Search Documents

By Clarence Thom

This chapter presents, in summarized form, standard procedures for making separations of minerals from their ores by the froth flotation process to produce marketable concentrates. These are typical mineral separations which are being made commercially with the reagents and conditions generally used in the mining industry. Typical separations are presented for 17 metallic and 11 nonmetallic ores. The review of each includes a brief description of the mineral and the particular problem presented, general market specifications for its concentrates, an outline of treatment method, and kinds and quantities of reagents usually employed. This chapter does not include de- tails about ore preparation (crushing, grinding, and classification), elements of ore and pulp transportation (conveying and pumping), or concentrate preparation for market (thickening, filtering, and drying). In each presentation it is assumed, if not detailed further, that the ore is ground to the economical point of liberation of the minerals to be separated. Specific information, such as ratio of concentration and recovery, that depends upon the grade of ore being treated is considered beyond the scope of this chapter. Effective flotation separations that produce marketable concentrates may produce widely varying results in terms of percent recovery and still be economically profitable operations. Details of plant practice on specific ores are presented in Chapters 16 and 17. In this chapter the chemical names of the reagents are given. The extent to which different reagents are used in flotation plants in the U. S. is presented in Chapter 4. A compilation of the various flotation reagents, their trade names, manufacturers, and use has been prepared by H. T. Spedden. ANTIMONY The principal ore mineral of antimony, stibnite (Sb2 S3), is generally found in the U. S. in ore bodies in association with other valuable minerals such as galena (Pbs), sphalerite (ZnS), chalcopyrite (CuFeS2), or tetrahedrite (3Cu2 S – Sb2 S3), The sulfo-salt minerals of antimony, such as tetrahedrite or pyrargyrite, are often associated with high silver values, so that the presence of antimony may indicate economic importance even though the actual antimony content is low. Antimony is also significant to the mineral economy because of its occurrence in some ores where lead, gold, and silver are the

Jan 1, 1962

By T. S. Spicer, C. C. Wright

A CHARACTERISTIC property of bituminous coal is that upon being heated the coal becomes plastic, evolves volatile gases, and finally solidifies into coke This fundamental characteristic is of utmost importance and is utilized in the production of the high-temperature coke upon which the steel industry is so dependent, but from the standpoint of operation in the domestic underfeed stoker this coking tendency seriously interferes with efficient combustion When the coke formed has too strong a structure, certain difficulties result, such as low rate of burning, slow response to heat demand, and, in extreme cases, extinction of fire The plastic mass prevents uniform distribution of air through the fuel bed and, With strongly coking coals, large dense pieces of coke are produced which have much less reacting surface thin was possessed by the original coal In both ignition and combustion of solid fuels, the extent of the reacting surface is an accelerating factor Poor combustion permits a surplus of fuel to accumulate in the furnace because the rate of feed and the rate of combustion are not in equilibrium, and this produces an unbalanced condition detrimental to continued) automatic service In order to burn strongly coking coals satisfactorily in a conventional stoker during the three requisite types of operation continuous, intermittent and hold-fire, frequent attention is necessary Domestic stokers are defined by the industry as residential stoker heaters that burn 60 lb of coal or less per hour With a few exceptions, these units employ the underfeed principle of combustion in which both air and coal move in the same direction up and through the fuel-bed Domestic combustion equipment has difficulty in meeting the problems presented by the several variations in ash and volatile matter, in ash-clinkering tendencies, in coking properties, and in the particle size of bituminous coals The work of Bituminous Coal Research Inc at Battelle Memorial Institute has shown that, of these, coking characteristics and the clinkering tendencies have the greatest effect upon the operation of the conventional clinkering type of stoker Typical coke formations in a clinkering type of underfeed domestic stoker are illustrated in Fig. I, which shows (A) the ideal fuel bed obtained with a noncoking or free-burning coal, (B) the type of fuel bed formed -with, a coal that produces a weal coke, and (C) the type of fuel bed obtained with a strongly coking coal C is characteristic of the fuel bed developed when the average Pennsylvania bituminous coal is ,burned in an underfeed stoker of conventional type It is apparent from these pictures that the formation of coke trees will seriously interfere with the efficient automatic combustion of Pennsylvania bituminous coals

Jan 1, 1942

By J. Serra, M. Turpin, R. Alberny

A new method is proposed to obtain automatically an unbiased estimate of the interdendritic spacing A. It is shown that the structure can be built by a random distribution of a rectangular basic unit. The usual definition of the interdendritic spacing yields a value 1 which, coupled with A, gives the shape of the basic rectangular unit. A study of the relationship between dendrite arm spacing and solidification rate was conducted as a part of a research program on dendritic solidification. For any comparison between theory and experiments to be meaningful, it is necessary to measure reproducible and clearly defined spacings. Fig. 1 shows clearly that even in a fairly simple structure such measurements are difficult. if we compare photos (a) and (b), we can hardly assess which one shows the larger spacing. Moreover, the quantity to be measured can be defined in several ways. On a small scale, dendrites seem to be distributed in a very regular and ordered way. However, on a larger scale, this regularity no longer exists. The usual way to measure spacings is to pick up some rows of dendrite stalks; such measurements are obviously biased since less orderly regions are not taken into account. A more objective method is to section the picture with randomly oriented straight lines and average the measured interdendritic spacings. The purpose of this paper is to show that such measurements, which can be conducted automatically, yield objective and reproducible results which are directly related to characteristic features of the dendritic structure. I) THEORETICAL ANALYSIS 1-1) Mathematical Morphology and Function of Co-variance. Matheronl and Serra2 enlarced- the definition and geometrical meaning of the notion of covariance to encompass problems in mathematical morphology. A brief review of part of their theory can be stated as follows. Let A' be an isolated particle, and let us consider a group of two scanning points h is the vector joinlng these points, h its modulus, and a its direction. Let us also define a boolean function, k(x), whose value is 1 if x lies inside the particle and 0 if it 1s outside. The total number of events in which both points are inside A' IS the covariance Ii',(h): is the measure of the intersection of A' with the particle ALh obtained by translating A' of -h Obviously K,(O) is the volume of the particle A', or its area if A' is a two-dimensional body. The average value of K,(h), when the direction of a vector h of constant modulus is rotated, is: An important property of the covariance is illustrated on Fig. 2: if the shape of a particle shows some regularity along a direction a, K,(h) generally presents a maximum. We now consider a group A, made of many particles A' distributed in space; then k(x) is taken as the realization of a stationary random f~nction.~ The volume fraction (or fraction of area if the problem is two-dimensional) occupied by A equals the average value q of k(x): meaning "average value of"). We also replace

Jan 1, 1970

By Walter McKee

WHEN mixed with common cast steel in quantities ranging from 11 to 13 ½ per cent. and properly treated, manganese increases the ductility of the metal and adds greatly to its toughness and resistance to abrasive action, which properties comprise the distinctive characteristics that make manganese steel so valuable for many purposes at the present time. Manganese steel has been manufactured for about 26 years. .It was first made in a small way in England and subsequently produced in the United States in 1892. At present the manganese-steel foundries of this country have an annual capacity of about 60,000 tons and most of the growth has occurred within the past 10 years. In the early days of the industry it was impracticable to make manganese castings weighing over a few thousand pounds, but at present crusher heads, rolling-mill pinions, and similar castings weighing up to 30,000 lb. each are produced, and it does not appear that the limit of weight has been reached by a considerable margin. Manganese steel is similar in analysis to ordinary first-class converter metal except that it is high in carbon and contains from 11 to 13 ½ per cent. of manganese. From one standpoint manganese steel is similar to malleable iron in that the casting as it comes out of the sand is hard and brittle and must be made ductile by a heat-treating process. The heat treatment is an essential part of the process of making manganese-steel castings and must be properly carried out to secure satisfactory results. The necessity for heat treatment limits the thickness of sections which may be made of manganese steel. Originally the annealing depth was comparatively small, but researches carried on during the past few years have resulted in an increase in the thickness of section up to 5 ½ in., which it is possible to treat successfully. Large castings are cored out to a minimum thickness of 5 ½ in., thus not only eliminating some of the internal stresses which are invariably set up in a very thick casting, but also reducing the weight and inertia of the piece, an

Jan 12, 1915

By W. T. Lankford, Low J. R., Gensamer M.

The problem of sheet metal formability is one which has received a vast amount of attention during recent years. In spite of the great amount of study and experimental work which has been devoted to this problem, many of its fundamental aspects are still not well understood. No generally satisfactory test has been developed which is capable of providing a reasonably adequate evaluation of sheet metal formability, particularly in borderline cases. Anomalies persistently arise in which a lot of supposedly satisfactory material exhibits excessive breakage when formed. This lack of suitable technological tests greatly hinders the design of new parts and the substitution of new materials in parts of existing design, frequently necessitating considerable costly trial and error experimentation on an actual production basis. When, at the beginning of World War 11, it became apparent that mass production methods of forming would bc required in the aircraft industry if the large numbers of military aircraft needed were to be supplied, renewed attention was focussed on the problem of sheet metal formability. It was widely recognized that the formability requirements placed on sheet metals had been steadily increasing in severity through the years, especially as greater and greater emphasis was placed on streamlined designs with the resultant freer application of doubly curved surfaces. The recent advent of several new high strength aluminum alloys of more limited formability than some of the older alloys also served to emphasize the need for new approaches to the problem. It seemed evident that progress in the technology of sheet metal forming would depend to a great extent on the development of more reliable criteria for the evaluation of formability. Although the problem is admittedly very complex, the most logical approach appeared to be through studies of the fundamental material properties of sheet metals, especially under complex stress conditions simulating those prevailing in actual forming operations. Most previous investigations have failed to make full use of existing knowledge of fundamental material properties, and in many instances have attempted correlations with properties which are now recognized as being ambiguous in nature. This investigation was undertaken, therefore, with the aim of developing methods for the study of the flow and fracture of sheet meta1s under combined stresses, and of making use of such methods as might be developed in

Jan 1, 1947

By Low J. R., Gensamer M., W. T. Lankford

The problem of sheet metal formability is one which has received a vast amount of attention during recent years. In spite of the great amount of study and experimental work which has been devoted to this problem, many of its fundamental aspects are still not well understood. No generally satisfactory test has been developed which is capable of providing a reasonably adequate evaluation of sheet metal formability, particularly in borderline cases. Anomalies persistently arise in which a lot of supposedly satisfactory material exhibits excessive breakage when formed. This lack of suitable technological tests greatly hinders the design of new parts and the substitution of new materials in parts of existing design, frequently necessitating considerable costly trial and error experimentation on an actual production basis. When, at the beginning of World War 11, it became apparent that mass production methods of forming would bc required in the aircraft industry if the large numbers of military aircraft needed were to be supplied, renewed attention was focussed on the problem of sheet metal formability. It was widely recognized that the formability requirements placed on sheet metals had been steadily increasing in severity through the years, especially as greater and greater emphasis was placed on streamlined designs with the resultant freer application of doubly curved surfaces. The recent advent of several new high strength aluminum alloys of more limited formability than some of the older alloys also served to emphasize the need for new approaches to the problem. It seemed evident that progress in the technology of sheet metal forming would depend to a great extent on the development of more reliable criteria for the evaluation of formability. Although the problem is admittedly very complex, the most logical approach appeared to be through studies of the fundamental material properties of sheet metals, especially under complex stress conditions simulating those prevailing in actual forming operations. Most previous investigations have failed to make full use of existing knowledge of fundamental material properties, and in many instances have attempted correlations with properties which are now recognized as being ambiguous in nature. This investigation was undertaken, therefore, with the aim of developing methods for the study of the flow and fracture of sheet meta1s under combined stresses, and of making use of such methods as might be developed in

Jan 1, 1947

Jan 1, 1918

By D. G. Westlake, D. T. Peterson

The saturation solubility of thorium dihydride in thorium was studied by saturation of samples and subsequent analysis. The solubility increased from about 1 at. pct at 300°C to above 20 at. pct at 800 °C. Over this temperature range the log of the solubility was a linear function of the reciprocal absolute temperature for thorium of good purity. The heat of solution of thorium dihydride was found to be 7.9 kcal per atom of hydrogen in crystal bar thorium and 6.6 kcal per atom of hydrogen in Ames thorium, The important effect of hydrogen on the physical and mechanical properties of many metals is receiving increasing recognition. The basic physical and chemical data necessary to help explain the observed effects of hydrogen on the mechanical proper ties of metals are all too often not available. The solubility of hydrogen in thorium metal was determined to provide a portion of this basic data for the thorium-hydrogen system. The absorption of hydrogen by thorium metal and the formation of thorium hydrides was studied by several investigators, beginning in 1891, and their work is summarized in Gmelin's Handbuch.1 No effort was made to determine the extent of solid solubility in the metal in these early investigations and the impure metal available made interpretation of the results uncertain. Nottorf2 reported the results of a careful study of pressure-composition isotherms for the thorium-hydrogen system. The principal interest in this work was in the composition and dissociation pressures of the thorium hydrides. Mallett and campbel13 reported the pressure-composition isotherms for the thorium-hydrogen system up to the composition of thorium dihydride. The saturation solubility of thorium dihydride in thorium was reported to be 13 at. pct at 650°C and 23 at. pct at about 900° C. Mallett and Campbell used thorium metal which had been prepared by the calcium reduction of thorium tetra-fluoride or thorium oxide. The results obtained with thorium of these two types agreed within the experimental error. PROCEDURE AND MATERIALS Procedure—The method used to determine the solubility was to saturate a sample of thorium with hydrogen and analyze a portion of the saturated sample. This method was chosen rather than a determination of pressure-composition isotherms since it was much less time consuming and could be applied at temperatures at which the equilibrium hydrogen pressure was too low to measure. The

Jan 1, 1960

By Kenneth K. Humphreys, F. R. Zachar, A. G. Gilbert

INTRODUCTION by F. R. ZACHAR and A. G. GILBERT Coal producers are not only faced with the problems of mining coal, but must also decide to what extent they can invest capital and what operating and maintenance expense they can afford, after mining, to market their product in sufficient volume and at a reasonable profit. Regardless of whether the operator is contemplating a new operation or merely considering expanding present facilities, market requirements, ability to make a product meeting requirements, probable costs and possible future changes in raw coal or finished product must be considered. In addition, such items as flow sheet, structural designs, storage facilities, etc, must be examined individually and collectively. In estimating preparation costs to meet predetermined market specifications, the operator must calculate the economics of present preparation practices to anticipate the increase to total production which results when the quality of the finished product is increased. The consumers of coal are continually seeking to obtain the best and most adaptable product for their money. Regardless of whether coal is used for coking, industrial requirements, electric power generation, domestic fuel or for other purposes, it will be scrutinized from such standpoints as delivered cost, suitability for utilization in certain equipment, ease of ash disposal, adaptability to material handling system plans and its potential for generating dust problems. Utilities, due to large capacity volume requirements, are generally in a position to select coal that will result in the lowest over-all cost per million Btu. Freight costs, paid by the utility, are important and are given utmost consideration when a coal is under consideration. Steel companies, whether producing or purchasing coking coal, are continually seeking coal that will result in lowering the cost of pig iron production. Since it is usually necessary to clean to lower specific gravities, say 1.40, to turn out a product meeting metallurgical requirements, it follows that a high ash "middling" product is created. These low quality middlings do not command a good price. Therefore, unless the metallurgical coal can command sufficient realization to carry or subsidize the middlings, the operator may be ahead economically to prepare steam coal at a higher specific gravity. While the "unit-train" rate reductions have been helpful to the economy of the coal industry, the establishment of these rates has made mandatory the installation of storage and rapid car loading facilities at mines and plants shipping utility coal (see Chapter 15). A study of the economics

Jan 1, 1968

By Edward Keller

About a dozen years ago the art of bessemerizing copper- * matte, brought to these shores from France, was first established at the smelter, in Butte, Montana, of the Parrot Silver and Copper Company, which had bought the process from Mr. Manhks, the inventor. Through the efforts of Mr. J. E. Gaylord, general manager, and Mr. A. J. Schumacher, snperintendent,, assisted by an able staff, the new method rapidly underwent, at the Parrot establishment, an evolution towards higher perfedion, and within a few years its success and its advantages were so marked that all the great works in the west followed in the footsteps of this pioneer. The converter-process has now practically superseded the reverberatory-process in this country. The latter will undoubtedly, in a not very distant future, be relegated to metallurgical history. The writer has availed himself of what was perhaps the last chance to make comparisons of the two methods, working practically on the same material on an extensive scale, the reverberatory process being that of the Baltimore Copper Smelting and Rolling Company,* while the converter-process is that of the Anaconda Copper Company—both using the matte from the latter company's works in Anaconda, Montana. For the greater portion of the material considered in this paper, the writer is indebted to the two companies. In order to understand the difference of behavior of the several elements, and the difference of the copper produced in the two processes, it is best to study and follow those elements

Jan 1, 1899

By Francis Donaldson

THE direct injection of cement grout into water-bearing fissures as a means of checking or stopping the flow of water into shafts and tunnels has been experimented with for a decade or longer and seems to have been first attempted in Europe. The earliest application of which the writer has found a record was at a shaft sunk by the Mining Society of Lens; this is described by C. Dinoire in the Transactions of the Institution of Mining Engineers.1. It is only lately, however, that the process has been entirely successful. This success has been accomplished on the Catskill Aqueduct, now under construction by the city of New York. This aqueduct includes a number of deep pressure tunnels, reached by shafts for both waterway and construction purposes. In portions of these shafts and tunnels considerable underground water was met. The contract for the first of these deep pressure tunnels was let to the T. A. Gillespie Co.; this section is known as the Rondout Siphon. It leads under the Rondout valley at a depth of from 400 to 800 ft. and is about 5 miles long. The engineers expected that considerable water would be encountered, but fortunately this was not the case except at one shaft, known as No. 4, which penetrated the rock at a junction between limestone and conglomerate. Water-bearing fissures were encountered almost immediately. At a depth of about 200 ft. a flow of 1,500 gal. per minute was struck. The shaft then contained as many pumps as could be used, and it seemed impossible to sink it further. After vain efforts had been made to proceed, John P. Hogan, a division engineer of the Board of Water Supply, suggested that cementation of the fissures be tried. The process was attempted for the first time in this country. Since the shaft was partly full of water it was necessary to drill grout holes with a diamond drill. Platforms were placed on the timbers at the water level, the diamond drill was installed and six 90-ft. holes were drilled in the bottom of the shaft. Several car loads of cement were pumped through these holes into the fissures, the drill casings being used for grout pipes. This largely cut off the flow of water from the bottom and sinking could then

Jan 1, 1914

By R. H. Hawkins

AN investigation of the applicability of geophysical methods to north-ern Ontario lignite deposits was undertaken early in 1930 by the Ontario Research Foundation at the request of the Ontario Department of Mines TABLE 1.-Formations Associated with Moose River Basin Maximum System Formation Lithology Observed Correlation Thickness, Ft. Pleistocene Marine clays 150 Glacial till (Minimum Interglacial 30) clay and peat Glacial till Lower Cretaceous or Mattagami Fireclay, sand 138 Kootenay (?) Upper Jurassic. and lignite Devonian (Upper) Long Rapids Petroliferous, 50 Portage and black and gray Genesee shale Williams Limestone and 87 Tully (?) Island calcareous shale Devonian (Middle).... Abitibi River Gray fossiliferous 65 Onondaga limestone Devonian (Lower) ?... Moose Rive- Limestone and 50 gypsum Devonian (Loner) Sextant Arkose, clay, etc. 50 Pre-Cambrian Syenite, granite gneiss, etc. Igneous intrusives. . Lamprophyre dikes cut the Abitibi River and lower formations. (Permission of Ontario Dept. of Mines) and was financed in part from a research grant made by the latter organ-ization. The work to date has included gravitational, magnetic and electrical resistivity studies. The gravitational and magnetic measure-

Jan 1, 1933

By T. G. R. Rawlins, L. E. Brosselard

Direct platinum carbon replicas have been used to study substrates prior to growth and after initial nu-cleation of the layer. Replicas have been directly stripped and correlations have been made with other replica techniques. Mechanically polished substrates are very flat with occasional areas of "dirt", which is apparently silicon. When such substrates are etched in hydrochloric acid gas, scratches and hexagonal defects (thought to be polishing compound) are revealed, together with areas of apparent redeposition. Chemically polished substrates are much less flat although much more homogeneous in appearance. Heat treat)nents have no effect. Nuclei deposited on these surfaces, using a normal silicon tetrachloride system, have been examined. Nuclei on mechanically polished subsrates occur in random areas only, whereas on chemically polished surfaces they are more uniformly distributed. THE interest in the study of thin films and now their rapidly expanding use in many fields has increased over a period of years. Much of this current interest, particularly in the field of single-crystal or epitaxial thin films, has derived its stimulus not only from possibilities for application but also from fundamental electron-microscope studies which have indicated the manner of growth of such layers from the initial nuclei.1-5 Previous work involving study of growth processes may be divided into three categories. First, vacuum deposition, primarily of metals, on a variety of substrates has been studied by electron microscopy and electron-diffraction techniques. These have shown the three-dimensional aspect of nucleation and the remarkable liquidlike behavior of the growing nuclei which coalesce to form a complete layer. More recently this work has been expanded in two ways: by growth inside the electron microscope this has obvious advantages for kinetic studies; and by growth in ultrahigh vacuum—much of this work has been done on semiconductors.8-11 It is of interest to note that metals, specifically gold deposited on rock salt, will form only polycrystalline layers in ultrahigh vacuum unless the substrate surface is contaminated.12 In general the mode of growth for vacuum-deposited semiconductor films is the same as that for metal films. The second method of growth that has been studied is that of electrodeposition.13,14 The little that has been published suggests that the mode of growth is similar to the vacuum case, except that irregularities may perturb the electric field and disturb the growth process. The third and last primary method of growing epitaxial layers is by use of chemical methods. These techniques have generated much interest and much has been published on them. Considerable electron-microscope work has been done on the defects in the layers; however comparatively little work has been undertaken on the initial nucleation and early stages of growth. Confining ourselves now exclusively to the case of silicon, Charig et a1.15 have considered the growth of silicon on silicon substrates by hydrogen reduction of trichlorosilane, and studied the films by means of replica and transmission techniques. Subsequently they have studied the same system for growth on quartz,16 and with the addition of pyrolysis of silane on quartz and alumina.17 Also Manasevit el al. have studied deposits using silane and silicon tetrachloride on sapphire.18-14 Finally, in this volume studies of deposition on beryllia and sapphire are reported. Although Revesz and Evans20 have examined complete layers, grown by means of the widely used silicon tetrachloride reaction, no detailed examination similar to that published by Charig and Joyce21 for the trichlorosilane system has been given. Therefore this investigation has examined substrate surfaces prior to growth and then nucleation on these surfaces for the silicon tetrachloride system. EXPERIMENTAL In this work the surfaces have been studied by means of standard replica techniques. Because of the very real problems associated with artifacts introduced,22 different replicas and different cleaning

Jan 1, 1967

By G. B. Gould

EVERY mathematical statement of a measure of anything (as distin-guished from a count) is followed by a qualification always implied if not explicity stated--that the statement is only an estimate, which may vary from absolute accuracy within certain limits, according to the accu-racy of the measuring instrument. This basic fact, so obvious to engineers, is not so well understood by many that make use of laboratory coal tests. The tolerances that must be allowed in measurements of coal quality are very important in both their commercial and engineering applica-tions-and the significance of these tolerances depends upon the use made of the laboratory coal test. Only in recent years has there been any intensive study of this ques-tion of tolerances as applied to measurements of coal quality. There is very little in our published literature on the subject, and what has been published is not, readily comprehended by those who sell coal, or buy coal and use it, unless they happen to have made a study of the subject them-selves. There is great need for more widespread understanding of what has been discovered and how it applies to the use of laboratory coal tests. What follows is an attempt to condense into a few pages the results of the major investigations so far reported, and to explain their meaning in simple nontechnical language, with the addition of some recent illustrative experiments.

Jan 1, 1937

By Francis Crockard

DURING the past five years we have probably witnessed greater technological advances than in any similar period. Industry and science have steadily marched ahead. The makers of iron and steel products have watched with great interest the development of stream-lined trains, faster and safer airplanes, the entirely new science of air-conditioning and the widespread use of stainless steels. Since 1930, we have witnessed the erection of the world's largest suspension bridge, the largest and fastest ocean liner and the spectacular Boulder Dam, while even greater things are planned in these particular fields. Other indus-tries, too, have been moving ahead rapidly. This advance in a few years has been caused primarily by the fierce competition of the depression. Now, more than ever, is the emphasis placed upon quality and service. Makers of southern merchant pig iron have been no exception and have been confronted with increasingly strict chemical specifications and with much greater stress on physical characteristics than ever before. For example, sulfur in the iron must be held very low, competition demanding that it be in the 0.020's and low 0.030's; silicon content must be held within a very narrow range, and definite requirements of phos-phorus and manganese are an essential part of the specifications. Physical characteristics are becoming of increasingly greater impor-tance. The introduction of triple-skimmed, slow-cooled iron several years ago was the first step in this direction. Now there are a few customers who buy iron by chemical analysis and physical appear-ance, having found that the analysis alone is an insufficient guide to their requirements.

Jan 1, 1935

By Nathaniel Arbiter

T. M. Morris (School of Mines and Metallurgy, Rolla, Mo.)—Rate studies promise to help quantify flotation operations. The author's exposition of rate studies is therefore laudable. However his exposition of a second order rate equation rather than a first order rate equation is not convincing. It is important to use the correct equation, otherwise erroneous conclusions may be drawn. The data assembled by the author and plotted according to a second order rate equation can be plotted according to a first order rate equation. As a matter of fact much of the data used reveals that a second order rate equation is not applicable. According to the method used by the author for plotting data, the reciprocal of the slope of the line is the maximum possible recovery. Physically this cannot exceed 100 pct, yet several graphs yield maximum recoveries greater than 100 pct. For example: l—Curve 2, Fig. 1 yields a value of 120 pct; 2—Curve 2, Fig. 2 yields a value of 115 pct; 3—Fig. 7 yields a value of 110 pct. The real test of the graphical method is, as the author points out, whether or not the earliest points agree with a straight line. The second order rate plot does not fulfill this requirement. Fig. 10 shows the data used by the author to obtain Curve 2 in Fig. 1, plotted according to both a second and first order rate equation. Fig. 11 shows the two rate plots made from data published by Ludt and DeWitt.19 In Fig. 10 the first order rate plot gives a very good fit and obeys the boundary condition of passing through the origin. For the second order rate plot a straight line can be drawn through the last three points but the earliest points are not in agreement with this line. The reciprocal of the slope of the straight line gives a value of maximum possible recovery of 112 pct. The maximum possible recovery according to the first order rate plot is 78 pct. In Fig. 11 the first order rate plot again fits all of the points very well and passes through the origin. The second order rate plot shows wide deviation of the earliest point, indicating that the second order rate equation is not applicable. The reason for the fit of data to the second order rate equation during longer flotation times is that R, the cumulative percent recovery, changes slowly toward the end of the flotation operation, so that when t/R is plotted against time, one is, in effect plotting t against t and one would certainly expect a straight line. The author attempts to show that the second order rate equation is correct by citing evidence which shows that recovery is a function of initial concentration. This is a debatable point especially since, in the author's original presentation of this paper at the St. Louis

Jan 1, 1952

By Vito J. Colangelo

The primary object of this study was to determine the effect of ferrite and its orientation upon the mechanical properties of a precipitation -hardening stainless steel with particular attention to the short-transverse properties. The investigation consisted of Jour major parts : the preliminary investigation of billet properties, the effect of forging reduction and ferrite content upon mechanical properties, the effect of notch orientation upon impact strength, and the relationship of heat composition to ferrite content. Low ductility and impact strength in the short transverse direction were found to he associated with the orientation and shape of- the ferrite plates. It was also determined that impact strength varied with notch orientation. The test values obtained with the notch perpendicular to the plane of the ferrite plate were lower than those obtained in the notch-parallel condition. The over-all investigation showed that high ferrite contents in general had a deleterious effect upon mechanical properties and that the ferrite content could he minimized by exercising rigorous control of the heat composition. A careful balance of elements, nitrogen in particular, must he maintained in order to reduce the formation of ferrite. THE precipitation-hardening stainless steels were developed to fulfill a need for high-strength corrosion-resistant alloys. In the annealed condition they are soft and ductile and possess many of the desirable characteristics of the austenitic stainless steels. In the hardened condition, the alloys exhibit the high strength and hardness of the martensitic stainless steels. The alloy under consideration in this investigation has a nominal composition as follows: C Mn Si Cr Ni Mo N 0.13 0.95 0.25 15.50 4.30 2.75 0.10 The hardening mechanism is identical to that of other hardenable steels in that it depends upon the transformation of austenite to martensite. This alloy because of its annealed structure and its ability to be hardened combines the desirable forming and corrosion properties of the austenitic grades with the high hardness and strength levels attainable with the hardenable grades. The reason for this apparent duplicity of proper- ties can be explained by considering a basic metallurgical difference between the hardenable stainless steels and those of the austenitic group. Both types are austenitic at 1800°F but, while the martensitic grades transform to martensite upon rapid cooling to room temperature, the austenitic grades remain austenitic even when cooled to temperatures below room temperature. The major difference then is in the degree of austenite stability. This stability can quantitatively be described by the Ms temperature. The Ms is defined as that temperature at which austenite begins to transform to martensite. The austenitic grades for example may be cooled to -300°F without producing significant quantities of martensite. The hardenable stainless steels on the other hand have an Ms temperature in the vicinity of 400" to 700°F. In cooling to room temperature, these alloys traverse the entire Ms-Mf range and show almost complete transformation to martensite. The semiaustenitic stainless steel, however, occupies an intermediate position with respect to its austenite stability. The analysis is so balanced that the Ills temperature lies at or slightly above room temperature. The resulting alloy retains much of its austenite at room temperature and yet responds to hardening heat treatments. Achieving this delicate balance of elements is therefore of great importance. Slight imbalances of the equivalent Cr-Ni ratios frequently result in the presence of 6 ferrite. It is the effects of this ferrit with which we are concerned, more specifically the effect of the quantity and ferrite orientation upon mechanical properties, particularly ductility. PROCEDURE A) Preliminary Investigation of Billet and Forging Properties. In order to determine the effect of ferrite on billet properties, billet stock from three heats with various ferrite contents was utilized. Tensile specimens were obtained in the transverse and longitudinal directions from this material and heat-treated as shown in Tables I and 11. Forgings were made from these same heats, the purpose being to determine what effect, if any, the ferrite might have upon the mechanical properties. These forgings were made in such a manner as to elongate the ferrite in the longitudinal and transverse directions. The method of forging was as follows. A section was cut from a 6-in.-sq billet of Heat A and flat-forged to 1-1/2 in. thick. Working was done from one direction only with no edging passes as shown

Jan 1, 1965

By W. M. Weigel

Salt production in Louisiana and Texas at the present time is entirely from salt domes of the interior and coastal groups. Before and during the Civil War salt was recovered from numerous salines and salt springs by evaporation in open kettles. The location of these in nearly every instance was near what is now known to be a salt dome, and the source of the salt in the salines and spring waters was that in the salt core. The tops of many of the shallower domes have been subjected to erosion1. The discovery that the salt occurred as large masses of rock salt in the form of domes was made in May, 1802, at Avery Island, La., by John Marsh Avery, grandson of the original owner, John C. Marsh, who built the old salt works in 18122. The first shaft for mining was sunk on the Avery dome in 1867 by Chouteau and Price. It was 90 ft. deep, about 58 ft. being in solid salt. It was abandoned in 1870. There are three general groups or fields of salt domes; interior Louisiana in northern Louisiana, interior Texas in northeastern Texas, and the coastal domes nearer the Gulf Coast and extending from the Mississippi River to the Rio Grande. This last group contains by far the greatest number of domes. As many of the coastal domes especially are prolific producers of petroleum and a few of sulfur, their geology has been intensively studied and fully covered in the literature. The depth to the top of the salt varies from near the surface, where shallow ground waters have dissolved the salt to just below recent deposits, to several thousand feet, where the depth has been cstimated only by geophysical methods. The diameter of the salt core varies from less than 1/2 mile to over 2 miles. Only domes where the salt is comparatively near the surface have been developed for commercial salt. Three deeper domes, which will be described later, have recently been developed or are in process of development, as a source of brine for chemical use. Fig. 1 shows the location of the domes so far developed for commercial salt and brine. Nos. 1, 2, 4, 7, 8, 9 and 10 are in the Gulf Coastal field,

Jan 1, 1938

By W. M. Weigel

Salt production in Louisiana and Texas at the present time is entirely from salt domes of the interior and coastal groups. Before and during the Civil War salt was recovered from numerous salines and salt springs by evaporation in open kettles. The location of these in nearly every instance was near what is now known to be a salt dome, and the source of the salt in the salines and spring waters was that in the salt core. The tops of many of the shallower domes have been subjected to erosion1. The discovery that the salt occurred as large masses of rock salt in the form of domes was made in May, 1802, at Avery Island, La., by John Marsh Avery, grandson of the original owner, John C. Marsh, who built the old salt works in 18122. The first shaft for mining was sunk on the Avery dome in 1867 by Chouteau and Price. It was 90 ft. deep, about 58 ft. being in solid salt. It was abandoned in 1870. There are three general groups or fields of salt domes; interior Louisiana in northern Louisiana, interior Texas in northeastern Texas, and the coastal domes nearer the Gulf Coast and extending from the Mississippi River to the Rio Grande. This last group contains by far the greatest number of domes. As many of the coastal domes especially are prolific producers of petroleum and a few of sulfur, their geology has been intensively studied and fully covered in the literature. The depth to the top of the salt varies from near the surface, where shallow ground waters have dissolved the salt to just below recent deposits, to several thousand feet, where the depth has been cstimated only by geophysical methods. The diameter of the salt core varies from less than 1/2 mile to over 2 miles. Only domes where the salt is comparatively near the surface have been developed for commercial salt. Three deeper domes, which will be described later, have recently been developed or are in process of development, as a source of brine for chemical use. Fig. 1 shows the location of the domes so far developed for commercial salt and brine. Nos. 1, 2, 4, 7, 8, 9 and 10 are in the Gulf Coastal field,

Jan 1, 1938

APPROXIMATELY 90 per cent of the steel that is melted and refined in the United States and poured into ingots is made in basic open-hearth furnaces, as shown in Table 1-1. The annual ingot capacity of the steel industry reported January 1,1950, by the American Iron and Steel Institute8* was 99,040,160 tons, of which the basic open-hearth process accounted for 85,896,580 tons, 86.7 per cent of the total. The capacity of the individual furnaces varies over a wide range, a large majority falling within limits of 50 to 200 tons (Fig 1-1). Most of the units constructed [ ] since 1942 are in the larger size groups, between 175 and 225 tons capacity.

Jan 1, 1951