Search Documents

By R. B. Schluter, M. M. Fine

Processes for manufacturing prereduced pellets have heretofore required temperatures of 2100°F or higher. Sulfides will accelerate the liquid-phase sintering of metallic iron, yet do not deter the reduction of iron oxides. The sulfides may be introduced as gases to the kiln atmosphere or as solids in the re-ductants. The net result is that well metallized iron pellets with good crushing strength can now be produced at a little over 1800°F. One of the most persistent topics at technical gatherings and in the recent scientific press has been the reduction of iron ore. In May 1960, a symposium on the subject was sponsored by the Electrochemical Society. The proceedings, comprising two dozen papers, were later published.' More recently, in November 1966, a similar gathering took place at Michigan Technological University, Houghton, Mich. The latest meeting was the International Congress on Production and Utilization of Reduced Materials at Evian, France, in May 1967. If the volume of literature, symposia and conferences is a measure of industry concern, then the current interest in reduction must be at a high level. Barrett,2 one of the early pioneers, stated some years ago that "The history of sponge iron has been so discouraging that many men in the iron and steel industry are violently opposed to giving it any further consideration." In spite of the "violent opposition" noted by Barrett, research people in and out of the industry continue to be attracted by the elusive prospect of uncovering a simple, viable means of direct reduction. Wild,3 one of the speakers at Evian, listed no less than 48 direct reduction processes (laboratory, pilot plant and commercial). Some of these were of historical interest only, but many others had resulted from developments within this decade. The previous big thrust into direct reduction occurred under the artificial impetus of a wartime economy (World War 11) and was largely an effort to provide more melting stock without coke ovens and blast furnaces. The present-day inquiry is proceeding at a more leisurely pace and the emphasis is different. For one thing, there is much less anxiety to circumvent the blast furnace. On the contrary, a whole new research endeavor has grown from the discovery that metallized burdens are exceptionally productive.4 Although the search for a melting stock

Jan 1, 1970

By Samuel S. Wyer

THE following description of methods for conducting gas-producer tests is probably the first attempt to give the subject an analytical, thorough and comprehensive treatment. In some cases where tests have been made, the methods have been so unsystematic and ambiguous that it has been impossible to secure comparable results. To eliminate this difficulty, the following provisional code of gas-producer tests-which has some resemblance to the code of boiler-trials of the American Society of Mechanical Engineers-has been developed. The primary object in testing a gas-producer is to determine whether the producer is working satisfactorily or, what is the same. thing, to see if the efficiency is as high as it should be with the type of producer in question, and also to find out if the composition of the resulting gas is adapted to the work it has to do. In order that the test shall be of any value, it must be thorough and comprehensive, and must be conducted with skill and care. When so conducted, the test will reveal the economy of the producer; and, by making suitable changes, the efficiency will often be increased very much. As a result of the tests made by Jenkins, 1 the efficiency was raised from 56.2 to 71.2 per cent. This shows the large saving that may frequently be made in the fuel-consumption by studying the results of a careful test.. The log of the test, given in Fig. 1, shows that, just as soon as the temperature became regular, the percentage of CO, decreased and that of CO increased.

Mar 1, 1905

By M. C. Flemings, T. S. Piwonka

Pore formation is examined analytically in cellu-larly solidified single crystals, in cylindrical castings of pure metals and alloys, and in unidirectionally solidified castings. Effects are considered of fluid flow. dissolved gas, and surface tension. Experimental results show that flow through a partially solid "mushy" aluminum alloy obeys relations similar to those applicable for flow through other types of porous beds. Flow rate is proportional to the square of the fraction liquid (fL) for fL less than 0.3. Results indicate models chosen for mathematical description of pore formation in alloy solidification are valid. ONE of the solidification variables which is influential in determining mechanical properties of castings and of wrought material produced from cast ingots is porosity. This porosity may result from shrinkage, dissolved gases, or a combination of both, and may take the form of either macroscopic pores in localized areas of the casting or microporosity evenly distributed throughout large areas of the casting. In alloys which freeze over a range of temperatures some microporosity is generally found after solidification. There has been much discussion as to whether the micropores are caused primarily by shrinkage, by gas, or by a combination of both.'-3 There has, however, been little experimental or analytical work performed to delineate the relative contributions of shrinkage and gas in causing microporosity or to quantitatively describe the influence of processing variables on microporosity. Porosity other than microporosity (e.g., center line shrinkage) has also received only limited quantitative treatment.495 The aim of this work is to examine analytically the general problem of pore formation in solidification and to perform limited confirmatory experiments. Consideration is first given to shrinkage porosity in pure and nearly pure metals (shrinkage in cellular growth, centerline shrinkage in cylinders). Next, a discussion is given of formation of shrinkage-caused microporosity in unidirectional solidification and in "mushy" solidification. Finally, influences of dissolved gas and surface tension on microporosity are examined. Numerical results are given for aluminum and an aluminum alloy. Typical examples of microporosity are shown in Figs. 1 to 3, for 1) cellularly solidified aluminum, 2) sand-cast aluminum alloy, and 3) low alloy steel. SHRINKAGE POROSITY IN PURE AND NEARLY PURE METALS 1) Cellular Growth. In cellular freezing of an impure liquid, liquid grooves may exist over a considerable length of the growing crystal.6 The cross-sectional area of the grooves decreases with increasing distance from the cell tips; the root of the groove is blunt if the liquid at this point reaches eutectic composition. As a result of volume contraction during solidification, flow occurs down the groove, parallel to the growth direction; hence, there must be a pressure drop from the groove entrance to points within the groove. The geometry of the groove is simplified to that of a circular cylinder of radius r and length L, Fig. 4, L » r, and a simple and useful limiting case is obtained. This is that, in the circular cylinder freezing at constant velocity, the pressure at the root of the groove is lower than that pressure at radius r in grooves of other geometries where r decreases continuously to a lower limit at L. As discussed below, a pore resulting from a given pressure difference

Jan 1, 1967

One of the newest and most modern surface mining operations in the East is gathering steam at Mapco Inc.'s Martiki mine in anticipation of yielding 2.7 million tons (3 million st) of coal annually.

Jan 10, 1977

By Nicholas J. Grant, Oliver Preston

PUBLICATION of data by Irmann' indicating outstanding thermal stability and elevated-temperature strength properties in a sintered aluminum powder product (SAP) stimulated interest in the strengthening of metals by means of a highly dispersed oxide phase. This material was produced by compacting, sintering and extruding a fine flake aluminum powder, resulting in a dense product containing 10 to 16 volume pct alumina, which arises from the thin oxide film on the starting powder, highly dispersed in a matrix of pure aluminum. The method of producing SAP, and the stable high-temperature properties obtained from it, introduced the possibility of developing superior materials for high-temperature service by powder metallurgy methods. The composition of the materials of this type which are presently under consideration is predominantly metallic, containing from less than 1 pct up to about 20 volume pct of the oxide. As a result, other properties of these materials, such as electrical and thermal conductivity, thermal shock resistance, and to a certain extent ductility, notch sensitivity, machinability and hot working properties, are also predominantly metallic. These alloys do not constitute, therefore, a completely new class of materials as do the cermets, but rather present a new means of modifying the properties of a metallic matrix. In this sense, SAP type alloys are more closely analogous to the alloy aging systems. While the strength properties realized in the oxide-pure metal systems at the lower temperatures are substantially less than the best attainable in the aging systems, the thermal instabilities in the latter make them of less value for use at temperature much above their optimum aging temperatures, as indicated in Fig. 1. While the means of obtaining an oxide dispersion are more difficult and costly than conventional aging processes, in the light of the as yet limited understanding of such systems there is considerable promise of improved high temperature properties arising from the thermal stability of these structures. Since the development of SAP in 1946, its properties and the properties of a series of similarAl,O,-A1 products containing from about 1 to 20 pct aluminum oxide have been fairly extensively studied and reported.'- "articular attention has been given to

Jan 1, 1958

By Charles E. Parsons

One of the greatest factors in our industrial development is cheap and convenient power. Long-distance electrical transmission has now reached such a stage that it is feasible, and practicable, to utilize the water-power of the country which was heretofore too remote for consideration. In all of the changes of energy from its various sources to its electrical applications, water-power stands pre-eminent in point of economy. Power-users the world over have endeavored to utilize this force in preference to any other, and until long-distance transmission was found practicable it seemed that every available water-power in this section of the country was doing its full share for the benefit of mankind. The success of each great industrial development has been clue in a greater part to some one man one who is just a step in advance of the rest in his particular field; one who is able to grasp a situation and foresee possibilities; and, above all, one who has that indomitable pluck and perseverance which sees in each obstacle one more step toward success. Such a mail is Eugene L. Ashley, for it was through his efforts that the development of the greatest power on the Hudson river was made possible. For several years prior to 1897 the various properties along the river between Glens Falls and Palmer Falls were in the hands of speculators. These men knew the value of waterrights, but they had not the ability to assemble the properties and finance such an undertaking. In 1897 Mr. Ashley began buying these water-rights, and, after two years of litigation, title mas secured to all of the properties along each side of the river, and the Hudson River Water-Power Company was organized to construct a dam and transmit power to the surrounding cities and villages. A contract was let for a dam

Jan 1, 1904

By M. W. Burkart, B. Lustman

Uranium-base alloys exposed to high temperature water fail either by uniform oxidation or by sudden cracking and disintegration of the metal. The disintegration results from the oxidation of a second phase which is precipitated during the corrosion process. The precipitate has been identified as a metastable hydride of uranium. URANIUM-BASE alloys consisting of the body-centered-cubic ? phase are susceptible to two different modes of corrosion failure when exposed to high temperature water. In the first process, a smooth oxide film is formed on the metal surface which continually flakes off during exposure and results in a uniform weight loss of the specimen. The oxide is present as a thin, adherent layer whose thickness remains approximately constant. As the metal oxidizes during corrosion, a nonadherent layer is built up on this film and continually sloughs off. Coincident with the uniform corrosion just mentioned, another process occurs which eventually leads to failure of the metal by cracking and general disintegration. The failure takes place during a relatively short time compared to the total exposure. To distinguish this type of failure from the uniform corrosion, the cracking or disintegration of the metal will be referred to as discontinuous failure. For the ? phase uranium alloys it is discontinuous failure rather than uniform corrosion that limits the useful corrosion life of the alloy. This paper will be concerned primarily with the mechanism of discontinuous failure. Physical Changes During Corrosion—The alloys used in this investigation were ? phase uranium alloys containing 7 to 12 wt pet Mo or Cb. The preparation of the alloys, the method of corrosion testing, and the actual corrosion results are presented in another paper.' The ? quenching treatment consists of annealing the alloy for 24 hr at 900°C in a sealed Vycor glass tube filled with helium and then water quenching to room temperature without breaking the tube. The corrosion behavior typical of a ? phase uranium alloy is shown in Fig. 1. This specimen was a U-12 wt pet Mo alloy tested in pressurized, degassed water at 650°F. The corrosion rate was practically constant at 0.28 mg per sq cm per hr or increased slightly until about 15 to 20 days of exposure, when the onset of discontinuous failure occurred in this particular sample, and the specimen soon began to crack and disintegrate. The simultaneous increase in the observed corrosion rate is a result of the increased area of exposure due to cracking of the specimen. The microstructure of a specimen that failed by cracking is shown in Fig. 2. The presence of a plate-like precipitate can readily be seen. Metallographic examination of corrosion specimens reveals that the onset of discontinuous failure is always preceded by the formation of a plate-like second phase in the ? uranium matrix. Hydrogen analyses of specimens periodically withdrawn from corrosion test reveal that the hydrogen content of the alloy increases on exposure to the high temperature water, as shown in Fig. 3. The hydrogen is available as a corrosion product resulting from the formation of UO2 by the reaction of the alloy with water. Specimens analyzed just prior to discontinuous failure contained as much as 1200 ppm H, whereas the plate-like phase appears to precipitate out at a hydrogen concentration of between 10 and 25 ppm. The observed increase in hydrogen content prior to and during the formation of the plate-like precipitate suggests that this constituent may be a hydride of uranium. Additional evidence linking the identity of this phase to a hydride is that it can be removed by vacuum annealing at temperatures of 100°C and above. Decomposition products of the ? phase would certainly not dissolve at such temperatures, nor could other likely products of corrosion, such as oxides, be dissipated at any of the test temperatures. The precipitation and growth of the second phase during corrosion is accompanied by an increase in hardness of the specimen. The hardness increase results from the dispersion of the harder precipitated

Jan 1, 1959

The Climax design is for the human being and his needs. Climax President Arthur Bunker has likened the high mountain operation to a giant, 250 million tons in weight, and 12 thousand feet high. No matter how huge or complicated the plant, the design must assure efficient operation by its human operators. By the same token, living and playing facilities must be designed for fullest satisfaction in use-else the capital investment is not justified. Even the product, molybdenum, finds its application through the ever growing demands of a highly industrialized society of humans. Research in Climax Laboratories, in tune with our technical age, helps guide molybdenum to its maximum use for society.

Aug 1, 1955

By Robert Goodrich

EXPERIMENTS ON A PORPHYRY COPPER ORE FROM BISBEE, ARIZ. THIS research was done partly in the non-ferrous laboratory of the Department of Metallurgy of Columbia University, under the direction of Dr. Edward F. Kern, and completed elsewhere. Acknowledgment is due to Prof. Arthur L. Walker, Dr. Edward F. Kern and Dr. William Campbell of the Department of Metallurgy, for their kind advice and for the inspiration derived from their instruction. This report is given under the following heads: Petrographic Description (Microscopic Study); Sampling and Preparing Ore for Treatment; Chemical Analysis; Treatment of Ore. PETROGRAPHIC DESCRIPTION Texture: Variable. Fine to medium mixed aggregate. Original structure: Obscure. Secondary structure: Fractured; healed.

Jan 8, 1915

By W. L. Saunders

It has been estimated that the value of the mineral products of the United States is about $2,000,000,000 a year; that about $25,000,000 is expended annually for explosives and that about double this sum is paid in wages where blasting is done. The value of the mineral products does not adequately express the importance of the industry involved in the excavation of rock and ore because of the enormous sums of money expended in tunnel driving, in quarries, and in open-cut excavation generally. We know that the Catskill Aqueduct in the neighborhood of New York, which is now nearing completion, has cost some $165,000,000 and that about one-third of this may be rated as rock excavation. These illustrations are given in order to call attention to the great importance of an industry the extension and development of which in our industrial life depend so much upon the economics of rock drilling. Reference has been made to the new Catskill Aqueduct. There are three aqueducts leading into New York, each built at periods separated by some 20 years of time. The first one, known as the Old Aqueduct, conveys the waters of the Croton river to New York City in a manner which reminds one of the old Roman aqueducts, the ruins of which are still in evidence. The engineers who laid out these old conduits sought to direct their lines around the hills and into the valleys, at all times avoiding the rock. When it was necessary to cross a river or a deep ravine, a bridge or causeway was constructed. High Bridge, over the Harlem river, is an arched masonry viaduct differing in no essential features from the aqueducts of the Romans. When the second Croton Aqueduct was built, about the year 1890, the art of drilling rock had been so far perfected, and the use of explosives, through the invention of dynamite, had become so general, that this waterway was planned and executed on straight lines, following rather than avoiding the rock. The second Croton Aqueduct is a tunnel through rock, about 32 miles in length; material gneiss, almost as hard as granite. Its construction was made practicable by sinking

Jan 1, 1914

By John Burns

THE object of this chapter is to present data concerning the effect of the introduction of relatively slight amounts of carbon and nitrogen into supersaturated solution in iron. The study is confined to the alpha temperature range of both the Fe-C and Fe-N systems. The age-harden-ing characteristics of these two systems are considered. These data are compared to those of other age-hardening alloy systems and a "classifica-tion" is essayed. A.-RELATION OF LATTICE PARAMETER AND ELECTRICAL CONDUCTIVITY TO CHANGES IN PHYSICAL PROPERTIES DUE TO AGING OF FE-C ALLOYS Since Whiteley1 in 1927 showed that some of the iron carbide that is normally present in slowly cooled low carbon-iron alloys disappears on rapid cooling from just below the A1 point, interest has been manifested in the possibilities of age-hardening in these alloys. Masing and Koch,2 and at the same time and independently, W. Koster,3 proved these alloys to be age-hardenable. A. A. Bates4 a little later also published an interesting paper on changes in physical properties due to the aging of low-carbon steels. Many other papers have appeared showing changes in physical properties in specific instances due to this same phenomenon.

Jan 1, 1934

By J. L. Rodda

THE desirability of a uniformly sized abrasive for metallographic polishing has probably been recognized in a general way for a long time. Certainly all metallographers have recognized the damage that can be done to a polished surface by a piece of grit, especially if one of the softer metals, such as zinc or aluminum, is being polished. It is to be doubted, however, whether many metallographers have had any adequate idea of the particle size of the abrasives they were using or of the range of sizes encountered in any given grade of abrasive. At any rate, the descriptions of abrasives for metallographic work found in the literature are generally very meager. It was with the idea of securing an abrasive with a limited range of particle size that a study of this problem was commenced. Commercial abrasives, even when recommended for metallographic work, are made up of particles of varying sizes. One such abrasive contains some particles so fine that they remain in suspension for days and other particles so coarse that they settle at the rate of 3 in. per minute. It is evident that the coarsest particles are over 100 times the diameter of the smallest ones, or over 1,000,000 times the volume. The hopelessness of avoiding scratches under these conditions is evident. Vanderwilt1 has described a laboratory method for grading abrasives in which the elutriator is used. Le Chatelier's method, described by Goerens,2 also makes use of an elutriator. However, the elutriator is too slow for this purpose and requires too delicate a control for the range of sizes desired. The method of stirring up the abrasive in water, allowing it to settle for as given time, then drawing a measured depth off the top of the suspension, has been finally adopted as the simplest proce-dure. The largest particle in a given portion is. then determined by Stokes' law:3

Jan 1, 1931

By Frederic E. Carter

THERE have been many attempts to prove that platinum was known to the ancients, but since no traces of the metal have been found in the relics of early times, it must be concluded that it was not known to them. As far as records go, it was actually first discovered in the 16th century in a Spanish mine on the Pinto River in South America; from which source it received its name of Platina del Pinto (little silver from the Pinto). It was more or less of a rarity and was a subject of interest to a few chemists only, until the year 1822 when the metal was first discovered in Russia. In 1819 there were noticed in the washings of the gold sands of the southern part of the Ural Mountains, grains of a heavy white substance, but it was not until three years later that this substance was found to contain platinum. While at first the amounts of platinum brought from the Urals were meager, prospecting soon disclosed rich deposits extending over a considerable area, and nuggets from 10 to 20 lb. were by no means rare. This discovery assured to chemists an ample supply of platinum for their crucibles, etc. The ore is now found in various parts of the world but the richest deposits are still found in the Ural Mountains. The platinum of commerce is obtained entirely from alluvial deposits at depths varying from 6 to 40 ft. The sand and gravel of former river beds are subjected to a series of screenings and washings to effect the separation of the ore. Actually, probably all gold-bearing gravel beds of the world contain platinum, and it is more than likely that large quantities of platinum ore have been thrown away with the black sand washings from gold placer deposits. This is especially true of the alluvial deposits of the Pacific Coast in California and Oregon. Platinum ore is usually found in the form of rounded or flattened grains of "sand," and occasionally in irregular lumps of the size of peas. Large nuggets are very rare. The ore has a metallic luster and is distinguished by its steel gray color, but shows light gray streak when rubbed on a hard white surface; it has a high specific gravity, 16 to 19; is infusible in the hottest blast furnaces, and insoluble in any single acid. Platinum ore is a complex body consisting of the metal in combination with varying proportions of the other members of the platinum group; iridium,

Jan 1, 1928

By Leon Eliel

TEN years ago a broad knowledge of aerial mapping, coupled with a smattering of geology, qualified one to speak on the subject of the appli-cation of aerial mapping to geology. Today, with aerial maps a common tool in the hands of expert geologists on every continent throughout the world, it would be nothing short of presumptuous for the author of this paper, who is not a geologist, to give any geological statements on his own authority. Relatively, today we are only purveyors of general geological gossip, with a definite case here and there by way of illustration. But we can present a story of the really marvellous strides that have been made in the evolution of aerial mapping, built around a skeleton of geological tidbits, from which some useful conclusions may be drawn. The average geologist goes about reading his aerial maps much as one would approach the problem of deciphering a cryptogram. To begin with, typical key expressions appear in recurring sequences and under certain conditions. If once the meaning of these isolated bits of infor-mation can be ascertained, the message begins to take meaning. In a similar fashion, the geologist works out his key from aerial maps of territory with which he has some familiarity. He learns that a certain type of thin, white line may mean a vein of quartz. He sees that a certain change in the photographic tone of vegetation on the ground reflects two kinds of soils on opposite sides of, a contact. He sees that a certain type of alignment of topographical features often means a fault. He learns that by the erosion pattern .he can frequently distinguish soft formations from harder ones. And so, bit by bit, he ties together the information of the picture with his experience on the ground until he develops a reasonably creditable capacity of interpretation. Through the complete gamut of surface conditions, ranging all the way from flat, arid, exposed desert terrain to dense jungle, or rugged mountains, the evidence from which the geologist must make his inter-pretation varies with bewildering profusion. The quality of photographs which are obtainable may range from perfect pictures in the desert to almost useless smudges in the steaming jungles. One thing he has learned with certainty-the airplane carrying its mapping camera is a superb reconnaissance tool, only awaiting his ingenuity in correlating the pictures with the ground to simplify most exploratory problems.

Jan 1, 1936

APPROXIMATELY 90 per cent of the steel that is melted and refined in the United States and poured into ingots is made in basic open-hearth furnaces, as shown in Table 1-1. The annual ingot capacity of the steel industry reported January 1, 1950, by the American Iron and Steel Institute3* was 99,040,160 tons, of which the basic open-hearth process accounted for 85,896,580 tons, 86.7 per cent of the .total. The capacity of the individual furnaces varies over a wide range, a large majority falling within limits of 50 to 200 tons (Fig 1-1). Most of the units constructed [ ] since 1942 are in the larger size groups, between 175 and 225 tons capacity.

Jan 1, 1964

By G. Van Esbroeck, M. Van Weyenbergh

The copper mines of the Katanga region in the Belgian Congo lie along the same mineralized belt as those of Northern Rhodesia. There are two distinct types of deposits in that belt, the dolomitic and the quartzitic. In the dolomitic type the metallic minerals are found in a dolomitic limestone country rock. Through oxidation and enrichment, large deposits of high-grade oxidized copper ores were formed, some of which are being worked by the Union Minière du Haut Katanga. Such deposits are all in Katanga. The quartzitic deposits are found in Katanga and Northern Rhodesia. Here the primary mineralization occurred in sandstones and quartzites, in horizons stratigraphically lower than the dolomites. These rocks are not favorable to secondary enrichment and the oxidized zone is poorer than the sulphide zone, which alone contains the ore. There are also in Katanga a few ore-bearing veins. One of them is being worked in the Prince Leopold mine at Kipushi. Prince Leopold Mine The Kipushi ore body fills a fault vein and invades the wall rocks more or less extensively by metasomatic replacement. The vein strikes north-northeast and south-southwest and dips to the west. The variable dip averages 60' to a depth of 300 ft., and more uniformly 80' below 400 ft. In the upper section the average width is 200 ft. and below the width is about 150 ft. The length of the ore body is 2300 feet. The eastern side of the vein—the footwall—is dolomitic and contains irregular masses of ore sometimes extending 100 ft. or more from the main

Jan 1, 1940

By M. Van Weyenbergh, G. Van Esbroeck

The copper mines of the Katanga region in the Belgian Congo lie along the same mineralized belt as those of Northern Rhodesia. There are two distinct types of deposits in that belt, the dolomitic and the quartzitic. In the dolomitic type the metallic minerals are found in a dolomitic limestone country rock. Through oxidation and enrichment, large deposits of high-grade oxidized copper ores were formed, some of which are being worked by the Union Minière du Haut Katanga. Such deposits are all in Katanga. The quartzitic deposits are found in Katanga and Northern Rhodesia. Here the primary mineralization occurred in sandstones and quartzites, in horizons stratigraphically lower than the dolomites. These rocks are not favorable to secondary enrichment and the oxidized zone is poorer than the sulphide zone, which alone contains the ore. There are also in Katanga a few ore-bearing veins. One of them is being worked in the Prince Leopold mine at Kipushi. Prince Leopold Mine The Kipushi ore body fills a fault vein and invades the wall rocks more or less extensively by metasomatic replacement. The vein strikes north-northeast and south-southwest and dips to the west. The variable dip averages 60' to a depth of 300 ft., and more uniformly 80' below 400 ft. In the upper section the average width is 200 ft. and below the width is about 150 ft. The length of the ore body is 2300 feet. The eastern side of the vein—the footwall—is dolomitic and contains irregular masses of ore sometimes extending 100 ft. or more from the main

Jan 1, 1940

By J. H. Craig

As a result of information that the Navy Department was questioning the advisability of raising the maximum allowable exposure temperature for zinc-coated steel parts from 500 to 750 F., it was decided to make a series of high temperature tension tests on several types of uncoated and zinc-coated steels. The objective was to determine at what temperature intergranular penetration of galvanized steel by zinc might take place under conditions of rapidly applied stress and temperature. Tests were conducted in the range from room temperature to 1400 F. In this range, low-carbon and high-carbon steels did not suffer any adverse effects due to zinc coatings. In fact, at 1400 F. the zinc coatings appeared to have a beneficial effect. In stainless steel, the coating had no effect up to 1000 F. Above this temperature, the zinc coating appeared to cause a marked loss in ductility and a less pronounced loss in strength. There was no visible evidence of zinc penetration of the stainless steel structure, but it was assumed that this was the cause of the adverse effect.

Jan 1, 1945

By D. T. Novick, M. B. Bever, B. Roessler

Ordered and disordered specimens of the alloy CusAu were cold worked and then annealed at 2880, 310°, and 340°C, together with disordered unworked specimens. me resistivity decreased during annealing mainly as a result of ordering; the resistivity measurements suggest that in cold-worked specimens the growth of antiphase domains is impeded. The strength properties increased during annealing at 288 "C; in cold-worked specimens this increase was lo a level above that for cold-worked specimens which had not been annealed. X-ray diffraction showed that after annealing for a few hours at 288ºC, the long-range order increased to a constant value; additional annealing at 288ºC resulted in the growth of antiphase domains in which the degree of order was constant. Changes in peak breadth and particle size confirmed that in cold-worked specimens the major effects of cold work were not eliminated during annealing at 288 "C, although a slight recovery process occurred. When a specimen of the alloy Cu3Au is heated to a temperature below the critical temperature (388ºC), long-range ordering tends to occur in a specimen containing less than the equilibrium amount of order characteristic of that temperature Ideally, a specimen of Cu3Au contains no long-range order if it has been quenched from above the critical temperature. Long-range order is reduced by cold work. If cold-worked specimens are heated, restoration processes such as recovery and recrystallization may occur,

Jan 1, 1963

By George J. Clark

One of the major problems of operation in the anthracite industry is the disposal and handling of refuse—not because of its complexity but because of the quantity and type of material involved. It is the purpose of this paper to describe the kinds of refuse, methods of disposal, quantities of material to be handled and equipment used, together with present day application at specific operations in the Northern, Eastern Middle, Western Middle and Southern anthracite fields. For the purpose of this paper, refuse is considered to be any material that has no present or foreseeable future value and that must be handled and disposed of in the process of mining and preparing anthracite for market. Included in this classification are tunnel rock, mine rock, cleaner plant refuse, breaker refuse, old timber, ashes and silt. Disposal Methods Old timber is disposed of either by burning or by depositing on the refuse bank. Burning is preferred because timber on the refuse bank is a potential fire hazard. Ashes are deposited on a separate bank, mixed with other refuse, or flushed into old mine workings. In many places, the latter practice has caused considerable difficulty in preparation of coal mined from these areas. In depositing ashes on the surface, it is wise to refrain from mixing them with material containing coal as such contamination may prevent reclamation of the coal in future years. Tunnel work, mine rock, cleaner plant and breaker refuse compose the bulk of the material to be disposed of and handled, and are referred to collectively as "refuse" in this paper. Waste material in or adjacent to the coal beds may be removed at the working face wherever possible. This can be done in flat or lightly pitching beds, and in the Northern field represents a sizable percentage of this type of refuse handled. In the other three coal fields, this method of disposal cannot often be used. Refuse not removed at the working face is taken to the surface and generally is deposited on banks; occasionally it is crushed and flushed into old mine workings. Breaker refuse often is used for constructing berms for silt-retention basins. Disposal Problems The problem of handling refuse is different for each operation, owing to topographical conditions, quantity of material to be handled, anticipated requirements and types of equipment in use elsewhere at the operation. Preparation plants with limited refuse-disposal areas, excessive grades to reach the required elevation and long hauls to disposal areas not readily accessible require the selection of equipment to best meet the conditions. The quantity of refuse to be handled from a given amount of raw material varies considerably throughout the four fields. In mine coal, this varies from a low

Jan 1, 1949