By R. W. Raymond

THIS meeting was held in the new home of the Institute, the United Engineering Society Building, 29 West 39th Street, New York City, directly following the Dedication ceremonies. The first session was held in the large Auditorium, Thursday, April 18. The meeting was called to order by Mr. John Hays Hammond, President of the Council, who said Before taking up the reading and discussion of papers, I will call upon Dr. Rossiter W. Raymond, the oldest living past-President of the Institute, who has been in harness almost continuously for thirty-six years, and who has contributed more than any one else to bring this society to its present great success and to establish the reputation of the American mining engineer the world over, for a few words supplementary to those which were uttered to engineers generally, during the sessions of yesterday and the day before. ADDRESS BY R. W. RAYMOND. The generally accepted Darwinian doctrine of the survival of the fittest is sometimes illustrated by persons who are supposed to be the fittest because they have simply survived. I fear that I come under that category. Almost all of my contemporaries in the early history of this Institute have passed away. Only one or two of the original founders remain, and I may fairly say that scarcely any remain who were active at that : time in shaping the organization and the future career of the Institute. In May, 1871, I was thirty-one years old. Next week I shall be sixty-seven years old. All the intervening years have been devoted to the service of this Institute almost continuously, either as President or Vice-President or Secretary. You may easily imagine, therefore, with what pleasure I greet you on this occasion. I am not here to extend to you the welcome of the City - of

May 1, 1907

Ware B. Gay, Richmond, Va.: Having followed the remarks of Prof. Woodworth with great interest, especially his suggestions for drilling in the part of the coal-field on the south side of the James river, I would like to inquire of him if he reached his conclusions after fully considering the situation as existing upon the north side of the James ? My reason for this inquiry is, that upon the north side the eastern and western outcrops are much nearer each other than appears to me to be the case upon the south side, and also that the western outcrop on the north side is much more clearly defined than upon the south side. It is now about twelve years since I first became interested in the Richmond coal-field—and until about six years ago I passed much time in investigation and spent thousands of dollars in developments. About six years ago the properties in which I was more especially interested were leased to other parties, and since that time I have had little or nothing to do with the mining operations. I regret to say the price of coals has ruled so low during most of the time since the lease was made that the developments have not been as extensive as the lessees had originally intended. The result of my investigations after considering all the theories, expert reports, legends and other information I could obtain bearing upon the subject, was the opinion, which I still hold, that the most practicable and most economical way for proving the extent and value of the field is by sinking slopes from the eastern outcrop, and by prosecuting such slopes in the vein and following the coal to the western outcrop, thus obtaining an actual cross-section in fact and not in theory. Proceeding upon this hypothesis, I sought for the positions where this could probably be accomplished most quickly and develop a marketable coal-area as the work thus progressed. The outcrops on the north side being nearer each other, and

Jan 1, 1902

By David L. Holt

The contribution of grain boundary shear to total elongation, CS/E&apos;, has been measured in an Al-Zn eu-tectoid alloy that was quenched from above the invariant temperature, then annealed at 250° C to a grain size of&apos; 1.8 p. At 250°C, ks/E&apos; is low at both high and low strain rates, but reaches a maximum, estimated as 60 pct at an intermediate rate of 5 X 10 per rnin. Rate sensitivity, as measured by the index m = a log a/a log E&apos;, follows the same trend, and furthermore the maximum values of m and -cur at approximately the same strain rate. This result, combined with the metallographic observation that boundary migration enhances boundary shearing, is interpreted as supporting a previous suggestion that the high rate sensitivity characterizing super-plasticity is the result of combined boundary shearing and migration. It is suggested that the latter event relieves stress concentrations at triple points, and smoothes boundaries so that stress is governed largely by a viscous boundary shear. GrAIN boundary shear has been considered in relation to superplasticity in several recent papers.&apos; The problem has been to explain the high strain rate sensitivity of flow stress, and the variation of rate sensitivity with strain rate (E&apos;) and grain size (L). The requirements for superplasticity, small L and high T, suggest the reasonableness of an approach to high rate sensitivity involving grain boundary shear. Further support came from experiments on the A1-Cu eutectic alloy,&apos; where it was found that strain rate sensitivity of cast material annealed to produce an equiaxed, micron-size grain is always low; taking as an index of rate sensitivity m = a log a/a log <, m < 0.3. However, m in hot-worked alloy of comparable grain size can be as high as 0.7. In the cast and annealed material, each phase is a single crystal, the only boundaries are interphase boundaries, and it is, consequently, geometrically impossible for boundary shear to contribute to deformation in any major way. Other observations (for hot-worked material) were a-L at constant (low) strain rates and indications that the rate of recrystallization was enhanced as strain rate increased. As a result of this work, it was proposed that high rate sensitivity arises from a deformation mode of boundary shear associated with boundary migration. Migration serves to relieve stress concentrations at triple points, and smoothes boundaries so that they assume properties of fluid films. On the other hand, the low rate sensitivity observed at high and low strain rates reflects deformation of bulk material. Measurement of the variation of grain boundary shear with strain rate and m have not yet been made. Such measurements are important, especially in view of a proposal, differing in detail from the above, that high m arises merely from a transition between a grain boundary shear mode of deformation at low rates to a transgranular mode at high rates.2&apos;4 In the present work, the contribution of boundary shear to total deformation is measured and in addition metallographic observations are made on surfaces of deformed specimens to look at the interaction between boundary shear and migration. The Al-Zn eutectoid alloy was chosen for its homogeneous, fine-grained structure, which is obtained readily without hot-working. It has also been the subject of a previous phenom-enologically directed study. EXPERIMENTAL Material. Compression specimens, cross section 4 by + in., length \ in., were machined from a sand-cast ingot of composition 77.5 wt pct Zn, 22.5 wt pct Al. (The melt was prepared from 99.9 pct Zn and 99.99 pct Al.) After homogenization at 375°C for 50 hr, the specimens were quenched in brine and removed before the heat evolution that accompanies de -composition of the high-temperature phase.5&apos;6 The resulting microstructure, see Fig. l(a), was too fine for grain boundary sliding to be easily studied; coarser structures were obtained by annealing for various times at 2 50°C. Annealing was terminated by a brine quench. Final average intercept lengths between all grain boundaries (both interphase and those lying in a phase), L, were: 0.5 p [annealed for 15 min, Fig. (a)], 0.8, 1.1, and 1.8 p [Fig. l(b)l. Testing Procedure. An Instron machine was used for most of the compressive deformation. Tests were of two types: those in which crosshead velocity was changed in steps to measure m as a function of strain rate15 and tests at constant velocity to a fixed (engineering) strain of -0.2 (20 pct). Stress reached a steady-state value (a) which was plotted, on a logarithmic scale, against log strain rate (E&apos;). An alternate and equivalent evaluation of m was to take the slope of the log o vs log 6 curve. Time at temperature before testing was 15 min. Strain rates covered by the Instron (4 x lo-&apos; to 4 x 10&apos; per min) were insufficient; at a higher rate of 5 x lo2 per min a gas-operated testing machine was used, the gas driving a piston to compress the specimen at a controlled velocity.&apos; To obtain points on the log a vs log E&apos; curve at low rates, specimens were compressed by a dead weight. strain rate was an average value computed by dividing strain at the end of test by loading time. In some tests strain was measured at fractions of the loading time; creep rate was found to be reasonably constant.

Jan 1, 1969

By D. K. Bose, C. K. Gupta, K. U. Nair

A new approach to processing an indigenously available low grade molysulfide concentrate by chlorination with elemental chlorine in presence of oxygen is reported. Recovery of nickel and copper values associated with the sulfide concentrate by suitably treating the residue obtained after chlorination is also reported. In the chlorination process, a gaseous mixture of chlorine and oxygen in the volume ratio bf 2:5 has been passed at 1.66 x 10- 5 m3/s for 1800 s over a 0.01 kg batch of molysulfide concentrate at a temperature of 573°K. Most of the molybdenum has been volatilized as molybdenum oxychloride which has subsequently been extracted in water. The molybdenum value from the aqueous solution has been recovered in the form of calcium molybdate (CaO.MoO3) by treatment with calcium chloride (CaCI2). In an alternative processing scheme, the molybdenum rich solution has been treated with an oxidizing agent (K2S20f.J) and allowed to boil to recover a major portion of the molybdenum value in the form of molybdic oxide (MOOS). The spent charge obtained after molysulfide chlorination has been mixed with about 1 wt % sodium chloride and heated at 773K under an oxygen atmosphere. The reacted mass has been water-leached to yield a nickel-copper bearing solution with limited iron. The process liquor appears to be well suited for further processing by known hydrometallurgical recovery processes for nickel and copper. In the conventional process of molybdenum extraction, the molysulfide concentrate (-59% Mo) is first subjected to roasting to produce molybdic oxide. The oxide is then further processed in sequential steps involving vacuum distillation, ammonia leaching, and calcination to higher purity prior to hydrogen reduction to metal. In India there is at present some small tonnage production of molysulfide concentrate from a byproduct recovery plant of the M/s. Uranium Corp. of India Ltd. (M/s UCIL), Bihar. Efforts are being made at this laboratory to process the low grade fraction of the concentrate which contains sulfides of copper, nickel, and iron; quartz; and chlorites. Here, the conventional routes involving roasting and vacuum distillation appear unsuitable to produce an acceptable quality of molybdic oxide at high recoveries. Formation during roasting molybdates of some of the impurities present in the sulfide concentrate make subsequent vacuum distillation less efficient. In view of these problems, in earlier work reported from this laboratory the low grade concentrate has been processed hydrometallurgically to P. produce calcium molybdate. Starting from this molybdenum intermediate, processes have also been developed for the production of molybdenum and ferromolybdenum. Chlorination as an alternative to roasting for metal sulfides has been drawing considerable interest. The high reactivity of chlorine, the relatively low temperature of operation, the suitability of application to low grade resources, the convenience of recovering sulfur in non-polluting form, and the purity of chlorides which are separated by distillation all favor chlorination. In recent years, considerable work has been reported on the chlorination of common metal sulfides. In the field of molybdenum extraction from its sulfide resource, use of chlorination technology has been rather limited. Senderoff and Labrie3 were the first to chlorinate molysulfide concentrate with elemental chlorine at about 823°K to molybdenum pentachloride for use in the electrolytic preparation of molybdenum. The only other reported work, by Haver, Uchida and Wong, involved reaction between molysulfide and chlorine at 673°K to recover sulfur. The reaction products were, however, identified as molybdenum pentachloride and sulfur monochloride.

Jan 1, 1979

By C. G. Dunn, W. W. Martin

Various X ray diffraction techniques have been developed for determining orientations of crystals. Transmission and back-reflection Laue methods1,2,3 in particular have been found to be very useful. In many applications, however, a need still exists for a simplification of the details of analysis so that orientations can be determined more rapidly, and operators with little or no training in crystallography can be easily instructed in the necessary procedures. Filling this need in part is a system of analysis that has been in use for several years in the Metals Section of the Laboratory, General Electric Co., Pittsfield, Mass. This method is an extension of the one of Majima and Togino,4 which uses fifty-five indexed standard transmission Lauemams to cover the entire range of crystal orientations. Greater rapidity in determining the orientation of a crystal is achieved by using a slightly larger set of standard Lauegrams and by systematizing the steps followed. This system of analysis in its present form constitutes the subject matter of the present paper. Although the method uses transmission X ray Laue patterns, many of the operations are applicable to the analysis of back-reflection Lauegrams. Very briefly the method is based on the fact that Bragg and azimuthal angles for two or more identified Laue diffraction spots completely determine the orientation of a crystal, and standard Laue photographs of the Majima and Togino type provide a ready means for identifying Laue spots. After a preliminary analysis, which consists of identifying the pattern in terms of one of the standard patterns, a correctly marked Lauegram is selected to carry out the final analysis. From measured Bragg and azimuthal angles, the normals (poles) of the reflecting planes for the selected Laue spots are located on a stereographic projection and the orient.at.ion of the crystal determined (in terms of the positions of cube poles for example) by a few additional operations on a \I1ulff net. The actual procedure followed will be illustrated in detail after a brief treatment or X ray problems connected with orientation determinations and a discussion of useful principles and techniques. X Ray and Plotting Problems RELATIVE ADVANTAGES OF BACK-REFLECTION AND TRANSMISSION LAUE DIFFRACTION METHODS In the back-reflection Laue method it is easy to make a direct measurement of the tilt of a zone of Laue spots. Specimen thickness also is generally no problem. In the case of thin specimens, however, the time of exposure is less for the transmission Laue method. For example, with silicon ferrite this advantage holds up to a thickness of 0.6 mm if tungsten radiation at 40 kv peak voltage is used. Furthermore, the transmission photograph represents the entire thickness of the crystal whereas the back-reflection picture represents only a surface layer (a thickness of less than 0.05 mm for silicon ferrite), the deeper layers supplying a negligible amount to the diffraction pattern. If a crystal is distorted, the transmission Laue pattern gives more information particularly with regard to the orientation of the crystal and the overall amount of spread in orientation. Finally a 3 1/4 X 4 in. film suffices for transmission photograms; a 4 X 5 in. or 5 X 7 in. film with a central hole is needed for back-reflection patterns Not only is the manipulation of film easier because of the size of film, but

Jan 1, 1950

By Cyril Stanley Smith, Earl W. Palmer

STRIP of any of the metals used for deep drawing operations occasionally yields cups that are defective because of a rim that varies in height around the cup in a wave-like manner. Some such defects are traceable to tools or other press factors, but when the protuberances formed (usually four in number on brass and other copper alloys) are symmetrically disposed with respect to the rolling direction of the strip, they are invariably attributable to the metal. The effect is known as "earing" and the protuberances are called "ears." Other terms frequently heard are "tips," "scallops," and "corners." It is recognized that the effect is most commonly a result of a directional crystal structure produced by rolling and annealing operations in the manufacture of the metal strip. &apos;Numerous papers dealing with various aspects of the earing effect have appeared in the literature, those listed in the references1 being especially interesting and valuable. An investigation of the factors influencing earing of brass cups has been in progress in the laboratories of the American Brass Co. for several years, and it was thought desirable to make some of the results generally available in summarized form. The present paper discusses many factors that do and do not contribute to ear formation. In addition, a section is devoted to methods of minimizing the earing tendency of brass sheet by proper selection of the cold-rolling and annealing schedule by which it is produced. In the space available, it is impossible to quote detailed experimental procedures and numerical results. However, the authors make no statement that they do not believe to be properly substantiated, either by experimental evidence obtained under laboratory conditions or by experience in the actual production of deep-drawing brass in the brass mill. MECHANISM OF EAR FORMATION It must be clearly understood that the formation on cups of symmetrical ears, four or more in number, is attributable solely to the strip metal, and results from the strip having different deformation characteristics in different directions. The tools used in the drawing process, or the type and completeness of lubrication of the strip, have nothing to do with the problem of ears, although they do, of course, greatly affect the "drawing quality" of the strip and the general appearance of the cup. A single tip may be drawn up on the rim of a cup because of misalignment of the tools, or because the gauge of metal varies from side to side of the strip. The two-ear form that sometimes appears is also traceable to gauge variations. However, the four-ear and six-ear symmetrical forms that we are concerned with here are caused by factors inherent in the structure of the metal itself.

Jan 1, 1942

By C. A. Siebert, S. H. Bush

Isothermal temper-embrittlement studies were conducted on a 5140 steel at various temperatures for times as long as 3000 hr. Specimens from the embrittled steel were subjected to impact tests, metallographic examination, microhardness, and lattice-parameter measurements. SEVERAL of the steels in the low alloy group are subject to a pronounced decrease in impact energy if held within, or cooled slowly through, a range of temperatures below the lower critical. This phenomenon, known as temper embrittlement, is quite pronounced in the chromium steels of which AISI 5140 is typical. This study considered the response of one heat of 5140 steel when embrittled isothermally at various temperatures for times as long as 3000 hr. Excellent reviews of the work done in the field of temper embrittlement have been written by Hollomonl and Woodfine.&apos; Both authors list the various theories which have been advanced to explain temper embrittlement. Some of the mechanisms considered were: 1—a transformation below 700°C; 2—an allotropic modification of iron; 3—precipitation from the ferrite of such compounds as carbides, nitrides, phosphides, or chromium oxides; 4—decomposition of retained austenite; 5—modification of special carbides; 6—grain-boundary segregation; and 7—selective distribution of carbides. The present study investigated the changes in hardness, Meyer&apos;s number, impact properties, micro-structure, and lattice parameter which occurred on embrittlement. Previous studies considered the influence of microstructure and of prior austenitic grain size3 on the response of 5140 steel to temper embrittlement. Equipment and Procedure All samples were taken from one heat of 5140 steel; the chemical composition of this steel was: 0.43 pct C, 0.86 pct Mn, 0.020 pct P, 0.019 pct S, 0.27 pct Si, 0.84 pct Cr, 0.10 pct Ni, 0.06 pct Mo, 0.10 pct Cu, and the remainder Fe. The material was received as % in. rounds. This stock was cut down to blanks measuring approximately 0.425~0.425~2.196 in. Heat Treatment: The rough blanks were normalized at 1600°F (870°C) for 1 hr, then austenitized at 1600°F (870°C) for 1 1/2 hr, and quenched into an agitated oil bath. The specimens were tempered at 1275°F (690°C) for 5 hr and water quenched. These tempered specimens were designated as the toughened state. Embrittling Treatments: The tempered bars were divided into sets and subjected to the various embrittling treatments listed in Table I. Temperatures from 750" to 1050°F were investigated for times of 1 to 3000 hr. Special tests to determine the effect of heating a short time at a higher temperature after long-time embrittlement at some lower temperature were also conducted. All specimens were water quenched at the end of the embrittling cycle, then ground and notched to obtain standard Charpy V-notch specimens. Impact Tests: The bars were fractured in a 260 ft-lb Charpy impact unit; specimens were fractured at temperatures ranging from —315°F to room temperature. Fixed temperatures used consisted of —315°F with liquid nitrogen, —115°F with dry ice and acetone, and 32°F with ice and water. Intermediate temperatures were obtained by suspending the bars in a jig over the liquid nitrogen, dry ice and acetone, or ice and water.

Jan 1, 1955

By D. G. Westlake

NUMEROUS hydride habit planes in zirconium, Zircaloy-2, and Zircaloy-4 have been observed by various researchers and have been compiled by Louthan and Angerman.1 While only partial agreement exists on the identification of these habit planes, there is a growing consensus that a tensile stress applied on a polycrystalline rod during slow cooling will cause the hydride platelets to lie perpendicular to the tensile axis. walters2 agrees with Louthan and Angerman who reason that "The particular plane on which precipitation will occur is the plane that will result in the maximum relief of stress by precipitation of the low-density hydride." The experiment described below was initiated to test this hypothesis on a single crystal of zirconium. A single-crystalline tensile specimen of zone-refined zirconium, designated number 13 in a previous study,3 had a square cross section with one pair of parallel faces only 4 deg from the basal plane of the hcp structure. The tensile axis was about 86 deg from the (0001) pole, 14 deg from the (1010) pole, and 16 deg from the (1150) pole. The specimen was charged to 50 ppm H by allowing reaction with the correct amount of hydrogen at 1073°K, homogenizing at this temperature for 2 hr, and cooling in the furnace. Two- surface analysis revealed that hydride platelets had precipitated parallel to the three {1010} prism planes. The specimen was heated to 673°K, in air, for 16 hr to bring the hydrogen back into solid solution, and furnace-cooled to 573°K.* It was then stressed in ten- sion at 1.2 kg per sq mm. (This produced a resolved shear stress of 0.6 kg per sq mm for glide on the prism plane with the highest Schmid factor. A higher stress would have produced significant strain at this temperature because the critical resolved shear stress for prism-plane glide in this crystal was only 1.0 kg per sq mm at ambient temperature.) The poles of the three prism planes were at angles of 14, 46, and 74 deg to the tensile axis so that an applied stress would exert normal stresses on the three planes in the approximate ratios 10:5:1, respectively. As soon as the stress was applied, the sample was furnace-cooled to room temperature. It was ground on wet Sic paper and chemically polished in 50 parts HNO3, 50 parts water, and 7 parts HF before examination. The result of the experiment was negative; i.e., the three (1010) planes were of equal importance as hydride habit planes.* It must be admitted that the ex- periment is not entirely comparable to those performed by walters,2 Louthan,5 and Louthan and Marshall6 on polycrystalline materials. They have found that some critical stress (below the macroscopic yield stress) is required for stress-orienting the hydrides. The applied stress in the present experiment was, by necessity, smaller by an order of magnitude than the critical stresses they report for the various materials. If the critical stress was related to the microstructure, one might postulate that it should be decreased by increasing the degree of perfection of the metal lattice and by increasing the grain size. But the experiment above suggests that, for the extreme case of a zone-refined single crystal of zirconium, the critical stress lies above that which one can apply without introducing gross plastic strain as another variable.

Jan 1, 1967

By M. A. Dayananda

Based on the Kirkendall frame of reference, a method is proposed for the determination of atomic mobilities of all the diffusing species in a multicorn-ponent system with a single diffusion couple. The method is based on an atomic mobility model developed on the concept of negligible interactions among the intrinsic fluxes. It is shown in the model that mobilities can be obtained directly from the cumulative intrinsic fluxes past the Kirkendall interface. The proposed method replaces the need for a prior determination of interdiffusion coefficients far the calculation of mobilities. Relations between intrinsic diffusion coefficients and mobilities are derived and the mobility calculations are illustrated with diffusion data in Cu-Zn-Mn alloys at 850°C. ThE concept of "intrinsic flux" with respect to a fixed lattice was introduced "i Darken1 to explain toa Kirkendall effect2 demonstrated by the motion of inert markers during isothermal diffusion in single-phase binary solid solutions. Based on this concept, intrinsic diffusion studies have been made in various binary metallic systems3,4 employing such a lattice frame of reference, commonly referred to as the Kirkendall interface. Similar approaches, both theoretical and experimental, have been presented5"10 to study intrinsic diffusion in multicomponent systems. Based on the direct integration of Fick&apos;s law extended to multicomponent diffusion, Philibert and Guy8 proposed a method for the determination of intrinsic diffusion coefficients. For an n-component system, this procedure requires an experimental study with (n — 1) diffusion couples, all having their Kirkendall interfaces at the same compositio;, where n(n — 1) intrinsic diffusion coefficients are defined. This technique has been employed for ternary diffusion studies by Dayananda and Grace" and Guy and Leroy.11 A different approach is recommended by Ziebold and Cooper,12 who have derived relations between interdiffusion coefficients and atomic mobilities employing fluxes referred to the local center of volume. Their analysis is based on the simplifying assumption of negligible interactions among intrinsic fluxes. This assumption has been considered satisfactory for dilute solutions.5"7 The use of this analysis for the calculation of mobilities requires an initial determination of interdiffusion coefficients with a set of diffusion couples having intersecting diffusion paths. It is the purpose of this paper to propose a method that would permit a direct determination of mobilities of all components of a multicomponent system from a single diffusion couple. This method is based on a mo- bility model developed with diffusion fluxes referred directly to the Kirkendall interface, generally identified by inert markers. gen erall, like that of Ziebold and Cooper,12 employs the simplifying assumption that the flux of each component relative to a fixed lattice is caused only by the driving force of its own chemical potential gradient. THE KIRKENDALL INTERFACE Inert markers are employed in diffusion couples to locate experimentally the position of the Kirkendall interface. They are initially placed at the weld interface for "sandwich" couples, or at the original vapor-solid interface for vapor-solid couples. Studies of marker motion in binary systems3&apos;4 with both types of couples indicate that markers remain in a plane of constant composition and move with this plane para-bolically with time. Parabolic marker movements were also observed in ternary Cu-Zn-Mn couples by Dayananda and Grace.10 It is reasonable to expect a similar marker behavior even for diffusion couples with a higher number of components.

Jan 1, 1969

By G. Derge, R. E. Grace

Diffusivity of bismuth in liquid Pb-Bi alloys has been measured by the capillary reservoir method as a function of temperature and composition. Fair agreement between theory and experiment is found for the measured diffusion coefficients and activation energies of diffusivity and viscosity in dilute lead alloys. The measured diffusion coefficients in the high bismuth alloys describe mass transport in special concentration gradients. THE study of diffusion in liquid metals has been restricted largely to the amalgams over small ranges of temperature and composition. In contrast to this, diffusion and transport of ions and molecules in aqueous and organic solvents have been studied extensively for the past 50 years. The general difficulty of measuring diffusion coefficients in both gases and liquids at high temperatures has been that of eliminating convection currents. Measuring techniques based on freezing and sectioning after the diffusion period1 are not particularly satisfactory because of the volume changes and segregation which occur during freezing. The most promising technique which is currently being developed for liquid metals is the capillary reservoir method. This eliminates convection currents from the diffusion zone and requires measurements only of the length and initial and final compositions of the alloy within the capillary. Anderson and Saddington&apos; have measured the diffusion coefficient of tungstate anions in aqueous Na,W04; Wane4&apos; and Hoffman- ave studied structure and self-diffusion in water and self-diffusion in mercury, respectively, by similar techniques. Selection of the Pb-Bi system for initial study was made for several reasons: I—It afforded a low temperature system for development of techniques which would be suitable for high temperature measurements in liquid iron. This research on diffusion in liquid iron is now in progress as a part of a general program on the rates and mechanisms of slag-metal reactions. 2—Activity data on liquid Pb-Bi alloys of all compositions are available from the emf meas- urements of Strickler and Seltz.9 3—Some data are available on the diffusion of bismuth into solid lead. The measurements on solid alloys were made by von Hevesy and Seith7 for the concentration range of 0 to 2 pct Bi. An appropriate solution to Fick&apos;s law (unsteady state) for the capillary reservoir has been found by considering the mass flow which passes through a unit area of surface on a slab of infinite thickness as a function of time. This is the first application of this solution to diffusion measurements, although a similar solution is available for identical boundary conditions.&apos; By analogy with heat conduction, the problem reduces to a perfectly insulated infinite slab at temperature C,, one surface of which is quenched to C, for all times, t. Heat is permitted to flow from quenched surface of the slab to an infinite supply of coolant at C.&apos; (see Appendix). For the corresponding solution for diffusion in liquids, these terms become Where Cu is the initial concentration of component A" in entire capillary at t - 0, C, is the final con- In this case. component A is bismuth, and C, = 0. centration of component A in entire capillary at t = t, C, is the concentration of component A in bath for all t, 1 is the length of the capillary in centimeters, t is the time of diffusion period in seconds, and D is the diffusion coefficient in square centimeters per second. By comparison with solutions to Fick&apos;s law used in the solid state, this solution for liquids is similar to the Grube solution for solids, where the change in D with chemical composition is not taken into consideration. Difficulty is to be expected if large concentration gradients are employed and if the concentration gradients extend over an appreciable length of the capillary.

Jan 1, 1956

By S. H. McFarlane, K. H. Zaininger, G. W. Cullen, C. C. Wang, G. E. Gottlieb

Heteroepitaxy of silicon on stoichiometric spinel has been studied. Both boron-doped (p-type) and arsenic-doped (n-type) single-crystal silicon films have been grown by the pyrolysis of silane on sioichiometric spinel (MgAl2O4) substrates prepared by a flux technique. The spinel crystals are free from strain and subgrains, and exhibit no thermal instability at temperatures employed for silicon deposition. The growth parameters of epitaxial silicon have been studied. Effects of substrate orientation, surface preparation, and growth conditions on the silicon Properties have been determined. The silicon-spinel composite was characterized by X-ray diffraction, electron diffraction, electron microscopy, and optical techniques. Information on epitaxial orientation relationship, defect structures and film-substrate interface has been obtained. A parallel orientation relationship was found between silicon and spinel. The silicon films exhibit no subgrain structures. However, growth pyramids, microtwins, stacking faults, and dislocations are the prevalent defects. The deformation of epitaxial silicon was measured by an X-ray technique. It was found that the epitaxial silicon is strained under compres-sive stress due to the thermal expansion difference between the film and substrate. The stress was estimated using the classical plate theory and beam equation. Electrical properties of the epitaxial silicon have been measured, including resistivity, carrier concentration, and Hall mobility. MIS and vertical through diffused junction structures have been fabricated wing silicon-spinel composite. Information on MIS characteristics, minority carrier life time, and junction properties has been obtained. THE achievement of single-crystal growth of large area silicon semiconductor films on oxide insulating substrates is of technical importance to many solid state electronic devices. The semiconductor-insulator composite structure is also of scientific interest because the heteroepitaxy is determined by the spatial relationship between the atomic arrangement in the substrate and that of the atoms in the appropriate crystallographic plane of silicon. The degree of crystalline perfection of the silicon deposits depends also on the physical condition of substrate surface. Epitaxial growth of silicon on commercial flame fusion Al-rich spinel (MgO:3.3A12O3) has been reported by several investigators.&apos;-4 The lattice of spinel of this composition is distorted. The material cracks and exsolves the excess alumina in the lattice at temperatures (-1200°C) used in fabricating silicon devices. Stoichiometric MgA12O4 spinel exhibits neither lattice distortion nor thermal instability. Results are given on the epitaxial growth and characterization of silicon on stoichiometric spinel. EXPERIMENTAL Fabrication of Silicon-Spinel Composite Structures. The MgA12O4 spinel substrate wafers were prepared from bulk single crystals grown at about 1200°C by a flux technique5 using a PbF2 flux. The crystals are free from strain and subgrains, and exhibit a typical dislocation density of less than 50 lines per sq cm. The crystals are thermally stable without cracking and exsolution of alumina to at least 1500°C. The spinel crystals were oriented for cutting by the Laue X-ray back-reflection method.6 Substrate wafers (about 25 mil thick) of (Ill), (loo), and (110) orientations have been obtained bu cutting the X-ray oriented crystals using a standard type diamond wheel. An accuracy of better than 1/2 deg is maintained throughout the operation. The spinel substrate wafers were mechanically lapped and polished to produce the flat and smooth surface which is required for silicon epitaxy. Lapping was carried out with about 30-µ boron carbide abrasives to obtain a flat coplanar surface. The lapped surface was further polished using successively finer grades of alumina, ending with the 0.3-µ grade. After polishing the wafers generally have a flatness of ±0.4 µ per cm, as revealed by interferometry. Fig. 1 shows (111) oriented MgA12O4 spinel wafers of various shapes.

Jan 1, 1970

By AIME AIME

Air transport supplants the old methods. The 3-piece canoe fits in the plane and likewise makes possible not a bad division of labor over a 5-mile portage

Jan 1, 1933

By Charles W. Sweetwood

THE Western phosphate field, virtually ignored for 40 years, has been undergoing a rapid climb to economic importance. Until World War II there seemed to be no reason for developing the phosphate rock region of the Intermountain Empire. But the tremendously increased demand for food production and the needs of many branches of the chemical industry changed all that. Quite suddenly a report made by the U. S. Geological Survey at the turn of the century became important. The survey showed that 60 pet of the nation&apos;s phosphate reserves were in the western phosphate field. Simplot Fertilizer Co. was one of the first to become actively interested in the development of the area. In August, 1945 the company began exploration of the Phosphoria Formation on the Fort Hall Indian Reservation. The result was the Gay Mine, about 18 miles east of Indian Agency Headquarters at Fort Hall, Idaho, developed to supply high grade phosphate rock for processing into superphosphate fertilizer at the company&apos;s Pocatello plant. Six ft of high grade oolitic phosphate rock (ranging from 32.5 to 34.5 pet P2O5) were discovered at the base of the Phosphoria Formation by diamond drilling and dozer trenching. High quality and thickness, plus the fact that the formation lay flat and near the surface made strip and open pit mining possible. In one year of mining, starting June 1946, a total of 53,000 tons of main bed oolitic phosphate rock was hauled to Pocatello for processing into supersulphate. The first year&apos;s operation was in

Jan 1, 1952

By A. U. Seybolt, D. H. Haman

The rate of oxidation of the lowest nitride of chromium, Cr2N, was measured to be equal to the rate of oxidation of chromium metal. It was found that, while the presence of Cr2N in chromium does not affect the oxidation mechanism, a long exposure at high temperature affects the morphology of Cr2N in chromium, causing a massive internal nitriding along chromium pain boundaries. Marker expen&apos; -ments showed that the rate of oxidation of Cr2N layers on chromium is determined by the rate of chromium diffusion through Cr,03. The rate of formation of Cr2N is determined by diffusion rate of nitrogen through Cr2N. This rate at 1000°C is around thirty times faster than the rate of oxiahtion. Evidence is presented which suggests that nitrogen from the air reaches the chromium through the Cr2O9 by migration through pores or cracks rather than by a diffusive process. IT has long been recognized that, when chromium or alloys containing substantial amounts of chromium are oxidized in air, some chromium nitride (Cr2N) is formed under the oxide scale. Although the presence of this nitride layer has often been described, there appears to have been no systematic study of the role played by the nitride during the oxidation process. Indeed, there have been conflicting re-ports&apos;92 on the kinetics of oxidation of chromium and chromium alloys in air and in oxygen. However, it is now well-established&apos;-5 that the rate-controlling process during the parabolic oxidation of chromium to Cr2O3 is chromium-ion diffusion through Cr2O3. Because of the importance of chromium-containing alloys as oxidation-resistant materials, it seemed desirable to investigate the behavior of chromium during oxidation with and without the presence of chromium nitride. Since a semicontinuous Cr2N layer forms relatively early during the oxidation of chromium in the air, chromium atoms must either pass out of or through the Cr2N layer to become incorporated in the growing Cr2O3 scale. Therefore, it seemed desirable to examine the oxidation behavior of the pure nitride. MATERIALS AND EXPERIMENTAL PROCEDURE The chromium used in this investigation consisted of slices of an ingot made from "five-nine" iodide chromium which had been argon-atmosphere melted in a Y2O 3-stabilized ZrO2 crucible in an induction furnace. The only impurity of any significance was 625 ppm of 0, which was usually reduced to a microscopically invisible amount by hydrogen annealing at 1400°C. However, one sample of chromium was used with the as-cast oxygen level as explained below. The samples were used after abrading through 600 Sic paper and then washing in toluene and alcohol. Both nitriding and oxidation experiments were performed in a vertical tube furnace connected to a glass vacuum system. &apos;This system was equipped with pressure measuring instruments for the range of 10 p to 1 atm, and a cartesian-diver pressure-control device was used in conjunction with a needle valve to allow control of pressure in the range of about 10 to 760 mm. The nitrogen or hydrogen gas was purified by passing through hot copper chips at 600°C, anhydrous calcium sulfate (Drierite), and liquid nitrogen. Oxygen gas was dried through the Drierite column and a dry-ice trap (-78°C). Changes in specimen weight were followed by a Pyrex helix used in conjunction with a cathetometer which could reproducibly be read to +0.001 cm, yielding an accuracy of about +0.2 mg. The spring was maintained in the cool upper part of the furnace tube where the temperature did not rise above about 35°C. The nitride in equilibrium with metallic chro-

Jan 1, 1964

By Rizo-Pairón Alfonso, A. M. Gaudin

PREVIOUS studies of activation in flotation have directed attention to the action of the activator on the mineral to be floated rather than to the relationship of the activator to the collector The latter phase of the problem, however, seems to have definite scientific, if not also practical, interest In the investigation reported in this paper, experiments were carried out, largely with quartz as subject, barium as activator, and oleate as collector The results obtained indicate that a I I ratio of collector ion to activator ion gives optimum results, and that a 2 I ratio almost fails to achieve activation and flotation Yet, a 2 I ratio would have been expected on stoichiometric grounds, had the coating been a normal salt of the activator ion with the collector ion, since barium is a divalent cation and oleate a monovalent anion To interpret and rationalize the observations, considerations of the crystal chemistry of quartz are helpful The point of view to which these considerations lead may be of general applicability to systems involving suspensions of solids in liquids, they confirm that an adsorbed coating is inescapable APPARATUS AND SUPPLIES The experimental work consisted in barium-ion abstraction tests, hydrogen-ion and hydroxyl-ion abstraction tests, flotation tests, and determinations of the surface of the crushed quartz The flotation machine was built according to the design of D W McGlashan It consists of a drill press in which the bit has been replaced by a stainless-steel impellor surrounding a stainless-steel stator, as in the Fagergren laboratory machine The air intake is controlled by a valve, and the cell consists of a beaker The quartz was obtained from vein quartz stored in large chunks It was first crushed to 20 mesh, then sized on a 28-mesh screen The 20 to 28-mesh size alone was retained for use This size was freed of coarse iron by passage through a Ball-Norton magnetic separator, bleached with boiling hydrochloric acid to remove residual abraded iron, washed with distilled water until the washings were thoroughly free of ferrous, ferric, and excess hydrogen ion, and stored in covered Pyrex beakers under water until used The barium was used as barium chloride, Baker&apos;s analyzed C P The oleate was used as sodium oleate It was prepared from sodium hydroxide, Baker&apos;s analyzed C P , and oleic acid purified by R R de Arellano3 in the laboratories at the Massachusetts Institute of Technology The purification procedure was elaborated from the recent researches of Brown and Shinowara 2 It consisted in (I) saponification of olive oil with potassium

Jan 1, 1942

By Alfonso Rizo-Patrón, A. M. Gaudin

PREVIOUS studies of activation in flotation have directed attention to the action of the activator on the mineral to be floated rather than to the relationship of the activator to the collector. The latter phase of the problem, however, seems to have definite scientific, if not also practical, interest. In the investigation reported in this paper, experiments were carried out, largely with quartz as subject, barium as activator, and oleate as collector. The results obtained indicate that a I : I ratio of collector ion to activator ion gives optimum results, and that a 2:I ratio almost fails to achieve activation and flotation. Yet, a 2:I ratio would have been expected on stoichiometric grounds, had the coating been a normal salt of the activator ion with the collector ion, since barium is a divalent cation and oleate a monovalent anion. To interpret and rationalize the observations, considerations of the crystal chemistry of quartz are helpful. The point of view to which these considerations lead may be of general applicability to systems involving suspensions of solids in liquids; they confirm that an adsorbed coating is inescapable. APPARATUS AND SUPPLIES The experimental work consisted in barium-ion abstraction tests, hydrogen-ion and hydroxyl-ion abstraction tests, flotation tests, and determinations of the surface of the crushed quartz. The flotation machine was built according to the design of D. W. McGlashan.* It consists of a drill press in which the bit has been replaced by a stainless-steel impellor surrounding a stainless-steel stator, as in the Fagergren laboratory machine. The air intake is controlled by a valve, and the cell consists of a beaker. The quartz was obtained from vein quartz stored in large chunks. It was first crushed to 20 mesh, then sized on a 28-mesh screen. The 20 to 28-mesh size alone was retained for use. This size was freed of coarse iron by passage through a Ball Norton magnetic separator, bleached with boiling hydrochloric acid to remove residual abraded iron, washed with distilled water until the washings were thoroughly free of ferrous, ferric, and excess hydrogen ion, and stored in covered Pyrex beakers under water until used. The barium was used as barium chloride, Baker&apos;s analyzed C. P. The oleate was used as sodium oleate. It was prepared from sodium hydroxide, Baker&apos;s analyzed C. P., and oleic acid purified by R. R. de Arellano3 in the laboratories at the Massachusetts Institute of Technology. The purification procedure was elaborated from the recent researches of Brown and Shinowara.2 It consisted in: (I) saponification of olive oil with potassium

Jan 1, 1942

By W. C. Knoblaugh

ROTARY kilns are adaptable to many fuels, but this paper deals principally with the use of powdered coal. The observations and conclusions presented are based on rotary kilns used in the manufacture of basic refractories for steel furnaces. Solid fuels are pulverized for two principal reasons: (I) ease of control, and (2) rapidity of combustion. By the use of pulverized coal, the operator can increase or decrease the fuel supply by small increments and with very little time lag between the change of control and the resultant change in the flame. This is extremely important in this type of furnace, as the temperature range for maturing the clinker is very narrow. By fine grinding, it is possible to increase the rate of burning of the coal, thereby liberating great quantities of heat within a small space in a short time. Under given conditions, temperature is a measure of the heat liberated per unit of time. To attain the temperatures of 2950° to 3150°F., which are encountered in the manufacture of various steel-furnace refractories, it is estimated that it is necessary to liberate 125,000 to I75,000 B.t.u. per cubic foot of the burning zone per hour. The manufacture of dolomitic refractories is a ceramic process and, as is true in most such processes, the material must be subjected to a certain critical temperature for a certain length of time in order to complete the reaction. If the time of reaction is reduced, the temperature must be increased; in other words, if the rate at which the material flows through the hot zone of the kiln is increased, the temperature of the hot zone must be increased to compensate for this shorter exposure to the flame. FIRING WITH PULVERIZED COAL Fig. I is a line drawing of a rotary kiln with the attendant equipment indicated in their relative positions. The kiln proper consists of a sloping, refractory-lined steel tube rotating slowly about its longitudinal axis (0.75 r.p.m.), and is countercurrent in operation in that the raw feed is introduced at the stack end and gradually approaches the zone of highest temperature at the lower end, where the fuel is introduced. Before 1930, the usual method of firing a rotary kiln was to store the coal in the pulverized form and then feed from this storage to the kiln as needed. This proved unsatisfactory and dangerous because of dust explosions and the inability to obtain an even feed to the kiln caused by arching of the coal in storage and flooding of the coal feeders. In later years the practice has been to store the raw coal and grind it as it is needed. Such a layout is indicated in Fig. I. The coal is stored in bins, charged from the top and drawn from the bottom into recording scales and then into some type of unit pulverizer. There are a number of good pulverizers on the market, each incorporating features that the manufacturer considers outstanding.

Jan 1, 1946

By J. I. Paige, T. T. Campbell, A. W. Henderson, H. M. Harris

The chlorination of ilmenite concentrates and slags to produce Tic14 suitable for pigment or metal production was investigated by the Bureau of Mines along with the dechlorination of byproduct iron chloride to produce chlorine for recycle and iron oxide., Ilmenite concentrates or slag powders were fed into the bottom of a fluidized coke bed at 1,050º C using chlorine flow rates up to 20 l/min in a 10.2-cm-dim reactor. Tests showed that >95 percent of the various ilmenite concentrates reacted at optimum conditions, and recovery of TiC14 ranged from 95 to 100 percent of stoichiometric. Impurity dusts were removed from the vapors by cyclones and a fiberglass cloth filter. Iron chloride was condensed as a powder with less than 0.4 percent insoluble material. The TiC14 was collected in refrigerated condensers. Iron chloride was dechlorinated at 500º to 550º C by reaction with oxygen in a 16.5-cm-dim reactor using a fluidized bed of Fe2O3. Optimum processing was attained with a FeC13 feed containing 25 wt-pct Fe203 granules treated with 2 wt-pct NaCl catalyst; Under the above conditions, off gas chlorine concentrations of 62 to 90 wt-pct were obtained. During 2- and 3-day tests with technical-grade FeC13, conversion of FeC13 was 94 to 97 percent, chlorine concentrations were 76 to 90 wt-pct, and up to 92 pct of the stoichio- metric Fe203 was removed in the primary reactor discharge. Chlorine

Jan 1, 1976

Joseph HartshoRnE, Pottstown, Pa.: I have read Professor Akerman&apos;s valuable paper with great interest. Few of the present generation of American steel metallurgists are aware of the very important part taken by Swedish engineers in the successful development of the Bessemer proeess, and I am afraid some of the older ones have forgotten it. Certainly, I think, most of us would have said that Terre Noire was the first to introduce the use of metal direct from the blast-furnace. It is very well, therefore, that honor should be given to whom honor is due. I can speak from personal experience upon one part only of Prof. Akerman&apos;s paper; namely, the effect of the temperature at which the molten metal is cast upon the quality of the finished steel. In a general way I have, of course, known for a long time that the

Jan 1, 1894

By R. B. Sosman, J. C. Hostetter

It is well known that ferric oxide, Fe2O3, is paramagnetic, while magnetite, Fe3o4, is classed among the highly ferromagnetic substances. But magnetic data on oxides intermediate in composition between Fe2o3 and Fe3O4 have been almost completely lacking. Fe2O3 and Fe3O4 form a solid-solution series, according to present evidence.&apos; In this series the properties change continuously from Fe2O3 toward Fe3O4, as the percentage of FeO increases from zero toward 31.03, which is the percentage in magnetite. It is possible that there is a break in the series near Fe3O4, but it has not yet been possible to establish the existence of such a break experimentally. The occurrence of solid solution in this series is shown by the dissociation pressure, or oxygen pressure in equilibrium with the oxides, which falls continuously over the range from Fe2O3 to Fe3O4. The oxygen-pressure curves at 1100" and 1200" are shown in Fig. 1. The existence of solid solution is also demonstrated by the continuous change in optical properties from Fe2O3 over to a composition containing about 18 per cent. FeO, at which point the opacity of the oxide becomes so great that it is impossible to obtain measurements at higher percentages of ferrous iron. Natural oxides of iron intermediate in composition between Fe2O3 and Fe3O4 are much more common than is generally supposed. If a mineral oxide is not strongly attracted by a small hand magnet and if it gives a red streak, it is usually labeled "hematite." If it is strongly attracted by the hand magnet it is usually labeled "magnetite" without further tests. As we shall show later, oxides containing from 1 up to 31 per cent. FeO can be thus erroneously lumped together as "magnetite." It is a fact, nevertheless, that the great bulk of natural oxides of iron lie fairly near either Fe2O3 or Fe3O4 in composition. The reason will be

Jan 1, 1918