rich crust, the metallurgist has increased the heat to a considerable degree, upon the assumption that at the higher temperature the zinc-dver alloy could be squeezed free from the adhering lead. A further possibility for improvement suggested itself in the freezing-point curve of Prof. H. C. Carpenter, upon zinc and silver. Study of this curve disclosed the existence of a definite chemical compound, Zn3Ag2, with a freezing point of 665" C., a promising compound for practical application. In the experiment undertaken it was endeavored to force this compound into the crust, hoping thereby to obtain a higher concentration than formerly. It was recognized that in bringing a large kettle of lead to such a heat, more fuel would be used, the life of the kettle would perhaps be shorter, and other disadvantages would be experienced. AS a commercial operation, the project would have to stand on its own feet,

Jan 1, 1915

By M. Sheffield

This paper presents a technique lor predicting the flow of oil, gas and water through a petroleum reservoir. Gravitational, viscous arid capillary lorces are considered, and all fluids are considered to be slightly compressible. Some theoretical work concerning the fluid flow in one-, two- and three-space dimensions is given along with example performance predictions in one- and two-space dimensions. INTRODUCTION Since the introduction of high speed computing equipment, one of the goals of reservoir engineering research has been to develop more accurate methods of describing fluid movement through underground reservoirs. Various mathematical methods have been developed or used by reservoir engineers to predict reservoir performance, 193-5,7,8 The work reported in this paper extends previously published work on three-phase fluid flow (1) by including a rigorous treatment of capillary forces and (2) by showing certain theoretical mathematical results proving that these equations can be approximated by certain numerical techniques and that a unique solution exists. DISCUSSION The method of predicting three-phase compressible fluid flow. in a reservoir can be summarized briefly by the following steps. 1. The reservoir, or a section of a reservoir, is characterized by a series of mesh points with varying rock and fluid properties simulated at each mesh point. 2. Three partial differential equations are written to describe the movement at any point in the reservoir of each of the three compressible fluids. All forces influencing movement are considered in the equations. 3. At each mesh point, the partial differential equations are replaced by a system of analogous difference equations. 4. A numerical technique is used to solve the resulting system of difference equations. Capillary forces have been included in two-phase flow calculations.1,4,8 The literature, however, does not contain examples of prediction techniques for three-phase flow that include capillary forces. Where capillary forces are considered, each of the three partial differential equations previously discussed has a different dependent variable, namely pressure in one of the three fluid phases. Therefore, three difference equations must be solved at each point in the reservoir. Where large systems of equations must be solved simultaneously, an engineer might question whether a unique solution to this system of equations actually exists and, if so, what numerical techniques may be used to obtain a good approximation to the solution. It is shown in the Appendix that a unique solution to the three-phase flow problem, as formulated, always exists. It is also shown that several methods may be used to obtain a good approximation to the solution. The partial differential equations and differenceequations used are shown in the Appendix. Matrix notation has been used in developing the mathematical results. Two sample problems were solved on a CDC 1604. They illustrate the type of problems that can be solved using a three-phase prediction technique. SAMPLE ONE-DIMENSIONAL RESERVOIR PERFORMANCE PREDICTION A hypothetical reservoir was studied to provide an example of a one-dimensional problem that can be solved. Of the several techniques available, the direct method of solution as shown in the Appendix was used. The reservoir section studied was a truncated, wedge-shaped section, 2,400 ft long, with a 6' dip. (A schematic is shown in Fig. 1.) This section was represented by 49 mesh points, uniformly spaced at 50-ft intervals. The upper end of the wedge was 2 ft wide, and the lower end was 6 ft wide. The section

Jan 1, 1970

By David T. Peterson

Calcium metal was found to deoxidize thorizcm at 1000° to 1200° C. The reaction kinetics were determilled and related to the diffusion coefficients of oxygen in thorium. The solubility of oxygen in thorium, the minimum oxygen concentration, and the diffusion coefficient were determined from 1000° to 1200°C. This firocess results in the lowest oxygen concentrations zohich have been reported for thorium metal. FOR many years it has been known that calcium metal will reduce thorium oxide to thorium metal. This reaction has been the basis for several methods of preparing thorium metal. From the equations giv-by Kubaschewski and vans, ' AF" for the reaction Cao, + Tho,(,) - CaO(,, + Th(,) was calculated and found to be -3.4 kcal at 1000°C, -2.5 kcal at llOO°C, and -2.0 kcal at 1200°c. Thorium is very slightly soluble in liquid calcium, and the solubility of calcium in solid thorium is very low. Consequently these metals would be in essentially their reference states. If thorium containing oxygen were equilibrated with liquid calcium between 1000° and 1200°C, the oxygen content of the thorium would have to be below the solubility limit in thorium. Oxygen is one of the impurities most difficult to remove from thorium and is the most abundant impurity in metal prepared by almost all known methods. Fortunately, oxygen does not have a large influence on the properties of thorium because the solubility in solid thorium is very low. EvenT in thorium containing 100 ppm of 0, particles of thorium oxide can be observed in the microstructure. In view of the incompatibility of thorium oxide and liquid calcium and the low solubility of thorium oxide in thorium, the deoxidation of thorium by this method was investigated. For thorium containing an amount of oxygen well in excess of the solubility limit, the reaction should proceed in the following sequence. The oxygen content of the thorium matrix near the surface would be depleted by the diffusion of oxygen to the surface. At the surface, the oxygen would react with calcium to form calcium oxide. To maintain equilibrium within the thorium, thorium oxide would dissolve to keep the matrix saturated. Consequently, the thorium-oxide particles would disappear first at the surface and then the particle-free rim would grow in thickness. If the rate-controlling step were the diffusion of oxygen through this layer of thorium which was growing in thickness in direct proportion to the amount of oxygen removed, the well known parabolic time law should be observed. If the oxygen concentration at the surface of the thorium and at the inner surface of the deoxidized rim were known, the diffusion coefficient of oxygen in thorium could be calculated from the parabolic rate constant. EXPERIMENTAL PROCEDURE The thorium metal used in this study was prepared by calcium reduction of ThF, by the method described by Wilhelm.' The analysis of this metal is given in Table I. The carbon was determined by combustion, the oxygen by the HC1-insoluble residue method, nitrogen by the Kjeldahl method, and the other elements by emission spectroscopy. A section of this ingot was hot rolled at 600°C to 1/4 and 1/8-in. thick plates. Specimens approximately 7/8 in. square were cut from these plates, and all surfaces of the specimens were cleaned and smoothed by filing with a clean file. Individual specimens were placed in 1-in. diam by 2-in.-long tantalum capsules. Approximately 1 g of clean, high-purity calcium was placed in the capsules and an end closure arc-welded in place. The tantalum capsules were sealed in Inconel crucibles to protect the reactive metals from oxidation. The entire loading procedure was done in a glove box filled with pure argon. The loaded crucibles were placed in a muffle furnace, controlled within 2OC of the desired temperature, for a measured length of time. After the specimen had cooled to room temperature, it was sectioned perpendicular to the large faces and through the mid-point of two of the sides. The sectioned specimen was mounted and polished through Linde A abrasive. The rim which was free of thorium-oxide particles could be clearly observed microscopically as mechanically polished. Twenty measurements of the thickness of the rim were made at equally spaced points far enough from the end of the

Jan 1, 1962

By R. Kossowsky, W. C. Johnston

CONSIDERABLE experimental data has been published in recent years on a few directionally solidified aluminum base eutectic alloys. The mechanical properties of A1-Al3Ni eutectic have been studied by Lemkey, Hertzberg, and Ford1',2 and Salkind et a1.3 where the alloy has been demonstrated to behave as a whisker reinforced composite with superior properties over many aluminum alloys. It has also been shown4 that aluminum reinforced with Al3Ni whiskers R. KOSSOWSKY, Member AIME, is Senior Metallurgist, Westing-house Research Laboratories, Pittsburgh, Pa. W. C. JOHNSTON, formerly with Westinghouse Research Laboratories, is Head, Department of Physics, George Mason College, University of Virginia, Fairfax, Va. Manuscript submitted March 28. 1969. IMD__________________ possesses excellent microstructural stability to 508°C. The effect of lamellar structure in A1-CuA12 eutectic was compared3 to the rod-like structure in the A1-Al3Ni eutectic, and was found to be better in low cycle fatigue. This was rationalized3 by postulating that a lamellar reinforcement was more efficient at blocking lateral plastic flow than a rod-like rein-forcement. The purpose of this study is to explore eutectic strengthening in other aluminum base alloys. The Al-Pd system5 forms a eutectic with aluminum and the intermetallic compound A13Pd at 25 wt pct Pd, and has a melting point of 615°C. A13Pd has an orthorhom-bic structure and transforms to hexagonal Pd2A13 at 785°C. Growth characteristics, compression yield strength, creep rupture, and microstructural stability of directionally solidified and as-cast alloys are investigated. Eutectic ingots having a nominal composition of 25 wt pct Pd were prepared by first compacting 1/2 in. diam by a in. high pellets from 99.99+ pct A1 and 99.99 pct Pd powders. The pellets were then levitation cast into 1/4 in. diam by 2 in. long copper molds. Directionally solidified bars were prepared by grinding the cast ingots to 0.195 in. diam, inserting them into alumina

Jan 1, 1970

Jan 1, 1969

By W. Vickers

Single-point rotating cantilever fatigue tests have been carried out at 550" to 650°C on beryllium produced by a variety of fabrication routes. All the specimens gave similar plots of stress against number of cycles to failure but failure occurred at a lower stress range in the hot-pressed material than in the extruded material. A discontinuity or "kink" appears to exist in the curves and this is considered. A true endurance limit was not evident up to 10 cycles. When Brush hot-pressed warm-extruded beryllium was tested at 600oC a relationship where Nf = number of cycles to failure, ?ep = plastic strain range, and c = constant, was shown to be applicable for values of ?ep > 6.3 x 10-4. Further for this moterial and temperature and for frequencies between 150 and 4500 cycles per min, the variation of number of cycles to failure with frequency obeyed the expression N = Af0.44 where N =number of cycles to failure, f = frequency, and A = constant. Examination of the fracture surfaces indicated that they were generally intergranular and in all cases the higher the stress the more irregular was the fracture. Microexamination has shown that grain boundary cavities and fine intergranular cracks were associated with the fractures. REVERSING or cyclic stresses set up in fuel elements can lead to failure by fatigue. Fatigue stresses may be developed by instability of the fuel element in the coolant flow leading to rattling against the channel wall or fin vibration. Thermal cycling also sets up reversing stresses due to differential expansion of fuel and can. Fatigue resistance is of some importance therefore in the evaluation of canning materials. At the time the work described in this paper was initiated, beryllium was being considered for the can and endcaps of an advanced gas-cooled reactor fuel element. With this in mind, beryllium obtained from different manufacturing routes was tested on single-point rotating cantilever fatigue machines at temperatures the same as those envisaged in the reactor to obtain appropriate fatigue data. The results obtained indicated a discontinuity in the S-N curves coinciding with the yield stress in the specimens. Although in some cases the data is insufficient to warrant a detailed quantitative analysis, a qualitative analysis of this effect was thought to be justified. 1) EXPERIMENTAL DETAILS The materials used are given in Table I together with the production route and available analyses. The specimen shape is shown in Fig. 1. The fatigue specimens were machined slightly oversize, after which they were given a stress-relieving anneal of 1 hr at '750° C in vacuum. This was followed by an etch in sulfuric-phosphoric-chromic acid mixture down to the finished dimensions given in Fig. 1. Etching served to remove the interference colored oxide film formed on the surface during annealing and very small recrystallized surface grains too. The specimen was mounted in the grips of a cantilever machine and rotated inside a furnace controlled at the testing temperature. The specimen was loaded in increments as the speed was increased until the required load was applied at 5000 cycles per min. A revolution counter was used to record the total number of cycles.

Jan 1, 1964

By E. Buehler, J. E. Kunzler

High-pu.1-ity molybdenum has been heat treated, melted, and zone refined and the physical and chemical changes that are produced by these processes have been studied by making resistance ratio measurements. Pronounced effects are observed that are associated with recrystalliza-tion at about 1200°C and with melting. Melting alone is found to result in a substantial purification by the evaporation of impurities such as iron. Zone refining is found to be reasonably effective with four passes producing a three-fold decrease in resistance ratio and a minimum ratio of 0.0003. With the aid of low temperature measurenzents, it has been shown that the build-up of a deposit of the material being zone refined on the radio frequency coil used for heating can lead to contamination of the sample. CONSIDERABLE interest in high-purity refractory metals for the study of mechanical properties has developed during recent years. Also the need for highly pure metals in certain fundamental studies, such as electronic band structure, has become quite widely appreciated. Molybdenum can now be produced with sufficiently high purity to make it attractive for such investigations. The most suitable measure of chemical purity of metals used for many of these studies is its resistance ratio, R,.,o,/Ro, During the purification of molybdenum by zone refining and its subsequent evaluation by this technique, a number of informative observations were made. These observations concern the effectiveness of zone refining, the volatilization of impurities at the melting point, and the recrystallization of molybdenum and appear to be pertinent to other refractory metals. Also, the usefulness of low-temperature resistance measurements as an analytical tool for evaluating the presence of chemical impurities and physical defects in metals is again illustrated. Samples of high-purity molybdenum of known mechanical history were heated to various temperatures between 800°c and their melting point. Resistance ratios of the samples were measured after they had been given a specified treatment. The data were used, along with mass spectrographic analysis, as an aid in interpreting the nature of the processes that occurred in conjunction with each treatment. Changes in the concentrations of chemical impurities and physical defects are typical of things that effect the low-temperature resistivity. SAMPLES The starting material was obtained from Westing-house Corp., Bloomfield, N.J. It was in the form of molybdenum rods, usually 1/8 or 3/16 in. in diameter. These had been previously processed from bars, 5/8 in, in diameter, originally reduced from 4 in. diam arc-cast ingots, by hot swaging at about 1300°c. In the final step, the temperature was lowered to about l lOO°C which resulted in the production of elongated grains. Typical grains were about 0.03 mm thick and 0.6 mm long. The molybdenum was quite pure as is indicated by the results of mass spectro-scopic analysis1 given in Column 2 of Table I. Other nongaseous elements not listed in the table were not detected. ZONE REFINING AND THERMAL TREATMENT OF SAMPLES Several sample rods, 8 to 10 in. long, were zone refined or were heat treated at several temperatures. Both types of operations were performed using 3 me-

Jan 1, 1962

Jan 1, 1970

By F. H. Wilson

Copper base alloys containing various amounts of aluminum and silicon are of considerable commercial interest. In particular the alloy containing 7 pct aluminum and 2 pet silicon shows an attractive combination of high strength with excellent, machinability. Since there is no evidence ill the literature that this ternary system has been studied since the recognition by Smith1 and Anderson2 in 1939 of the kappa phase of the binary copper-silicon system, the determination of the equilibrium phase relationships in the copper corner of the ternary diagram has been undertaken to provide a fundamental basis for understanding the behavior of these alloys. Phase boundaries have been determined by the micrographic examination of quenched samples while points on the liquidus surface have been obtained by thermal analysis. The results, of sufficient precision to serve their major purpose of providing a guide for the control of the manufacture of alloys in the region covered, are presented in a series of both isothermal and vertical sections of the diagram. Alloys StVdied For a rough survey of the copper corner of this ternary system the compositions listed in Table I (Series A) were employed. The results of examinations of these alloys indicated that the compositions listed in Table 2 (Series B) would further clarify regions of greater complexity. All alloys were prepared as 1200 g heats, the copper being melted under charcoal, and then first silicon and then aluminum were added. An excess of 0.05 pet silicon was allowed to cover deoxidation losses. Two small bars 5/8 by 1 1/4 by 5 1/4 in. were cast using Durville type casting equipment. Ailalyses were made on all alloys using material which was hot-rolled at 800 or 850°C and annealed 17 hr at 650°C. All analyses were found to be within 0.05 pet of the nominal composition. Since the precision of analysis is not much better than this, the points of both isothermal sections and vertical sections at fixed aluminum and silicon contents have been plotted at the compositions indicated by the nominal composition.

Jan 1, 1949

By W. L. Dumoulin

A RATHER detailed description of the entire plant and leaching process was given in a paper recently presented to the Institute,1 so this paper will cover briefly only the crushing practice of the New Cornelia Copper Co. for the year, 1918. The ore, which is mined by steam shovels and loaded in side-dump cars, passes through two crushing plants. These crushing plants were constructed to crush the ore required by a leaching plant of 5000 tons daily, capacity, during a crushing period of 16 hours. The primary plant reduces to less than 3 in. (76 mm.) and the secondary plant, to ¼ in. (6.35 mm.), which is sufficiently fine for satisfactory percolation of solution through the ore in the leaching tanks, and to give good extraction. The ore is then conveyed to the leaching tanks by a system of 28-in.. (71-cm.) belt conveyors. On the way to the leaching tanks, it passes through an automatic sampling plant, where a 1-per cent. sample is taken. From the primary crushing plant, the ore is conveyed by two 36-in. (91-cm.) belt conveyors to a 10,000-ton steel storage bin, with a reinforced-concrete flat bottom. The ore discharges from the bottom of this bin onto four 20-in. belt conveyors, which deliver it to the four units of crushers in the secondary crushing plant. There is no storage bin between the mine and the primary crushing plant. The ore breaks very coarse, is very hard, and contains a great many boulders, some as large as 4 ½ by 4 1/2 by 10 ft. (1.3 by 1.3 by 3 m.). Jams form in the bowl of the coarse crusher in the primary crushing plant, as a consequence, and are freed by means of an immense steel hook operated from a 40-ton electric traveling crane.

Jan 8, 1919

By David L. Holt

It is well-established that hydrostatic pressure distribution is hardly achieved during uniaxial compaction of powders. All the previous investigations1-4 give consistent results and this variation is attributed to the die-wall friction. The conclusions are based on measurements of the density of very small portions of the compact. Although the analysis of the density or the strain distribution in the compact is very helpful in obtaining information about the stress distribution within a powder compact, it does not describe the problem from a more fundamental point of view. The densification in metal powder compacts takes place chiefly by plastic deformation (ignoring particle rearrangement) at the points of contact of the powder particles. The onset of yielding and subsequent growth of the contact areas (for spherical powders) take place fixed by a constant stress equal to three times the yield stress in tension or compression,5-7 assuming little or no work hardening. Therefore, by deforming spherical powders in the die and measuring the contact areas on each particle, the load at each contact point can be determined. In the present investigation, this was done by hot-pressing uniform spheres of lead, K-Monel, and sapphire. The details of the experiment have been described elsewhere.' The spheres were studied for the size and the number of contact points on each particle using a specially designed goniometer. It was found that the deformed faces that were approximately normal to the direction of pressing were about 2.2 times larger than those parallel to the direction of pressing. Fig. 1 shows the typical deformed sphere. A detailed study showed that the mean value of the contact areas on each sphere was within 5 pct for all the spheres in the die (ignoring those touching the die walls and the top and bottom of the die).' The spheres touching the die walls and the top and bottom of the die were found to have larger contact areas (8 to 10 pct) which indicates higher pressures in these regions of the compact and thus higher compact densities in these regions. These results show that density distribution calculated from such an experiment will give results consistent with the previous investigators. It is concluded, therefore, that the pressure distribution in the die is better understood by studying contact areas on each particle. 'R. Kamm, M. A. Steinberg, and J. Wulff: Trans. TMS-AIME, 1947, vol. 171, p. 439. 'Pol Duwez and Leo Zwell: I. Metals, 1949, vol. 1, p. 137. 'G. C. Kucynski and I. Zaplatynskyj: Trans. TMS-AIIME, 1956, vol. 206, p. 215. 'R. P. Seelig and J. Wulff: Trans. TMS-AIME, 1946, vol. 166, p. 492. 'H. Hencky: Z. Angew. Math. Mech., 1923, vol. 3, p. 241. "J. Ishlinsky: I. Appl. Math. Mech. USSR, 1944, vol. 8, p. 233. 'D. Tabor: Proc. Roy. Soc. (London), Ser. A, 1948, vol. 192, p. 247. 'Ashok K. Kakar and A. C. D. Chaklader: 1. Appl. Phys., 1967, vol. 38, p. 3223. Superplasticity in 60Zn-40Al David L. Holt THE occurrence of superplasticity in Al-Zn alloys is of interest because of its possible industrial exploitation.' The eutectoid composition (78Zn-22A1) has been the most extensively studied;'-= neck resistant flow and high strain rate sensitivity of flow stress (characteristic of superplasticity) are associated with a micron-size grain conferred on the alloy by an homo-genization and quench.5'6 Compositions away from the eutectoid have received comparatively little attention, especially from the viewpoint of relating the structural

Jan 1, 1969

By R. E. Hoffman, R. A. Ward

The self-diffusion coefficient in high purity nickel has been measured over the temperature range 870' to 1248°C. The results are described by the relation D = 1.27 exp[—-66,800/RT 1cm2ec-1. The measured activation energy correlates satisfactorily with absolute melting point, heat of fusion, and heat of sublimation. KNOWING the rates of self-diffusion is important in the understanding of many metallurgical reactions. However, in spite of the rather widespread interest in nickel, both commercially and in fundamental investigations, no measurement of the self-diffusion in solid nickel has previously been re- ported." In connection with a program of measuring rates of diffusion in some nickel alloys, self-diffusion in pure nickel has been investigated over a rather wide temperature range by combining a sectioning technique and a surface counting technique.

Jan 1, 1957

By I. R. Kramer, P. D. Gorsuch, D. L. Newhouse

Although many methods have been suggested for the calculation of tensile strength and yield point from chemical composition, their usefulness has been limited to a particular cooling rate or section size. Further limitations have been imposed by failure to take into account many of the alloying elements that exert a considerable influence on the tensile strength or yield point. These systems, nevertheless, have filled an important need in many instances. The value of a system for the calculation of the tensile properties from the chemical composition and cooling rate is that it permits the prediction of the effect of alloying elements and heat-treatment on the mechanical properties, so that more efficient use of alloying elements may be made. Furthermore, it aids in the choice of steel for a given application aid tends to decrease the number of steels that otherwise would have to be tested. It is the purpose of this work to present a method of calculating tensile strength and yield point from the chemical composition and to suggest a method of correlating the tensile-strength and yield-point factors and cooling rate. Steelmakers have been interested for many years in the calculation of the tensile strength of hot-rolled steels. Quest and Washburn' summarize several of the attempts that have been made to devise formulas. They show the inadequacy of each of these formulas and present one of their own. It is apparent from their work that a simple additive equation of the type TS = A + BX + Cy + DZ + . . . , where A, B, C, D, etc. are experimentally determined constants and x, y, z, etc., are the percentages of alloying elements present in the steel, is not adequate to analyze fully the situation encountered in the calculation of tensile strength. For example, it was found that the difference between the calculated and observed values became progressively greater as the carbon and manganese contents were increased. Therefore, the effect of manganese was given as a function of the carbon content. Grossmann, in his work on the harden-ability of quenched steels, and Walter, in his method of calculation of tensile strength of normalized steels, present two cases in which multiplying factors were successfully used to express the combined effect of alloying elements. The factors in both cases were obtained from the fractional increase in hardenability or tensile strength with increase of alloy content. Yield point often is more important in design than tensile strength. For quenched and tempered steels a linear correlation exists between yield 2nd tensile strength.4 This is not true, however, for normalized

Jan 1, 1948