A New Economical Method for Fabricating High-Purity Bi2O3 via Extraction-Precipitation Stripping and Post Annealing

High-purity Bi2O3 was prepared via extraction-preparation stripping method use BiCl3 leaching solution. Parameters such as oxalic acid concentration, phase ration, aging duration, feeding duration, were examined for their effect on the size and morphology of precipitate. The precipitate was characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), particle size analysis, differential scanning calorimetry and thermal gravity analysis (DSC-TGA) and infrared spectroscopy analysis (FT-IR). Bi2O3 was characterized by elements analysis, particle size analysis and scanning electron microscopy (SEM). Bi2O3 product of 680 nm was obtained using 15 g/L oxalic acid, 1/1 phase ration, 0 min aging duration, 0 min feeding duration and calcinating at 500 °C for 2 h.