By G Hope, C Young, R. N. Gow

"The presence of enargite (Cu3AsS4) is problematic in gold processing as it is refractory, increasing cyanide and oxygen consumption, and enviromnentally hazardous. Selective leaching and treatment of the arsenic would prove advantageous to conventional gold leaching methods. The reactivity of enargite samples from Montana, US and Quiruvilca, Peru were studied under alkaline conditions, pH range of 8-13, using a cyclic voltammetry corrosion cell setup. Raman spectra of the surface were taken during and after cycling to compare surface species against theoretical predominance diagrams. Under slightly oxidizing conditions, covellite (CuS) peaks were found on the surface in a short matter of time, above - 200m V vs SHE for pH 9-13, suggesting arsenic leaching, but for longer conditioning times, elemental sulfur peaks were also found, which created a passivating surface layer. By operating above pH 12, under reducing conditions, ~-500mV vs SHE, arsenic can be leached as a thioarsenate (AsS4-xOx3-), without sulfur formation.IntroductionEnviromnental limitations on pyrometallurgical processing of arsenic has pushed the desire to process enargite-, Cu3AsS4, bearing concentrates towards a hydrometallurgical solution. Attempts to process can be broken down into two categories - the co-dissolution of arsenic and copper under acidic conditions or the selective leaching of arsenic under basic conditions. The selective leaching of arsenic would preferably leave behind a chalcocite, Cu2S, or covellite, CuS, phase that would be more amenable to conventional processing methods of the copper and gold industries. These methods employ bi- or poly-sulfides to leach arsenic as Assl· [1-4], hypochlorite leaching [5-7], ammoniacal leaching [8] or fine grinding to mechanically activate the enargite surface and increase normally slow reaction kinetics[9]. This study looked into the surface formations of an enargite electrode under alkaline conditions, in a pH range from 8-13, as it cycled from -1000 mV to 1000 mV vs SHE. The understanding of the formations and under what conditions they form will be helpful in further development of any of the aforementioned processes."

Jan 1, 2012

By E. A. Loria

High-quality sheet of electrowon molybdenum was attained by a sequence of procedure on pressed and arc-melted crystalline powders. The procedures included high-temperature, high-vacuum sintering treatments and the use of metal deoxidizers instead of carbon to improve the mechanical properties of the molybdenum sheet. Rolled sheet 60 mils thick was evaluated by tensile and bend tests, hardness measurements, microstructures, and recrystallization treatments. After stress relieving, yield strength ranged from 85,000 to 110,500 psi (0.2- percent offset) and ultimate strength ranged from 87,200 to 117,250 psi with 4.5- to 25-percent elongation observed for arc-melted sheet, and 5.0- to 23- percent elongation observed for powder metallurgy sheet. In room temperature bend tests the sheet yielded plastically, indicating that the ductile-brittle transition point was below room temperature. The diamond pyramid hardness (DPH) of the molybdenum sheet changed from 214 to 293 DPH for the stress-relieved condition to 177 to 185 DPH for the fully recrystallized condition. The brittleness of recrystallized molybdenum, reported by other investigators as characteristic of sheet prepared from commercial-grade hydrogen-reduced powders, was not in evidence. Recrystallized tensile specimens pulled at room temperature had an average elongation of 31 percent.

Jan 1, 1966

By J. O. Mack, J. B. Russell

IN recent years, solders containing 20 per cent tin with no bismuth or cadmium have been developed by a few companies, and personnel have been properly instructed in their use. In addition, since the tin shortage, a number of solders containing less than 10 per cent Sn, and some with no tin, are being used in special applications; however, a solder of this type has yet to be developed that is satisfactory for general use. [ ] The purpose of this investigation was to develop an alloy containing a maximum of 15 per cent tin, with no cadmium or bismuth, having solder properties equivalent to or better than those of substitute solders now specified containing i8 to 20 per cent tin (Table I), or even approaching the properties of the standard 40 to 60 tin-lead solder. The wartime restriction of bismuth and cadmium, elements that have beneficial effects on fluidity, solidification range and strength, makes it increasingly difficult to develop a general-purpose solder containing a maximum of 15 per cent tin. In the course of this investigation, 11 elements were used in various combinations with the basic 15-85 tin-lead alloy. These elements were antimony, silver, copper, indium, thallium, lithium, calcium, barium, potassium, sodium and arsenic. In all, 116 low-tin solders were investigated, with the idea of developing a solder that will give satisfactory working properties, specifically in regard to "wetting" of copper, brass and iron, solidification range, capillarity and shear strength of a soldered joint. The relative importance of these various properties plays an important role in the search for substitute solders, since it is almost impossible to retain all of the desired qualities of a high-tin solder and still make drastic changes in the alloy composition. Because of the expected uses of a general-purpose solder, it is necessary that it have properties, especially in regard to wettability, that will enable it to be used on the metals in common use. BASIC CONSIDERATIONS The maximum liquidus temperature of a solder is determined by the particular application involved and the temperature that can be obtained by the source of heat.

Jan 1, 1944

By I. L. Barker

ALTHOUGH valuable information has been pub-lished on the important problems of slag losses with which every copper metallurgist has to contend, a great deal of money is still being wasted in copper smelters all over the world, through metal being irretrievably lost in reverberatory slags. When smelting a relatively low-grade pyritic concentrate together with a proportion of direct-smelting oxi- dized ore, as is done in Oroya, slag volumes are of necessity high, and even a relatively clean slag, say of 0.5 pct Cu, means a loss of almost 4 pct of all the copper charged, or over $1,000,000 annually at present output and prices. While it is known that such losses can often be reduced by allowing the slag time to settle, with or without addition of a reducing agent such as coal or pyrite, the facilities for such treatment are not always available in a plant of old design working to capacity under severe space limitations. Nor is it easy under such conditions to run large scale tests which may endanger the smooth flow of production for considerable periods without yielding

Jan 1, 1958

Three separate and unconfined aquifers occur in the Hilton area, named relative to position in relation to ore horizons: Footwall Aquifer in the east; Ore-Zone Aquifer within the ore-bearing Urquhart Shales; and the Hangingwall Aquifer in the west.It is the on-going strategy it Hilton to drain the Ore-Zone Aquifer which occupies structurally- and sulphide-controlled leached zones in the steeply west dipping strata. The aquifer affects considerable ore reserves to 480 m below the surface. Dewatering began in 1976, and is essentially completed to 4 level (240 m below surface). Dewatering efforts are now based on 8 level (480 m below surface).

Jan 1, 1993

By Ryan Lindmark, Guoxing Gu, Zhenghe Xu, Jacob H. Masllyah

Induction time is often referred to the time required to form a stable three-phase contact between a gas bubble and a flat or droplet surface in a liquid medium. It can be used to quantify the attachment process in aflotation system. Various techniques have been developed to measure this important parameter. Due to its importance in flotation systems and other processes, significant advances in refining the induction time measurement techniques have recently been made. This paper summarizes these recent advances and describes a novel method developed to monitor bubble attachment to a pendant bitumen drop or bitumen-coated flat surface. This visualization-based method offers a higher sensitivity and accuracy than the previously developed apparatuses in the induction time measurement. As an example, the induction time for oxygen bubble-bitumen attachment was measured at a fixed bubble size as a function of temperature in two different aqueous solutions. The results showed that higher process temperature is favorable for oxygen bubble-bitumen attachment and hence bitumen flotation. Addition of calcium to the aqueous solution slightly decreased induction time.

Jan 1, 2005

By Raymond S. Weimer

OF the several characteristics of a coal that influence its suitability for use in a given piece of burning equipment, the clinkering and slagging characteristics of the ash of the coal are highly important. They determine the maximum rate at which the coal may be burned on a stoker or in pulverized form without difficulty from damage to metal parts, from erosion of refractory walls, or from stoppage of gas passages by accumulation on the tubes. They also determine the minimum rate at which a slag-tap furnace may be operated without difficulty in removal of the ash in fluid form. NEED FOR A BETTER CRITERION In common with other producers and users of coal, the Northern Illinois Coal Corporation has long used the available methods for the measurement of the clinkering characteristics of coal ash, chemical composition and fusion temperature of the ash, as criteria for the selection of coal that would suit the particular requirements of its customers. These two available criteria have greatly helped in the problem of selection but it is unnecessary to dwell upon the fact that they are not completely adequate for the purpose. The composition of the ash and its clinkering tendency vary widely over the company's mining area. In a certain period, some years ago, an unusual amount of severe clinkering of the ash of coal shipped made extremely acute the need for a better criterion of the clinkering that might be expected. It was also desirable that the criterion result from a reasonably rapid method, so that the clinkering characteristics of the coal would be known before shipment. Complaints on the severe clinkering of the ash came from only a fraction of the output of the mine but the occurrence of the clinkering seemed quite unpredictable. Attempts to relate the chemical composition of the ash and the fusion temperatures to the clinkering were unsuccessful. Coal from the area of the mine in which the fusion temperature of the ash was the lowest gave the least trouble from clinkering. Chemical analysis of the ash from that section giving the most trouble showed high contents of iron and low contents of silica, but frequently these were not greatly different from those of coals that gave little trouble from clinker. Aside from the clinkering difficulty, the coal was quite satisfactory. The ash content was normal and high rates of burning could be obtained, but again and again such severe clinkering would occur that the furnace would be shut down because of the accumulation of clinker. Examination of the clinker from the customers' plants showed that the clinkers that adhered to the grates and fouled the fuel beds were hard, flat, dense, and usually dark in color. Coal that was satisfactory gave clinkers that were softer, bulky rather than flat, of low density, and usually lighter in color.

Jan 1, 1944

By E. D. Gardner

The Bureau of nines, in cooperation with the mining companies of the Southwest, is conducting an investigating to ascertain the safest and most economical explosives to use in metal mines, and to ascertain the best methods of blasting under various conditions. A part of this investigation has been a study of drilling and blasting drift rounds in metal mines. This paper covers one phase of work on drift rounds and discusses the methods of loading the individual holes of the rounds. The blasting tests, on which this paper is based, were made at the Copper queen Branch of the Phelps Dodge Corporation at Bisbee, Arizona.

Jan 1, 1927

In 2006, a total of 280 metal mining operations reported employment to the Mine Safety and Health Administration (MSHA).1 Metal mines were the smallest mining commodity sector, comprising 1.9% of all mining operations. ? Gold mines comprised 46.8% (n=131) of all metal mining operations. Other common types of metal mines were copper ore (n=34; 12.1%), and iron ore (n=33; 11.8%). Nevada had the largest number of metal mines (n=53; 18.9%), followed by Alaska (n=31; 11.1%).

Sep 1, 2008

By M J. Saynor, W D. Erskine an, D R. Moliere

The Jabiluka uranium mine was constructed in the Ngarradj catchment, a right bank tributary of Magela Creek in the Northern Territory. The Jabiluka Mineral Lease is adjacent to Kakadu National Park, near an area listed as Wetlands of International Importance under the Ramsar Convention and recognised under the World Heritage Convention. In the late dry season of 1998 and prior to the 1998 - 1999 wet season, a stream-monitoring program was implemented in the Ngarradj catchment to collect baseline data on sediment transport within the catchment to assess and proactively manage associated impacts caused by mining at Jabiluka. Stream suspended mud concentration, stream discharge and rainfall data were collected for four wet seasons (1998 - 2002) giving an almost continuous data set. The stream system has high natural variability dependent on rainfall intensity and subsequent discharge and pre-wet season fire distribution and intensity. In general, mud concentration is elevated at the commencement of the wet season until about February. This is caused by first-flush removal of surface material detached during the dry season by agents such as bioturbation (including anthropogenic activity), wind erosion and surface desiccation. Water quality trigger values downstream of the mine were derived using upstream percentiles and the before-after-control-impact, paired site design. Both analyses showed no observable impact from mine construction in 1998 or during the study period. However, the impacts of dry season fires could be clearly detected. The data set provides good baseline information for future assessment at Jabiluka and demonstrates the need to view measured parameter values on a catchment-wide basis with knowledge of rainfall, discharge and fire distribution.

Jan 1, 2004

By A. B. Campbell

The Bureau of Mines is developing alloys using ion implantation as an alternative to bulk alloys that consume large quantities of strategic materials such as chromium and nickel. These alloys are formed at the outer layer of relatively common materials. To more fully understand the corrosion characteristics and physical properties of this outer layer, it was necessary to deter-mine the alloy concentration as a function of depth into the substrate material. Also, since many of the ion-implanted alloys would be utilized at elevated temperatures, it was necessary to determine the diffusion behavior of the implanted element. Proton-induced X-ray emission and inert gas ion sputtering have been utilized to generate composition depth profiles for Fe-Cr, Fe-Ni, and Fe-AI ion implanted alloys fabricated by implanting 25-kev Cr+, Ni+, or AI+ into iron substrates. The data were fitted (utilizing a computer program) with symmetrical Gaussian profiles yielding values for the range and range straggle of the ions. These parameters were then compared with those calculated from theory. Changes in the profiles due to annealing were investigated and values for the diffusion coefficient were obtained assuming diffusion according to Fick's Law. For the Cr+ and Ni+ implantation, the profiles as-implanted agree reason-ably well with theory and exhibit ?norrmal" diffusion characteristics at 500° C. For the Al+ implantation, the profile as-implanted is much broader than predicted and exhibits substantial enhanced diffusion at temperatures up to 500° C.

Jan 1, 1979

The ever increasing demand for energy and the progressive depletion of crude oil resources, have renewed interest in oil shale as an alternative fuel resource. Weathered oil shale samples were assembled from El-Nakheil phosphate mine in Quseir area, Eastern desert, Egypt. The oil shale samples were prepared and analyzed by XRD (X-ray diffraction), XRF (X-ray fluorescence spectrometry), and optical microscopic techniques. Rock-Eval pyrolysis and total organic carbon were used to study shale hydrocarbon potential. A leaching procedure using inorganic and organic acids was used to selectively dissolve the oil shale associated ash forming minerals. XRD results showed that calcite is the dominant carbonate mineral, whereas primary silicate minerals are quartz and montmorillonite. SEM (Scanning Electron Microscopy) observations indicated that the organic matter is dispersed throughout the rock matrix. The acid soluble fraction upon leaching was determined to be 37.59 and 42.74 wt% by using 5% HCl and 10% HCl, respectively. The TOC was increased from 20.78 to 29.88 and 34.09 wt% by using 5% HCl and 10% HCl, respectively. Keywords: el nakheil oil shale, characterization, xrd, xrf, sem, elemental analysis, proximate analysis, ultimate analysis, thin section, rock eval pyrolysis, acid leaching

Sep 1, 2012

By P. G. Pigott

This investigation by the Bureau of Mines demonstrated that building bricks can be produced by the steam-curing process from various types of industrial mineral wastes. Wastes, utilized to produce bricks, consisted of copper mill tailings, roofing granule fines, asbestos fines, and zinc mill tailings. Bonding of the wastes with either Ca(OH)2 or portland cement resulted in building bricks that met ASTM specification C73-67 for grade SW and MW bricks when evaluated in accordance with ASTM designation C67-66 on sampling and testing of brick. An economic evaluation of the process indicates the total operating cost per 1,000 bricks is about $36.

Jan 1, 1974

By Max W. Ball

An intelligent discussion of the oil situation and its needs, whether from the standpoint of the prospector, the operator, the engineer, or the public administrative officer, must be founded upon a knowledge of the law under which oil lands are obtained. A consideration of new legislation must be prefaced by an understanding of the present law and its results. This paper undertakes to present no new remedy for the ills of the present situation, no new solution of the problems the oil business is facing. It attempts merely to summarize the present law, its provisions, its origin, its development, and its effects. The discussion does not pretend to be exhaustive from a legal standpoint. It aims to avoid legal intricacies which tend to. confuse rather than clarify. It seeks but to present the essentials of the existing situation. The title to government lands known to contain valuable deposits of petroleum may be acquired only under the terms of the placer law as embodied in Section 2329 et seq. of the Revised Statutes. As a preliminary to considering the desirability of this situation it is profitable to examine into its origin. Origin of the Law Congress has left no room for doubt as to the legal applicability of the placer law to oil lands. The Act of Feb.11, 1897(29 Stat., 526), provides: "that any person authorized to enter lands under the mining laws of the United States may enter and obtain patent to land containing petroleum or other mineral oils, and chiefly valuable therefor, under the provisions of the laws relating to placer mineral claims.' . The immediate cause for the passage of this Act was stated in a brief report in the, House of Representatives (there was no debate in the Senate) to be a decision of the Department rendered Aug. 27, 1896 (Union Oil Co., 23 L. D., 223), directing the cancellation of an oil placer entry on the ground that land containing petroleum cannot be located and entered as a placer mine. The report of the Public Lands Committee of the House contains the following interesting statements Congressional Record, vol. xxix, p. 1409):

Jan 1, 1915

By Carrasco .. P. J. A., R. Parada, I. Saavedra, F. Parada, R. Parra, E. Balladares

In most of the smelters, the management of flue dust has a double objective: the control of minor elements in the anodes and the management of volatiles compounds that can cause contamination due to fugitive gas emissions. This is a special concern when high content of Va elements (As, Sb & Bi) are present in concentrates. We present the results of the experimental study to prove the principle of a novel process that recovers, via volatilization, the As, Sb and Bi in the flue dust as gaseous sulfides, due to a previous sulfidization. In the case of as control any further classical treatment for its stabilization is possible from the gas. The clean calcine can be returned to the smelter avoiding any concentration of these minor elements in the circuit. This process is now tested at pilot scale and shows better indices on carbon footprint than the classical hydrometallurgical process for flue dust.

Jan 1, 2011

By V. Lepetic, C. C. Harris

A systematic program of investigations covering all aspects of cell hydrodynamics,1-3 flotation kinetics,4,5 surface chemistry and their interactions has as a major objective the elucidation of the flotation micromechanism and the principles of cell design and scale-up.6 Purely from the scale-up point of view, a family of reactors should enable different throughputs of the same material to be similarly treated or, at least, to be treated in a manner which differs beween reactors in a predictable way. Thus, for the same material and residence time, the recovery and grade from differently sized cells of the same family should, ideally, be similar or, at least, be related to each other in a known way. It is well known, however, that different-sized cells do not always achieve similar results, and it is necessary to enquire into the reasons for these differences. For example, it may be that the relative dimensions of different-sized cells result in hydrodynamic conditions which preclude similarity; if so, different scaling may improve the situation. The major question concerns identifying the dynamic conditions and their associated geometric requirements which govern the flotation process, and the criteria which are necessary for their fulfillment. It is to answer such questions that the program referred to earlier was instituted. In connection with this program and in order to examine data concerning the physical features and operating conditions of existing flotation cells, the following survey was carried out. This work represents an approach which is complementary to experimental investigations, for it recognizes that the design of existing cells may embody several of the principles being sought. If data for enough cells, especially families of cells, are examined, some broad requirements common to all cells may emerge.

Jan 9, 1966

By G. E. Pellissier, C. W. Mason

Tin has long been cited as offering a classic example of polymorphism, second in repute only to the allotropy of sulphul.. The notorious "tin disease," which Cohenl has studied so exhaustively in terms of the enantiotropic transformation of tetragonal white P tin to cubic gray a tin, has apparently encouraged the expectation that one or more additional polymorphic modifications might exist. The search for confirnmntion of this idea has, as might be anticipated, led to the accumulation of a body of miscellaneous evidence, much of which would probably never have been sought, or taken seriously even by its discoverers, but fur previous assumptions. The ball apparently was started rolling iii 1880 by Trechmann,2 who reported a new modification of tin (7 tin), which was brittle and found in "hard head," a highly arsenical, slaggy material produced in a certain stage of tin smelting. A mixture of two kinds of crystals was obtained from a Cornish tin furnace, and those thought to be 7 tin were studied crystallographically. The results indicated that these crystals were rhombic and of different density from the tetragonal tin prepared electrolytically by Miller. Their analysis was given as 98.7 per cent Sn, 1.3 per cent Fe, and traces of As, Sb, Bi and S. In 1881 von Foullon4 obtained similar crystals from a Bohemian tin furnace. Headden5 examined crystals similar to those of Trechmann and von Foullon and reported them to be monoclinic, but of analysis corresponding to stannous sulphide. Later, Stevanovic,~ by goniometric measurements, proved that these crystals of SnS were really rhombic. Groth7 pictures and describes both "rhombic tin" (Fig. 9, vol. 1) ant1 stannous sulphide (Fig. 84, vol. 1); their faces and angles correspond within the accuracy of measurement. Spencers in 1921 examined the above evidence critically; lie lound similar crystals from Cornish tin furnaces, proved them to be SnS, and even was able to analyze some of Trechmann's original specimens, finding high sulphur content. (Apparently Trechmann's analysis had been based on :L second lot of crystals, not described crystallographically.)

Jan 1, 1939

By G. E. Pellissier, C. W. Mason

Tin has long been cited as offering a classic example of polymorphism, second in repute only to the allotropy of sulphul.. The notorious "tin disease," which Cohenl has studied so exhaustively in terms of the enantiotropic transformation of tetragonal white P tin to cubic gray a tin, has apparently encouraged the expectation that one or more additional polymorphic modifications might exist. The search for confirnmntion of this idea has, as might be anticipated, led to the accumulation of a body of miscellaneous evidence, much of which would probably never have been sought, or taken seriously even by its discoverers, but fur previous assumptions. The ball apparently was started rolling iii 1880 by Trechmann,2 who reported a new modification of tin (7 tin), which was brittle and found in "hard head," a highly arsenical, slaggy material produced in a certain stage of tin smelting. A mixture of two kinds of crystals was obtained from a Cornish tin furnace, and those thought to be 7 tin were studied crystallographically. The results indicated that these crystals were rhombic and of different density from the tetragonal tin prepared electrolytically by Miller. Their analysis was given as 98.7 per cent Sn, 1.3 per cent Fe, and traces of As, Sb, Bi and S. In 1881 von Foullon4 obtained similar crystals from a Bohemian tin furnace. Headden5 examined crystals similar to those of Trechmann and von Foullon and reported them to be monoclinic, but of analysis corresponding to stannous sulphide. Later, Stevanovic,~ by goniometric measurements, proved that these crystals of SnS were really rhombic. Groth7 pictures and describes both "rhombic tin" (Fig. 9, vol. 1) ant1 stannous sulphide (Fig. 84, vol. 1); their faces and angles correspond within the accuracy of measurement. Spencers in 1921 examined the above evidence critically; lie lound similar crystals from Cornish tin furnaces, proved them to be SnS, and even was able to analyze some of Trechmann's original specimens, finding high sulphur content. (Apparently Trechmann's analysis had been based on :L second lot of crystals, not described crystallographically.)

Jan 1, 1939

Rock mass classification systems are extensively used in rock engineering design work, and mine design is no exception. Among the systems most widely used for mining-related design work are the NGI 0-system (Barton et al., 1974), the RMR system (Bieniawski, 1976), the MRMR system (Laubscher and Taylor, 1976) and, more recently, the GSI system (Hoek et al., 1998). Classifying the rock mass is widely seen as being the fieldwork required to characterize the rock mass and enable the application of empirical design methods associated with the different classification systems. This paper argues that it is fundamentally important to recognize the distinction between rock mass characterization and rock mass classification. These two processes should, in most cases, be separated from each other. Rock mass characterization should be used to determine the intrinsic properties of the rock mass independently of the application; i.e. independent from the infrastructure to be designed, the size, shape, and orientation of the excavation(s) or pillar(s), etc. Rock mass characterization should also be compatible with most classification systems and empirical design methods to be used. Rock mass characterization is the background fieldwork required to perform rock mass classification and/or engineering design work. Rock mass classification is the subsequent step to the characterization, and an integral part of the design process. Parameters that vary according to the design, such as the relative orientation of geological structures compared to the opening or the mine-induced stresses, should be calculated as part of the rock mass classification and design process, rather than during the rock mass characterization process. The failure to distinguish between rock mass characterization and rock mass classification can lead to major design errors and poor results.

Jan 1, 2012

The properties required for a com-pound to form useful thermoelectric materials are described. Uranium compounds which might have these properties are reviewed. Several of these compounds have been prepared and fabricated into compacts. The apparatus used for hot pressing, and for the measurement of thermoelectric power, electrical conductivity and thermal conductivity, is described. Detailed attention has been given to the properties of the nitrides. Preliminary studies on a number of other uranium compounds are reported. The figures of merit of the best materials so far examined are one-tenth of those necessary for a useful thermo-electric material. THE efficiency of thermoelectric materials for power generation and cooling is determined by their figure of merit, Z = a2 a/K, where a, a and K are thermoelectric power, electrical conductivity and thermal conductivity, respectively. It is well known that the largest values of Z are achieved with semiconductors (1). High mobility of charge carriers is necessary for simultaneously high thermoelectric power and electrical conductivity.The properties required for a com-pound to form useful thermoelectric materials are described. Uranium compounds which might have these properties are reviewed. Several of these compounds have been prepared and fabricated into compacts. The apparatus used for hot pressing, and for the measurement of thermoelectric power, electrical conductivity and thermal conductivity, is described. Detailed attention has been given to the properties of the nitrides. Preliminary studies on a number of other uranium compounds are reported. The figures of merit of the best materials so far examined are one-tenth of those necessary for a useful thermo-electric material. THE efficiency of thermoelectric materials for power generation and cooling is determined by their figure of merit, Z = a2 a/K, where a, a and K are thermoelectric power, electrical conductivity and thermal conductivity, respectively. It is well known that the largest values of Z are achieved with semiconductors (1). High mobility of charge carriers is necessary for simultaneously high thermoelectric power and electrical conductivity.

Jan 1, 1963