Search Documents

By R. K. McGeary, B. Lustman

The textures produced in zirconium by cold and hot rolling, and by recrystallization above and below the transformation temperature were determined. Thermal expansivities were measured in the thickness, transverse, and rolling directions of preferentially oriented zirconium and were correlated with the texture scatter in these directions. REVIOUS investigations have indicated that minor differences between hexagonal close-packed metals of similar axial ratio may appear with respect to the textures produced both on cold rolling and on subsequent recrystallization. In the case of magnesium, beryllium, and titanium, metals of axial ratio similar to that of zirconium, the ideal orientations produced by rolling are fundamentally the same, although marked variance is reported in the degree and type of scatter about the mean orientation; in those instances where recrystallization textures were observed, they were reported to be similar to the rolling textures. Measurement of the anisot-ropy of thermal expansion of both rolled and re-crystallized zirconium could not be correlated satisfactorily with the textures reported for the above metals, and therefore a study was made of the preferred orientations produced in zirconium. Reported below are the textures produced in zirconium by cold and hot rolling, and recrystallization above and below the transformation temperature, together with the results of thermal expansion measurements. Determination of Preferred Orientation Two types of zirconium were investigated: 1— "crystal bar" zirconium obtained from the Foote Mineral Co., produced by the thermal decomposition of zirconium tetraiodide, and 2—zirconium ingot obtained from the Bureau of Mines prepared by melting sponge zirconium in a graphite resistor vacuum furnace in a graphite crucible. The major impurities present in the two materials used are listed in Table I. Several of the pole figures were later checked with 0.03 pct hafnium crystal bar material and the results were identical with those to be shown for the 1.5 pct hafnium material. The materials were cold rolled to 0.014 in. in thickness as shown in Table 11. Specimens were cut from the 0.014 in. thick rolled sheets and etched to thicknesses of 0.002 to 0.010 in. Such specimens were used for exposures up to a 50' to 60" angle between the beam and plane of the specimen; for higher angles a wire shape, similar to that described by Bakarian,' was formed on an end of the original 0.014 in. sheet. A fine-bladed abrasive cut-off wheel was used to slot the sheet and to form the cylindrical cross-section. The wire shaped ends were then etched to 0.006 to 0.010 in. in diam. Although absorption of X-rays in the wire-shaped specimens does not vary with angle of rotation, the line width around the diffraction rings was not uniform, because the wire was narrower than the X-ray beam, and this condition caused some uncertainty in the estimation of azimuthal intensities. Furthermore, scanning was not practicable with this type of specimen so that spottiness of the rings due to large grain size was excessive for specimens which had been heated above about 650°C. Nevertheless, satisfactory information could be obtained for high angle exposures from the negatives by the use of both types of specimens. Transmission Laue photograms were taken using unfiltered molybdenum radiation (47.5 kv, 18 ma) and a 0.025 in. pinhole. With the film 8 cm from a 0.005 in. thick specimen exposures of about 30 min were adequate. For specimens with a coarse grain size, a device that scanned about 0.15 sq in. of sheet surface was used. An attempt was made to plot the pole figures by use of an X-ray spectrometer as described by Norton.' However, for the particular technique used, the intensity variations obtained were not considered definite enough to give reliable results, especially for the large grained recrystallized and transformed specimens. This method was therefore abandoned in favor of the standard photographic method. Nine exposures were taken of each specimen: seven exposures with the beam perpendicular to the rolling direction and at 0°, 10°, 20°, 35", 50°, 65", and 80" to the transverse direction, and two exposures with the beam perpendicular to the transverse direction and at 60" and 80" to the rolling direction. Additional exposures were then made where necessary. The intensity variations of the diffraction rings were estimated by eye. It was usually possible to estimate 3 degrees of intensity from the photograms but in some cases 2, 4, or 5 degrees were estimated. Experimental Results The preferred orientation was determined for the following treatments: 1—cold-rolled, 2—low temperature rolled, 3—cold-rolled surface layer, 4— cross-rolled, 5—hot-rolled, 6—recrystallized below the transformation temperature, and 7-—recrystallized above the transformation temperature. I—Cold-Rolled Textures: The slip plane in hexag-

Jan 1, 1952

Jan 1, 1968

By C. D. Thurmond

Jan 1, 1968

Jan 1, 1968

By R. Shuttleworth, R. Smith

A Knudsen effusion tnethod I~as been used lo measure the vapor pressure of pure iron in the temperature range 1000° to 1500°C. Neutron-irradiated , natural iron was used and the Mn'~proclzdced by the (n, p) reaction removed by evaporation at high temperature. The results can be represented by the equation: where pM - 1.088 x 107 atm and T, = 20,890°K. A value of 100.2 kcal per g- atom was obtained for AH;. THE vapor pressure of pure iron in the temperature range 1000" to 1500°C has been measured. Radioactive iron and a Knudsen cell technique were used and the Mn' produced by an (n, p) reaction removed by evaporation at high temperature. From the variation of vapor pressure with temperature values of the enthalpy and entropy of solid iron have been found. Previous workers2 used a Lang-muir method and measurements were made over a smaller temperature range than that in this work. EXPERIMENTAL The apparatus used was similar to that of Pyle and Shuttleworth, and McLellan and Shuttle worth. However, because of the higher temperatures the Knudsen cell was machined from tungsten bar and the flanged furnace tube was beryllia. Heating was by passing a high current (70 amp at 7 v for 1500°K) through a strip of tantalum foil laid across the top of the cell and through a turn of molybdenum wire around the furnace tube. This method of heating ensured that the top of the cell was slightly hotter than the base and prevented condensation and re-evaporation from the orifice. The temperature was measured by means of a pt/Pt 13 pct Rh thermocouple spot-welded to the base of the crucible. To ensure accurate temperature measurement the iron was in the form of a thin disc (0.75 cm diam by 0.075 cm) which lay on the base of the cell. The high-purity iron was irradiated in the Harwell pile for a week at a neutron flux of 1.2 X 10" neutrons per sq cm per sec. The isotopes fe'~ and Fe" are produced by (n! y) reactions but only Fe", half-life 45.1 days, is a emitter; Mn which is also a y emitter, half-life 300 days, is produced simultaneously by an (n,p) reaction.' Immediately after irradiation of natural iron the ratio of ~e" to Mn y activity was 100:l. However, manganese is very much more volatile than iron and almost all the y activity of the condensate is due to Mn'~. Thus it was essential to eliminate all the manganeses before any measurement of the vapor pressure of iron was made and this was done by preliminary heating for 20 hr at 1400°C. For each determination the iron was dissolved from the target with acid and the y activity compared to a known weight of iron. By means of a y-ray spectrometer the y-activity measurements were made at the 1.09-mev peak of the 17e5' spectrum where the background was of the order of 3 cpm. Despite the low specific activity of ~e" a mass of 10- " g of iron could be determined corresponding to a vapor pressure of about l0-'' atm. RESULTS The vapor pressures were calculated from the equation: Where m is the mass of iron effusing in a time t through an orifice of area a2, r is the radius of the target, Z is the distance from the orifice to the

Jan 1, 1965

By R. C. Canby

The difficulty of exact neutralization by ammonia of the acid solution obtained in the determination of arsenic by the method of fusion with carbonate of soda and nitrate of potassium, led me to try the effect of neutralization by oxide of zinc. I obtained most satisfactory results, and found a great saving of time. The oxide of zinc being added in excess, there is no delicate testing with lit? mils paper and tedious alternate adding of dilute ammonia arid acid until the proper point is reached. The excess of oxide of zinc, too, seems to hold, from the filter, the gelatinous silica and alumina, which are usually precipitated upon neutralization, and thus to render the washing of the precipitated arseniate of silver almost invariably much more rapid. Except the substitution of the neutralization by oxide of zinc for the more tedious method by ammonia, the details of the process are practically the same as those published by Mr. Richard Pearce, of Argo, Colorado (Proceedings of the Colorado Scientific Society, vol. i.), who shows what very accurate results can be obtained by the fusion process. I have made numerous tests of comparison between the two methods of neutralization, and find that those by the oxide of zinc agree almost exactly with the old method. Increasing the quantity of nitric acid, even to considerable excess, to be neutralized by the oxide of zinc did not affect the precipitation of arseniate of silver. The process may be outlined as follows : Take 4 to 1 gramme finely pulverized ore, and mix in a porcelain crucible with eight to ten times its weight of a mixture of equal parts of carbonate of soda and nitrate of potassium (Kerl. Metallurgische Probirkunst gives 4 to 5 nitre to 14 soda). Gradually bring to fusion and keep so, three to five minutes. Cool. Disintegrate in hot water. Filter and wash with hot water. Acidify the filtrate with nitric acid, and boil to expel carbonic acid and nitrous fumes. Cool. Add an excess of an emulsion of oxide of zinc. The bottom of the beaker should have quite a layer of oxide of zinc, after stirring.

Jan 1, 1889

By Shiou-Chuan Sun

THIS paper presents the design and operation of a frothmeter capable of measuring the frothing characteristics of pine oils and other frothing reagents. The experimental data show that the frothability of pine oil is governed by: 1-rate of aeration, 2-time of aeration, 3-height of liquid column, 4-chemical composition of pine oil, 5-pH value of solution, 6-temperature of, solution, and 7-concentration of pine oil in solution. The effect of mineral particles on the behavior of froth also was studied, and the results can be found in a separate paper.1 The results also show that the relative frothabilities of pine oils in the frothmeter generally correlate with those in actual flotation, provided that other factors are kept constant. In addition to pine oils, the other well-established flotation frothers were tested, and the results are included. In this paper, compressed air frothing is the frothing process performed by means of purified compressed air, whereas sucked air frothing is the frothing process accomplished by purified air sucked into the glass cylinder by a vacuum system. The term vacuum frothing denotes that froth was formed by degassing of the air-saturated liquid under a closed vacuum system. Apparatus The frothmeter, shown in Fig. 1, is capable of reproducibly measuring the volume and persistence of froth as well as the volume of air bubbles entrapped in the liquid and is capable of being used for compressed air frothing, sucked air frothing, and vacuum frothing. Fig. la shows that for compressed air frothing, the apparatus consists of an airflow regulating system, 1-3; a purifying and drying system, 4-8; a standardized flowmeter to measure the rate of airflow from zero to 500 cc per sec, 9; and a graduated glass cylinder, 13; equipped with an air regulating stopcock, 10; an air chamber, 11; and a fritted glass disk to produce froth, 12. The fritted glass disk, 5 cm in diam and 0.3 cm thick, has an average pore diameter of 85 to 145 microns. The pyrex glass cylinder has a uniform ID of 5.588 cm and an effective height of 63 cm. The inside cross-sectional area of the glass cylinder was calculated to be 24.53 sq cm, or 3.8 sq in. For sucked air frothing, Fig. lb shows that the apparatus for compressed air frothing is used again, with the following modifications: 1-compressed air and its regulating system, 1-3, are eliminated; and 2-a vacuum system, 16, equipped with a vapor trap, 15, and a vacuum manometer, 17, is added. The vacuum system can be .either a water aspirator or a laboratory vacuum pump. Any desired rate of airflow can be drawn into the glass cylinder, 13, by adjusting the opening of the air regulating stopcock, 10. The sucked air stream is cleaned by the purifing and drying system, 4-8, before entering the glass cylinder, 13. When this setup is used for vacuum frothing, the air regulating stopcock is closed. The frothmeter has been used for almost 3 years and has proved to give reproducible results, as illustrated in Table I. With a magnifying glass and suitable illumination, the frothmeter also can be used to study the attachment of air bubbles to coarse mineral particles.2 Experimental Procedures Except where otherwise stated, the data presented were established by means of the compressed air method. The volume and persistence of froth were recorded respectively at the end of 4 and 6 min of aeration at a constant rate of airflow of 29.3 cc per sec which is equivalent to 71.6 cc per sq cm per min, or 462.6 cc per sq in. per min. The aqueous solution for each test, containing 1000 cc of distilled water and 19.2 ± 0.5 mg frothing reagent, was adjusted to a pH of 6.9 ± 0.2. The volume of froth is expressed as cubic centimeter per square centimeter and is equivalent to the height of the froth column (the distance between the bottom and the meniscus of the froth). The volume of froth was obtained by multiplying the height of froth by the cross-sectional area of the glass cylinder, 24.53 sq cm. Before each test, the glass cylinder, 13, was cleaned thoroughly with jets of tap water, ethyl alcohol, tap water, cleaning solution, tap water, and finally distilled water. The cylinder with stopcock,

Jan 1, 1952

By Shiou-Chuan Sun

THIS paper presents the design and operation of a frothmeter capable of measuring the frothing characteristics of pine oils and other frothing reagents. The experimental data show that the froth-ability of pine oil is governed by: 1—rate of aeration, 2—time of aeration, 3—height of liquid column, 4—chemical composition of pine oil, 5—pH value of solution, 6—temperature of solution, and 7—concentration of pine oil in solution. The effect of mineral particles on the behavior of froth also was studied, and the results can be found in a separate paper.' The results also show that the relative froth-abilities of pine oils in the frothmeter generally correlate with those in actual flotation, provided that other factors are kept constant. In addition to pine oils, the other well-established flotation frothers were tested, and the results are included. In this paper, compressed air frothing is the frothing process performed by means of purified compressed air, whereas sucked air frothing is the frothing process accomplished by purified air sucked into the glass cylinder by a vacuum system. The term vacuum frothing denotes that froth was formed by degassing of the air-saturated liquid under a closed vacuum system. Apparatus The frothmeter, shown in Fig. 1, is capable of re-producibly measuring the volume and persistence of froth as well as the volume of air bubbles entrapped in the liquid and is capable of being used for compressed air frothing, sucked air frothing, and vacuum frothing. Fig. la shows that for compressed air frothing, the apparatus consists of an airflow regulating system, 1-3; a purifying and drying system, 4-8; a standardized flowmeter to measure the rate of airflow from zero to 500 cc per sec, 9; and a graduated glass cylinder, 13; equipped with an air regulating stopcock, 10; an air chamber, 11; and a fritted glass disk to produce froth, 12. The fritted glass disk, 5 cm in diam and 0.3 cm thick, has an average pore diameter of 85 to 145 microns. The pyrex glass cylinder has a uniform ID of 5.588 cm and an effective height of 63 cm. The inside cross-sectional area of the glass cylinder was calculated to be 24.53 sq cm, or 3.8 sq in. For sucked air frothing, Fig. lb shows that the apparatus for compressed air frothing is used again, with the following modifications: 1—compressed air and its regulating system, 1-3, are eliminated; and 2—a vacuum system, 16, equipped with a vapor trap, 15, and a vacuum manometer, 17, is added. The vacuum system can be either a water aspirator or a laboratory vacuum pump. Any desired rate of airflow can be drawn into the glass cylinder, 13, by adjusting the opening of the air regulating stopcock, 10. The sucked air stream is cleaned by the purifying and drying system, 4-8, before entering the glass cylinder, 13. When this setup is used for vacuum frothing, the air regulating stopcock is closed. The frothmeter has been used for almost 3 years and has proved to give reproducible results, as illustrated in Table I. With a magnifying glass and suitable illumination, the frothmeter also can be used to study the attachment of air bubbles to coarse mineral particles.' Experimental Procedures Except where otherwise stated, the data presented were established by means of the compressed air method. The volume and persistence of froth were recorded respectively at the end of 4 and 6 min of aeration at a constant rate of airflow of 29.3 cc per sec, which is equivalent to 71.6 cc per sq cm per min, or 462.6 cc per sq in. per min. The aqueous solution for each test, containing 1000 cc of distilled water and 19.2 ± 0.5 mg frothing reagent, was adjusted to a pH of 6.9 0.2. The volume of froth is expressed as cubic centimeter per square centimeter and is equivalent to the height of the froth column (the distance between the bottom and the meniscus of the froth). The volume of froth was obtained by multiplying the height of froth by the cross-sectional area of the glass cylinder, 24.53 sq cm. Before each test, the glass cylinder, 13, was cleaned thoroughly with jets of tap water, ethyl alcohol, tap water, cleaning solution, tap water, and finally distilled water. The cylinder with stopcock,

Jan 1, 1953

By Shiou-Chuan Sun

THIS paper presents the design and operation of a frothmeter capable of measuring the frothing characteristics of pine oils and other frothing reagents. The experimental data show that the froth-ability of pine oil is governed by: 1—rate of aeration, 2—time of aeration, 3—height of liquid column, 4—chemical composition of pine oil, 5—pH value of solution, 6—temperature of solution, and 7—concentration of pine oil in solution. The effect of mineral particles on the behavior of froth also was studied, and the results can be found in a separate paper.' The results also show that the relative froth-abilities of pine oils in the frothmeter generally correlate with those in actual flotation, provided that other factors are kept constant. In addition to pine oils, the other well-established flotation frothers were tested, and the results are included. In this paper, compressed air frothing is the frothing process performed by means of purified compressed air, whereas sucked air frothing is the frothing process accomplished by purified air sucked into the glass cylinder by a vacuum system. The term vacuum frothing denotes that froth was formed by degassing of the air-saturated liquid under a closed vacuum system. Apparatus The frothmeter, shown in Fig. 1, is capable of re-producibly measuring the volume and persistence of froth as well as the volume of air bubbles entrapped in the liquid and is capable of being used for compressed air frothing, sucked air frothing, and vacuum frothing. Fig. la shows that for compressed air frothing, the apparatus consists of an airflow regulating system, 1-3; a purifying and drying system, 4-8; a standardized flowmeter to measure the rate of airflow from zero to 500 cc per sec, 9; and a graduated glass cylinder, 13; equipped with an air regulating stopcock, 10; an air chamber, 11; and a fritted glass disk to produce froth, 12. The fritted glass disk, 5 cm in diam and 0.3 cm thick, has an average pore diameter of 85 to 145 microns. The pyrex glass cylinder has a uniform ID of 5.588 cm and an effective height of 63 cm. The inside cross-sectional area of the glass cylinder was calculated to be 24.53 sq cm, or 3.8 sq in. For sucked air frothing, Fig. lb shows that the apparatus for compressed air frothing is used again, with the following modifications: 1—compressed air and its regulating system, 1-3, are eliminated; and 2—a vacuum system, 16, equipped with a vapor trap, 15, and a vacuum manometer, 17, is added. The vacuum system can be either a water aspirator or a laboratory vacuum pump. Any desired rate of airflow can be drawn into the glass cylinder, 13, by adjusting the opening of the air regulating stopcock, 10. The sucked air stream is cleaned by the purifying and drying system, 4-8, before entering the glass cylinder, 13. When this setup is used for vacuum frothing, the air regulating stopcock is closed. The frothmeter has been used for almost 3 years and has proved to give reproducible results, as illustrated in Table I. With a magnifying glass and suitable illumination, the frothmeter also can be used to study the attachment of air bubbles to coarse mineral particles.' Experimental Procedures Except where otherwise stated, the data presented were established by means of the compressed air method. The volume and persistence of froth were recorded respectively at the end of 4 and 6 min of aeration at a constant rate of airflow of 29.3 cc per sec, which is equivalent to 71.6 cc per sq cm per min, or 462.6 cc per sq in. per min. The aqueous solution for each test, containing 1000 cc of distilled water and 19.2 ± 0.5 mg frothing reagent, was adjusted to a pH of 6.9 0.2. The volume of froth is expressed as cubic centimeter per square centimeter and is equivalent to the height of the froth column (the distance between the bottom and the meniscus of the froth). The volume of froth was obtained by multiplying the height of froth by the cross-sectional area of the glass cylinder, 24.53 sq cm. Before each test, the glass cylinder, 13, was cleaned thoroughly with jets of tap water, ethyl alcohol, tap water, cleaning solution, tap water, and finally distilled water. The cylinder with stopcock,

Jan 1, 1953

By A. Lee Barrett

SO commonplace that they are seldom noticed, mining-machinr, bits have a definite and important bearing on the cost of coal production. At the average mine many thousands of bits are used during the year. The actual cost represented by the purchase of the bits used, as well as that of sharpening and handling them, represents a considerable sum of money. From the point of view of indirect costs they are important, as the lack of good bits at a mining machine can seriously impair production. Good bits tend to ensure an adequate supply of coal. Classes OF Bits Mining-machine bits may be divided into three general classes, based on shape and method of use: (I) chisel, (2) pick-point and (3) one-use. The chisel and pick-point bits are shown in Fig. I. The so-called "chisel" bits were made of steel of various sizes and were sharpened to a wide chisel cutting edge. Few of this type of bit are used, except in places where coring is very bad. Sometimes chisel bits are used with standard bits to help cut out the core. The "pick-point" bit is widely used today. Normally it is made from ½ by I-in. steel, is about 4½ in. long when new, has a rake angle of about 25°, a front clearance of about 23O, a side clearance of approximsteji 8".' There are many variations in the shape of this bit, depending on the ideas of the individual that may be dressing the dies of the bit machine. This bit has been generally used for many years and at present, in one form or another, is by far the most popular bit used in coal mines. This bit usually is made from 0.85 carbon steel, although in recent years some alloy-steel bits have made their appearance. At present, carbon-steel bits are frequently tipped in. hard facing materials. A third class of bits might be called the L'one-use" bit; that is, a small bit that is used once and then thrown away. These bits have two or three points, are usually made from 0.85 carbon steel and sometimes from higher alloys. Recently some. of them have been tipped with hard facing material. Most of them were used at first with special

Jan 1, 1942

By A. Lee Barrett

SO commonplace that they are seldom noticed, mining-machinr, bits have a definite and important bearing on the cost of coal production. At the average mine many thousands of bits are used during the year. The actual cost represented by the purchase of the bits used, as well as that of sharpening and handling them, represents a considerable sum of money. From the point of view of indirect costs they are important, as the lack of good bits at a mining machine can seriously impair production. Good bits tend to ensure an adequate supply of coal. Classes OF Bits Mining-machine bits may be divided into three general classes, based on shape and method of use: (I) chisel, (2) pick-point and (3) one-use. The chisel and pick-point bits are shown in Fig. I. The so-called "chisel" bits were made of steel of various sizes and were sharpened to a wide chisel cutting edge. Few of this type of bit are used, except in places where coring is very bad. Sometimes chisel bits are used with standard bits to help cut out the core. The "pick-point" bit is widely used today. Normally it is made from ½ by I-in. steel, is about 4½ in. long when new, has a rake angle of about 25°, a front clearance of about 23O, a side clearance of approximsteji 8".' There are many variations in the shape of this bit, depending on the ideas of the individual that may be dressing the dies of the bit machine. This bit has been generally used for many years and at present, in one form or another, is by far the most popular bit used in coal mines. This bit usually is made from 0.85 carbon steel, although in recent years some alloy-steel bits have made their appearance. At present, carbon-steel bits are frequently tipped in. hard facing materials. A third class of bits might be called the L'one-use" bit; that is, a small bit that is used once and then thrown away. These bits have two or three points, are usually made from 0.85 carbon steel and sometimes from higher alloys. Recently some. of them have been tipped with hard facing material. Most of them were used at first with special

Jan 1, 1942

By Joseph C. Kieffer

THE Duquesne property of the Callahan Zinc-Lead Co. is about 20 miles east of Nogales, in southern Arizona. One mine is near the mill, but most of the mill feed is hauled in by truck from a number of small mines. The same sulphides are found in all the ores, in general, but the amounts vary considerably. All ores contain silver, copper, lead and zinc minerals but one mine ships ore high in silver and lead and low in copper and zinc; while another mine ships ore high in copper and zinc, and low in silver and lead. The common sulphides are galena, carrying most of the silver; chalcopyrite; sphalerite, carrying iron in solid solution; and pyrite, in a gangue consisting of limestone, quartz and garnet. Mineralization, is fairly coarse. At the present grind of about 66 per cent minus 200 mesh most of the sulphides are liberated. A small amount of chalcopyrite is locked up with the sphalerite and cannot be liberated at an economic grind, and the copper carried into the zinc concentrate with the sphalerite accounts for the comparatively poor recovery of copper in the copper-lead concentrate. PRODUCTION OF TWO CONCENTRATES The milling problem, which was complicated by the extreme variation in the grade of the feed, was first attacked with the idea of producing a silver-copper-lead concentrate and a zinc concentrate, both with satisfactory grades and recoveries. By February 194I, it was felt that these objectives had been attained, when the grades of the various products and the recoveries were as shown in Table I. [ ] A rough outline of the flowsheet and reagents used is as follows: Minus ¾ -in. feed to a 7-ft. by 36-in. Hardinge ball mill working in closed circuit with a 36-in. Wemco classifier. The classifier overflow passes to the second cell of an 8-cell bank of No. I8 Special Denver Sub-A flotation machines (volume, 22.5 cu. ft. per cell). A rougher concentrate is removed from the second to the fifth cells inclusive, and returned to the first cell, which is the cleaner. A scavenger concentrate is removed from the sixth, seventh, and eighth cells, and returned to the third cell. Consump-

Jan 1, 1942

By R. S. Archibald, L. S. Chabot

The Blueberry mine is about 10 miles west of Ishpeming, Marquette County, Michigan. The property consists of about 2000 acres in sees. 3, 4 and 5, T. 47, N.R. 28W. and secs. 32, 33 and 34, T. 48, N.R. 28W., and, excepting one intervening 80-acre tract, contains the iron formation for a length of about 21/4 miles. The property is traversed by State Highway M-28 and is served by three railways, the Chicago & Northwestern, the Duluth, South Shore & Atlantic, and the Lake Superior & Ishpeming. The Northwestern transports the ore to a dock at Escanaba; the other railways, to Marquette. Ore for Chicago goes via Escanaba and that for Lower Lake ports, as Detroit, Cleveland, and Buffalo, via Marquette. History The presence of iron formation in this property has been known for many years, and mining operations on a small scale have been carried on intermittently. The Dexter mine, on the SE.1/4 of the NW.1/4 of sec. 3, was worked from 1883 to 1897 and 118,000 tons of ore was mined. From 1907 to 1915 extensive exploration was carried on over the whole of sec. 3, including 79 diamond-drill holes with a total footage of 26,000 ft. The Chase mine, on the NE.1/4 of the NE.1/4 of sec. 3, was developed from this exploration work, but after about 200,000 tons had been mined the property was abandoned. From 1908 to 1910 exploration was carried on by another company on sec. 4, 47-28, including four drill holes with a total footage of about 5000 ft. Much of the drilling on sec. 3 and of the exploration work on sec. 4 are within the present developed area of the Blueberry mine. A general campaign of diamond-drill exploration was undertaken in 1924, and within a year a considerable amount of ore was developed. The Ford Motor Co. then took an option on the property and carried on check drilling and diamond-drill work until the spring of 1926, when enough ore had been developed to warrant the sinking of a shaft

Jan 1, 1937

By H. R. Deeth, C. J. Koenig

ABOUT ten years ago nepheline syenite was introduced to the ceramic industry and the material has now found application in the various branches of the industry, namely, as a vitrifying agent in white-wares and as a source of alumina and alkalies in glasses, glazes, and porcelain enamels. Spence1 described the early mining and processing developments regarding this material. Since the time of his article many research papers have appeared relating to the usage of nepheline syenite but little has been published relative to subsequent mining and processing methods. A complete indexed review of the literature was issued recently by Ohio State University.2 Since "Lakefield" nepheline syenite from Blue Mountain, Ontario (Fig I); is the only commercial ceramic-grade nepheline syenite now being marketed on this continent, discussion is limited to this operation carried on by American Nepheline Limited, Lakefield, Ont., and its subsidiary in the United States, American Nepheline Corp. at Rochester, N. Y. THE DEPOSIT Blue Mountain is a long ridge rising to an elevation of about 350 ft at its highest point above the surrounding country and extending for about six miles in a northeasterly direction across Methuen township, Peterborough County. The rock of the Blue Mountain central alkaline intrusive is fine grained, light colored and of even granitic texture. The solidified mass consists predominately of the minerals albite, nepheline and microcline in order of abundance. The average mineralogical composition for the deposit obtained by a study of 112 samples taken regularly over the whole formation is as follows:3 [VOLUMETRIC MINERAL PER CENT Albite54 Microcline20 Nepheline22 Muscovite2 Mafics2 (Biotite, hastingsite, magnetite) Total100] The mineral nepheline (or nephelite) belongs to the feldspathoid group but is lower in silica content than are the feldspars. It is a silicate of soda, potash, and alumina (NaKAl2O32SiO2). Its presence with albite (Na2O A1203 6SiO2) and microcline (K20 A12O3 6SiO2) gives the Blue Mountain deposit an alkali content of 15 pct and an alumina content of approximately 24 pct. While this huge alkaline mass is somewhat variable mineralogically, it has a uniform chemical composition. When the iron, mostly in the form of magnetite, is removed during processing, a remarkably uniform finished product is obtained. Geological surveying has disclosed many million tons of nepheline syenite in the Blue Mountain deposit. Diamond drilling in the area where mining is now being carried out indicates a block of about one million tons.

Jan 1, 1947

By G. S. Ansell, J. Weertman

The creep behavior of an aluminum alloy hardened with a finely dispersed phase of aluminum oxide was investigated. The as-extruded alloy shows an approximate steady-state creep in which the creed rate depends exponentially on the applied stress. The activation energy of creeb is abbroximately 150,000 cal per mole. The recrystallized alloy shows no steady-state creep. ONE method of improving the creep resistance of a metal is to introduce a finely dispersed second phase into the metal matrix. The improvement of the creep resistance has been qualitatively explained by assuming that the dispersed second-phase particles act as obstacles to dislocation motion. If the main effect of second-phase particles is simply to hinder dislocation motion then it is possible to derive a high-temperature creep equation for a dispersion-hardened alloy in a straightforward manner. In the Appendix of this paper such an equation is derived from a creep model which works very well for pure metals. Recently, F. V. Lenel has fabricated, for the first time, powder extrusions of aluminum-aluminum oxide in a large-grained recrystallized form. This alloy, designated as MD 2100, consists of a fine dispersion of aluminum oxide plates in a matrix of commercial purity aluminum. A considerable amount of investigation has been carried out concerning the microstructure and physical properties of this alloy.&apos; ) The aluminum oxide is present in the form of flakes 130A units thick and 0.3 u on edge. They are dispersed in the aluminum matrix with an average spacing of approximately 0.5 jx. The spacing varies in the range of 0.05 to 1.5 µ. The alloy structure is extremely stable at high temperatures. For this reason the alloy offers a unique opportunity for a fundamental study of creep of a very finely dispersed two-phase alloy. Lenel supplied specimens in both the unrecrystallized and recrystallized condition. This paper reports high-temperature creep experiments carried out on these specimens. The results obtained were rather unexpected. No steady-state creep was observed in the recrys-tallized material. In fact, after some transient creep which takes place upon loading, the creep rate is essentially zero ( < 10-8per min). If the second-phase particles acted solely as obstacles to the motion of dislocations, measurable steady-state creep would be expected. Since none is observed it appears that the main effect of the fine dispersion in the recrystallized material is to inactivate the dislocation sources themselves, rather than hinder the motion of dislocation loops created at these sources. EXPERIMENTAL DETAILS Specimens were tested in wire form, 0.087 in. in diam for the as-extruded alloy, and 0.035 in. in diam for the recrystallized alloy. These samples were held in friction-type wire grips; a gage length of 2.5 cm was used for all the creep tests. The specimens were held at 600°C in the test apparatus for at least 15 hr prior to each test. The tests were run under the condition of constant loading and, since the creep strains were small, can be considered as constant stress tests. The temperature of testing was held constant within 3°C. Elongations were measured with an optical cathetometer which was capable of measuring strains as smaIl as 0.00012. This allowed the measurement of strain rates as low as l0-8&apos;per rnin. In addition to the creep tests optical micrographs were made in order to determine both the grain size and microstructure of these materials. RESULTS Fig. 1 shows a few typical creep curves obtained from the as-extruded material. The elongations were somewhat erratic, but each curve shows a region of quasi-steady-state creep from which an approximate steady-state creep rate can be obtained. In general the higher the stress at a given temperature, the greater the total elongation before fracture. The lower the applied stress, the longer is the region where the creep rate is almost constant. Summary data from the creep tests of the as-extruded material are listed in Table I. The steady-state creep data of the as-extruded material for a range of stresses at a constant temperature follow a creep equation of the type creep rate = K&apos; = A exp (&) [11 where A and B are constants, k is Boltzmann&apos;s constant, T is the absolute temperature, and a the stress. The standard error of estimate of the data received is less than one order of magnitude. As shown in Fig. 2, if one compensates the creep-rate data for the effect of temperature over the range of test temperature, the steady-state creep data roughly follow a creep equation of the type Temperature compensated creep rate = K* = A exp

Jan 1, 1960

Jan 1, 1955

The paper relates to the laboratory and pilot plant studies that have been carried out by Sherritt Gordon Mines Ltd., Metallurgical Research Div., in developing the ammonia pressure leach process for extracting Cu, Ni, Co, and S from high grade Ni concentrate produced from Lynn Lake ores and describes in some detail the chemistry of the process. In the leaching stage air, ammonia, and sulphide minerals react in a sequence of inter-related steps to produce soluble amines of Ni, Cu, and Co in a solution containing sulphate, thiosulphate, polythionate, and sulphamate ions and a controlled amount of free ammonia, the iron and other components of the concentrate remaining as an insoluble residue which is separated from the leach solution by filtration. The pregnant solution produced in leaching is further treated by boiling to precipitate and remove Cu as cuprous sulphide, leaving a copper-free solution with a composition suitable for subsequent precipitation of Ni and Cu by H,

Jan 3, 1955

Jan 1, 1967

By Ralph D. Parker

A STRIKING testimonial to the value of safety was contained in an ad- dress given in May, 1936, by A. R. Young, vice-president of the United States Steel Corp.: In the period from 1906 to 1935 we have spent $24,860,540 on safety work. By comparing the cost of "prevented" accidents by the cost of settling similar accidents, we found that we had made a saving of $117,224,238. Even if those figures are 50 per cent wrong, at least we got back every dollar we paid for safety and another with it. I don&apos;t think anyone has to blush before his board of directors for an investment of that kind.

Jan 1, 1937

By J. E. Johnson

Discussion of the paper of Prof. Henry M. Howe, presented in abstract by Bradley Stoughton at the Cleveland meeting, October, 1912, and printed in Bulletin No. 71, November, 1912, pp. 1181 to 1227. J. E. JOHNSON, JR., Ashland, Wis. :-This material is largely beyond the understanding of most of us practical men, but there are certain portions of that diagram that are of enormous importance. We have been conducting a, very extensive investigation of the quality of charcoal-iron and of all iron, and we have found that this eutectic point here (indicating on chart) is a sort of balance point between the good irons and the bad ones, and I have some slides to show what practical results we have found depending on this point here on the d diagram; and it would be a mistake for men who were -concerned with operation and were getting practical results, to think that these things are of no importance. They are exceedingly hard to understand, and I confess that a great deal of them is beyond me, but there is no doubt that the quality of iron depends to an enormous extent on the location of the carbon content of the iron to the right and left of this point, and the position of that point is dependent upon the silicon, and I wish to make a plea to the practical and operating members of the Institute not to disregard this material on account of its being highly scientific, because I hope to show later that there are matters of the highest practical importance that depend directly upon certain portions of this diagram. HENRY D. HIBBARD, Plainfield, N. J. :-T understand that washed metal, which, is practically pure iron and carbon, does not solidify at one instant, is cast-iron does, but passes through a mushy stage. That has been an enigma as to how and why it did so, and possibly some light might be thrown on it in this connection. BRADLEY STOUGHTON, New York, N. Y.:-If Wittorff&apos;s propositions are accepted, washed metal containing more than 4.1 per cent. of carbon would begin to solidify as liquid plus Fe4C

Dec 1, 1912