By Ryosuke Matsuoka

Keywords: Tantalum capacitor, Scrap, Recovery, Titanium, Chlorination A recycling process for tantalum from capacitor scraps using an oxidation process followed by mechanical separation and chemical treatment was investigated. This study demonstrates that sintered tantalum electrodes inside the capacitor scraps can be mechanically collected after the oxidation of the scraps in air, and high-purity tantalum oxide powder (Ta2O5) was efficiently recovered after chemical treatment. By reducing the Ta2O5 obtained through magnesiothermic reduction, tantalum powder with 99 mass-% purity was obtained. Using the chlorination for tantalum recovery was also investigated, and the tantalum or tantalum compounds were reacted with chloride wastes such as FeClx. It was found that tantalum was effectively separated and purified when tantalum powder is reacted with FeClx at 1100 K under an argon atmosphere. This recycling process utilizing chloride scrap has now been extended to other reactive metals such as titanium.

Jan 1, 2004

By Mingchun Lu, Zhe Wang, Mingming Cao, Xiangdong Xing, Shan Ren, Jianliang Zhang, Zhengjian Liu

"The effect of reduction temperature on the vanadium titano-magnetite carbon composite pellets was investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM), and the discussion has put emphasis upon the enhanced reduction mechanism of additives containing CaF2 and NaF in this paper. The results showed that the reduction temperature of 1350°C was needed for the generation, mergence and growing up of metallic iron as well as monomer dissociation between metallic iron particles and slag phase in the vanadium titano-magnetite metallization pellets. The iron compound was completely reduced into metal iron, and Fe2Ti04 was mainly transformed into metal iron, (Fe,Mg)Ti205 and FeTi03 at 1350°C. The maximum metallization ratio was only 88.5% at 13500 for 30 min without any additive. However, with the addition of 3.0% CaF2 or NaF, the metallization degree of pellets could reach up to 94.8% and 92.5%, respectively.IntroductionVanadium titano-magnetite which is mainly distributed in the area of Panxi, Chengde and Maanshan in China is a kind of complex iron ore which contains various valuable metal elements such as iron, vanadium, titanium, etc. Among the above areas, Panzhihua (Sichuan Province in China) area possesses the largest deposits of vanadium titano-magnetite and the future reserves are more than 100x108t, and the reserves of Ti existing as Ti02 reach to 8.7x108t which occupy over 91% of the whole nation and ranked No.1 in the world[1]. Lots of researches on the comprehensive utilization of vanadium titano-magnetite have been conducted in the world. And many technological processes have been applied successfully in industrial production. Among these processes, the process of rotary kiln-electric furnace is employed to recover iron and vanadium in South-Africa, while the process of blast furnace-rotary furnace is widely used in Russia and China. Besides, many researchers have made efforts on employing new direct reduction process to realize the effective comprehensive utilization of vanadium titano-magnetite[2-4]. However, the direct reduction process is only researched in laboratory and it has not been used in industry."

Jan 1, 2013

By Nam-Il Um

Bottom ash contains several ferrous materials (ferrous metals, Fe3O4, Fe2O3, FeS, etc.). In particular, ferrous metals contain heavy metal because Ni and Cr are chemically attracted to iron. Likewise, Cu is used to coat Ni and Cr metals as polish or to prevent corrosion. In this study, an Fe3O4-Fe2O3 double layer (similar to pure Fe) was found to have been formed in ferrous metal during air-annealing in an incinerator (1000°C). A strong thermal shock such as one that occurs during the water-cooling of bottom ash results in the breakdown of this oxidation layer, facilitating the degradation of ferrous metals and formation of corrosion products. Therefore, Fe-ion (heavy metal) oxides may be formed on ferrous metals and may be separated from bottom ash via magnetic separation. This study sought to investigate the separation ratio of heavy metals as magnetic separation and mineralogical formation of Fe-ion (heavy metal).

Jan 1, 2006

By Caisa Samuelsson, Sina Mostaghel, Theo Lehner

"Rönnskär smelter of Boliden Mineral AB, Sweden, is well known for recycling of base and precious metals. Slag from the electrical furnace is processed at the fuming plant to produce zinc clinker. The granulated slag is a by-product used as e.g. construction material. In this paper, influences of Al2O3 on mineralogy of the slag, which can affect its chemical and physical properties, are investigated. Different mixtures of Al2O3/fumed slag were prepared. Re-melting was carried out in a Thermo-Gravimetry (TG) furnace with an inert atmosphere. Scanning electron microscopy (SEM) and X-ray diffractometer (XRD) were then applied for the analyses. Investigations depict that addition of alumina to slag, results in an increase in the number of spinels and a transformation from iron rich to aluminum rich spinels. Anorthite (CaAl2Si2O8) will also be formed.IntroductionRönnskär smelter of Boliden Mineral AB is located in north of Sweden; the main products of this smelter are: Copper, Zinc clinker, Lead, Gold, and Silver, while sulphuric acid, liquid sulphuric dioxide, and Iron sand are some of the by-products. Reducing the energy consumption and decreasing the usage of finite natural resources are becoming more and more important for the Rönnskär smelter; this result in use of different recycling and scrap materials. Metal residues, from brass foundries, steel mills, and electronic scrap are recycled at Rönnskär smelter [1]. Most of the electronic scraps contain mixtures of various metals together with plastics and ceramics, which can affect the composition and properties of the slag considerably [2]. At the same time, treatment of slag and controlling its composition and properties are of much interest for Base Metals producers from different aspects. Composition of slag influences the physical properties such as: 1) Liquidus temperature [3-4] 2) Viscosity, which controls separation of valuable metals, especially copper by gravity separation [2] and also heat and mass transfer [5] 3) Electrical conductivity [6]."

Jan 1, 2008

By Alexey Lozhko

The technical-and-economic furnace exploitation indices are considerably influenced by the system of heat utilization. In the situation of total output decrease works are forced to exploit furnaces at the partial loading, sometimes even at the idle running for the sake of steam production. The furnace exploitation in this regeme is known to cause the increase of the heat portion, taken away together with waste flue gases. The losses can be partially compensated at the expense of heat exchange efficiency development in the recuperator or heat-exchanger. One of the well-known methods, characterised by high efficiency and low expenditures is the intencification of the heat exchange process by the means of pulsation method.

Jan 1, 2006

By Jesús Contreras

Within its programme for continuous improvement and cultural change, Atlantic Copper has installed the Six Sigma methodology as a basic tool for the improvement of management techniques in all its production centres. Following an implementation period, the methodology is widely used for analysis and improvement, not only in the fields of production and maintenance, but also in other areas of the business such as supplies or energy management. The present paper describes, phase-by-phase, the project that was developed to improve the quality of converter slag through the application of Six Sigma techniques, from the initial set up to the final results obtained.

Jan 1, 2005

By Pekka Parvinen, Saija Luukkanen, Pentti Pirkonen, Väinö Hintikka, Hannu Sekki

In the study was developed a new method for the treatment soils contaminated by polychlorinated dibenzodioxin and dibenzofuran. The method is based on attrition of soil so that the contaminants absorbed on the particle surfaces are liberated with the fine fraction formed in the attrition process. Same the attrition process produces active surface which can absorb the free contaminants. Before starting the remediation process must be decided the limit value under which the residual concentration must lie. Then in the laboratory is performed an experiment in the base of which is determined the grain size level; material under which much be removed together with the contaminant. In the real sample has been found that after the attrition the limit value 0.5 ng/g (I-TEQ) is obtained when the fine under 0.1mm fraction (20% of the original soils amount) is removed together with the contaminants 96% (original level 10 ng/g; 100%).

Jan 1, 2008

By Andreas Stieben, Pierre Lutomski, Wolfgang Bleck, Martin Fischer

"For steel investigation and development, exact knowledge about the microstructural state is required. The information gained from 2D images often can't properly reflect the real 3D microstructural properties. In order to gain reliable information for meaningful models, simulations and correlations, it is necessary to accompany standard metallography with 3D information, which, unfortunately, is very difficult to access. This article presents a procedure for serial sectioning in combination with light optical microscopy. Only standard metallographic tools are employed in combination with image manipulation freeware. 3D microstructural data were extracted from three multiphase steel grades and in two cases virtual 3D-models of microstructural phases were generated.Three Dimensions Of MicrostructuresSince the invention of steel, craftsmen, inventers and engineers tried to improve its properties and tailor them to the requirements of new developments. For systematic development and enhancement of steels, the capability to investigate its inner structure is highly important, because it represents the linchpin between material production and properties. By having an in-depth understanding how production conditions form the microstructure and also how the microstructural state determines the material properties, steel design can be drastically improved. With this knowledge, microstructures can be designed to provide target material properties and process conditions can be identified that form these structures. Due to the key role of microstructure, the capability to gain accurate information about it is indispensable. It is the task of metallography to access and extract descriptive quantitative microstructural data like fractions, sizes, shapes and distributions of the different constituents. The most commonly used investigation tool in metallography is the light optical microscope (LOM). Besides this tool, additional high resolution techniques like Scanning Electron Microscopy (SEM) or Transmission Electron Microscopy (TEM) have become increasingly important. With these and other available methods, extensive information on the microstructural state of a material can be gained. Unfortunately, most metallographic methods have a major loss of information systematically built in. Analyses of microstructures are usually performed on surfaces, i.e. on 2D areas that emerge by cutting through the 3D material structure. This means, a complete dimension of information is not taken into account. How serious this reduction of information is and how it can affect interpretation of structures is exemplarily demonstrated in figure 1, which displays the planar structure emerging from a random cut through a simple 3D structure. It is very difficult to deduce or even imagine the original spatial structure from which this projection emerged and it is impossible to reconstruct it with absolute certainty without further information. The image has emerged from a random cut through a 3D structure of stacked cubes that is displayed in figure 2. The area shown in figure I is outlined. Although artificially constructed, this example demonstrates how distorted and misleading the view on structures can become by ignoring a spatial dimension."

Jan 1, 2012

By Esher Hsu

In Taiwan, around 8,000 tons of batteries are consumed per year but only 17% of which were collected and transported to oversea for recovery. The dumping used batteries have become a potential environment problem. How to increase the collection efficiency of used batteries is an important issue for EPA in Taiwan. Besides, some treatment plants are on process to get permission for recovering used batteries. The objective of this study is to estimate the recycling cost of spent consumer battery and explore the feasibility of recovering used consumer batteries in Taiwan based upon the principle of cost-efficiency. The recycling cost including collection cost and recovery is estimated based on a survey. Results would provide some suggestions to Taiwan EPA regarding feasibility of recovering used batteries in Taiwan.

Jan 1, 2006

By Dong Liang, Honggang Zhong, Zhenxing Yin, Qijie Zhai

"2507 super duplex stainless steel (SDSS) has been widely applied in a marine environment, attributing to its excellent pitting corrosion resistance and mechanical properties which are particularly determined by the nitrogen precipitation behaviors and volume fraction of ferrite. In this paper, various cooling rates were obtained by applying four different moulds with the common gating system. By which the influence of cooling rates on nitrogen precipitation behaviors and the ferrite fraction in cast 2507 SDSS was comparatively investigated. The results showed that nitrogen porosity could easily precipitate in cast 2507 SDSS under standard atmospheric pressure. The number of nitrogen holes increased with decreasing the cooling rates, and the holes mainly distributed in three zones, i.e. the interface between the horizontal and vertical columnar grains, top vertical columnar grains and the final solidification region. Additionally, higher ferrite fraction was obtained with lower cooling rates.IntroductionDuplex stainless steels (DSS) have a dual-phase microstructure consisting of ferrite (d) and aus-tenite (?). Due to the combined advantageous properties of d and ? phase, their application rapid-ly increased in industry [1, 2]. Super duplex Stainless Steel (SDSS) is the third generation of du-plex stainless steels, of which the alloy elements Cr, Ni and N content are higher than the stand-ard 2205 DSS. Because it has high contents of alloy elements, the SDSS has better mechanical properties, and its pitting resistance equivalent number (PREN) reached a point 43. Hence SDSS has been used in petroleum chemical industry, the marine equipment and harsh corrosion environments [3]. SDSS contains ferrite stabilizing elements, such as Cr, Mo and Si, and austenite stabilizing elements like Ni, Mn and N [4]. Many researchers have studied the effects of these elements on the stabilization of d and ? phase and the ratio of the two phases. High nitrogen con-tent is another prominent feature of SDSS. Nitrogen addition to SDSS is very effective for improving its mechanical properties [5] and corrosion resistance [6], such as pitting resistance in NOx environment. To increase the nitrogen content in steels, a lot of work had been done. N. Nakamura and S. Takaki [7] examined the behavior of nitrogen absorption in Fe-23Cr alloy powder by sintering in nitrogen gas atmosphere, they found nitrogen content easily up to 1.0 wt. %. Using devised NH3 gas injection system, W. Park et al. [8] successfully produced austenitic Fe–23.5Cr alloys containing over 3 wt. % of nitrogen. Further-more, W.P. Tong et al. [9] stated that nitrogen percent was extraordinary high (about 10 wt. %) in pure iron plate. However, the above methods are difficult to be applied to large-scale industrial production."

Jan 1, 2012

By George P. Demopoulos

In this paper the production and stability of crystalline scorodite (FeAsO4·2H2O) is discussed both on the basis of previously published work as well as recent work performed in our laboratory. The production of scorodite, especially from arsenic-rich and iron-deficient sulphate solutions offers a number of operational advantages such as high arsenic content, stoichiometriciron demand, and excellent dewatering characteristics. In addition to hydrothermal production of scorodite the work done over the last 10 years in our laboratory has determined that it is feasible to produce scorodite by step-wise lime neutralization at 90°C. The atmospheric scorodite possesses the same structural and solubility characteristics with the hydrothermally produced scorodite. Long term equilibration tests (up to 66 weeks) in the pH range 5 to 9 and temperatures from 22 °C to 75 °C revealed scorodite to undergo slow incongruent dissolutionyielding a highly metastable nano-sized 2-line ferrihydrite phase. The equilibrium arsenic concentration with this phase was 0.35, 0.96 and 5.87 mg/L at pH 5, 6, and 7 respectively at 22°C. In the presence of gypsum slightly lower concentrations were measured, this being more pronounced at pH>7. It was tentatively deduced that a Fe-Ca-AsO4 association (in the form of a phase resembling the mineral yukonite) contributes to the lowering of As concentration. Finally thermodynamic calculations determined that scorodite is stable in the presence of ferrihydriteunder oxic conditions up to pH 6.75 at 22 °C or higher pH at lower temperature and gypsum-saturated solutions. Keywords: Scorodite, Crystallization, Arsenic, Solubility, Stability, Precipitation, Disposal, Extraction, Processing, Metals, and Environment.

Jan 1, 2005

By T. V. Jayaraman, D. Das, B. Mallesham, A. R. James

The PNN-PZT xPb(Ni0.3Nb0.67)03-(1-x)Pb(Zr0.31 Ti0 69)03 (0.2=x=0.6) based relaxor-ferroelectric material was synthesized by colurnbite precursor (NiNb206) method via conventional solid state reaction. Homogeneous mixture of required oxides and precursor was calcined at 850°C for 4 hrs to obtain phase pure perovskite. Pellets of PNN-PZT ceramics were sintered at 1100oC for 4 hrs. Phase pure perovskite structure was confirmed by the X-ray diffraction analysis. From the X-ray diffraction analysis it is also confirmed that there is a structural transformation from the rhombohedral to tetragonal with increase in PZT content and existence of morphotrophic phase boundary (MPB) at x = 0.5 composition. The morphology and microstructure of the sintered pellets were observed using the scanning electron microscope. P-E loop measurement shows the high remnant polarization (19.12 µC/cm2) and low coercive field (6.89 kV/cm) at MPB compared to all other compositions. The electromechanical planar coupling coefficient (kp) was measured through the resonance and anti-resonance method using the LCR meter. The piezoelectric strain coefficient (d33) measured directly using the d33-meter. At x = 0.5 composition the highest value of d33 = 398 pC/N is obtained.

Jan 1, 2012

The purpose of this study was to investigate the immobilization as a host for metallic pollutants (Cr, Cu, Pb, and Zn) by ettringite phase. Ettringite phase is produced through hydration reaction of calcium aluminate with gypsum. From the XRD patterns, it is known that the distance between spaces in 010 planes in ettringite crystal increase with an increase of ionic radius of heavy metal except Pb; no big difference is shown. For this reason, the d-value of 010 planes in ettringite crystal increased with the substitution of Cr, Cu and Zn having a big Al ironic radius. But in case of Pb, because the substitution occurred at calcium site, it does not influence to increase d-value of 010 planes.

Jan 1, 2006

By Tiebao Yang

In high pressure die casting processes, a die plays a critical role in removing heat from the molten metal during the cavity filling and solidification stages. Proper control of die temperature is essential for producing superior quality components and yielding high production rates. This paper proposes a local temperature control scheme for die thermal management based on a computerized intelligent real-time monitoring and control system (IRMCS). In this scheme, cooling water lines are controlled by a pump and solenoid valves. A controller is designed according to the law of die temperature fluctuations. The results obtained from the experiments carried out on a laboratory die casting process simulator indicate that the controller can limit the local die insert temperatures in a given band. Hence, the desired thermal pattern of the die insert becomes achievable.

Jan 1, 2006

By Wang Zhi

High-Mg-content concentrates are usually treated in Jinchuan flash smelting Furnace. Because the viscosities of high-Mg-content slag is very high, the operation of flash smelting becomes very difficult. To solve this problem, the viscosities of the semi-synthesized FeO-MgO-Si02 slag of different compositions were measured. The results showed that when in the slag the weight percentage of MgO [m(Mgo)] is 6-10%, the ratio of the weight percentage of iron to that of Si02, m(Fe)/m(SiO2) is 1.1-1.4 and the temperatures are within 1473?1773K, the slag viscosities increased with the increase of m(Mgo) and m(Fe)/m(sio,). When m(Mgo)<6%, the smelting temperature should be controlled at I 300°C in order to to keep the smooth operation. When m(Mgo» 10%, the temperature should be kept above 1633K. When the content of MgO is higher, a lower viscosity slag ean be produced by decreasing the ratio of m(Fe)/m(sio,). The appropriate ratio of m(Fe)/m(sio,) for Jinchuan flash smelting furnace is about 1.2.

Jan 1, 2003

By Jinliang Zhang, Jian Pan, Deqing Zhu

"Limestone and burnt magnesite were added to vary MgO content and basicity (CaO/SiO2 ratio) of pellets for investigating their influences on the properties of specularite pellets. At fixed MgO content, the addition of limestone does not affect on the properties of green balls significantly. The addition of burnt magnesite has obvious influence on the quality of green balls, especially on the thermal shock temperature. Without burnt magnesite, the thermal shock temperatures are about 400°C, and, the thermal shock temperature increases to 600~630°C by adding burnt magnesite. For preheated pellets, when the burnt magnesite is added, the compressive strength will be decreased. For roasted pellets without burnt magnesite, the calcium additives can form binding phase of calcium-ferrite, and suitable liquid phase will improve recrystallization of hematite, but excessive liquid will destroy the structure of pellets, so the compressive strength of pellet increases firstly and then decreases. When adding burnt magnesite, the compressive strength will increase as the basicity increases. When the basicity is more than 0.2, the compressive strength of the pellets various MgO content and basicity is above 2500N/pellet and then MgO-bearing fluxes can be added to prepare pellets with good high temperature properties.IntroductionWith the rapid development of the steel industry in China, oxidized pellets, possessing good mechanical and metallurgical properties, are becoming indispensable burdens for blast furnace ironmaking [1-3]. However, this has resulted in the shortage of domestic iron concentrates, so many Chinese steel plants begin to use imported hematite concentrate to prepare pellets. Compared with magnetite pellets, the hematite pellets require high roasting temperature and narrow roasting temperature range (1300–1350°C) and possess low compressive strength [4,5].1"

Jan 1, 2012

By Hideki Yamamoto, Junji Shibata

"The chemical reactions of fluoride and chloride gases with metal chloride or metal oxide are utilized as an effective treatment for harmless disposal. These chemical reactions can be adopted in the temperature range of 80°C~400°C, which is lower than that in the combustion treatment (800°C). Reaction products are metal fluoride or metal chloride which are a harmless and a valuable chemical material as one of new resources. This paper, concerns with a new harmless disposal treatment of toxic global warming gases.IntroductionNew technology to make fluoride and chloride gases such as NF3, CF4, SF6 BF3, Cl2 and BCl3 harmless has been developed and a new concept on the removing toxic gas to be used in the advanced process of materials has been established. The fluoride gases ~re toxic and special type of gases to be used in the process of manufacturing semiconductors and their specific applications include the dry etching of semiconductors, cleaning of CVD systems, an oxidation agent for rocket fuel etc. Especially, NF3 is also attracting an attention as a high-energy source for chemical laser systems. As a fluoride gas like NF3 is, however; toxic and highly stable chemically, if discharged into the atmosphere, it is liable to cause far-reaching adverse influences on global warming in the same manner as carbon dioxide gas and feron gas.Up till now, the combustion treatment method has been adopted for the disposal of the gas, and when treating the gas by high-temperature combustion (800""C), the generation of nitrogen oxides (NOx), sulfur oxides (SOx) and hydrogen fluoride (HF) have been confirmed: These chemical substances are not only linked with an intense c0rrosion of the combustion systems but also create the generation of atmospheric pollution and acid rains, and therefore, constitute a serious social issue."

Jan 1, 2000

By G. G. Krishna Murthy

Several experiments were carried out to simulate the bath smelting reactions where iron oxide particles were dropped on to an iron-carbon bath containing molten CaO-SiO2-Al2O3 slag layer on its surface. The composition of the slags used in the experiments was %CaO:46.1; %SiO2:41.7; and %A1203:12.2. Experiments were con¬ducted with carbon saturated iron melts contained in either a pure graphite crucible whose walls were covered with a pure alumina tube, or a pure flat bottom alumina crucible, at 1723-1823 K. Degree of reduction of a pure iron oxide particle was linear with time in the initial stages (up to about 20% oxygen of the original pellet was reduced). The rate of reduction of smaller oxide pellets was smaller than that of a bigger pellet - the time for complete reduction of a 5.6 g wustite pellet was smaller than that for a 1.2 g wustite pellet. It was also established that the interaction rates obtained by adding a molten pure oxide particle of given weight to the system were lower than that determined by using a solid oxide particle of same weight. The overall rates of reduction decreased with decreasing the bath temperature. The experimentally determined rates of reduction based on the time for 70% reduction were influenced substantially by addition of slag up to about 50 g on to a bath of 78.8 mm in diameter, and remained constant when slag present on the bath surface was between 50 g and 200 g.

Jan 1, 1993

By A. Deepatana

Bioleaching of nickel laterite ores is based on the use of heterotrophic fungi organisms and their metabolites (organic acids) to dissolve nickel and cobalt from oxide minerals to form metal-organic complexes. Metal recovery from this process using an aminophosphonic acid based chelating resin (Purolite S950) was investigated as a function of metal concentrations, complexing agent including citric, dL-malic and lactic acids. Batch adsorptions were conducted using synthetic leachate solutions of nickel and cobalt with concentrations from 15 to 2000 mg/L prepared in 0.01 and 0.1 M organic acids. Adsorption equilibrium data were interpreted using the Langmuir, Freundlich and Dubinin-Kagner-Radushkevich (DKR) models. The results showed that equilibrium adsorption data for nickel-organic complexes followed the Freundlich model and those for cobalt agreed with the Langmuir model. It was observed that the maximum adsorption capacities of nickel and cobalt were 3.26 and 10.48 mg/g resins respectively. These were achieved in metal complexes prepared from 0.01 M lactic acid. Metal elution was conducted using 2 M nitric acid. High metal recoveries were achieved from low metal concentrations but were found to decrease with increasing metal concentration. The results suggest that effective recovery of nickel and cobalt from low concentration of metals, such as those generated from bioleaching operations, can be achieved suitably using chelating resins.

Jan 1, 2006

By Xiaowen Liu

The thermal decomposition of diaspore was investigated by thermogravimetry (TG),differential scanning calorimetry (DSC), X-ray power diffraction(XRD),infrared (IR)spectrain this paper. The thermal decomposition mechanism of diaspore was discussed according to Coat-Redfer equation. It was found that the decomposition of diaspore was carried out at 500?,and the peak temperature was 530?. The electrovalent balance of diaspore was destroyed. The previous crystal structure was changed. a- Al2O3 was obtained after thermal decomposition. The activation energy is 287KJ/mol.

Jan 1, 2006